CN116807210A - 一种多功能防霉桌布 - Google Patents
一种多功能防霉桌布 Download PDFInfo
- Publication number
- CN116807210A CN116807210A CN202310381836.XA CN202310381836A CN116807210A CN 116807210 A CN116807210 A CN 116807210A CN 202310381836 A CN202310381836 A CN 202310381836A CN 116807210 A CN116807210 A CN 116807210A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- film layer
- tablecloth
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于餐具用品技术领域,尤其涉及一种多功能防霉桌布,该多功能防霉桌布包括自上而下贴合的离型膜层、粘结层、无纺布层、功能复合层、抗刮膜层、防潮膜层和防水膜层;所述功能复合层包括载体以及包覆于所述载体表面的功能材料,所述功能材料包括以下重量份数的组成:8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷。本发明所制备的桌布中各原料物质均能有效吸收潮湿空气中的水分,各组分之间特定量的组合有效起到防潮和防霉的作用,加上功能复合层之上依次设置的抗刮防潮防水层,能与外界起到更好的隔绝作用,具有优越的防虫防霉性能。
Description
技术领域
本发明属于餐具用品技术领域,尤其涉及一种多功能防霉桌布。
背景技术
随着社会经济的发展和人们生活水平的提高,人们对于日常的衣食住行要求也在提高,对于餐具用品的质量,例如覆盖于台面、桌面上用以防污或增加美观的桌布,现如今市面上的桌布多分为两大类,一类是实用性的PVC塑料桌布,另一类为装饰纺织类桌布,这两类桌布通常容易滋生细菌,且无法将美观与功能同时兼顾,餐具直接接触这些病菌,再传入到人体内,会对对身体健康造成影响。
发明内容
本发明的目的在于:提供一种多功能防霉桌布,在实现防霉的同时,还具有防潮抗菌等功能,且兼顾外观与实用性,使用寿命长,能满足广大消费者的需求。
为了实现上述目的,本发明采用以下技术方案:
根据本申请的一方面,本申请提供一种多功能防霉桌布,包括自下而上贴合的离型膜层、粘结层、无纺布层、功能复合层、抗刮膜层、防潮膜层和防水膜层;所述功能复合层包括载体以及包覆于所述载体表面的功能材料,所述功能材料包括以下重量份数的组成:8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷。
优选的,所述功能材料还包括4-6份丙烯酸聚合物、2-5份N-乙酰丙氨酸铜。
优选的,所述功能材料还包括3-5份纳米银、4-6份氯化铵。
优选的,所述功能材料还包括3-6份含氟聚合物、2-3份4,4'-二氨基二苯亚甲烷
优选的,所述重质碳酸钙颗粒粒径为1-10μm。
优选的,所述载体为活性氧化铝颗粒。
优选的,所述活性氧化铝颗粒的比表面积为1000~1100m2/g。
优选的,所述离型膜为PET膜,所述粘结层为丙烯酸酯、聚氨酯、橡胶和硅胶中的至少一种。
优选的,所述抗刮膜层为PE膜,所述防潮膜层为乙烯-乙烯醇共系物,所述防水膜层为POE膜。
前文任一段所述的多功能防霉桌布的制作方法,包括如下步骤:
S1,按照质量份数,将功能材料的各组分混合均匀,微波加热10~15min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为6000~8000CPS,面涂胶粘度为2000~4000CPS,涂层胶厚度为1.0~1.3mm,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置抗刮膜层、防潮膜层和防水层,并在无纺布的另一面依次设置粘接层和离型膜层,最后采用二浸二轧车进行轧制整理,设置温度在150~170℃,车速为10-25m/min,得到所述的一种多功能防霉桌布。
本发明的有益效果在于:本发明的功能复合层中以活性氧化铝颗粒作为载体,功能材料中添加重质碳酸钙、活性炭、硼酸、二氧化钛、吡啶硫酮脲和黄烷;各物质均能有效吸收潮湿空气中的水分,有效起到防潮和防霉的作用,且重质碳酸钙价格低廉,资源丰富,粉体自分散性好,改性效果良好,黄烷通过使细胞内部渗透压增大,使微生物丧失活力,达到很好的抗菌效果,加上功能复合层之上依次设置的抗刮防磨防水层,能与外界起到更好的隔绝作用。本申请的功能复合层具有优越的防虫防霉性能,且生产原料简单,价格低廉,所制作的桌布不仅能兼顾美观与实用性,使用寿命也长,可以满足市场需求。
附图说明
图1是本发明实施例1的结构示意图。
