CN104927677A - 一种高效热熔转印用粘合剂及其制备方法 - Google Patents
一种高效热熔转印用粘合剂及其制备方法 Download PDFInfo
- Publication number
- CN104927677A CN104927677A CN201510305195.5A CN201510305195A CN104927677A CN 104927677 A CN104927677 A CN 104927677A CN 201510305195 A CN201510305195 A CN 201510305195A CN 104927677 A CN104927677 A CN 104927677A
- Authority
- CN
- China
- Prior art keywords
- stirred
- joined
- add
- water
- organic zirconium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了高效热熔转印用粘合剂，本发明以乳酸/丙三醇有机锆为交联剂，其具有明显的温敏交联特性，以乙烯-丙烯酸乙酯共聚物纤维基液为稠化剂，通过交联作用，可以形成具有良好的耐温耐剪切性能的凝胶，采用纤维处理的共聚物基液，可以提高共聚物表面活性，促进交联效果，提高粘弹性和触变性。
Description
技术领域
本发明涉及一种粘合剂，尤其涉及一种高效热熔转印用粘合剂及其制备方法。
背景技术
传统的植物胶粘合剂，在高温下易水解，粘合性差，对基材的保护性差，而乙烯-丙烯酸乙酯共聚物的增稠能力强、耐温性能好；
通常获得聚合物凝胶最常用的交联剂是有机硼或有机锆，而有机硼交联剂耐温最高只能达到150℃，有机锆可在酸性条件下交联，且耐温高，可达200℃，具有广阔的应用前景。
发明内容
本发明的目的就是提供一种高效热熔转印用粘合剂及其制备方法。
本发明是通过以下技术方案实现的：
一种高效热熔转印用粘合剂，它是由下述重量份的原料组成的：
丙烯酸羟丙酯3-4、肉豆蔻酸钠皂13-20、sp-80 0.8-2、10-12mol/l的硝酸溶液0.3-0.4、乙烯-丙烯酸乙酯共聚物200-210、刺槐豆胶1-2、柠檬酸1-2、氧氯化锆1.3-2、乳酸0.5-1、丙三醇0.6-1、剑麻纤维10-15、N-羟甲基丙烯酰胺2.6-5、氟硼酸钠2-3。
一种高效热熔转印用粘合剂的制备方法，包括以下步骤：
（1）将丙烯酸羟丙酯加入到4-6倍水中，搅拌溶解，加入氟硼酸钠，得氟化溶解液；
（2）将肉豆蔻酸钠皂加入到2-3倍水中，加入sp-80，60-70℃下保温搅拌3-4分钟，得乳化皂液；
（3）将剑麻纤维加入到浓度为5-7%的亚硫酸氢钾溶液中浸润3-4小时，出料后烘干磨粉，加入40-50倍水，加入乳化皂液，200-300转/分搅拌10-20分钟，滴加10-12mol/l的硝酸溶液，加热至沸腾，加入乙烯-丙烯酸乙酯共聚物，并调节PH为6-6.5，搅拌至常温，得聚合物纤维基液；
（4）将氧氯化锆加入到2-3倍水中，搅拌溶解，加入乳酸、丙三醇，调节体系pH 值至4-5，搅拌混合4-5小时，得有机锆交联剂；
（5）将上述聚合物纤维基液、有机锆交联剂混合，搅拌条件下滴加氟化溶解液，滴加完毕后在80-90℃的恒温油浴中搅拌20-30分钟，出料冷却，得有机锆凝胶；
（6）将有机锆凝胶与剩余各原料混合，升高温度为170-180℃，保温搅拌2-3小时，经水槽冷却，切断成型，脱水，真空干燥，即得。
