CN105108067A - 一种提升射芯模充砂成型的方法 - Google Patents

一种提升射芯模充砂成型的方法 Download PDF

Info

Publication number
CN105108067A
CN105108067A CN201510545175.5A CN201510545175A CN105108067A CN 105108067 A CN105108067 A CN 105108067A CN 201510545175 A CN201510545175 A CN 201510545175A CN 105108067 A CN105108067 A CN 105108067A
Authority
CN
China
Prior art keywords
sand
die
mould
core
die cavity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510545175.5A
Other languages
English (en)
Other versions
CN105108067B (zh
Inventor
李冠
刘岳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kocel Machinery Co Ltd
Original Assignee
Ningxia Kocel Pattern Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningxia Kocel Pattern Co Ltd filed Critical Ningxia Kocel Pattern Co Ltd
Priority to CN201510545175.5A priority Critical patent/CN105108067B/zh
Publication of CN105108067A publication Critical patent/CN105108067A/zh
Application granted granted Critical
Publication of CN105108067B publication Critical patent/CN105108067B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种提升射芯模充砂成型的方法，通过将射芯模模具整体密封，利用机械泵对模具内腔整体进行抽真空，充砂时实现模具内腔整体负压，从而达到降低充砂阻力、提高充砂速率、改善砂芯质量的目的。本发明的有益效果为：打破常规设计观念，利用充砂时模具内腔整体负压的特点，增加了排气压力差，增加了排气动力，减小了充砂阻力；保证了排气的通畅，提高了砂子的流动速率，增加了砂子的动能；砂芯质量得到明显提高；砂芯缺陷减少，降低人为修补耗时耗工，降低了生产成本，提高了生产效率；由于模具实现整体密封，避免了催化剂气体外泄，实现了绿色生产的目标；模具设计结构得到优化，模具质量提高，使用寿命得以延长。

Description

一种提升射芯模充砂成型的方法
技术领域
本发明属于模具成型领域，具体涉及一种提升射芯模充砂成型的方法。
背景技术
当前使用的射芯模具是将充砂板与上模之间预留一定设计间隙，在充砂过程中模具型腔中空气的排出从上下模两部分分别排出。上模排气由上模与充砂板之间的间隙排出，下模排气经过支座空间由机械泵抽出。这种结构使得射芯模具与外界处于接通状态，排气压力差小，充砂成型阻力大，砂芯易出现质量缺陷。
随着砂芯结构的不断复杂化以及砂芯质量要求的不断提高，对射芯模具、射芯设备以及射芯工艺的要求也更加严格。因此，当前使用的射芯模具设计方案显现出了明显的缺陷和不足，射芯模具设计制作难度大，影响实际生产中充砂成型。砂芯的质量问题，直接影响铸造生产效率和质量，为铸造生产造成严重损失。此外，生产现场还比较容易出现充砂漏气甚至漏砂现象。因此，改进模具结构，从而联合设备降低充砂阻力、提高充砂速率、改善砂芯质量和改善尾气处理和排放十分重要。
发明内容
针对现有技术的不足，本发明提供一种提升射芯模充砂成型的方法，通过将射芯模模具整体密封，利用机械泵对模具内腔整体进行抽真空，充砂时实现模具内腔整体负压，从而达到降低充砂阻力、提高充砂速率、改善砂芯质量的目的。
为了解决以上技术问题，本发明提供以下技术方案：
一种射芯模充砂成型的方法，其步骤包括：
步骤一，将射芯模具的上、下模整体密封，上、下模配合采用镶嵌结构，下模的顶部嵌入上模中，然后将设有填砂嘴的填砂板放置在上模上，上模与填砂板之间取消间隙设计并采用密封条密封，实现模具整体密封；
步骤二，上、下模上分别设有排气塞，并且在上模和下模中设置贯通上、下模的连通孔，然后利用机械泵通过上、下模的排气塞将上、下模之间模腔内的空气抽出并通过连通孔排出上、下模模腔，通过下端的排气口排到外界，使得上、下模模腔内处于负压状态；
步骤三，在上、下模模腔处于负压状态下，将砂子通过填砂嘴进入模腔内，直至砂子填满上、下模模腔；
步骤四，当砂子填满上、下模模腔后，将带有密封棒的吹气板取代填砂板的位置放置在上模上，同时吹气板与上模之间采用密封条进行密封，在吹气催化过程中吹气板上的密封棒将上下模腔通道连通孔阻断，保证催化剂全部均匀地通过砂芯，使砂芯快速有效固化；
步骤五，当模腔内的砂子固定成型后，射芯模充砂成型完成，拆卸上、下模即可得到成型砂。
进一步的，步骤一中所述填砂板上设有多个填砂嘴；
进一步的，步骤二中所述上模、下模设有多个排气塞及连通孔；
进一步的，步骤五中具体工作过程为：当模腔内的砂子固定成型后，射芯模充砂成型完成，拆卸上模，下模位于支座上，支座上设有下顶板，下顶板上固定有多个顶杆，顶杆穿过下模底部且与砂子接触，当砂成型后下顶板沿着下顶板导向杆向上运动，顶杆随之将成型砂顶出下模，最后得到成型砂。
本发明所述技术方案的有益效果为：打破常规设计观念，利用充砂时模具内腔整体负压的特点，即增加了排气压力差，增加了排气动力，也减小了充砂阻力；既保证了排气的通畅，也提高了砂子的流动速率，增加了砂子的动能；充砂过程得到优化改善，砂芯质量得到明显提高；砂芯缺陷减少，降低人为修补耗时耗工，降低了生产成本，提高了生产效率。由于模具实现整体密封，避免了催化剂气体外泄，实现了绿色生产的目标；模具设计结构得到优化，模具质量提高，使用寿命得以延长；提高了模具一次性成功率，降低首件返修成本，提高了模具利润。
附图说明
图1射芯模具负压成型示意图；
图中：1、排气口，2、砂芯，3、排气塞，4、填砂嘴，5、填砂板，6、上模，7、下模，8、连通孔。
具体实施方式
为了使本领域技术人员更好地理解本发明的技术方案，下面结合附图对本发明作进一步的详细说明。
如图1所示，一种提升射芯模充砂成型的方法，包括以下步骤：
步骤一，将射芯模具的上模6、下模7整体密封，上模6、下模7配合采用镶嵌结构，下模7部分嵌入上模6，然后将设有填砂嘴4的填砂板5放置在上模6上，上模6与填砂板5之间取消间隙设计并采用密封条密封；
步骤二，上模6、下模7上分别设有排气塞，并且在上模和下模中设置贯通上、下模的连通孔8，然后利用机械泵通过上模6、下模7的排气塞3将上模6、下模7之间模腔内的空气抽出并通过连通孔排出上模6、下模7模腔，通过排气口1排到外界，使得上模6、下模7模腔内处于负压状态；
步骤三，当上模6、下模7模腔处于负压状态时，将砂子通过填砂嘴4进入模腔内，直至砂子填满上模6、下模7模腔；
步骤四，当砂子填满上模6、下模7模腔后，将带有密封棒的吹气板取代填砂板5的位置放置在上模6上，同时吹气板与上模之间采用密封条进行密封，在吹气催化过程中吹气板上的密封棒将上下模腔通道连通孔8阻断，保证催化剂全部均匀地通过砂芯2，使砂芯2快速有效固化；
步骤五，当模腔内的砂子固定成型后，射芯模充砂成型完成，拆卸上模6，下模7位于支座上，支座上设有下顶板，下顶板上固定有多个顶杆，顶杆穿过下模底部且与砂子接触，当砂成型后下顶板沿着下顶板导向杆向上运动，顶杆随之将成型砂顶出下模，最后得到成型砂。
以上对本申请所提供的技术方案进行了详细介绍，以上说明只是用于帮助理解本申请的方法及其核心思想；同时，对于本领域的一般技术人员，依据本申请的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本申请的限制。

