CN105462496A - 一种抗菌防霉聚合物改性喷涂沥青防水涂料及其使用方法 - Google Patents
一种抗菌防霉聚合物改性喷涂沥青防水涂料及其使用方法 Download PDFInfo
- Publication number
- CN105462496A CN105462496A CN201610009429.6A CN201610009429A CN105462496A CN 105462496 A CN105462496 A CN 105462496A CN 201610009429 A CN201610009429 A CN 201610009429A CN 105462496 A CN105462496 A CN 105462496A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- component
- mouldproof
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种抗菌防霉聚合物改性喷涂沥青防水涂料及其使用方法，所述涂料由A、B两组分组成，其中，A组分为聚合物改性沥青乳液，由以下重量份数的原料制成，阴离子乳化沥青90-120份，聚合物乳液40-90份，增稠剂0.5-5份，填料10-60份；B组分为特种固化剂，由以下重量份数的原料，水100份，固化剂5-15份，抗菌剂0.5-5份。本发明还包括抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法。本发明产品具有高延伸率，高回弹，高粘接强度，抗菌防霉，且低温性能优异，施工速度快的优点，而且能够与基层紧密粘接，可有效地抵抗基层形变对材料防水性能带来的影响；同时，有效地有效的防治菌类在涂膜表面滋生，破坏防水层涂的功能以及减少抗菌剂对水体产生二次污染的可能性。
Description
技术领域
本发明涉及一种聚合物改性喷涂沥青防水涂料及其制备方法，具体涉及一种抗菌防霉聚合物改性喷涂沥青防水涂料及其制备方法。
背景技术
随着我国经济建设特别是基础设施的快速发展，对防水材料的需求量越来越大，应用范围也是迅速扩展。聚合物改性沥青具有优异的防水性能、弹性好、耐候性强、耐疲劳、抗老化等特点，并具有可靠性及经济性等优点，广泛应用于地下室底板、侧墙、地铁、隧道、屋面、垃圾填埋等防渗、防水工程。然而，随着人民生活水平的提高及工业产业的蓬勃发展，污水导致的水资源的富营养化问题越来越严重。
目前，聚合物改性橡胶沥青防水涂料由于含有高分子聚合物，长期在地下被富营养化的地下水浸泡时，细菌及藻类可能会附着在防水层上，从而导致防水涂膜受到侵蚀，甚至发生生物降解产生渗漏，失去防水效果。例如CN201210500017.4公开了污水处理厂专用喷涂速凝橡胶防水涂料，通过在沥青组分中加入防霉剂的方法使得喷涂速凝橡胶防水涂料具有防微生物滋生的功效，但该发明是将防霉剂直接添加到阴离子沥青乳液组分中，容易导致产品的不稳定，并且防霉剂在沥青乳液组分中直接接触外部水层，可能会导致水体的二次污染。
因此，针对地下防水中防水涂层需要长期与水体接触，且水体存在营养化可能的地下防水工程，亟待研制一种具有抗菌防霉作用的喷涂聚合物改性沥青防水涂料，必将在地下防水施工中具有广阔的应用前景。
发明内容
本发明所要解决的技术问题是，提供了一种能够抑制细菌生长，防止微生物在防水涂膜表面附着、滋生，防止防水材料发生生物降解，导致防水层失效的抗菌防霉聚合物改性喷涂沥青防水涂料。
本发明解决其技术问题采用的技术方案是，一种抗菌防霉聚合物改性喷涂沥青防水涂料，由A、B两组分组成，其中，A组分为聚合物改性沥青乳液，由以下重量份数的原料制成，阴离子乳化沥青90-120份(优选90-100份)，聚合物乳液40-90份(优选50-70份)，增稠剂0.5-5份(优选1-2份)，填料10-60份(优选15-40份)；B组分为特种固化剂，由以下重量份数的原料，水100份，固化剂5-15份(优选5-10份)，抗菌剂0.5-5份(优选0.5-1.5份)。
进一步，所述阴离子乳化沥青是由以下重量份数的原料制成，液体沥青40-80份(优选60-70份)，水20-50份(优选40-50份)，十二烷基苯磺酸钠或/和烷基酚聚氧乙烯醚分别0.5-2份(优选十二烷基苯磺酸钠和烷基酚聚氧乙烯醚分别1-1.5份)和1-5份聚乙烯醇(优选2-3份)。
