CN105128469A - 防静电超轻离型力的功能薄膜 - Google Patents

防静电超轻离型力的功能薄膜 Download PDF

Info

Publication number
CN105128469A
CN105128469A CN201510222834.1A CN201510222834A CN105128469A CN 105128469 A CN105128469 A CN 105128469A CN 201510222834 A CN201510222834 A CN 201510222834A CN 105128469 A CN105128469 A CN 105128469A
Authority
CN
China
Prior art keywords
mold
superlight
antistatic
ultralight
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510222834.1A
Other languages
English (en)
Inventor
彭权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Dingli Film Technology Co Ltd
Original Assignee
Dongguan Dingli Film Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Dingli Film Technology Co Ltd filed Critical Dongguan Dingli Film Technology Co Ltd
Priority to CN201510222834.1A priority Critical patent/CN105128469A/zh
Publication of CN105128469A publication Critical patent/CN105128469A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防静电超轻离型力的功能薄膜，其包括PET膜层、防静电涂层和超轻离型涂层，所述PET膜层、防静电涂层、超轻离型涂层按照从上至下的顺序依次贴合；本发明结构设计合理，巧妙将防静电涂层、超轻离型涂层和PET膜层相结合，并通过合理优化防静电涂层和超轻离型涂层的组份配比，不仅具有较好的防静电效果，还可以加固离型涂层的固化效果，附合效果好，而且具有超轻离型力1～3g，可以满足客户模切分离的效果，易于加工，有效提高加工精度；另外整体结构紧凑、配方合理，方便生产制造，提高生产效率，实用性强，利于广泛推广应用。

