CN105541229A - Vitrified brick gum adhesive - Google Patents

Vitrified brick gum adhesive Download PDF

Info

Publication number
CN105541229A
CN105541229A CN201511002691.XA CN201511002691A CN105541229A CN 105541229 A CN105541229 A CN 105541229A CN 201511002691 A CN201511002691 A CN 201511002691A CN 105541229 A CN105541229 A CN 105541229A
Authority
CN
China
Prior art keywords
vitrified brick
adhesive composition
composition according
gum adhesive
brick gum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511002691.XA
Other languages
Chinese (zh)
Inventor
于全伟
黄海涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Yawa New Building Material Co Ltd
Original Assignee
Shanghai Yawa New Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Yawa New Building Material Co Ltd filed Critical Shanghai Yawa New Building Material Co Ltd
Priority to CN201511002691.XA priority Critical patent/CN105541229A/en
Publication of CN105541229A publication Critical patent/CN105541229A/en
Pending legal-status Critical Current

Abstract

The invention discloses a vitrified brick gum adhesive, which is prepared from the following powder and liquid in parts by weight, wherein the powder is prepared from: 30-60 parts of cement, 40-70 parts of grading aggregate, 0.2-0.8 part of water-retaining agent, 0.01-0.5 part of anti-sagging agent, 0.5-2.0 parts of early strength agent, 1-5 parts of redispersible powder, 0.3-1 part of anti-cracking fiber and the liquid is prepared from: 20-40 parts of emulsion, 60-80 parts of water, 0.05-0.3 part of defoaming agent and 0.02-0.4 part of corrosion remover. By using organic combining of the ordinary Portland cement, high molecular redispersible powder and emulsion, the adhering strength of a large-sized vitrified brick is improved, the large-sized vitrified brick can be repasted to different base materials; construction performance is improved under the effect of the anti-sagging agent and operation is more convenient.

Description

Vitrified brick gum sizing agent
Technical field
The present invention relates to a kind of vitrified brick gum sizing agent.
Background technology
Vitrified brick gum sizing agent is made up of pulvis and liquor two portions; the pulverulent mixture that pulvis is made up of cement, mineral aggregate, organic admixture; liquor is by emulsion; sanitas; defoamer; water and other auxiliary agents composition, pulvis and liquor mix according to a certain percentage during use, for paving at the finishing material back sides such as large-size ceramic tile, large size vitrified tile, floor tiles.In prior art, during in particular for places such as inside and outside metope, bathrooms, because environment reason has a strong impact on the adhesive strength between ceramic tile and base material, cause cohesive strength to reduce, hollowing, cracking, ceramic tile comes off.Vitrified brick gum increases the cohesive strength between ceramic tile and base material, greatly reduces above-mentioned quality problems.
Summary of the invention
For defect of the prior art, the object of this invention is to provide a kind of vitrified brick gum sizing agent.
The present invention is achieved by the following technical solutions:
The invention provides a kind of vitrified brick gum Adhesive composition, comprise with the pulvis of parts by weight and liquor; Wherein, pulvis comprises:
Liquor comprises:
Preferably, described cement comprises ordinary Portland cement.
Preferably, the consumption of described cement is 30 ~ 50 parts.
Preferably, the consumption of described graded aggregate is 50 ~ 70 parts; The size of described graded aggregate is 50 ~ 100 orders.
Preferably, described water-holding agent comprises methyl cellulose ether or methylhydroxypropylcellulose ether.
Preferably, the consumption of described water-holding agent is 0.2 ~ 0.3 part.
Preferably, described anti-sag agent comprises inorganic laminated silicate minerals material or starch ethers.
Preferably, the consumption of described anti-sag agent is 0.04 ~ 0.2 part.
Preferably, described hardening accelerator comprises calcium formiate or Quilonum Retard.
Preferably, the consumption of described hardening accelerator is 1 ~ 1.5 part.
Preferably, described redispersable latex powder comprises VAE or vinyl acetate polymer.
Preferably, the consumption of described redispersable latex powder is 2 ~ 5 parts.
Preferably, the described anti-crack fiber lignocellulosic material that to be natural pulp make through milled processed or be the polypropylene fibre of raw material through processing treatment with polypropylene.
Preferably, described emulsion comprises benzene emulsion, styrene-butadiene emulsion or ACRYLIC EMULSION.
Preferably, described defoamer is mineral oil defoaming agent, as ADEKANATEB-943.
Preferably, the consumption of described defoamer is 0.08 ~ 0.1 part.
Preferably, described sanitas is water-borne coatings sanitas, as isothiazolinone (BIT) sanitas.
Preferably, the consumption of described sanitas is 0.12 ~ 0.2 part.
Compared with prior art, the present invention has following beneficial effect:
(1) the present invention utilizes the combination of ordinary Portland cement and polymer polymer dispersion powder end and emulsion, improves the cohesive strength with large size vitrified tile, large-sized vitrified tile can be turned and be posted on different base materials;
(2) in anti-sag agent as under the effect of starch ethers, improve workability, make it more convenient to operate.Simultaneously under the effect of hardening accelerator, the cohesive strength of tackiness agent is fast-growth, and uses brushing technique, and brushing thickness is thin, greatly saves material.Due to high by the vitrified brick gum bonding strength of two component (referring to pulvis and the liquor of vitrified brick gum sizing agent), brush and can not cause the technical problems such as the stripping of large size vitrified tile and ceramic tile come off at the back side of vitrified tile.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
embodiment 1 ~ 3
Following embodiment provides a kind of vitrified brick gum Adhesive composition, comprises with the pulvis of parts by weight calculating and liquor, specifically in table 1:
Table 1
comparative example 1 ~ 6
Following comparative example 1 ~ 6 is comparative examples of embodiment 1, provides vitrified brick gum Adhesive composition, comprises with the pulvis of parts by weight calculating and liquor, specifically in table 2 and table 3:
Table 2
Table 3
implementation result
Adopt this area common detection methods, test the performance of the resulting composition of above-described embodiment and comparative example, detected result is as shown in table 4 below:
Table 4
The detected result of comparative example 4 ~ 6 is identical with comparative example 1 ~ 3.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.

Claims (10)

1. a vitrified brick gum Adhesive composition, is characterized in that, comprises as follows with the pulvis of parts by weight calculating and liquor; Wherein, pulvis comprises:
Liquor comprises:
2. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described cement comprises ordinary Portland cement.
3. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described water-holding agent comprises methyl cellulose ether or methylhydroxypropylcellulose ether.
4. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described anti-sag agent comprises inorganic laminated silicate minerals material or starch ethers.
5. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described hardening accelerator comprises calcium formiate or Quilonum Retard.
6. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described redispersable latex powder comprises VAE or vinyl acetate polymer.
7. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, the described anti-crack fiber lignocellulosic material that to be natural pulp make through milled processed or be the polypropylene fibre of raw material through processing treatment with polypropylene.
8. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described emulsion comprises benzene emulsion, styrene-butadiene emulsion or ACRYLIC EMULSION.
9. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described defoamer comprises silicone antifoam agent.
10. vitrified brick gum Adhesive composition according to claim 1, is characterized in that, described sanitas comprises water-borne coatings sanitas.
CN201511002691.XA 2015-12-28 2015-12-28 Vitrified brick gum adhesive Pending CN105541229A (en)