CN105304210A - 一种银纳米线的制备方法 - Google Patents

一种银纳米线的制备方法 Download PDF

Info

Publication number
CN105304210A
CN105304210A CN201510645541.4A CN201510645541A CN105304210A CN 105304210 A CN105304210 A CN 105304210A CN 201510645541 A CN201510645541 A CN 201510645541A CN 105304210 A CN105304210 A CN 105304210A
Authority
CN
China
Prior art keywords
solution
nano
mixed solution
nano silver
silver wire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510645541.4A
Other languages
English (en)
Inventor
刘碧桃
金容�
向成单
李璐
黎军军
关有为
陈善勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing University of Arts and Sciences
Original Assignee
Chongqing University of Arts and Sciences
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing University of Arts and Sciences filed Critical Chongqing University of Arts and Sciences
Priority to CN201510645541.4A priority Critical patent/CN105304210A/zh
Publication of CN105304210A publication Critical patent/CN105304210A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种银纳米线制备方法。将聚乙烯吡咯烷酮和多元醇粉末溶解于多元醇溶液中配置成混合溶液，然后将前驱物溶解于多元醇溶液中配置成混合透明溶液，再将前驱物溶液转入分散剂混合溶液中搅拌均匀，最后将以上混合溶液转移至反应釜中，再放入设定温度150℃的烘箱保温一段时间结束反应。将Ag纳米线的母液用酒精稀释后离心分离有机物，得到长径比高，且均匀的Ag纳米线。本发明制备银纳米线的方法简单，易操作。

Description

一种银纳米线的制备方法
技术领域
本发明涉及金属纳米线的制备技术领域，具体涉及一种银纳米线制备方法。
背景技术
ITO薄膜由于其优良的导电性、高可见光透过率、高红外区反射率、与玻璃基底结合牢固、抗擦伤、良好的化学稳定性等优点，所以在光伏电池、触摸屏、LCD面板、电子纸显示器以及电致发光板等电子产品上得到广泛的应用。但是金属铟的成本高，资源稀缺，导致ITO透明导电薄膜替代产品出现。银纳米线成为ITO替代产品之一。银纳米线具有银单质优良导电的性质，且具有纳米材料的尺寸效应，而且有优异的透光性和耐曲挠性，可实现柔性、可弯折LED显示、触摸屏等。
银纳米线薄膜的研发，推动银纳米线制备成为热点。银纳米线透明导电薄膜的导电性能和透过率能达到或者超过ITO透明导电薄膜的性能成为研究难点。然而银纳米线的长径比是影响银纳米线透明导电薄膜导电性和透过率的影响因素之一。高长径比的银纳米线可以提高薄膜的性能，因此制备高长径比的银纳米线，且制备方法简单易操作，成本经济是制备银纳米线薄膜必须考虑的因素。发明发明一种操作简单，成本经济，大批量生产高长径比的银纳米线方法尤为重要。
发明内容
本发明的目的是获得一种简单易控制、成本经济的高长径比Ag纳米线制备方法。
本发明提出高长径比银纳米线的制备方法的步骤如下：
将聚乙烯吡咯烷酮和葡萄糖溶解于多元醇中配置成混合溶液，然后将硝酸银溶解于多元醇中配置成透明溶液，再将硝酸银溶液转入混合溶液中搅拌均匀，搅拌均匀后将溶液转移至反应釜中，再放入设定温度150℃的烘箱保温一段时间结束反应；
将得到的粘稠的含有Ag纳米线母液用无水乙醇稀释后离心分离有机物，得到均匀的高长径比银纳米线，分散在无水乙醇中；
附图说明
图1是本发明实施例1合成的银纳米线扫描电子显微镜(SEM)图；
图2是本发明实施例2合成的银纳米线扫描电子显微镜(SEM)图；
图3是本发明实施例3合成的银纳米线扫描电子显微镜(SEM)图；
具体实施方式
下面结合具体实施例对本发明技术作进一步说明。
实施例1：
将40ml，0.05M硝酸银/丙三醇溶液加入60ml，0.67M聚乙烯吡咯烷酮/1g葡萄糖粉末/丙三醇溶液中，搅拌混合均匀，然后将混合溶液转移至反应釜中，最后将反应釜放入温度已升至150℃的烘箱中，保温9h后取出结束实验；
将得到的粘稠的含有Ag纳米线母液用无水乙醇稀释离心分离，重复2次，得到直径30~60nm，长10~20mm的高长径比银纳米线分散在无水乙醇中；图1是本实施例得到的银纳米线的扫描电子显微镜(SEM)照片。
实施例2：
将40ml，0.05M硝酸银/丙三醇溶液加入60ml，0.67M聚乙烯吡咯烷酮/2g葡萄糖粉末/丙三醇溶液中，搅拌混合均匀，然后将混合溶液转移至反应釜中，最后将反应釜放入温度已升至150℃的烘箱中，保温9h后取出结束实验；
将得到的粘稠的含有Ag纳米线母液用无水乙醇稀释离心分离，重复2次，得到直径30~60nm，长10~20mm的高长径比银纳米线分散在无水乙醇中；图2是本实施例得到的银纳米线的扫描电子显微镜(SEM)照片。
将40ml，0.1M硝酸银/乙二醇溶液加入60ml，0.67M聚乙烯吡咯烷酮/2g葡萄糖粉末/乙二醇溶液中，搅拌混合均匀，然后将混合溶液转移至反应釜中，最后将反应釜放入温度已升至150℃的烘箱中，保温9h后取出结束实验；
将得到的粘稠的含有Ag纳米线母液用无水乙醇稀释离心分离，重复2次，得到直径30~60nm，长10~20mm的高长径比银纳米线分散在无水乙醇中；图3是本实施例得到的银纳米线的扫描电子显微镜(SEM)照片。

Claims (3)

1.一种银纳米线制备方法，其特征在于，所述方法包括下述具体步骤：
（1）将聚乙烯吡咯烷酮和多元醇粉末溶解于多元醇溶液中配置成混合溶液；（2）将前驱物溶解于多元醇溶液中配置成混合透明溶液；
（3）再将溶液（2）转入混合溶液（1）混合搅拌均匀，得到混合溶液（3）；
（4）将以上混合溶液（3）转移至反应釜中，再放入设定温度150℃的烘箱保温9h结束反应；
（5）将得到黏稠的含Ag纳米线的母液用酒精稀释后离心分离有机物，得到高长径比，且均匀的Ag纳米线。
2.按照权利要求1所述的一种银纳米线制备方法，其特征在于：聚乙烯吡咯烷酮和多元醇粉末溶解于多元醇溶液中配置成混合溶液，其多元醇粉末选择葡萄糖粉末。
3.按照权利要求1所述的一种银纳米线制备方法，其特征在于：多元醇溶液选择乙二醇或者丙三醇。
CN201510645541.4A 2015-10-09 2015-10-09 一种银纳米线的制备方法 Pending CN105304210A (zh)