进一步，所述聚合物乳液为氯丁乳液，丁苯乳液，苯丙乳液，丙烯酸乳液，醋酸乙烯乳液，聚醋酸乙烯酯乳液中的一种或两种以上的混合物；所述增稠剂为甲基纤维素，羟丙基甲基纤维素，羟甲基纤维素钠，羟乙基纤维素，海藻酸钠，聚丙烯酰胺，聚乙烯醇，乙烯氧化聚氨酯中的一种或两种以上的混合物。
进一步，所述填料是由以下重量份数的原料制成，水50-150份(优选80-100份)，稳定剂0.2-1份(优选0.5-0.8份)，分散剂2-10份(优选3-5份)，润湿剂1-8份(优选4-7份)，消泡剂0.5-5份(优选1-2份)，细粉料100-500份(优选200-300份)，pH调节剂0.2-3份(优选0.5-1.5份)；其中，所述细粉料为重质碳酸钙、轻质碳酸钙、钠基膨润土、高岭土、滑石粉中的一种或两种以上的混合物。
进一步，所述分散剂为水玻璃，三聚磷酸钠，三乙基己基磷酸，十二烷基硫酸钠，甲基戊醇，纤维素衍生物中的一种或两种以上的混合物；所述润湿剂为丙二醇，甘油，聚乙二醇，烷基硫酸钠，烷基硫酸钾，聚氧乙烯脂肪醇醚中的一种或两种以上的混合物；所述消泡剂为聚二甲基硅氧烷，聚氧丙烯氧化乙烯甘油醚，聚丙二醇，聚醚改性硅中的一种或两种以上混合物。
进一步，所述固化剂为氯化钙、氯化锌、氯化铵、聚合氯化铝、聚合硫酸铁和聚合硫酸铝铁中的一种或两种以上的混合物。
进一步，所述抗菌剂为纳米银溶胶，磷酸银，玻璃载银抗菌剂，磷酸镐载银抗菌剂，磷酸铜载银抗菌剂，磷酸钙载银抗菌剂，十二烷基三甲基氯化铵，十六烷基三甲基氯化铵，十二烷基二甲基苄基氯化铵，十四烷基二甲基苄基氯化铵，三甲基壳聚糖氯化铵中的一种或两种以上的混合物。
本发明进一步解决其技术问题采用的技术方案是，一种抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法，采用双组份外混式双枪头喷涂设备将A、B两组分以体积比为1-6:1经两枪头喷出，在空气中雾化混合，喷涂到基层上，形成防水涂膜。
本发明与传统聚合物改性沥青卷材相比，具有高延伸率，高回弹，高粘接强度，抗菌防霉，且低温性能优异，施工速度快的优点。本发明产品能够与基层紧密粘接，可有效地抵抗基层形变对材料防水性能带来的影响；同时，本发明将阳离子或非离子的抗菌剂引入到涂料的B组分中，喷涂施工时与A组分雾化混合迅速固化，将抗菌剂包裹在形成的防水涂膜中，有效抗菌成分逐渐从涂膜中释放出来，起到了一个缓释的作用，不仅有效保证了抗菌成分不会轻易被流水冲刷走，而且能确保防水涂膜上不会附着、滋生微生物及藻类，减少了抗菌剂对水体产生二次污染的可能。
具体实施方式
下面结合实施例对本发明进一步加以说明。
实施例1
1、A组分聚合物改性沥青乳液的制备
将30份氯丁乳液与20份丁苯乳液加入到15份填料中，搅拌均匀后加入1份增稠剂，然后加入90份从中石化购买的阴离子乳化沥青，并持续搅拌，待完全混匀后即得到产品的A组分。其中填料的制备方法如下，将稳定剂0.5份，分散剂3份，润湿剂4份，消泡剂1份，pH调节剂0.5份加入100份水中，分散均匀后加入230份高岭土，高速分散30分钟得到所用填料。
2、B组分特种固化剂的制备
将2份聚合氯化铝和8份氯化铵溶于100份水中，再加入4份十六烷基三甲基氯化铵，分散均匀后即得到产品的B组分。
3、抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法
施工时通过双头喷枪，将A、B组分以体积比为1:1在空气中雾化混合喷涂到基层上，形成防水涂膜。
将涂膜依据GB/T21353-2008进行测试，抗藻性能可达到0级，即无藻类生长。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为1.01MPa，断裂伸长率为1125％，粘接强度为0.41MPa。
实施例2
1、A组分聚合物改性沥青乳液的制备
将20份氯丁乳液与20份苯丙乳液加入到10份填料中，搅拌均匀后加入0.5份增稠剂，然后加入100份自制的阴离子乳化沥青，并持续搅拌，待完全混匀后即得到产品的A组分。
其中，填料的制备方法如下：将稳定剂0.8份，分散剂4份，润湿剂4份，消泡剂1份，pH调节剂1份加入100份水中，分散均匀后加入200份滑石粉，高速分散30分钟得到所用填料。阴离子乳化沥青的制备方法如下：将2份聚乙烯醇在50℃下溶解到50份水中，然后加入十二烷基苯磺酸钠1份与烷基酚聚氧乙烯醚1份，充分溶解后，将该皂液与65份液体沥青在胶体磨中进行高速分散研磨，并采用pH调节剂调节使pH值保持在9-10，分散均匀后制成。
2、B组分特种固化剂的制备
