CN105401249A - 一种大直径聚对苯二甲酸丁二醇酯单丝及其生产方法 - Google Patents

一种大直径聚对苯二甲酸丁二醇酯单丝及其生产方法 Download PDF

Info

Publication number
CN105401249A
CN105401249A CN201510820044.3A CN201510820044A CN105401249A CN 105401249 A CN105401249 A CN 105401249A CN 201510820044 A CN201510820044 A CN 201510820044A CN 105401249 A CN105401249 A CN 105401249A
Authority
CN
China
Prior art keywords
pbt
heat setting
temperature
silk
polybutylene terephthalate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510820044.3A
Other languages
English (en)
Inventor
马海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510820044.3A priority Critical patent/CN105401249A/zh
Publication of CN105401249A publication Critical patent/CN105401249A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种大直径聚对苯二甲酸丁二醇酯单丝及其生产方法，由下列方法制成：PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品；PBT刷丝拉伸强度范围为3.5-5cN/dtex，断裂伸长率范围为15-25%。本发明工艺简便、产品性能好。

Description

一种大直径聚对苯二甲酸丁二醇酯单丝及其生产方法
技术领域
本发明涉及一种大直径聚对苯二甲酸丁二醇酯单丝的生产方法。
背景技术
聚对苯二甲酸丁二醇酯（英文名polybutyleneterephthalate；简称PBT），是通过对苯二甲酸和1,4丁二醇缩聚制成的聚酯。最重要的热塑性聚酯。五大工程塑料之一。PBT为乳白色半透明到不透明、半结晶型热塑性聚酯。具有高耐热性、可以在140℃下长期工作，韧性、耐疲劳性、自润滑、低摩擦系数。不耐强酸、强碱，能耐有机溶剂，可燃，高温下分解。由于这些优良的性能，在汽车、机械设备、精密仪器部件、电子电器、纺织等领域得到广泛的应用，近年来在技术、应用、产能、产量等得到飞快发展，特别是在中国。
PBT树脂与其它树脂共混改性是以不损害树脂本身性能为前提，来提高缺口冲击强度，改善因成型收缩而造成的翘曲变形，提高耐热性等。国外在这方面进行了大量的工作。如：PBT/ABS，PBT/聚烯烃，PBT/PET，PBT/PET/ASA（ASA为丙烯腈-苯乙烯-丙烯腈嵌段共聚物），PBT/聚丁二烯，PBT/SMA（SMA为苯乙烯-甲基丙烯酸甲酯-丙烯腈三元接枝共聚物），PBT/PPO/弹性体，PBT/PC，PBT/EPDM，PBT/ASA等，共混改性都取得了较好的效果。
尼龙610刷丝抗磨损性能较好，具有耐高温耐酸碱等特性，但PA610的弹性不是很好，长时间工作容易变形难于恢复。
发明内容
本发明的目的在于提供一种工艺简便、产品性能好的大直径聚对苯二甲酸丁二醇酯单丝及其生产方法。
本发明的技术解决方案是：
一种大直径聚对苯二甲酸丁二醇酯单丝，其特征是：由下列方法制成：PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品；PBT刷丝拉伸强度范围为3.5-5cN/dtex，断裂伸长率范围为15-25%，直径为1-5mm。
一种大直径聚对苯二甲酸丁二醇酯单丝的生产方法，其特征是：依次包括PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品的步骤；
PBT切片干燥温度为100-120℃，干燥时间为4-12小时；纺丝温度为270-285℃；液体冷却温度为30-60℃；拉伸倍率为3.5-4.5倍；拉伸温度为70-90℃；热定型温度为100-185℃；液体冷却的冷却液为水、丙三醇、聚乙二醇或由30%水、35%丙三醇、35%聚乙二醇组成（质量百分比）的混合冷却液。
本发明工艺简便、产品性能好。
下面结合实施例对本发明作进一步说明。
具体实施方式
一种大直径聚对苯二甲酸丁二醇酯单丝的生产方法，依次包括PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品的步骤；
PBT切片干燥温度为100-120℃，干燥时间为4-12小时；纺丝温度为270-285℃；液体冷却温度为30-60℃；拉伸倍率为3.5-4.5倍；拉伸温度为70-90℃；热定型温度为100-185℃；液体冷却的冷却液为水、丙三醇、聚乙二醇或由30%水、35%丙三醇、35%聚乙二醇组成（质量百分比）的混合冷却液。
得到的PBT刷丝拉伸强度范围为3.5-5cN/dtex，断裂伸长率范围为15-25%，直径为1-5mm。
采用由30%水、35%丙三醇、35%聚乙二醇组成（质量百分比）的混合冷却液时，PBT刷丝拉伸强度、断裂伸长率性能优于采用其他冷却液30%以上。

Claims (2)

1.一种大直径聚对苯二甲酸丁二醇酯单丝，其特征是：由下列方法制成：PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品；PBT刷丝拉伸强度范围为3.5-5cN/dtex，断裂伸长率范围为15-25%，直径为1-5mm。
2.一种大直径聚对苯二甲酸丁二醇酯单丝的生产方法，其特征是：依次包括PBT切片干燥、单螺杆熔融挤出、计量供料、喷丝、液体冷却、一牵伸辊、热水拉伸、热定型1、热定型2、卷绕收丝、热定型3、缠绕、切断成刷丝产品的步骤；
PBT切片干燥温度为100-120℃，干燥时间为4-12小时；纺丝温度为270-285℃；液体冷却温度为30-60℃；拉伸倍率为3.5-4.5倍；拉伸温度为70-90℃；热定型温度为100-185℃；液体冷却的冷却液为水、丙三醇、聚乙二醇或由30%水、35%丙三醇、35%聚乙二醇组成的混合冷却液。
CN201510820044.3A 2015-11-24 2015-11-24 一种大直径聚对苯二甲酸丁二醇酯单丝及其生产方法 Pending CN105401249A (zh)