Description

防静电超轻离型力的功能薄膜
技术领域
本发明涉及离型薄膜技术领域，特别涉及一种防静电超轻离型力的功能薄膜。
背景技术
离型膜是指表面具有分离性的薄膜，离型膜与特定的材料在有限的条件下接触后不具有粘性，或轻微的粘性。离型膜又称剥离膜、隔离膜、分离膜、阻胶膜、离形膜、薄膜、塑料薄膜、掩孔膜、硅油膜、硅油纸、防粘膜、型纸、打滑膜、天那纸或离型纸等。
目前离型膜广泛应用于电子胶粘剂、印刷线路板、手机等领域，其独特的低表面涨力使其自身不易附着其他材料。
随着手机产业的高速技术更新替换，手机部件保护膜的模切精度和过程防静电功能也越来越高，鉴于模切生产过程中对产品的防静电和超轻离型力两者并用的迫切需求，促使国内生产离型膜的制造商投入重金和技术力量进行研发。
发明内容
针对上述不足，本发明目的在于提供一种结构设计巧妙、合理，具有防静电功能，固化效果好，且易于加工的防静电超轻离型力的功能薄膜。
本发明为实现上述目的，所提供的技术方案是：一种防静电超轻离型力的功能薄膜，其包括PET膜层、防静电涂层和超轻离型涂层，所述PET膜层、防静电涂层、超轻离型涂层按照从上至下的顺序依次贴合。
作为本发明的一种改进，所述防静电涂层的电阻值为105～1012欧姆，其由以下重量份数的组份组成：导电液0.9～1.1份，异丙醇3.5～4.5份。较佳的，导电液为1份，异丙醇4为份，效果更佳。
作为本发明的一种改进，，所述防静电涂层的厚度为1～2微米。
作为本发明的一种改进，所述超轻离型涂层由以下重量份数的组份组成：硅油900～1100份，胶联剂30～40份，锚固剂13～18份，剥离剂40～60份，固化剂13～18份，乙酯2500～3500份，丁酮1800～2200份。较佳的，硅油1000份，胶联剂36份，锚固剂16份，剥离剂50份，固化剂16份，乙酯3000份，丁酮2000份，效果更佳。
作为本发明的一种改进，所述超轻离型涂层的厚度为1～2微米。
作为本发明的一种改进，所述PET膜层的厚度为25～125微米。
本发明的有益效果为：本发明结构设计合理，巧妙将防静电涂层、超轻离型涂层和PET膜层相结合，并通过合理优化防静电涂层和超轻离型涂层的组份配比，不仅具有较好的防静电效果，还可以加固离型涂层的固化效果，附合效果好，而且具有超轻离型力1～3g，可以满足客户模切分离的效果，易于加工，有效提高加工精度；另外整体结构紧凑、配方合理，方便生产制造，提高生产效率，实用性强，利于广泛推广应用。
附图说明
图1是本发明的截面结构示意图。
具体实施方式
实施例1：参见图1，本发明实施例提供一种防静电超轻离型力的功能薄膜，其包括PET膜层1、防静电涂层2和超轻离型涂层3，所述PET膜层1、防静电涂层2、超轻离型涂层3按照从上至下的顺序依次贴合。本发明结构设计合理，巧妙将防静电涂层2、超轻离型涂层3和PET膜层1相结合，不仅具有较好的防静电效果，还可以加固离型涂层的固化效果，附合效果好，而且具有超轻离型力1～3g，可以满足客户模切分离的效果，易于加工，有效提高加工精度。
具体的，所述防静电涂层2的电阻值为105～1012欧姆，其由以下重量配比的组份组成：导电液1kg，异丙醇4kg。
所述超轻离型涂层3由以下重量配比的组份组成：硅油1kg，胶联剂36g，锚固剂16g，剥离剂50g，固化剂16g，乙酯3kg，丁酮2kg。
较佳的，所述超轻离型涂层3的厚度为1～2微米,离型力为1～3g。所述PET膜层1的厚度为25～125微米。所述防静电涂层2的厚度为1～2微米。
实施例2，本发明实施例提供一种防静电超轻离型力的功能薄膜，其与实施例1基本相同，区别在于防静电涂层2和超轻离型涂层3的组份不同，具体为：
所述防静电涂层2由以下重量配比的组份组成：导电液0.9kg，异丙醇4.5kg。
所述超轻离型涂层3由以下重量配比的组份组成：硅油1.1kg，胶联剂30g，锚固剂15g，剥离剂40g，固化剂18g，乙酯2500kg，丁酮2.2kg。
实施例3，本发明实施例提供一种防静电超轻离型力的功能薄膜，其与实施例1基本相同，区别在于防静电涂层2和超轻离型涂层3的组份不同，具体为：
所述防静电涂层2由以下重量配比的组份组成：导电液1.1kg，异丙醇3.5kg。
所述超轻离型涂层3由以下重量配比的组份组成：硅油0.9kg，胶联剂40g，锚固剂18g，剥离剂60g，固化剂13g，乙酯3500kg，丁酮1.8kg。
实施例4，本发明实施例提供一种防静电超轻离型力的功能薄膜，其与实施例1基本相同，区别在于防静电涂层2和超轻离型涂层3的组份不同，具体为：
所述防静电涂层2由以下重量配比的组份组成：导电液1kg，异丙醇4.2kg。
所述超轻离型涂层3由以下重量配比的组份组成：硅油0.95kg，胶联剂36g，锚固剂17g，剥离剂52g，固化剂14g，乙酯3300kg，丁酮2.1kg。
实施例5，本发明实施例提供一种防静电超轻离型力的功能薄膜，其与实施例1基本相同，区别在于防静电涂层2和超轻离型涂层3的组份不同，具体为：
所述防静电涂层2由以下重量配比的组份组成：导电液1kg，异丙醇4.1kg。
所述超轻离型涂层3由以下重量配比的组份组成：硅油1kg，胶联剂35g，锚固剂16g，剥离剂53g，固化剂17g，乙酯3400kg，丁酮1.9kg。
上述实施例仅为本发明较好的实施方式，本发明不能一一列举出全部的实施方式，凡采用上述实施例之一的技术方案，或根据上述实施例所做的等同变化，均在本发明保护范围内。
根据上述说明书的揭示和教导，本发明所属领域的技术人员还可以对上述实施方式进行变更和修改。因此，本发明并不局限于上面揭示和描述的具体实施方式，对本发明的一些修改和变更也应当落入本发明的权利要求的保护范围内。此外，尽管本说明书中使用了一些特定的术语，但这些术语只是为了方便说明，并不对本发明构成任何限制，采用与其相同或相似的其它薄膜，均在本发明保护范围内。

Claims (6)

1.一种防静电超轻离型力的功能薄膜，其特征在于，其包括PET膜层、防静电涂层和超轻离型涂层，所述PET膜层、防静电涂层、超轻离型涂层按照从上至下的顺序依次贴合。
2.根据权利要求1所述的防静电超轻离型力的功能薄膜，其特征在于，所述防静电涂层的电阻值为105～1012欧姆，其由以下重量份数的组份组成：
导电液子0.9～1.1份，
异丙醇3.5～4.5份。
3.根据权利要求1或2所述的防静电超轻离型力的功能薄膜，其特征在于，所述防静电涂层的厚度为1～2微米。
4.根据权利要求1所述的防静电超轻离型力的功能薄膜，其特征在于，所述超轻离型涂层由以下重量份数的组份组成：
硅油900～1100份，
胶联剂30～40份，
锚固剂13～18份，
剥离剂40～60份，
固化剂13～18份，
乙酯2500～3500份，
丁酮1800～2200份。
5.根据权利要求1或4所述的防静电超轻离型力的功能薄膜，其特征在于，所述超轻离型涂层的厚度为1～2微米。
6.根据权利要求1所述的防静电超轻离型力的功能薄膜，其特征在于，所述PET膜层的厚度为25～125微米。
CN201510222834.1A 2015-05-05 2015-05-05 防静电超轻离型力的功能薄膜 Pending CN105128469A (zh)