CN105256267A - 消防喷淋用镀锌管的生产工艺 - Google Patents
消防喷淋用镀锌管的生产工艺 Download PDFInfo
- Publication number
- CN105256267A CN105256267A CN201510803796.9A CN201510803796A CN105256267A CN 105256267 A CN105256267 A CN 105256267A CN 201510803796 A CN201510803796 A CN 201510803796A CN 105256267 A CN105256267 A CN 105256267A
- Authority
- CN
- China
- Prior art keywords
- parts
- preheating
- pipeline
- pipe fitting
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种消防喷淋用镀锌管的生产工艺,包括如下步骤:1)对管件进行热浸镀锌;2)沥锌;3)冷却:以20℃/min使管件内外冷却至104℃;4)内吹:利用蒸汽进行内吹,内吹压力为1.4MPa,蒸汽的温度为113℃,时间为56秒,将管件内多余的锌粉吹入锌桶内;5)钝化成膜处理;6)表面处理;7)预热:预热温度为210℃,预热65min;8)涂塑;9)固化:管件置于245℃的烘箱中固化25min。本发明消防喷淋用镀锌管的生产工艺,其制备的管件耐蚀性强,使用寿命长。
Description
技术领域
本发明涉及消防喷淋用镀锌管的生产工艺。
背景技术
镀锌管,又称镀锌钢管,现有镀锌管的耐蚀性有待改进。
发明内容
本发明的目的在于提供一种消防喷淋用镀锌管的生产工艺,其制备的管件耐蚀性强,使用寿命长。
为实现上述目的,本发明的技术方案是设计一种消防喷淋用镀锌管的生产工艺,包括如下步骤:
1)对管件进行热浸镀锌;
2)沥锌;
3)冷却:以20℃/min使管件内外冷却至104℃;
4)内吹:利用蒸汽进行内吹,内吹压力为1.4MPa,蒸汽的温度为113℃,时间为56秒,将管件内多余的锌粉吹入锌桶内;
5)钝化成膜处理:按重量份计,所用处理液由以下组分组成:
2.6份苯甲酸,
9.3份丙烯酸树脂,
1.3份碳氮化物合金,
1.6份石膏粉,
2.8份季戊四醇,
0.9份甲酚,
0.9份二甲基乙醇胺;
6)表面处理;
7)预热:预热温度为210℃,预热65min;
8)涂塑;
9)固化:管件置于245℃的烘箱中固化25min。
本发明的优点和有益效果在于:提供一种消防喷淋用镀锌管的生产工艺,其制备的管件耐蚀性强,使用寿命长。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种消防喷淋用镀锌管的生产工艺,包括如下步骤:
1)对管件进行热浸镀锌;
2)沥锌;
3)冷却:以20℃/min使管件内外冷却至104℃;
4)内吹:利用蒸汽进行内吹,内吹压力为1.4MPa,蒸汽的温度为113℃,时间为56秒,将管件内多余的锌粉吹入锌桶内;
5)钝化成膜处理:按重量份计,所用处理液由以下组分组成:
2.6份苯甲酸,
9.3份丙烯酸树脂,
1.3份碳氮化物合金,
1.6份石膏粉,
2.8份季戊四醇,
0.9份甲酚,
0.9份二甲基乙醇胺;
6)表面处理;
7)预热:预热温度为210℃,预热65min;
8)涂塑;
9)固化:管件置于245℃的烘箱中固化25min。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.消防喷淋用镀锌管的生产工艺,其特征在于,包括如下步骤:
1)对管件进行热浸镀锌;
2)沥锌;
3)冷却:以20℃/min使管件内外冷却至104℃;
4)内吹:利用蒸汽进行内吹,内吹压力为1.4MPa,蒸汽的温度为113℃,时间为56秒,将管件内多余的锌粉吹入锌桶内;
5)钝化成膜处理:按重量份计,所用处理液由以下组分组成:
2.6份苯甲酸,
9.3份丙烯酸树脂,
1.3份碳氮化物合金,
1.6份石膏粉,
2.8份季戊四醇,
0.9份甲酚,
0.9份二甲基乙醇胺;
6)表面处理;
7)预热:预热温度为210℃,预热65min;
8)涂塑;
9)固化:管件置于245℃的烘箱中固化25min。