CN105695701A - 一种40Cr调质工艺 - Google Patents
一种40Cr调质工艺 Download PDFInfo
- Publication number
- CN105695701A CN105695701A CN201410698899.9A CN201410698899A CN105695701A CN 105695701 A CN105695701 A CN 105695701A CN 201410698899 A CN201410698899 A CN 201410698899A CN 105695701 A CN105695701 A CN 105695701A
- Authority
- CN
- China
- Prior art keywords
- quenching
- workpiece
- temperature
- tempering
- furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种40Cr调质工艺，其特征在于，包括如下步骤，1）淬火：升温到850℃保温1小时出炉；放入300℃ -350℃的淬火油中淬火冷却，持续0.5小时，取出冷至室温。2）高温回火：淬火后工件入炉，升温至520-530℃保温1小时出炉水冷。该工艺制的40Cr各方面性能显著提高，既能提高钢材强度，又可以改善钢材韧性。
Description
技术领域
本发明涉及一种40Cr调质工艺。
背景技术
40Cr钢是机械制造业使用最广泛的钢之一。调质处理后具有良好的综合力学性能，良好的低温冲击韧性和低的缺口敏感性。钢的淬透性良好，水淬时可淬透到Ф28～60mm,油淬时可淬透到Ф15～40mm。这种钢除调质处理外还适于氰化和高频淬火处理。切削性能较好，当硬度为HB174～229时，相对切削加工性为60%。该钢适于制作中型塑料模具。
目前40Cr生产工艺复杂，没有统一标准，造成生产的40Cr质量参差不齐，很多重复工序也使得生产效率底下，加大了工人的劳动负担，同时使得产品的市场竞争力不高。
发明内容
有鉴于现有技术的上述缺陷，本发明所要解决的技术问题是提供一种40Cr调质工艺，该工艺制的40Cr各方面性能显著提高，既能提高钢材强度，又可以改善钢材韧性。
为实现上述目的，本发明提供了一种40Cr调质工艺，包括如下步骤，1）淬火：升温到850℃保温1小时出炉；放入300℃-350℃的淬火油中淬火冷却，持续0.5小时，取出冷至室温。
2）高温回火：淬火后工件入炉，升温至520-530℃保温1小时出炉水冷；
本发明的有益效果是：本发明既能提高钢材强度，又可以改善钢材韧性。
具体实施方式
本发明公开的技术方案是一种40Cr调质工艺，包括如下步骤，1）淬火：升温到850℃保温1小时出炉；放入300℃-350℃的淬火油中淬火冷却，持续0.5小时，取出冷至室温。
2）高温回火：淬火后工件入炉，升温至520-530℃保温1小时出炉水冷；
该工艺制的40Cr各方面性能显著提高，既能提高钢材强度，又可以改善钢材韧性。
以上详细描述了本发明的较佳具体实施例。应当理解，本领域的普通技术人员无需创造性劳动就可以根据本发明的构思作出诸多修改和变化。因此，凡本技术领域中技术人员依本发明的构思在现有技术的基础上通过逻辑分析、推理或者有限的实验可以得到的技术方案，皆应在由权利要求书所确定的保护范围内。
Claims (1)
1.一种40Cr调质工艺，其特征在于，包括如下步骤，1）淬火：升温到850℃保温1小时出炉；放入300℃-350℃的淬火油中淬火冷却，持续0.5小时，取出冷至室温；
2）高温回火：淬火后工件入炉，升温至520-530℃保温1小时出炉水冷。