本发明的优点是：
本发明以乳酸/丙三醇有机锆为交联剂，其具有明显的温敏交联特性，以乙烯-丙烯酸乙酯共聚物纤维基液为稠化剂，通过交联作用，可以形成具有良好的耐温耐剪切性能的凝胶，采用纤维处理的共聚物基液，可以提高共聚物表面活性，促进交联效果，提高粘弹性和触变性。
本发明的粘合剂具有很好的防水性，耐热性好，特别适合用作热熔转印，使用方便，粘合性强。
具体实施方式
下面结合实施例对本发明作进一步详细描述：
实施例1：
一种高效热熔转印用粘合剂，它是由下述重量份的原料组成的：
丙烯酸羟丙酯3、肉豆蔻酸钠皂20、sp-80 0.8、12mol/l的硝酸溶液0.3、乙烯-丙烯酸乙酯共聚物210、刺槐豆胶1、柠檬酸2、氧氯化锆1.3、乳酸0.1、丙三醇0.6、剑麻纤维15、N-羟甲基丙烯酰胺2.6、氟硼酸钠3。
一种高效热熔转印用粘合剂的制备方法，包括以下步骤：
（1）将丙烯酸羟丙酯加入到4倍水中，搅拌溶解，加入氟硼酸钠，得氟化溶解液；
（2）将肉豆蔻酸钠皂加入到2倍水中，加入sp-80，70℃下保温搅拌3分钟，得乳化皂液；
（3）将剑麻纤维加入到浓度为5-7%的亚硫酸氢钾溶液中浸润4小时，出料后烘干磨粉，加入50倍水，加入乳化皂液，300转/分搅拌20分钟，滴加12mol/l的硝酸溶液，加热至沸腾，加入乙烯-丙烯酸乙酯共聚物，并调节PH为6.5，搅拌至常温，得聚合物纤维基液；
（4）将氧氯化锆加入到3倍水中，搅拌溶解，加入乳酸、丙三醇，调节体系pH 值至4，搅拌混合4小时，得有机锆交联剂；
（5）将上述聚合物纤维基液、有机锆交联剂混合，搅拌条件下滴加氟化溶解液，滴加完毕后在90℃的恒温油浴中搅拌30分钟，出料冷却，得有机锆凝胶；
（6）将有机锆凝胶与剩余各原料混合，升高温度为180℃，保温搅拌3小时，经水槽冷却，切断成型，脱水，真空干燥，即得。
性能测试：
粘结强度：3.7MPa；
粘度：3500mPa.s。
Claims (2)
1.一种高效热熔转印用粘合剂，其特征在于它是由下述重量份的原料组成的：
丙烯酸羟丙酯3-4、肉豆蔻酸钠皂13-20、sp-80 0.8-2、10-12mol/l的硝酸溶液0.3-0.4、乙烯-丙烯酸乙酯共聚物200-210、刺槐豆胶1-2、柠檬酸1-2、氧氯化锆1.3-2、乳酸0.5-1、丙三醇0.6-1、剑麻纤维10-15、N-羟甲基丙烯酰胺2.6-5、氟硼酸钠2-3。
2.一种如权利要求1所述的高效热熔转印用粘合剂的制备方法，其特征在于包括以下步骤：
（1）将丙烯酸羟丙酯加入到4-6倍水中，搅拌溶解，加入氟硼酸钠，得氟化溶解液；
（2）将肉豆蔻酸钠皂加入到2-3倍水中，加入sp-80，60-70℃下保温搅拌3-4分钟，得乳化皂液；
（3）将剑麻纤维加入到浓度为5-7%的亚硫酸氢钾溶液中浸润3-4小时，出料后烘干磨粉，加入40-50倍水，加入乳化皂液，200-300转/分搅拌10-20分钟，滴加10-12mol/l的硝酸溶液，加热至沸腾，加入乙烯-丙烯酸乙酯共聚物，并调节PH为6-6.5，搅拌至常温，得聚合物纤维基液；
（4）将氧氯化锆加入到2-3倍水中，搅拌溶解，加入乳酸、丙三醇，调节体系pH 值至4-5，搅拌混合4-5小时，得有机锆交联剂；
（5）将上述聚合物纤维基液、有机锆交联剂混合，搅拌条件下滴加氟化溶解液，滴加完毕后在80-90℃的恒温油浴中搅拌20-30分钟，出料冷却，得有机锆凝胶；
（6）将有机锆凝胶与剩余各原料混合，升高温度为170-180℃，保温搅拌2-3小时，经水槽冷却，切断成型，脱水，真空干燥，即得。