其中:1-离型膜层,2-粘结层,3-无纺布层,4-功能复合层,5-抗刮膜层,6-防潮膜层,7-防水膜层。
具体实施方式
为使本发明的技术方案和优点更加清楚,下面将结合具体实施例,对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
根据本申请的一方面,本申请提供一种多功能防霉桌布,包括自下而上贴合的离型膜层、粘结层、无纺布层、功能复合层、抗刮膜层、防潮膜层和防水膜层;功能复合层包括载体以及包覆于载体表面的功能材料,功能材料包括以下重量份数的组成:8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷,各物质均能有效吸收潮湿空气中的水分,有效起到防潮和防霉的作用,且重质碳酸钙价格低廉,资源丰富,粉体自分散性好,改性效果良好,吡啶硫酮脲作为常规的防霉剂,与功能材料的其他组分组合达到更好的抗菌效果,黄烷通过使细胞内部渗透压增大,使微生物丧失活力,加上功能复合层之上依次设置的抗刮防磨防水层,能与外界起到更好的隔绝作用,具有优越的防虫防霉性能。
在根据本申请的一实施例中,功能材料还包括4-6份丙烯酸聚合物、2-5份N-乙酰丙氨酸铜,丙烯酸聚合物作为乳液涂料和粘合剂,能够提高材料的抗水性和抗紫外线性能,抑制细菌的生长,N-乙酰丙氨酸铜通过释放出铜离子的方式杀灭细胞,展现了强力的抗菌性能。
在根据本申请的一实施例中,功能材料还包括3-5份纳米银、4-6份氯化铵,纳米银作为一种有机防菌剂,通过放出离子和生成的氧化银和氧化氢杀灭微生物,氯化铵则通过离子释放杀灭微生物,防止细菌、黄曲霉和青霉菌的生长。
在根据本申请的一实施例中,功能材料还包括3-6份含氟聚合物、2-3份4,4'-二氨基二苯亚甲烷,加入含氟聚合物可提高材料的耐温性和防水性能,并能抑制细菌的增长,而4,4'-二氨基二苯亚甲烷作为聚氨酯发泡剂,可避免水分进入内部,防止霉菌和霉变的产生。
在根据本申请的一实施例中,重质碳酸钙颗粒粒径为1-10μm,例如可以为1μm、2μm、3μm、5μm、7μm、8μm、9μm、10μm。
在根据本申请的一实施例中,载体为活性氧化铝颗粒。
在根据本申请的一实施例中,活性氧化铝颗粒的比表面积为1000~1100m2/g。
在根据本申请的一实施例中,离型膜为PET膜,粘接层为丙烯酸酯、聚氨酯、橡胶和硅胶中的至少一种。
在根据本申请的一实施例中,抗刮膜层为PE膜,防潮膜层为乙烯-乙烯醇共系物,防水膜层为POE膜。
所述的多功能防霉桌布的制作方法,包括如下步骤:
S1,按照质量份数,将功能材料的各组分混合均匀,微波加热10~15min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为6000~8000CPS,面涂胶粘度为2000~4000CPS,涂层胶厚度为1.0~1.3mm,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置抗刮膜层、防潮膜层和防水层,并在无纺布的另一面依次设置粘接层和离型膜层,最后采用二浸二轧车进行轧制整理,设置温度在150~170℃,车速为10-25m/min,得到所述的一种多功能防霉桌布。
下面将结合具体实施例和对比例对本申请技术方案及有益效果进行详细说明,但本发明的实施方式不限于此。
实施例
如图1所示,本实施例提供的一种多功能防霉桌布,包括自下而上贴合的离型膜层1、粘结层2、无纺布层3、功能复合层4、抗刮膜层5、防潮膜层6和防水膜层7;功能复合层4包括载体以及包覆于载体表面的功能材料,功能材料包括以下重量份数的组成:8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷。
本实施例中,离型膜层1为PET膜,粘结层2为丙烯酸酯,抗刮膜层5为PE膜,防潮膜层6为乙烯-乙烯醇共系物,防水膜层7为POE膜。
其中,该多功能防霉桌布的制备方法为:
S1,按照质量份数,将8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷混合均匀,微波加热10min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为6000CPS,面涂胶粘度为2000CPS,涂层胶厚度为1.2mm,均匀涂覆于无纺布的一面,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置PE膜、乙烯-乙烯醇共系物和POE膜,并在无纺布的另一面依次设置丙烯酸酯和PET膜,最后采用二浸二轧车进行轧制整理,设置温度在160℃,车速为15m/min,得到一种多功能防霉桌布。
实施例
与实施例1不同的是,本实施例提供一种多功能防霉桌布,其制备方法为:
S1,按照质量份数,将8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲、5份黄烷、5份丙烯酸聚合物和3份N-乙酰丙氨酸铜混合均匀,微波加热11min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为6500CPS,面涂胶粘度为2500CPS,涂层胶厚度为1.3mm,均匀涂覆于无纺布的一面,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置PE膜、乙烯-乙烯醇共系物和POE膜,并在无纺布的另一面依次设置聚氨酯和PET膜,最后采用二浸二轧车进行轧制整理,设置温度在150℃,车速为10m/min,得到一种多功能防霉桌布。
实施例
与实施例1不同的是,本实施例提供一种多功能防霉桌布,其制备方法为:
S1,按照质量份数,将8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲、5份黄烷、4份纳米银和6份氯化铵混合均匀,微波加热13min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为7000CPS,面涂胶粘度为3000CPS,涂层胶厚度为1.15mm,烘干后得到功能复合层;均匀涂覆于无纺布的一面,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置PE膜、乙烯-乙烯醇共系物和POE膜,并在无纺布的另一面依次设置橡胶和PET膜,最后采用二浸二轧车进行轧制整理,设置温度在170℃,车速为13.5m/min,得到一种多功能防霉桌布。
实施例
与实施例1不同的是,本实施例提供一种多功能防霉桌布,其制备方法为:
S1,按照质量份数,将8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲、5份黄烷、6份含氟聚合物和3份4,4'-二氨基二苯亚甲烷混合均匀,微波加热14min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为7200CPS,面涂胶粘度为3300CPS,涂层胶厚度为1.05 mm,均匀涂覆于无纺布的一面,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置PE膜、乙烯-乙烯醇共系物和POE膜,并在无纺布的另一面依次设置硅胶和PET膜,最后采用二浸二轧车进行轧制整理,设置温度在165℃,车速为14.2m/min,得到一种多功能防霉桌布。
实施例
与实施例1不同的是,本实施例提供一种多功能防霉桌布,其制备方法为:
S1,按照质量份数,将8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲、5份黄烷混合均匀、4份丙烯酸聚合物和3份N-乙酰丙氨酸铜,微波加热15min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为7500CPS,面涂胶粘度为3500CPS,涂层胶厚度为1.08 mm,均匀涂覆于无纺布的一面,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置PE膜、乙烯-乙烯醇共系物和POE膜,并在无纺布的另一面依次设置丙烯酸酯和PET膜,最后采用二浸二轧车进行轧制整理,设置温度在165℃,车速为18m/min,得到一种多功能防霉桌布。
对比例1
与实施例1不同的是:
功能复合层浆料的制备:将4份轻质碳酸钙、6份木炭粉末、8份竹叶粉、3份四硼酸钠、15份二氧化硅以及6份粘结剂溶于水中,混合均匀,形成浆料A,即为功能复合层浆料。
其余同实施例1,这里不再赘述。
分别对实施例及对比例1制备的桌布进行抗菌效果和防水防潮实验,实验结果如表1~2所示。
其中:
样品前处理用70%酒精擦拭样品表面,无菌水冲洗,自然晾干。
表1和表2中未处理对照样为对比例1制备的桌布;
Uo:未处理对照样在0h接触时间洗脱后获得细菌数(cells/cm²)的绝对值;
Ut:未处理对照样在24h接触时间洗脱后获得细菌数(cells/cm²)的绝对值;
At:本申请实施1所制作的样品在24h接触时间洗脱后获得的细菌数(cells/cm²)的绝对值;
R:抗菌活性值,R= Ut- At;
※抗菌率(%)计算公式为【(B-C)/B】※100%;
B:未处理对照样接种24h的菌数的平均值(cells/cm²);
C:本申请实施例1所制作的样品样品接种24h的菌数的平均值(cells/cm²)
表2中样品为本发明实施例1所制得,其表面观察到的霉菌生长结果由放大倍数为(50X)的显微镜进行观察确认,其评价等级为:0-不生长,1-痕迹生长(小于10%),2-轻微生长(10-30%),3-中度生长(30-60%),4-严重生长(60%-全面覆盖)。