将3份聚合硫酸铝铁和9份氯化钙溶于100份水中，再加入2份磷酸钙载银抗菌剂，分散均匀后即得到产品的B组分。
3、抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法
施工时通过双头喷枪，将A、B组分以体积比为4:1在空气中雾化混合喷涂到基层上，形成防水涂膜。
将涂膜依据GB/T21353-2008进行测试，抗藻性能可达到0级，即无藻类生长。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为0.92MPa，断裂伸长率为1031％，粘接强度为0.62MPa。
实施例3
1、A组分聚合物改性沥青乳液的制备
将20份丁苯乳液与20份丙烯酸乳液加入到10份填料中，搅拌均匀后加入0.5份增稠剂，然后加入90份自制的阴离子乳化沥青，并持续搅拌，待完全混匀后即得到产品的A组分。
其中，填料的制备方法如下：将稳定剂0.5份，分散剂3份，润湿剂4份，消泡剂0.5份，pH调节剂1份加入100份水中，分散均匀后加入160份重碳酸钙，高速分散30分钟得到所用填料。阴离子乳化沥青的制备方法如下：将2份聚乙烯醇在50℃下溶解到50份水中，然后加入十二烷基苯磺酸钠1份与烷基酚聚氧乙烯醚1份，充分溶解后，将该皂液与65份液体沥青在胶体磨中进行高速分散研磨，并采用pH调节剂调节使pH值保持在9-10，分散均匀后制成。
2、B组分特种固化剂的制备
将8份氯化钙溶于100份水中，再加入2份纳米银溶胶，分散均匀后即得到产品的B组分。
3、抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法
施工时通过双头喷枪，将A、B组分在空气中雾化混合喷涂到基层上，形成防水涂膜。
将涂膜依据GB/T21353-2008进行测试，抗藻性能可达到0级，即无藻类生长。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为0.67MPa，断裂伸长率为1017％，粘接强度为0.74MPa。
实施例4
1、A组分聚合物改性沥青乳液的制备
将氯丁乳液30份，丁苯乳液20份，苯丙乳液20份加入到40份填料中，搅拌均匀后加入2份增稠剂，然后加入100份自制的阴离子乳化沥青，并持续搅拌，待完全混匀后即得到产品的A组分。
其中，填料的制备方法如下：将稳定剂0.8份，分散剂5份，润湿剂7份，消泡剂2份，pH调节剂1.5份加入100份水中，分散均匀后加入300份轻质碳酸钙，高速分散30分钟得到所用填料。阴离子乳化沥青的制备方法如下：将3份聚乙烯醇在50℃下溶解到50份水中，然后加入十二烷基苯磺酸钠1.5份，充分溶解后，将该皂液与70份液体沥青在胶体磨中进行高速分散研磨，并采用pH调节剂调节使pH值保持在9-10，分散均匀后制成。
2、B组分特种固化剂的制备
将10份聚合氯化铝铁溶于100份水中，再加入0.5份玻璃载银抗菌剂和0.5份磷酸银，分散均匀后即得到产品的B组分。
3、抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法
施工时通过双头喷枪，将A、B组分在空气中雾化混合喷涂到基层上，形成防水涂膜。
将涂膜依据GB/T21353-2008进行测试，抗藻性能可达到0级，即无藻类生长。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为1.22MPa，断裂伸长率为854％，粘接强度为0.55MPa。
实施例5
1、A组分聚合物改性沥青乳液的制备
将60份聚醋酸乙烯酯乳液加入到30份填料中，搅拌均匀后加入1份增稠剂，然后加入95份自制的阴离子乳化沥青，并持续搅拌，待完全混匀后即得到产品的A组分。
其中，填料的制备方法如下：将稳定剂0.6份，分散剂4份，润湿剂5份，消泡剂2份，pH调节剂1.5份加入100份水中，分散均匀后加入250份重碳酸钙和50份钠基膨润土，高速分散30分钟得到所用填料。阴离子乳化沥青的制备方法如下：将3份聚乙烯醇在50℃下溶解到50份水中，然后加入烷基酚聚氧乙烯醚1份，充分溶解后，将该皂液与70份液体沥青在胶体磨中进行高速分散研磨，并采用pH调节剂调节使pH值保持在9-10，分散均匀后制成。
2、B组分特种固化剂的制备
将8份氯化钙溶于100份水中，再加入2份纳米银溶胶，分散均匀后即得到产品的B组分。
3、抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法
