CN105034123A - 一种室内结构用重竹板材及其制备方法 - Google Patents
一种室内结构用重竹板材及其制备方法 Download PDFInfo
- Publication number
- CN105034123A CN105034123A CN201510318842.6A CN201510318842A CN105034123A CN 105034123 A CN105034123 A CN 105034123A CN 201510318842 A CN201510318842 A CN 201510318842A CN 105034123 A CN105034123 A CN 105034123A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo
- bamboo board
- heavy bamboo
- board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种室内结构用重竹板材,由下列重量份的原料制成:干竹丝片100-120、油茶果壳液化树脂胶粘剂(固体含量为20-22%)400-450、渗透剂0.4-0.5、丙烯酸三氟乙酯5-6、纳米聚四氟乙烯5-6、甲基丙烯酸十二氟庚酯6-7、过氧化异丙苯0.4-0.5、高氰戊菊酯0.3-0.4、氮羟甲基树脂3-4、白炭黑1-2、氨基树脂1-1.5、纳米银0.7-1。本发明重竹板材通过使用氮羟甲基树脂、白炭黑,降低了板材含水率、提高尺寸稳定性、增强胶结强度;通过使用高氰戊菊酯、纳米银,使得板材具有防虫防霉功效,适用于别墅建筑的室内结构用板材,经久耐用。
Description
技术领域
本发明涉及重竹制造领域,尤其涉及一种室内结构用重竹板材及其制备方法。
背景技术
竹子作为我国第二大森林资源,因其具有繁殖再生能力强、生长周期短、材质优良等特性,其工业和商业价值日益显著。竹材可通过机械物理加工、化学加工,生产各种竹制品,以竹代木,减少木材消耗量,可以有效缓解木材供需之间的矛盾。
重竹板材通过竹材的劈篾拉丝,疏解,再经过炭化防腐处理,经高压压制成型。制备的板材具有高强度、高密度、抗紫外线、耐水防霉、环保等性能,并广泛应用于户外地板、高档家俱装饰面板、建筑结构梁柱用材、房屋建筑板材、户外园林制品、船甲板、冷冻库板及集装箱底板等各种类型户外用材。目前的重竹板材存在吸水厚度膨胀率偏大的问题,而且耐油性、耐磨性、防开裂性、防污性、抗菌性、抗变色性、强度还不够好,重量大,需要改进。
发明内容
本发明的目的在于提供一种室内结构用重竹板材及其制备方法,该重竹板材尺寸稳定性好、胶结强度高,具有防虫防霉功效,适用于别墅建筑的室内结构用板材,经久耐用。
本发明的技术方案如下:
一种室内结构用重竹板材,其特征在于由下列重量份的原料制成:干竹丝片100-120、油茶果壳液化树脂胶粘剂(固体含量为20-22%)400-450、渗透剂0.4-0.5、丙烯酸三氟乙酯5-6、纳米聚四氟乙烯5-6、甲基丙烯酸十二氟庚酯6-7、过氧化异丙苯0.4-0.5、高氰戊菊酯0.3-0.4、氮羟甲基树脂3-4、白炭黑1-2、氨基树脂1-1.5、纳米银0.7-1。
所述的室内结构用重竹板材,其特征在于:
(1)将干竹丝片进行蒸煮和碳化,再进行烘干至含水率为6-9%;
