CN105085784A - 环氧磷酸酯改性热固性丙烯酸树脂 - Google Patents
环氧磷酸酯改性热固性丙烯酸树脂 Download PDFInfo
- Publication number
- CN105085784A CN105085784A CN201510454180.5A CN201510454180A CN105085784A CN 105085784 A CN105085784 A CN 105085784A CN 201510454180 A CN201510454180 A CN 201510454180A CN 105085784 A CN105085784 A CN 105085784A
- Authority
- CN
- China
- Prior art keywords
- component
- acrylic resin
- resin
- butyl
- epoxy phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环氧磷酸酯改性热固性丙烯酸树脂，其特征在于，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：第一组份:二甲苯、丁醇；第二组份:甲基丙烯酸甲酯、甲基丙烯酸异冰片酯、丙烯酸异辛酯、丙烯酸、丙烯酸羟乙酯、甲基丙烯酸丁酯、丙烯酸丁酯、环氧磷酸酯、过氧化苯甲酸叔丁酯；第三组份：二甲苯、过氧化苯甲酸叔丁酯。本发明与普通的热固性丙烯酸树脂相比，具有以下有点：1.耐人工QUV加速老化时间长，耐候性能优异；2.粘度低，固含高，漆膜的光泽丰满度优；3.硬度高，可用于高档汽车的金属外壳原厂烤漆；4.附着力优，对底材的适应性更广。
Description
技术领域
本发明涉及高分子聚合物技术领域，尤其是一种环氧磷酸酯改性热固性丙烯酸树脂。
背景技术
热固性丙烯酸树脂是指以丙烯酸酯系单体为基本成分，经交联成网络结构的不熔，不溶丙烯酸系聚合物，也成交联型或反应型丙烯酸树脂。热固性丙烯酸树脂中带有一定的官能团，在制漆时通过加入的三聚氰胺树脂、环氧树脂、聚胺酯等官能团反应，最终形成网络结构，达到不溶不熔的效果，克服了热塑性丙烯酸树脂的缺点，使涂膜的机械性能，耐化学品性能大大提高。
随着热固性丙烯酸树脂的广泛应用，行业对高端烤漆树脂应用于室内金属家电、高档汽车等的需求愈发热切，因此，亟待需要一种树脂粘度低、固含高、光泽丰满度优、耐候性能优异、硬度高、抗刮伤性好的改性热固性丙烯酸树脂。
发明内容
本发明的目的是提供一种环氧磷酸酯改性热固性丙烯酸树脂。
为实现上述目的，本发明的技术方案是：
一种环氧磷酸酯改性热固性丙烯酸树脂，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯443-497
丁醇410-490
第二组份:甲基丙烯酸甲酯336-376
甲基丙烯酸异冰片酯680-720
丙烯酸异辛酯180-220
丙烯酸40-45
丙烯酸羟乙酯556-576
甲基丙烯酸丁酯380-420
丙烯酸丁酯630-690
环氧磷酸酯290-310
过氧化苯甲酸叔丁酯64-70
第三组份：二甲苯120-140
过氧化苯甲酸叔丁酯15-18
本发明的生产工艺为：
1、向容器中加入第一组份，并升温至回流，用4小时将第二组份滴入完毕；
2、四小时将第二组份滴入完毕保温2小时；
3、加入第三组份，保温2.5小时；
4、降温，出料即可。
本发明与普通的热固性丙烯酸树脂相比，具有以下有点：
1.耐人工QUV加速老化时间长，耐候性能优异；
2.粘度低，固含高，漆膜的光泽丰满度优；
3.硬度高，可用于高档汽车的金属外壳原厂烤漆；
4.附着力优，对底材的适应性更广。
具体实施方式
下面给出实施例对本发明作进一步的详细说明：
实施例1：一种环氧磷酸酯改性热固性丙烯酸树脂，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯445
丁醇415
第二组份:甲基丙烯酸甲酯340
甲基丙烯酸异冰片酯685
丙烯酸异辛酯185
丙烯酸40
丙烯酸羟乙酯558
甲基丙烯酸丁酯385
丙烯酸丁酯640
环氧磷酸酯292
过氧化苯甲酸叔丁酯64
第三组份：二甲苯122
过氧化苯甲酸叔丁酯15
实施例2：一种环氧磷酸酯改性热固性丙烯酸树脂，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯450
丁醇422
第二组份:甲基丙烯酸甲酯350
甲基丙烯酸异冰片酯691
丙烯酸异辛酯188
丙烯酸42
丙烯酸羟乙酯561
甲基丙烯酸丁酯389
丙烯酸丁酯655
环氧磷酸酯296
过氧化苯甲酸叔丁酯65
第三组份：二甲苯128
过氧化苯甲酸叔丁酯16
实施例3：一种环氧磷酸酯改性热固性丙烯酸树脂，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯472
丁醇466
第二组份:甲基丙烯酸甲酯361
甲基丙烯酸异冰片酯701
丙烯酸异辛酯206
丙烯酸44
丙烯酸羟乙酯566
甲基丙烯酸丁酯403
丙烯酸丁酯666
环氧磷酸酯302
过氧化苯甲酸叔丁酯68
第三组份：二甲苯133
过氧化苯甲酸叔丁酯17
实施例4：一种环氧磷酸酯改性热固性丙烯酸树脂，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯491
丁醇478
第二组份:甲基丙烯酸甲酯371
甲基丙烯酸异冰片酯711
丙烯酸异辛酯211
丙烯酸45
丙烯酸羟乙酯527
甲基丙烯酸丁酯412
丙烯酸丁酯682
环氧磷酸酯309
过氧化苯甲酸叔丁酯70
第三组份：二甲苯138
过氧化苯甲酸叔丁酯18
上述实例均按下述方法制备，制备方如下：
本发明的生产工艺为：
1、向容器中加入第一组份，并升温至回流，用4小时将第二组份滴入完毕；
2、四小时将第二组份滴入完毕保温2小时；
3、加入第三组份，保温2.5小时；
4、降温，出料即可。
本发明的产品固含高达75%，粘度低，与70%固含的氨基树脂配合使用，在有色金属底材上耐盐雾能达到200个小时以上，光泽在60℃能达到98%，硬度能达到3H，耐人工加速QUV能达到1000小时以上，在钢铁、合金、电镀底材上附着力皆优异，不仅可以应用于室内金属家电烤漆，也可用于高档汽车原厂烤漆，满足了行业内对高端烤漆树脂的热切盼望。
以上对本发明做了详尽的描述，其目的在于让熟悉此领域技术的人士能够了解本发明的内容并加以实施，并不能以此限制本发明的保护范围，凡根据本发明的精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围内。
Claims (1)
1.一种环氧磷酸酯改性热固性丙烯酸树脂，其特征在于，包括第一组份，第二组份和第三组份，所述各组份的成份以及质量份数具体如下：
第一组份:二甲苯443-497
丁醇410-490
第二组份:甲基丙烯酸甲酯336-376
甲基丙烯酸异冰片酯680-720
丙烯酸异辛酯180-220
丙烯酸40-45
丙烯酸羟乙酯556-576
甲基丙烯酸丁酯380-420
丙烯酸丁酯630-690
环氧磷酸酯290-310
过氧化苯甲酸叔丁酯64-70
第三组份：二甲苯120-140
过氧化苯甲酸叔丁酯15-18。