CN101974794A - 大直径高强度聚合物热熔单丝及其生产方法 - Google Patents

大直径高强度聚合物热熔单丝及其生产方法 Download PDF

Info

Publication number
CN101974794A
CN101974794A CN 201010520295 CN201010520295A CN101974794A CN 101974794 A CN101974794 A CN 101974794A CN 201010520295 CN201010520295 CN 201010520295 CN 201010520295 A CN201010520295 A CN 201010520295A CN 101974794 A CN101974794 A CN 101974794A
Authority
CN
China
Prior art keywords
polymer
fiber
core
diameter
monofilament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010520295
Other languages
English (en)
Inventor
马海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010520295 priority Critical patent/CN101974794A/zh
Publication of CN101974794A publication Critical patent/CN101974794A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种大直径高强度聚合物热熔单丝及其生产方法，纤维为皮芯型，直径为0.08～2mm；纤维的芯部聚合物为普通聚合物，纤维的皮部聚合物为比芯部聚合物熔点低的低熔点聚合物；纤维的芯部占纤维重量的50～80％，纤维的皮部占纤维重量的20～50％。本发明产品强度大，强度为5N/dtex以上；成网加工时，只需进行加热处理，即可形成粘接，十分方便。

Description

大直径高强度聚合物热熔单丝及其生产方法
技术领域：
本发明涉及一种单丝及其生产方法。
背景技术：
现有的单丝，在成网加工时，单丝的交叉点需要特殊的结合处理，加工不便，结合效果不理想。
发明内容：
本发明的目的在于提供一种结构合理，成网加工方便的大直径高强度聚合物热熔单丝及其生产方法。
本发明的技术解决方案是：
一种大直径高强度聚合物热熔单丝，其特征是：纤维为皮芯型，直径为0.08～2mm；纤维的芯部聚合物为普通聚合物，纤维的皮部聚合物为比芯部聚合物熔点低的低熔点聚合物；纤维的芯部占纤维重量的50～80％，纤维的皮部占纤维重量的20～50％。
所述普通聚合物为PET、PBT、PTT、PA6或PA66。
所述低熔点聚合物为低熔点PET、PP、PE或PA1010。
一种大直径高强度聚合物热熔单丝的生产方法，包括熔融挤出、冷却、拉伸、热定型步骤，采用双螺杆挤出机熔融挤出，冷却采用15～25℃水冷却，2道拉伸、1道热定型。
本发明产品强度大，强度为5N/dtex以上；成网加工时，只需进行加热处理，即可形成粘接，十分方便。
下面结合实施例对本发明作进一步说明。
具体实施方式：
一种大直径高强度聚合物热熔单丝，纤维为皮芯型，直径为0.08～2mm；纤维的芯部聚合物为普通聚合物，纤维的皮部聚合物为比芯部聚合物熔点低的低熔点聚合物；纤维的芯部占纤维重量的50～80％，纤维的皮部占纤维重量的20～50％。
所述普通聚合物为PET、PBT、PTT、PA6或PA66。
所述低熔点聚合物为低熔点PET、PP、PE或PA1010。
生产方法，包括熔融挤出、冷却、拉伸、热定型等常规步骤，采用双螺杆挤出机熔融挤出，冷却采用15～25℃水冷却，2道拉伸、1道热定型。

Claims (4)

1.一种大直径高强度聚合物热熔单丝，其特征是：纤维为皮芯型，直径为0.08～2mm；纤维的芯部聚合物为普通聚合物，纤维的皮部聚合物为比芯部聚合物熔点低的低熔点聚合物；纤维的芯部占纤维重量的50～80％，纤维的皮部占纤维重量的20～50％。
2.根据权利要求1所述的大直径高强度聚合物热熔单丝，其特征是：所述普通聚合物为PET、PBT、PTT、PA6或PA66。
3.根据权利要求1或2所述的大直径高强度聚合物热熔单丝，其特征是：所述低熔点聚合物为低熔点PET、PP、PE或PA1010。
4.一种大直径高强度聚合物热熔单丝的生产方法，包括熔融挤出、冷却、拉伸、热定型步骤，其特征是：采用双螺杆挤出机熔融挤出，冷却采用15～25℃水冷却，2道拉伸、1道热定型。
CN 201010520295 2010-10-26 2010-10-26 大直径高强度聚合物热熔单丝及其生产方法 Pending CN101974794A (zh)