表3中将本实施例样品对比例1的样品置于水中浸泡5天,测试其防水性能与力学性能;仪器自动引导刮擦头运动,速度1 000 mm/min,划痕间距 2 mm,长度为 40 mm,一个方向至少刮擦 20 道划痕,之后将样品旋转 90 度,在垂直的方向重复上述过程,最终形成纵横交错状网格痕刮擦。通过测色仪测试划伤前和划伤后的 L*值(L*反应颜色的深浅),计算DL*, DL*值越大说明刮擦后颜色发白越明显,材料的耐刮擦效果越差。
表1--抗菌效果实验
表2--抗真菌效果实验
表3—防潮抗磨损效果实验
项目 | 拉伸强度/MPa | 冲击强度/KJ·m-2 | 浸水处理5天后拉伸强度/MPa | 浸水处理5天后冲击强度/KJ·m-2 | 刮擦前后差值DL* |
实施例 1 | 65 | 33 | 61 | 29 | 0.19 |
实施例 2 | 63 | 35 | 58 | 30 | 0.28 |
实施例 3 | 64 | 38 | 59 | 34 | 0.26 |
实施例4 | 60 | 36 | 55 | 31 | 0.30 |
实施例 5 | 59 | 34 | 54 | 28 | 0.35 |
对比例1 | 43 | 25 | 23 | 9 | 1.26 |
根据表1可以看出未处理对照样在0-24h接触时间洗脱后获得的细菌数呈直线增加,而本发明经过处理的样品在24h接触时间洗脱后获得的细菌数依旧低于对照样0h的细菌数值,且样品接种24h的菌数的平均值明显低于未处理对照样的菌数平均值;
表2中可以看到经过28天后,本发明样品表面观察到的霉菌生长情况评价等级为零,即28天后样品表面仍未生长霉菌,说明本发明桌布的防霉抗菌和防虫效果十分优越。
表3中浸水处理5天后,对比例1拉伸强度和冲击强度明显下降,出现起皱现象,而实施例制得的桌布表面无明显变化,且实施例实施例所制得的样品中防水防潮性能和抗磨擦能力十分优越。
根据上述说明书的揭示和教导,本发明所属领域的技术人员还能够对上述实施方式进行变更和修改。因此,本发明并不局限于上述的具体实施方式,凡是本领域技术人员在本发明的基础上所作出的任何显而易见的改进、替换或变型均属于本发明的保护范围。此外,尽管本说明书中使用了一些特定的术语,但这些术语只是为了方便说明,并不对本发明构成任何限制。
Claims (10)
1.一种多功能防霉桌布,其特征在于:包括自下而上贴合的离型膜层、粘结层、无纺布层、功能复合层、抗刮膜层、防潮膜层和防水膜层;所述功能复合层包括载体以及包覆于所述载体表面的功能材料,所述功能材料包括以下重量份数的组成:8份重质碳酸钙、12份活性炭、3份硼酸、15份二氧化钛、15份水、1份吡啶硫酮脲和5份黄烷。
2.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述功能材料还包括4-6份丙烯酸聚合物、2-5份N-乙酰丙氨酸铜。
3.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述功能材料还包括3-5份纳米银、4-6份氯化铵。
4.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述功能材料还包括3-6份含氟聚合物、2-3份4,4'-二氨基二苯亚甲烷。
5.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述重质碳酸钙颗粒粒径为1-10μm。
6.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述载体为活性氧化铝颗粒。
7.根据权利要求6所述的一种多功能防霉桌布,其特征在于,所述活性氧化铝颗粒的比表面积为1000~1100m2/g。
8.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述离型膜为PET膜,所述粘结层为丙烯酸酯、聚氨酯、橡胶和硅胶中的至少一种。
9.根据权利要求1所述的一种多功能防霉桌布,其特征在于,所述抗刮膜层为PE膜,所述防潮膜层为乙烯-乙烯醇共系物,所述防水膜层为POE膜。
10.根据权利要求1~9任一项所述的一种多功能防霉桌布,其特征在于,所述的制备方法包括以下步骤:
S1,按照质量份数,将功能材料的各组分混合均匀,微波加热10~15min,得到混合均匀的浆料A,往浆料A中加入载体,搅拌均匀得到浆料B,将浆料B采用浮刀式涂层机涂覆于无纺布的一面,其中,底涂层胶粘度为6000~8000CPS,面涂胶粘度为2000~4000CPS,涂层胶厚度为1.0~1.3mm,烘干后得到功能复合层;
S2,在功能复合层的表面依次设置抗刮膜层、防潮膜层和防水层,并在无纺布的另一面依次设置粘接层和离型膜层,最后采用二浸二轧车进行轧制整理,设置温度在150~170℃,车速为10-25m/min,得到所述的一种多功能防霉桌布。