CN105251937A - 一种用于不锈钢铸件的铸型涂料 - Google Patents

一种用于不锈钢铸件的铸型涂料 Download PDF

Info

Publication number
CN105251937A
CN105251937A CN201510854064.2A CN201510854064A CN105251937A CN 105251937 A CN105251937 A CN 105251937A CN 201510854064 A CN201510854064 A CN 201510854064A CN 105251937 A CN105251937 A CN 105251937A
Authority
CN
China
Prior art keywords
parts
powder
paint
cast steel
casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510854064.2A
Other languages
English (en)
Other versions
CN105251937B (zh
Inventor
浦巧生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengzhou Advanced Coating Co ltd
Original Assignee
Wujiang Hydraulic Components Foundry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wujiang Hydraulic Components Foundry Co Ltd filed Critical Wujiang Hydraulic Components Foundry Co Ltd
Priority to CN201510854064.2A priority Critical patent/CN105251937B/zh
Publication of CN105251937A publication Critical patent/CN105251937A/zh
Application granted granted Critical
Publication of CN105251937B publication Critical patent/CN105251937B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于不锈钢铸件的铸型涂料，按重量份数计，包括以下组分：镁砂粉40-55份，含锆复合硅酸盐10-15份，钾长石粉10-15份，常温粘结剂1-3份，高温粘结剂1-3份，聚乙烯醇缩丁醛1-5份，聚乙二醇2-3份，锂基膨润土1-3份，表面活性剂2-5份，水16-35份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。本发明的涂料为水基涂料，不仅能有效降低生产成本，且绿色环保，再者，本涂料溶剂水的含量在20%左右，与其他水基涂料相比含水量明显少，在其他组份的协同下，本涂料的涂层不仅不会发生沾砂现象，而且自干速度快，性能优异。