(2)将油茶果壳液化树脂胶粘剂(固体含量为20-22%)、纳米聚四氟乙烯、丙烯酸三氟乙酯、甲基丙烯酸十二氟庚酯、高氰戊菊酯、氮羟甲基树脂、白炭黑、纳米银混合,加热至60-70℃,再加入过氧化异丙苯,搅拌反应30-40分钟,再加入其它剩余成分,混合均匀,得到胶液;
(3)将第(1)步得到的竹丝片放入胶液浸渍10-12分钟,然后超声处理1-2分钟,淋干多余胶液,通过太阳晒或烘房烘干,直至竹篾含水率降至13-18%,再经过冷压成型→固化→脱模→平头→成板材,即得。
本发明的有益效果
本发明使用丙烯酸三氟乙酯、纳米聚四氟乙烯、甲基丙烯酸十二氟庚酯,对胶液进行改性,能够提高重竹板材的耐水性、耐油性、耐磨性、防污性,减少板材尺寸变形;通过使用氮羟甲基树脂、白炭黑,降低了板材含水率、提高尺寸稳定性、增强胶结强度;通过使用高氰戊菊酯、纳米银,使得板材具有防虫防霉功效,适用于别墅建筑的室内结构用板材,经久耐用。
具体实施方式
一种室内结构用重竹板材,由下列重量份(公斤)的原料制成:干竹丝片110、油茶果壳液化树脂胶粘剂(固体含量为21%)430、渗透剂0.5、丙烯酸三氟乙酯5.5、纳米聚四氟乙烯5.5、甲基丙烯酸十二氟庚酯6.5、过氧化异丙苯0.4、高氰戊菊酯0.4、氮羟甲基树脂3.5、白炭黑1.5、氨基树脂1.3、纳米银0.9。
所述的室内结构用重竹板材,其特征在于:
(1)将干竹丝片进行蒸煮和碳化,再进行烘干至含水率为7%;
(2)将油茶果壳液化树脂胶粘剂(固体含量为21%)、纳米聚四氟乙烯、丙烯酸三氟乙酯、甲基丙烯酸十二氟庚酯、高氰戊菊酯、氮羟甲基树脂、白炭黑、纳米银混合,加热至65℃,再加入过氧化异丙苯,搅拌反应35分钟,再加入其它剩余成分,混合均匀,得到胶液;
(3)将第(1)步得到的竹丝片放入胶液浸渍11分钟,然后超声处理1分钟,淋干多余胶液,通过太阳晒或烘房烘干,直至竹篾含水率降至15%,再经过冷压成型→固化→脱模→平头→成板材,即得。
实验数据:
24h吸水厚度膨胀率为0.3%,28h循环吸水厚度膨胀率为1.6%,72h水煮后吸水厚度膨胀率为6.9%。
弯曲弹性模量为20×103,静屈强度为240MPa,拉伸强度为310MPa,压缩强度为160MPa,水平剪切强度为20.4MPa,甲醛释放量为0.1mg/L。
Claims (2)
1.一种室内结构用重竹板材,其特征在于由下列重量份的原料制成:干竹丝片100-120、油茶果壳液化树脂胶粘剂(固体含量为20-22%)400-450、渗透剂0.4-0.5、丙烯酸三氟乙酯5-6、纳米聚四氟乙烯5-6、甲基丙烯酸十二氟庚酯6-7、过氧化异丙苯0.4-0.5、高氰戊菊酯0.3-0.4、氮羟甲基树脂3-4、白炭黑1-2、氨基树脂1-1.5、纳米银0.7-1。
2.根据权利要求1所述的室内结构用重竹板材,其特征在于:
(1)将干竹丝片进行蒸煮和碳化,再进行烘干至含水率为6-9%;
(2)将油茶果壳液化树脂胶粘剂(固体含量为20-22%)、纳米聚四氟乙烯、丙烯酸三氟乙酯、甲基丙烯酸十二氟庚酯、高氰戊菊酯、氮羟甲基树脂、白炭黑、纳米银混合,加热至60-70℃,再加入过氧化异丙苯,搅拌反应30-40分钟,再加入其它剩余成分,混合均匀,得到胶液;
(3)将第(1)步得到的竹丝片放入胶液浸渍10-12分钟,然后超声处理1-2分钟,淋干多余胶液,通过太阳晒或烘房烘干,直至竹篾含水率降至13-18%,再经过冷压成型→固化→脱模→平头→成板材,即得。