CN104908345A - 一种输送带生产工艺 - Google Patents
一种输送带生产工艺 Download PDFInfo
- Publication number
- CN104908345A CN104908345A CN201510199746.4A CN201510199746A CN104908345A CN 104908345 A CN104908345 A CN 104908345A CN 201510199746 A CN201510199746 A CN 201510199746A CN 104908345 A CN104908345 A CN 104908345A
- Authority
- CN
- China
- Prior art keywords
- conveyer belt
- treatment
- embryo cloth
- production process
- belt production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种输送带生产工艺,涉及输送带生产领域,包括胚布处理,贴胶成型,预塑化凝胶处理,硫化处理,压平冷却,表面处理六个步骤,利用本发明生产出的输送带,不易粘灰、开裂,且耐磨性增加。
Description
技术领域
本发明涉及输送带生产领域,特别是涉及一种输送带生产工艺。
背景技术
输送带,英文名conveying belt,又称运输带,是用于皮带输送带中起承载和运送物料作用的橡胶与纤维、金属复合制品,或者是塑料和织物复合的制品。输送带广泛应用于水泥、焦化、冶金、化工、钢铁等行业中输送距离较短、输送量较小的场合,现在市面上有的输送带材料,往往易粘灰、开裂,且耐磨度不够,因此,设计出一种能解决以上问题的输送带的生产工艺成为了亟待解决的问题。
发明内容
为克服现有技术上的不足,本发明目的是提供一种输送带生产工艺。
为实现本发明的目的,本发明的技术方案如下:
一种输送带生产工艺,包括以下步骤:
A.胚布处理:将胚布浸浆处理后预热烫平;
B.贴胶成型:将处理后的胚布与输送带贴片间隔地粘合;
C.预塑化凝胶处理:将胚布送入烘干机中进行烘干;
D.硫化处理:将成型后的胚布经过硫化系统进行硫化处理成输送带;
E.压平冷却;
F.表面处理:压花后采用辊涂工艺进行表面处理;
优选的,所述步骤C中烘干机的温度为140℃-180℃,时间为20-40min。
优选的,所述步骤F中辊涂采用的材料为丙烯酸表面处理剂。
本发明的有益效果:本发明针对存在的问题, 设计了一种输送带生产工艺, 采用该工艺制备的输送带不易粘灰、开裂,且耐磨性增加。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1:一种输送带生产工艺,包括以下步骤:
A.胚布处理:将胚布浸浆处理后预热烫平;
B.贴胶成型:将处理后的胚布与输送带贴片间隔地粘合;
C.预塑化凝胶处理:将胚布送入烘干机中进行烘干;
D.硫化处理:将成型后的胚布经过硫化系统进行硫化处理成输送带;
E.压平冷却;
F.表面处理:压花后采用辊涂工艺进行表面处理;
其中,所述步骤C中烘干机的温度为140℃-180℃,时间为20-40min。
其中,所述步骤F中辊涂采用的材料为丙烯酸表面处理剂。
本发明提供一种输送带生产工艺,采用该工艺制备的输送带不易粘灰、开裂,且耐磨性增加。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种输送带生产工艺,其特征在于:包括以下步骤:
A.胚布处理:将胚布浸浆处理后预热烫平;
B.贴胶成型:将处理后的胚布与输送带贴片间隔地粘合;
C.预塑化凝胶处理:将胚布送入烘干机中进行烘干;
D.硫化处理:将成型后的胚布经过硫化系统进行硫化处理成输送带;
E.压平冷却;
F.表面处理:压花后采用辊涂工艺进行表面处理。
2.根据权利要求1所述的一种输送带生产工艺,其特征在于,所述步骤C中烘干机的温度为140℃-180℃,时间为20-40min。
3.根据权利要求1所述的一种输送带生产工艺,其特征在于,所述步骤F中辊涂采用的材料为丙烯酸表面处理剂。