施工时通过双头喷枪，将A、B组分在空气中雾化混合喷涂到基层上，形成防水涂膜。
将涂膜依据GB/T21353-2008进行测试，抗藻性能可达到0级，即无藻类生长。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为0.92MPa，断裂伸长率为487％，粘接强度为0.26MPa。
对比例1
将从市场购买的喷涂橡胶沥青防水涂料喷涂成膜后依据GB/T21353-2008进行测试，在防水膜表面出现藻类附着，面积约为13％，抗藻性能为2级。
依据GB/T16777-2008所述方法对涂膜进行力学性能测试，涂膜的拉伸强度为0.47MPa，断裂伸长率为1007％，粘接强度为0.31MPa。
Claims (10)
1.一种抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，由A、B两组分组成，其中，A组分由以下重量份数的原料制成，阴离子乳化沥青90-120份，聚合物乳液40-90份，增稠剂0.5-5份，填料10-60份；B组分由以下重量份数的原料，水100份，固化剂5-15份，抗菌剂0.5-5份。
2.根据权利要求1所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述A组分由以下重量份数的原料制成，阴离子乳化沥青90-100份，聚合物乳液50-70份，增稠剂1-2份，填料15-40份；所述B组分由以下重量份数的原料，水100份，固化剂5-10份，抗菌剂0.5-1.5份。
3.根据权利要求1或2所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述阴离子乳化沥青是由以下重量份数的原料制成，液体沥青40-80份，水20-50份，十二烷基苯磺酸钠或/和烷基酚聚氧乙烯醚分别0.5-2份和1-5份聚乙烯醇。
4.根据权利要求3所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述阴离子乳化沥青是由以下重量份数的原料制成，液体沥青60-70份，水40-50份，十二烷基苯磺酸钠1-1.5份、烷基酚聚氧乙烯醚1-1.5份和聚乙烯醇2-3份。
5.根据权利要求1或2所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述聚合物乳液为氯丁乳液，丁苯乳液，苯丙乳液，丙烯酸乳液，醋酸乙烯乳液，聚醋酸乙烯酯乳液中的一种或两种以上的混合物；所述增稠剂为甲基纤维素，羟丙基甲基纤维素，羟甲基纤维素钠，羟乙基纤维素，海藻酸钠，聚丙烯酰胺，聚乙烯醇，乙烯氧化聚氨酯中的一种或两种以上的混合物。
6.根据权利要求1或2所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述填料是由以下重量份数的原料制成，水50-150份，稳定剂0.2-1份，分散剂2-10份，润湿剂1-8份，消泡剂0.5-5份，细粉料100-500份，pH调节剂0.2-3份；其中，所述细粉料为重质碳酸钙、轻质碳酸钙、钠基膨润土、高岭土、滑石粉中的一种或两种以上的混合物。
7.根据权利要求6所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述填料是由以下重量份数的原料制成，水80-100份，稳定剂0.5-0.8份，分散剂3-5份，润湿剂4-7份，消泡剂1-2份，pH调节剂0.5-1.5份，细粉料200-300份。
8.根据权利要求1或2所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述固化剂为氯化钙、氯化锌、氯化铵、聚合氯化铝、聚合硫酸铁和聚合硫酸铝铁中的一种或两种以上的混合物。
9.根据权利要求1或2所述的抗菌防霉聚合物改性喷涂沥青防水涂料，其特征在于，所述抗菌剂为纳米银溶胶，磷酸银，玻璃载银抗菌剂，磷酸镐载银抗菌剂，磷酸铜载银抗菌剂，磷酸钙载银抗菌剂，十二烷基三甲基氯化铵，十六烷基三甲基氯化铵，十二烷基二甲基苄基氯化铵，十四烷基二甲基苄基氯化铵，三甲基壳聚糖氯化铵中的一种或两种以上的混合物。
10.一种如权利要求1-9之一所述的抗菌防霉聚合物改性喷涂沥青防水涂料的使用方法，其特征在于，采用双组份外混式双枪头喷涂设备将A、B两组分以体积比为1-6:1经两枪头喷出，在空气中雾化混合，喷涂到基层上，形成防水涂膜。