CN104972110A - 一种可防电磁干扰的球形铜粉及其制作方法 - Google Patents

一种可防电磁干扰的球形铜粉及其制作方法 Download PDF

Info

Publication number
CN104972110A
CN104972110A CN201510376049.1A CN201510376049A CN104972110A CN 104972110 A CN104972110 A CN 104972110A CN 201510376049 A CN201510376049 A CN 201510376049A CN 104972110 A CN104972110 A CN 104972110A
Authority
CN
China
Prior art keywords
copper powder
spherical copper
electromagnetic interference
stir
spherical
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510376049.1A
Other languages
English (en)
Inventor
曹仕勤
晏超
俞峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING COPPER-BASED POWDER TECHNOLOGY Co Ltd
Original Assignee
TONGLING COPPER-BASED POWDER TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING COPPER-BASED POWDER TECHNOLOGY Co Ltd filed Critical TONGLING COPPER-BASED POWDER TECHNOLOGY Co Ltd
Priority to CN201510376049.1A priority Critical patent/CN104972110A/zh
Publication of CN104972110A publication Critical patent/CN104972110A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种可防电磁干扰的球形铜粉，采用共聚改性法对球形铜粉进行包覆改性，以丙烯酸、苯乙烯、三羟甲基丙烷三甲基丙烯酸酯为单体，同时还添加纳米四氧化三铁及其他有效添加剂，在块状铜表面包覆一层致密的带有苯环和羧基的共聚物膜，其表面所形成的壳层不仅对球形铜粉能起到屏蔽作用，提高其抗氧化性能，还可以改变球形铜粉的表面电荷性质，有效削弱了金属粉末团聚间的作用力，改善了产品易团聚的缺点，制得的球形铜粉作为导电填料应用于导电油墨中导电性好，易于印刷且膜层柔韧耐磨，可广泛应用于智能包装、薄膜开关、导电线路以及传感器等轻、柔性电子产品中，具有防电磁干扰等优点，市场前景广阔。

