CN104109493B - 甲基纤维素‑干酪素混合标签胶黏剂配方及其制备工艺 - Google Patents
甲基纤维素‑干酪素混合标签胶黏剂配方及其制备工艺 Download PDFInfo
- Publication number
- CN104109493B CN104109493B CN201410306314.4A CN201410306314A CN104109493B CN 104109493 B CN104109493 B CN 104109493B CN 201410306314 A CN201410306314 A CN 201410306314A CN 104109493 B CN104109493 B CN 104109493B
- Authority
- CN
- China
- Prior art keywords
- casein
- methylcellulose
- water
- adhesive
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
甲基纤维素‑干酪素混合标签胶黏剂配方及其制备工艺,涉及一种胶黏剂,其成分主要包括甲基纤维素与干酪素胶黏剂,制备完成后,将甲基纤维素和干酪素混合,比重为100:40,加入7份聚乙烯醇,升温至190℃,加热时长1小时即可得到甲基纤维素‑干酪素混合标签胶黏剂。本发明的特点:无毒无害,工艺简单,性优价廉,用途广泛,稳定性好,抗水性强,粘结强度高,实用性强。
Description
技术领域:
本发明涉及一种胶黏剂,具体涉及甲基纤维素-干酪素混合标签胶黏剂配方及其制备工艺。
背景技术:
化学工业是近现代发展十分迅速的国民经济的支柱产业,而精细化工尾气重要组成部分,在20世纪得到了突飞猛进的发展,未解决人类的衣食住行以及能源、资源与环境问题作出重要贡献。
胶黏剂是现代工业发展和人类生活水平提高必不可少的重要材料,胶黏剂及粘结技术以其他连接方式无法比拟的特种工艺,在现代经济、现代国防、现代科技中发挥着重大的作用。
发明内容:
本发明所要解决的技术问题在于克服现有技术的缺陷,提供一种甲基纤维素-干酪素混合标签胶黏剂配方其制备工艺。
本发明所要解决的技术问题采用以下技术方案来实现。
甲基纤维素-干酪素混合标签胶黏剂配方,其特征在于:其成分主要包括甲基纤维素与干酪素胶黏剂,具体为
甲基纤维素包括:
棉短绒:100-120份,一氯醋酸:80-100份,乙醇:90-100份,氢氧化钠:60-70份,盐酸:50-60份;
干酪素包括:
聚乙烯醇:10-15份,交联剂:0.1-0.2份,聚丙烯酰胺0.5-1份,干酪素:2-5份,氢氧化钠:0.1-0.2份,磷酸钠:0.2-0.5份,尿素:1-2份,防腐剂:0.1-0.2份,玉米淀粉:5-10份,水100-120份。
甲基纤维素-干酪素混合标签胶黏剂制备工艺,其特征在于:包括甲基纤维素与酚醛树脂胶黏剂的制备,具体为:
甲基纤维素的制备包括:
先将棉短绒、一氯醋酸、乙醇、氢氧化钠和盐酸分别加入水稀释,得到95%棉短绒、98%一氯醋酸、95%乙醇、45%氢氧化钠和31%盐酸的水溶液,再将95%棉短绒水溶液和45%氢氧化钠水溶液混合,于30℃的环境下混合搅拌1-2小时,然后加入到真空反应釜中,加入98%一氯醋酸、95%乙醇和31%盐酸,在60℃-70℃温度下反应5小时;
干酪素胶黏剂的制备包括:
取聚乙烯醇、聚丙烯酰胺和75%的水进行混合搅拌,温度控制在90-92℃,待聚乙烯醇、聚丙烯酰胺完全溶解在水中,降温至65-70℃,加入玉米淀粉、干酪素、尿素、磷酸钠和15%的水保温反应2小时,然后加入交联剂和5%的水,继续保温反应1小时,加入防腐剂,搅拌,滴加氢氧化钠和5%的水混合液,调pH值在7.5-8,搅拌5-10分钟;
