CN105199122A - 一种半纤维素和明胶复合生物膜的制备方法 - Google Patents
一种半纤维素和明胶复合生物膜的制备方法 Download PDFInfo
- Publication number
- CN105199122A CN105199122A CN201510744270.8A CN201510744270A CN105199122A CN 105199122 A CN105199122 A CN 105199122A CN 201510744270 A CN201510744270 A CN 201510744270A CN 105199122 A CN105199122 A CN 105199122A
- Authority
- CN
- China
- Prior art keywords
- total mass
- mixing solutions
- hemicellulose
- gelatin
- composite biological
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种半纤维素和明胶复合生物膜的制备方法。本方法选择明胶、卡拉胶、甘油、半纤维素作为原料，设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的0.2～1.0％，混合均匀。再加入甘油质量为混合溶液总质量的0.8～1.6％，半纤维素质量为混合溶液总质量0～1.2％，在70℃水浴震荡30min，超声处理去除溶液中的气泡，将配置好的溶液以定量28g制膜，测定复合生物膜的拉伸强度和断裂伸长率。本发明与现有技术相比，本发明具有以下有益效果：本发明方法在明胶中加入半纤维素组分，混合膜的机械强度得到明显改善，也更有利于其工业化应用。
Description
技术领域
本发明涉及薄膜性能领域，具体是一种半纤维素和明胶复合生物膜的制备方法。
背景技术
明胶是胶原经温和以及不可逆断裂后的主要产物，为主要原料制备的材料在生物体内水解后安全无毒，亲水性好，易被生物体所吸收。明胶能够成膜，且具有无毒、无污染、可降解的优良特性。随着绿色化工理念深入人心，胶原蛋白这类天然高分子材料所特有的优越性会越来越得到人们的青睐，其在食品、化妆品及生物医学行业中的应用前景十分广阔。但胶原蛋白膜领域也有急需改进的方面，如机械强度不高，防潮性、阻湿性较弱。
发明内容
本发明的目的是提供了一种半纤维素和明胶复合生物膜的制备方法。
本发明解决上述技术问题的技术方案如下：
一种半纤维素和明胶复合生物膜的制备方法，所述方法包括如下步骤：
1.设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的0.2～1.0％，两者混合均匀后、加入甘油和半纤维素：加入甘油质量为混合溶液总质量的0.8～1.6％，半纤维素质量为混合溶液总质量0～1.2％；得到混合溶液，混合溶液在70℃水浴震荡30min。超声处理20min去除溶液中的气泡。
2.取步骤1配置好的溶液28g，均匀涂抹在塑料板上，置于35℃烘箱中，24小时后取出制备好的复合生物膜。
3.取步骤2制备好的复合生物膜，测定复合生物膜的拉伸强度和断裂伸长率。测定结果：复合生物膜的拉伸强度为32.2～53.9MPa，断裂伸长率的变化范围为8.8～32.2％。
上述步骤1中卡拉胶质量为混合溶液总质量的0.6％，甘油质量为混合溶液总质量的1.4％，半纤维素质量为混合溶液总质量的0.9％，复合生物膜的拉伸强度为53.9MPa，断裂伸长率为32.2％。
与现有技术相比，本发明具有以下有益效果：
在明胶中加入半纤维素组分，混合膜的机械强度得到明显改善，也更有利于其工业化应用。
具体实施方式
下面结合实施例对本发明方法作进一步的详细描述。
实施例1
一种半纤维素和明胶复合生物膜的制备方法，操作步骤如下：
1.设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的0.2％，两者混合均匀后、加入甘油，加入甘油质量为混合溶液总质量的0.8％；得到混合溶液，混合溶液在70℃水浴震荡30min。超声处理20min去除溶液中的气泡。
2.取步骤1配置好的溶液28g，均匀涂抹在塑料板上，置于35℃烘箱中，24小时后取出制备好的复合生物膜。
3.取步骤2制备好的复合生物膜，测定复合生物膜的拉伸强度和断裂伸长率。测定结果：复合生物膜的拉伸强度为32.2MPa，断裂伸长率的变化范围为8.8％。
实施例2
一种半纤维素和明胶复合生物膜的制备方法，操作步骤如下：
1.设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的0.6％，两者混合均匀后加、加入甘油和半纤维素：入甘油质量为混合溶液总质量的1.2％，半纤维素质量为混合溶液总质量的0.6％；得到混合溶液，混合溶液在70℃水浴震荡30min。超声处理20min去除溶液中的气泡。
2.与实例1步骤2相同：
3.取步骤2制备好的复合生物膜，测定复合生物膜的拉伸强度和断裂伸长率。测定结果：复合生物膜的拉伸强度为46.0MPa，断裂伸长率的变化范围为22.6％。
实施例3
一种半纤维素和明胶复合生物膜的制备方法，操作步骤如下：
1.设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的1.0％，两者混合均匀后、加入甘油和半纤维素：加入甘油质量为混合溶液总质量的1.6％，半纤维素质量为混合溶液总质量的1.2％；得到混合溶液，混合溶液在70℃水浴震荡30min。超声处理20min去除溶液中的气泡。
2.与实例1步骤2相同：
3.取步骤2制备好的复合生物膜，测定复合生物膜的拉伸强度和断裂伸长率。测定结果：拉伸强度和断裂伸长率。复合生物膜的拉伸强度为53.9MPa，断裂伸长率的变化范围为32.2％。
需要说明的是，以上列举的仅是本发明的若干个具体实施例。显然，本发明不限于以上实施例，还可以有许多变形。本领域的普通技术人员能从本发明公开的内容直接导出或联想到的所有变形，均应认为是本发明的保护范围。
Claims (2)
1.一种半纤维素和明胶复合生物膜的制备方法，其特征在于该方法通过在明胶中加入半纤维素组分，复合生物膜的机械强度得到明显改善，所述方法包括：
(1)设定混合溶液总质量为50g，加入明胶质量为混合溶液总质量的6％，卡拉胶质量为混合溶液总质量的0.2～1.0％，两者混合均匀后、加入甘油和半纤维素：甘油质量为混合溶液总质量的0.8～1.6％，半纤维素质量为混合溶液总质量0～1.2％；得到混合溶液，混合溶液在70℃水浴震荡30min，超声处理20min去除溶液中的气泡；
(2)取步骤(1)配置好的混合溶液28g，均匀涂抹在塑料板上，置于35℃烘箱中，24小时后取出制备好的复合生物膜；
(3)取步骤(2)制备好的复合生物膜，测定复合生物膜的拉伸强度和断裂伸长率，测定结果：复合生物膜的拉伸强度为32.2～53.9MPa，断裂伸长率的变化范围为8.8～32.2％。
2.根据权利要求1所述的一种半纤维素和明胶复合生物膜的制备方法，其特征在于，所述步骤(1)中卡拉胶质量为混合溶液总质量的0.6％，甘油质量为混合溶液总质量的1.4％，半纤维素质量为混合溶液总质量的0.9％，复合生物膜的拉伸强度为53.9MPa，断裂伸长率为32.2％。