Description

一种可防电磁干扰的球形铜粉及其制作方法
技术领域
本发明涉及金属粉体材料制备技术领域，具体涉及一种可防电磁干扰的球形铜粉及其制作方法。
背景技术
随着科学技术日新月异的发展，导电复合材料得到了广泛的研究和应用。作为其主要组成部分的导电填料也因此引起了人们极大的研究热情，导电填料的性能、成本直接关系着导电材料的导电性能、可靠性能和经济性。球形铜粉导电填料因其良好的耐金属迁移性能、成本优势，被认为是目前昂贵的银基导电填料的一种极具潜力的替代品，但是球形铜粉导电填料还存在抗氧化性能不足、易团聚、导电性差、易腐蚀耐候性差等缺点，限制了其规模化应用。众所周知，纳米材料是一种具有特殊物理化学性能的材料，它在材料改性方面有着极为广泛的应用和卓越的改性效果。为解决以上难题有必要对现有的球形铜粉进行改性，提高球形铜粉的抗氧化性、导电性、耐酸、耐碱、耐候、耐高温等性能，进而为实现球形铜粉作为导电填料在导电油墨等领域的广泛应用提供可能性。
发明内容
本发明的目的就是提供一种可防电磁干扰的球形铜粉及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种可防电磁干扰的球形铜粉，其特征在于，由下列重量份的原料制成：块状铜100、丙烯酸0.38-0.69、苯乙烯0.88-1.25、三羟甲基丙烷三甲基丙烯酸酯6-13、纳米四氧化三铁0.8-1.1、铝矾土粉1-3、氨基树脂7-9、二月桂酸二丁基锡0.1-0.3、二甘醇二苯甲酸酯5-8、戊二酸二甲酯4-6、不锈钢纤维3-5、正丁醇56-66。
所述的一种可防电磁干扰的球形铜粉的制备方法，其特征在于包括以下步骤：
（1）将不锈钢纤维烘干粉碎，加入纳米四氧化三铁搅拌混匀，喷入熔融状态的氨基树脂超声波分散30-50分钟，烘干粉碎；
（2）将二甘醇二苯甲酸酯、戊二酸二甲酯放入反应釜中升温至170-190℃，加入二月桂酸二丁基锡保持温度搅拌2-4小时，冷却至室温；
（3）将丙烯酸、苯乙烯、三羟甲基丙烷三甲基丙烯酸酯投入正丁醇中搅拌混匀，加入步骤（2）反应物料，升温至80-90℃并保持温度搅拌反应4-6小时；
（4）将清洗后的块状铜用氮气吹干研磨至200-300目，氮气保护下加入步骤（1）、（3）物料及其他剩余成分搅拌混匀，于80℃保温包覆反应4小时，过滤、清洗并用氮气吹干出料。
本发明有以下有益效果：本发明采用共聚改性法对球形铜粉进行包覆改性，以丙烯酸、苯乙烯、三羟甲基丙烷三甲基丙烯酸酯为单体，同时还添加纳米四氧化三铁及其他有效添加剂，于80℃通过共聚反应在块状铜表面包覆一层致密的带有苯环和羧基的共聚物膜，其表面所形成的壳层不仅对球形铜粉能起到屏蔽作用，提高其抗氧化性能，还可以改变球形铜粉的表面电荷性质，有效削弱了金属粉末团聚间的作用力，改善了产品易团聚的缺点，制得的球形铜粉作为导电填料应用于导电油墨中导电性好，易于印刷且膜层柔韧耐磨，可广泛应用于智能包装、薄膜开关、导电线路以及传感器等轻、柔性电子产品中，具有防电磁干扰等优点，市场前景广阔。
具体实施方式
所述的一种可防电磁干扰的球形铜粉，其特征在于，由下列重量份的原料制成：块状铜100、丙烯酸0.59、苯乙烯1.05、三羟甲基丙烷三甲基丙烯酸酯12、纳米四氧化三铁1.1、铝矾土粉1、氨基树脂7、二月桂酸二丁基锡0.2、二甘醇二苯甲酸酯6、戊二酸二甲酯5、不锈钢纤维4、正丁醇59。
制作方法包括以下步骤：
（1）将不锈钢纤维烘干粉碎，加入纳米四氧化三铁搅拌混匀，喷入熔融状态的氨基树脂超声波分散30-50分钟，烘干粉碎；
（2）将二甘醇二苯甲酸酯、戊二酸二甲酯放入反应釜中升温至170-190℃，加入二月桂酸二丁基锡保持温度搅拌2-4小时，冷却至室温；
（3）将丙烯酸、苯乙烯、三羟甲基丙烷三甲基丙烯酸酯投入正丁醇中搅拌混匀，加入步骤（2）反应物料，升温至80-90℃并保持温度搅拌反应4-6小时；
（4）将清洗后的块状铜用氮气吹干研磨至200-300目，氮气保护下加入步骤（1）、（3）物料及其他剩余成分搅拌混匀，于80℃保温包覆反应4小时，过滤、清洗并用氮气吹干出料。
使用本发明生产的球形铜粉的技术参数指标如下：
（1）体积电阻率下降88.54%；
（2）抗氧化温度提高了20.5℃；
（3）利用本发明填充导电油墨静止放置50天以上不会出现油墨板结的现象，其墨层耐磨性>80%。

Claims (2)

1.一种可防电磁干扰的球形铜粉，其特征在于，由下列重量份的原料制成：块状铜100、丙烯酸0.38-0.69、苯乙烯0.88-1.25、三羟甲基丙烷三甲基丙烯酸酯6-13、纳米四氧化三铁0.8-1.1、铝矾土粉1-3、氨基树脂7-9、二月桂酸二丁基锡0.1-0.3、二甘醇二苯甲酸酯5-8、戊二酸二甲酯4-6、不锈钢纤维3-5、正丁醇56-66。
2.根据权利要求1所述的一种可防电磁干扰的球形铜粉的制作方法，其特征在于包括以下步骤：
（1）将不锈钢纤维烘干粉碎，加入纳米四氧化三铁搅拌混匀，喷入熔融状态的氨基树脂超声波分散30-50分钟，烘干粉碎；
（2）将二甘醇二苯甲酸酯、戊二酸二甲酯放入反应釜中升温至170-190℃，加入二月桂酸二丁基锡保持温度搅拌2-4小时，冷却至室温；
（3）将丙烯酸、苯乙烯、三羟甲基丙烷三甲基丙烯酸酯投入正丁醇中搅拌混匀，加入步骤（2）反应物料，升温至80-90℃并保持温度搅拌反应4-6小时；
（4）将清洗后的块状铜用氮气吹干研磨至200-300目，氮气保护下加入步骤（1）、（3）物料及其他剩余成分搅拌混匀，于80℃保温包覆反应4小时，过滤、清洗并用氮气吹干出料。
CN201510376049.1A 2015-06-27 2015-06-27 一种可防电磁干扰的球形铜粉及其制作方法 Pending CN104972110A (zh)