Description

一种用于不锈钢铸件的铸型涂料
技术领域
本发明涉及一种用于不锈钢铸件的铸型涂料。
背景技术
根据实际生产情况估算，清理铸件的成本约占整个铸件生产成本的30%，而在涂覆涂料后，扣除涂料及施涂成本后，铸件的清理成本可降低至10%，除此经济上带来的优点外，涂覆了涂料的铸件表面质量和外观档次都有明显提高。
现有的醇基涂料虽然自干性较快，但成本高，污染较重，而水基涂料虽然绿色环保，但自干速度慢，涂层强度不够。申请号为200910105995.7号发明专利的涂料应用于不锈钢铸件中不仅自干速度较慢，对于较大型铸件还会出现不易出砂，铸件尺寸精度不够等问题。
发明内容
本发明要解决的一种技术问题是提供一种用于不锈钢铸件的铸型涂料。
为解决上述技术问题，本发明采用的技术方案是：
一种用于不锈钢铸件的铸型涂料，按重量份数计，包括以下组分：镁砂粉40-55份，含锆复合硅酸盐10-15份，钾长石粉10-15份，常温粘结剂1-3份，高温粘结剂1-3份，聚乙烯醇缩丁醛1-5份，聚乙二醇2-3份，锂基膨润土1-3份，表面活性剂2-5份，水16-35份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。
优选地，所述表面活性剂为阴离子型表面活性剂。
优选地，所述表面活性剂为木质素磺酸盐。
优选地，所述木质素磺酸盐为改性的含有酰胺结构的木质素磺酸盐。
优选地，所述常温粘结剂为硅溶胶和乳胶的混合物，所述高温粘结剂为硅酸盐类粘结剂。
优选地，所述镁砂粉、含锆复合硅酸盐、钾长石粉的平均粒度为500-1000目。
本发明所达到的有益效果：
不锈钢铸件呈碱性，而镁砂粉也呈碱性，选择以镁砂粉为主的多元复合型耐火基料显著提高了涂料的强度，避免了粘砂问题的出现，特别适合不锈钢铸件，而且耐火基料和本发明中粘结剂、悬浮剂及表面活性剂的协同作用保证了涂料的优异性能；
本发明的涂料为水基涂料，不仅能有效降低生产成本，且绿色环保，再者，本涂料溶剂水的含量在20%左右，与其他水基涂料相比含水量明显少，在其他组份的协同下，本涂料的涂层不仅不会发生沾砂现象，而且自干速度快，性能优异。
具体实施方式
下面结合具体实施例对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明实施例和对比例中的使用及喷涂方法均可用本领域公知的方法。
实施例一
按重量份数计，将以下组分制作成涂料：镁砂粉40份，含锆复合硅酸盐10份，钾长石粉10份，所述镁砂粉、含锆复合硅酸盐、钾长石粉的平均粒度为500目。常温粘结剂1份，高温粘结剂3份，聚乙烯醇缩丁醛1份，聚乙二醇2份，锂基膨润土1份，改性的含有酰胺结构的木质素磺酸盐2份，水16份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。未经煅烧或电熔处理的生料也可达到不错的结果，但熟料效果更优。
以上所称常温粘结剂为硅溶胶和乳胶的混合物，高温粘结剂为硅酸盐类粘结剂。
实施例二
按重量份数计，将以下组分制作成涂料：镁砂粉50份，含锆复合硅酸盐12份，钾长石粉15份，所述镁砂粉、含锆复合硅酸盐、钾长石粉的平均粒度为800目。常温粘结剂2份，高温粘结剂2份，聚乙烯醇缩丁醛1份，聚乙二醇3份，锂基膨润土3份，改性的含有酰胺结构的木质素磺酸盐5份，水20份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。
以上所称常温粘结剂为硅溶胶和乳胶的混合物，所述高温粘结剂为硅酸盐类粘结剂。
实施例三
一种用于不锈钢铸件的铸型涂料，按重量份数计，包括以下组分：镁砂粉55份，含锆复合硅酸盐15份，钾长石粉15份，所述镁砂粉、含锆复合硅酸盐、钾长石粉的平均粒度为800目。常温粘结剂3份，高温粘结剂3份，聚乙烯醇缩丁醛5份，聚乙二醇3份，锂基膨润土3份，改性的含有酰胺结构的木质素磺酸盐5份，水32份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。
以上所称常温粘结剂为硅溶胶和乳胶的混合物，所述高温粘结剂为硅酸盐类粘结剂。
对比例一
对比例一的各组分和含量同实施例二，唯一不同的是用刚玉粉代替镁砂粉。
对比例二
对比例二的各组分和含量同实施例二，唯一不同的是用烷基苯磺酸钠代替改性的含有酰胺结构的木质素磺酸盐。
对比例三
对比例二的各组分和含量同实施例二，唯一不同的是对比例三种不含有常温粘结剂，即硅酸盐类粘结剂。
性能测试
对实施例1-3和对比例1-3中的涂料进行性能测试，结果见下表：
效果测试包括涂层的自干时间：测试条件25℃、80%RH，涂层厚度0.6mm；
48小时悬浮率（涂料为涂覆之前），
涂层强度：测涂层自干3天后的磨损量/cm3：
编号 自干时间/min 磨损量/cm3 48小时候悬浮率
实施例一 68 0.13 98%
实施例二 72 0.16 94%
实施例三 78 0.15 96%
对比例一 70 0.32 91%
对比例二 100 0.22 80%
对比例三 93 0.29 89%
本涂料的涂层不仅不会发生沾砂现象，而且自干速度快，涂层强度高，性能优异。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。

Claims (6)

1.一种用于不锈钢铸件的铸型涂料，其特征在于，按重量份数计，包括以下组分：镁砂粉40-55份，含锆复合硅酸盐10-15份，钾长石粉10-15份，常温粘结剂1-3份，高温粘结剂1-3份，聚乙烯醇缩丁醛1-5份，聚乙二醇2-3份，锂基膨润土1-3份，表面活性剂2-5份，水16-35份，所述镁砂粉，含锆复合硅酸盐和钾长石粉均经过煅烧或电熔处理。
2.根据权利要求1所述的一种用于不锈钢铸件的铸型涂料，其特征在于，所述表面活性剂为阴离子型表面活性剂。
3.根据权利要求2所述的一种用于不锈钢铸件的铸型涂料，其特征在于，所述表面活性剂为木质素磺酸盐。
4.根据权利要求3所述的一种用于不锈钢铸件的铸型涂料，其特征在于，所述木质素磺酸盐为改性的含有酰胺结构的木质素磺酸盐。
5.根据权利要求1-4任一项所述的一种用于不锈钢铸件的铸型涂料，其特征在于，所述常温粘结剂为硅溶胶和乳胶的混合物，所述高温粘结剂为硅酸盐类粘结剂。
6.根据权利要求1所述的一种用于不锈钢铸件的铸型涂料，其特征在于，所述镁砂粉、含锆复合硅酸盐、钾长石粉的平均粒度为500-1000目。
CN201510854064.2A 2015-11-30 2015-11-30 一种用于不锈钢铸件的铸型涂料 Active CN105251937B (zh)