Claims (4)

1.一种射芯模充砂成型的方法，其特征在于，包括以下步骤：
步骤一，将射芯模具的上、下模整体密封，上、下模配合采用镶嵌结构，下模的顶部嵌入上模中，然后将设有填砂嘴的填砂板放置在上模上，上模与填砂板之间取消间隙设计并采用密封条密封，实现模具整体密封；
步骤二，上、下模上分别设有排气塞，并且在上模和下模中设置贯通上、下模的连通孔，然后利用机械泵通过上、下模的排气塞将上、下模之间模腔内的空气抽出并通过连通孔排出上、下模模腔，通过下端的排气口排到外界，使得上、下模模腔内处于负压状态；
步骤三，在上、下模模腔处于负压状态下，将砂子通过填砂嘴进入模腔内，直至砂子填满上、下模模腔；
步骤四，当砂子填满上、下模模腔后，将带有密封棒的吹气板取代填砂板的位置放置在上模上，同时吹气板与上模之间采用密封条进行密封，在吹气催化过程中吹气板上的密封棒将上下模腔通道连通孔阻断，保证催化剂全部均匀地通过砂芯，使砂芯快速有效固化；
步骤五，当模腔内的砂子固定成型后，射芯模充砂成型完成，拆卸上、下模即可得到成型砂。
2.根据权利要求1所述的一种提升射芯模充砂成型的方法，其特征在于，步骤一中所述填砂板上设有多个填砂嘴。
3.根据权利要求1所述的一种提升射芯模充砂成型的方法，其特征在于，步骤二中所述上模、下模设有多个排气塞及连通孔。
4.根据权利要求1所述的一种提升射芯模充砂成型的方法，其特征在于，步骤五中具体工作过程为：当模腔内的砂子固定成型后，射芯模充砂成型完成，拆卸上模，下模位于支座上，支座上设有下顶板，下顶板上固定有多个顶杆，顶杆穿过下模底部且与砂子接触，当砂成型后下顶板沿着下顶板导向杆向上运动，顶杆随之将成型砂顶出下模，最后得到成型砂。
CN201510545175.5A 2015-08-31 2015-08-31 一种提升射芯模充砂成型的方法 Active CN105108067B (zh)