CN105585878A - 一种水性防腐漆 - Google Patents
一种水性防腐漆 Download PDFInfo
- Publication number
- CN105585878A CN105585878A CN201410571990.4A CN201410571990A CN105585878A CN 105585878 A CN105585878 A CN 105585878A CN 201410571990 A CN201410571990 A CN 201410571990A CN 105585878 A CN105585878 A CN 105585878A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- anticorrosive paint
- emulsion
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了水性防腐漆,涉及防腐漆,解决现有水性防腐漆耐盐雾、耐老化性能低的问题。包括下列重量份的各组分:水260,分散剂1.2,润湿剂2,丙烯酸30,消泡剂1.2,颜料200,防锈料100,填料120,乳液200,成膜助剂15,增稠剂3;制备时,先将水加入反应釜内,在搅拌条件下加入润湿剂、分散剂、消泡剂;在搅拌的情况下加入颜料、填料;接着加入丙烯酸、乳液和防锈料;把料抽入研磨机进行研磨分散,研磨;在配化釜内,加入成膜助剂和增稠剂。本发明水性防腐漆耐盐雾达1000小时,防腐性能优异;具有良好的韧性及弯曲性;VOC含量仅为59.4g/L;施工清洗方便,能与各种溶剂型油漆配套使用。
Description
技术领域
本发明涉及防腐漆,具体涉及一种水性防腐漆。
背景技术
市场上现有的水性防腐漆的耐防腐性能都很低,耐盐雾仅200-300小时,耐老化仅100小时,而且其柔韧性和弯曲性都很差。
为了满足市场的需求,急需研发一种高防腐漆,但是由于成膜物得改性、颜填料的升级换代、助剂的增减等技术问题一直制约着高防腐漆的研发。
发明内容
本发明是为了解决现有水性防腐漆耐盐雾、耐老化性能低的问题,而提供了一种防腐漆,以延长耐盐雾和耐老化的时间。
本发明是通过以下技术方案实现的:
水性防腐漆,包括下列重量份的各组分:
水260,分散剂1.2,润湿剂2,丙烯酸30,消泡剂1.2,颜料200,防锈料100,填料120,乳液200,成膜助剂15,增稠剂3;
所述的成膜助剂为水性丙烯酸乳液、水性环氧乳液;
制备时,按照以下步骤:
(1)先将水加入反应釜内,在搅拌转速为200-300转/分钟的条件下加入润湿剂,搅拌3-5分钟,接着加入分散剂,搅拌3-分钟,再加入消泡剂,搅拌15-20分钟;
(2)在搅拌的情况下加入颜料、填料,以正转速500-600转/分钟的速率搅拌30分钟;
(3)接着加入丙烯酸、乳液和防锈料,将速率调整为800-1000转分钟,搅拌30分钟后停止;
(4)把料抽入研磨机进行研磨分散,研磨至细度达到20-25μm,停机;
(5)把研磨好的料抽入配化釜内,加入成膜助剂和增稠剂,调整粘度后即可出料,包装,即得成品。
本发明水性防腐漆具有以下突出的优点:
(1)耐盐雾达1000小时,防腐性能优异,而同类产品的耐盐雾达仅为200-300小时;
(2)良好的韧性及弯曲性,冲击强度达正、反冲50kg.cm,杯突≥8mm,而同类产品无此标准或仅为3-5mm;
(3)VOC含量仅为59.4g/L,远低于国家要求的150g/L,不含重金属,环保性优异;
(4)施工清洗方便,能与各种溶剂型油漆配套使用。
具体实施方式
实施例1
水性防腐漆,包括下列重量份的各组分:
水260,分散剂1.1,润湿剂1.5,丙烯酸30,消泡剂1.2,颜料200,防锈料100,填料120.,乳液200,成膜助剂15,增稠剂3.;
所述的成膜助剂为水性丙烯酸乳液;
制备时,按照以下步骤:
(1)先将水加入反应釜内,在搅拌转速为200转/分钟的条件下加入润湿剂,搅拌3分钟,接着加入分散剂,搅拌5分钟,再加入消泡剂,搅拌20分钟;
(2)在搅拌的情况下加入颜料、填料,以正转速550转/分钟的速率搅拌30分钟;
(3)接着加入丙烯酸、乳液和防锈料,将速率调整为1000转分钟,搅拌30分钟后停止;
(4)把料抽入研磨机进行研磨分散,研磨至细度达到20μm,停机;
(5)把研磨好的料抽入配化釜内,加入成膜助剂和增稠剂,调整粘度后即可出料,包装,即得成品。
实施例2
水性防腐漆,包括下列重量份的各组分:
水260,分散剂1.1,润湿剂1.5,丙烯酸30,消泡剂1.2,颜料200.0,防锈料100.0,填料120.0,乳液200.0,成膜助剂15.0,增稠剂3.2;
所述的成膜助剂为水性环氧乳液;
制备时,按照以下步骤:
(1)先将水加入反应釜内,在搅拌转速为300转/分钟的条件下加入润湿剂,搅拌4分钟,接着加入分散剂,搅拌4分钟,再加入消泡剂,搅拌15分钟;
(2)在搅拌的情况下加入颜料、填料,以正转速600转/分钟的速率搅拌30分钟;
(3)接着加入丙烯酸、乳液和防锈料,将速率调整为800转分钟,搅拌30分钟后停止;
(4)把料抽入研磨机进行研磨分散,研磨至细度达到22μm,停机;
(5)把研磨好的料抽入配化釜内,加入成膜助剂和增稠剂,调整粘度后即可出料,包装,即得成品。
实施例3
水性防腐漆,包括下列重量份的各组分:
水260,分散剂1.0,润湿剂1.5,丙烯酸30,消泡剂1.2,颜料200,防锈料100,填料120,乳液200,成膜助剂15,增稠剂3;
所述的成膜助剂为水性丙烯酸乳液;
制备时,按照以下步骤:
(1)先将水加入反应釜内,在搅拌转速为250转/分钟的条件下加入润湿剂,搅拌5分钟,接着加入分散剂,搅拌3分钟,再加入消泡剂,搅拌17分钟;
(2)在搅拌的情况下加入颜料、填料,以正转速500转/分钟的速率搅拌30分钟;
(3)接着加入丙烯酸、乳液和防锈料,将速率调整为900转/分钟,搅拌30分钟后停止;
(4)把料抽入研磨机进行研磨分散,研磨至细度达到25μm,停机;
(5)把研磨好的料抽入配化釜内,加入成膜助剂和增稠剂,调整粘度后即可出料,包装,即得成品。
Claims (1)
1.一种水性防腐漆,其特征是包括下列重量份的各组分:水260,分散剂1.2,润湿剂2,丙烯酸30,消泡剂1.2,颜料200,防锈料100,填料120,乳液200,成膜助剂15,增稠剂3;所述的成膜助剂为水性丙烯酸乳液、水性环氧乳液;制备时,按照以下步骤:
(1)先将水加入反应釜内,在搅拌转速为200-300转/分钟的条件下加入润湿剂,搅拌3-5分钟,接着加入分散剂,搅拌3-5分钟,再加入消泡剂,搅拌15-20分钟;
(2)在搅拌的情况下加入颜料、填料,以正转速500-600转/分钟的速率搅拌30分钟;
(3)接着加入丙烯酸、乳液和防锈料,将速率调整为800-1000转分钟,搅拌30分钟后停止;
(4)把料抽入研磨机进行研磨分散,研磨至细度达到20-25μm,停机;
(5)把研磨好的料抽入配化釜内,加入成膜助剂和增稠剂,调整粘度后即可出料,包装,即得成品。