制备完成后,将甲基纤维素和干酪素混合,比重为100:40,加入7份聚乙烯醇,升温至190℃,加热时长1小时即可得到甲基纤维素-干酪素混合标签胶黏剂。
本发明的特点:无毒无害,工艺简单,性优价廉,用途广泛,稳定性好,抗水性强,粘结强度高,实用性强。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
具体实施例:甲基纤维素-干酪素混合标签胶黏剂配方,其特征在于:其成分主要包括甲基纤维素与干酪素胶黏剂,具体为
甲基纤维素包括:
棉短绒:100份,一氯醋酸:100份,乙醇:100份,氢氧化钠:60份,盐酸:50份;
干酪素包括:
聚乙烯醇:10份,交联剂:0.1份,聚丙烯酰胺0.5份,干酪素:2份,氢氧化钠:0.1份,磷酸钠:0.2份,尿素:1份,防腐剂:0.1份,玉米淀粉:5份,水100份。
甲基纤维素-干酪素混合标签胶黏剂制备工艺,其特征在于:包括甲基纤维素与酚醛树脂胶黏剂的制备,具体为:
甲基纤维素的制备包括:
先将棉短绒、一氯醋酸、乙醇、氢氧化钠和盐酸分别加入水稀释,得到95%棉短绒、98%一氯醋酸、95%乙醇、45%氢氧化钠和31%盐酸的水溶液,再将95%棉短绒水溶液和45%氢氧化钠水溶液混合,于30℃的环境下混合搅拌1-2小时,然后加入到真空反应釜中,加入98%一氯醋酸、95%乙醇和31%盐酸,在60℃-70℃温度下反应5小时;
干酪素胶黏剂的制备包括:
取聚乙烯醇、聚丙烯酰胺和75%的水进行混合搅拌,温度控制在92℃,待聚乙烯醇、聚丙烯酰胺完全溶解在水中,降温至70℃,加入玉米淀粉、干酪素、尿素、磷酸钠和15%的水保温反应2小时,然后加入交联剂和5%的水,继续保温反应1小时,加入防腐剂,搅拌,滴加氢氧化钠和5%的水混合液,调pH值在7.5-8,搅拌10分钟;
制备完成后,将甲基纤维素和干酪素混合,比重为100:40,加入7份聚乙烯醇,升温至190℃,加热时长1小时即可得到甲基纤维素-干酪素混合标签胶黏剂。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.甲基纤维素-干酪素混合标签胶黏剂的制备方法,其特征在于:包括甲基纤维素与干酪素胶黏剂的制备,具体为
甲基纤维素包括:
棉短绒:100-120份,一氯醋酸:80-100份,乙醇:90-100份,氢氧化钠:60-70份,盐酸:50-60份;
干酪素包括:
聚乙烯醇:10-15份,交联剂:0.1-0.2份,聚丙烯酰胺0.5-1份,干酪素:2-5份,氢氧化钠:0.1-0.2份,磷酸钠:0.2-0.5份,尿素:1-2份,防腐剂:0.1-0.2份,玉米淀粉:5-10份,水100-120份;
甲基纤维素的制备包括:
先将棉短绒、一氯醋酸、乙醇、氢氧化钠和盐酸分别加入水稀释,得到95%棉短绒、98%一氯醋酸、95%乙醇、45%氢氧化钠和31%盐酸的水溶液,再将95%棉短绒水溶液和45%氢氧化钠水溶液混合,于30℃的环境下混合搅拌1-2小时,然后加入到真空反应釜中,加入98%一氯醋酸、95%乙醇和31%盐酸,在60℃-70℃温度下反应5小时;
干酪素胶黏剂的制备包括:
取聚乙烯醇、聚丙烯酰胺和75%的水进行混合搅拌,温度控制在90-92℃,待聚乙烯醇、聚丙烯酰胺完全溶解在水中,降温至65-70℃,加入玉米淀粉、干酪素、尿素、磷酸钠和15%的水保温反应2小时,然后加入交联剂和5%的水,继续保温反应1小时,加入防腐剂,搅拌,滴加氢氧化钠和5%的水混合液,调pH值在7.5-8,搅拌5-10分钟;
制备完成后,将甲基纤维素和干酪素混合,比重为100:40,加入7份聚乙烯醇,升温至190℃,加热时长1小时即可得到甲基纤维素-干酪素混合标签胶黏剂。