CN105284566A - Planting substrate for clivia miniata regel - Google Patents

Abstract

The invention relates to the technical field of clivia miniata regel planting, particularly a planting substrate for clivia miniata regel. The planting substrate is divided into three tile layers from bottom to top: the first layer is river sand particles which are 6-8 cm thick, the second layer is a wood ball which is 5-6 cm thick, and the third layer is saw dust which is 2-4 cm thick. The planting substrate provided by the invention has a certain insect-expelling property, is good in ventilation and water permeability and high in water and nutrient retention, and vigorous growth of clivia miniata regel is facilitated. The clivia miniata regel has the advantages of being more in bud and high in survival rate.

Description

The planting matrix of a kind of kaffir lily

Technical field:

The present invention relates to kaffir lily planting technology field, be specifically related to the planting matrix of a kind of kaffir lily.

Background technology:

Kaffir lily, another name sword-like leave short-tube lycoris, great Ye short-tube lycoris are the ornamental flowers of Amaryllidaceae gentleman Cymbidium.Originate in southern South africa.Be herbaceos perennial, the florescence reaches 30-50 days, and based on Winter-Spring, New Year's Day, avoiding high light, was half heliophobous plant to also blooming around the Spring Festival, and happiness is nice and cool, avoids high temperature.Growth thermophilic is 15-25 DEG C, then stops growing lower than 5 DEG C.The soil that happiness is plump, drainage is good and damp soil, avoid dry environment.Kaffir lily has very high ornamental value, and China is everlasting greenhouse pot culture for viewing and admiring.Plant division or seminal propagation.Current kaffir lily plantation soil is conventional soil, can not meet the growth demand of kaffir lily completely, and cause kaffir lily growing way not prosperous, petal is less.

Summary of the invention:

Technical problem to be solved by this invention is to overcome the planting matrix that existing technological deficiency provides a kind of kaffir lily.

Technical problem to be solved by this invention adopts following technical scheme to realize:

A planting matrix for kaffir lily, is characterized in that, following steps for manufacturing:

(1) choose the river sand particle of diameter 0.5-1 centimetre, clean and then soak after 2 days, dry for subsequent use;

(2) dry clean for wood chip, use cracker to pulverize, size is 5-10 order, then makes medicate steep 0.5-1 hour, then carries out drying process;

(3) select the wooden ball of diameter 0.2-0.5 centimetre, then wooden ball is put into treatment fluid and soak 1-2 hour, then carry out drying and processing;

(4) planting matrix is divided into three layers of tiling from top to bottom: ground floor is river sand particle, and thickness is 6-8cm, and the second layer is wooden ball, and thickness is 5-6cm, and third layer is wood chip, and thickness is 2-4cm;

Described medicament is formed by the raw material decoction filtering of following weight portion: 30-40 part green onion black false hellebore, 23-27 part the bark of the root or stem of the tree of heaven, 1-5 part wolf's fang soap, the squeezing in August of 6-8 part, 3-5 part flower river, the gloomy number of 11-15 part, 2-4 part sulphur, 9-12 part rhizome of Chinese monkshood, 4-6 part Chinese prickly ash, 0.5-1 part pine nut, 2-5 part ground Taurus;

The raw material of following weight portion is comprised: 15-20 part sodium polyaspartate, 80-90 part water, 20-25 part potassium fulvate, 6-8 part methene succinic acid, 12-18 part boric acid, 5-10 part trace element, 1-3 part ferrous sulfate, 1-3 part zinc sulphate, 1-3 part manganese sulphate, 5-9 part carbonic hydroammonium, 2-5 part ammonium nitrate in described treatment fluid.

The present invention selects river sand as matrix, after immersion, makes it become neutral, can increase air capacity of soils and moisture capacity, the wood chip processed contains expelling parasite composition, in addition, the present invention does not need frequent fertilising yet, matrix is inherently containing certain nutrient, and the present invention has certain insect-repellent, and ventilating permeable is good, water conservation, keeping fertility are strong, be beneficial to kaffir lily robust growth, petal is many, the advantage that survival rate is high.

Embodiment:

The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.

In embodiment: the planting matrix of a kind of kaffir lily, is characterized in that, following steps for manufacturing:

(1) choose the river sand particle of diameter 0.5-1 centimetre, clean and then soak after 2 days, dry for subsequent use;

(2) dry clean for wood chip, use cracker to pulverize, size is 5-10 order, then makes medicate steep 0.5-1 hour, then carries out drying process;

(3) select the wooden ball of diameter 0.2-0.5 centimetre, then wooden ball is put into treatment fluid and soak 1-2 hour, then carry out drying and processing;

(4) planting matrix is divided into three layers of tiling from top to bottom: ground floor is river sand particle, and thickness is 6-8cm, and the second layer is wooden ball, and thickness is 5-6cm, and third layer is wood chip, and thickness is 2-4cm;

Described medicament is formed by the raw material decoction filtering of following weight portion: 35 parts of green onion black false hellebores, 25 parts of the bark of the root or stem of the tree of heaven, 4 parts of wolf's fang soaps, 7 parts of squeezinges in August, 4 parts of colored rivers, 13 parts of gloomy numbers, 3 parts of sulphur, 10 parts of rhizome of Chinese monkshoods, 5 portions of Chinese prickly ashes, 0.7 part of pine nut, 3 parts of ground Taurus;

The raw material of following weight portion is comprised: 17 parts of sodium polyaspartates, 85 parts of water, 23 parts of potassium fulvates, 7 parts of methene succinic acids, 15 parts of boric acid, 7 parts of trace elements, 2 parts of ferrous sulfate, 2 parts of zinc sulphate, 2 parts of manganese sulphates, 8 parts of carbonic hydroammonium, 3 parts of ammonium nitrate in described treatment fluid.

More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (1)

1. a planting matrix for kaffir lily, is characterized in that, following steps for manufacturing:

(1) choose the river sand particle of diameter 0.5-1 centimetre, clean and then soak after 2 days, dry for subsequent use;

(2) dry clean for wood chip, use cracker to pulverize, size is 5-10 order, then makes medicate steep 0.5-1 hour, then carries out drying process;

(3) select the wooden ball of diameter 0.2-0.5 centimetre, then wooden ball is put into treatment fluid and soak 1-2 hour, then carry out drying and processing;

(4) planting matrix is divided into three layers of tiling from top to bottom: ground floor is river sand particle, and thickness is 6-8cm, and the second layer is wooden ball, and thickness is 5-6cm, and third layer is wood chip, and thickness is 2-4cm;

Described medicament is formed by the raw material decoction filtering of following weight portion: 30-40 part green onion black false hellebore, 23-27 part the bark of the root or stem of the tree of heaven, 1-5 part wolf's fang soap, the squeezing in August of 6-8 part, 3-5 part flower river, the gloomy number of 11-15 part, 2-4 part sulphur, 9-12 part rhizome of Chinese monkshood, 4-6 part Chinese prickly ash, 0.5-1 part pine nut, 2-5 part ground Taurus;

The raw material of following weight portion is comprised: 15-20 part sodium polyaspartate, 80-90 part water, 20-25 part potassium fulvate, 6-8 part methene succinic acid, 12-18 part boric acid, 5-10 part trace element, 1-3 part ferrous sulfate, 1-3 part zinc sulphate, 1-3 part manganese sulphate, 5-9 part carbonic hydroammonium, 2-5 part ammonium nitrate in described treatment fluid.