CN104893324A - 一种阻燃沥青防水卷材 - Google Patents
一种阻燃沥青防水卷材 Download PDFInfo
- Publication number
- CN104893324A CN104893324A CN201510249004.8A CN201510249004A CN104893324A CN 104893324 A CN104893324 A CN 104893324A CN 201510249004 A CN201510249004 A CN 201510249004A CN 104893324 A CN104893324 A CN 104893324A
- Authority
- CN
- China
- Prior art keywords
- lignin
- methylisothiazolinone
- add
- zinc borate
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃沥青防水卷材,它是由下述重量份的原料组成的:沥青80-90、白油膏0.8-2、硅酸镁1-2、壬基酚聚氧乙烯醚0.2-1、聚偏氟乙烯4-6、甲基异噻唑啉酮0.5-1、水合硼酸锌4-6、滑石粉27-30、烯基丁二酸酯2-3、皮胶1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、c5石油树脂4-6,本发明将碱木质素、皮胶、甲基异噻唑啉酮混合进行环氧化处理,木质素分子交联度增加,加入到树脂体系中,可以有效提高成品的绝缘性、机械性能、热稳定性、粘合性和防腐效果,其中加入的滑石粉、水合硼酸锌具有很好的阻燃性能。
Description
技术领域
本发明主要涉及卷材领域,尤其涉及一种阻燃沥青防水卷材。
背景技术
将沥青类或高分子类防水材料浸渍在胎体上,制作成的防水材料产品,以卷材形式提供,称为防水卷材,是一种可弯曲的片状防水材料。防水卷材主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处,起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品,作为工程基础与建筑物之间无渗漏连接,是整个工程防水的第一道屏障,对整个工程起着至关重要的作用,而沥青是公认的具有较好防水性能的材料,但由于原沥青有低温脆,高温流淌抗、老化性能差的特点,需要通过技术进行改进。目前用于防水的技术改进主要有催化氧化沥青、聚合物改性沥青等,这些方法改性成本较高,工艺复杂,且存在随着时间的延长防水效果差,有的不利于施工等缺陷。
发明内容
本发明目的就是提供一种阻燃沥青防水卷材。
本发明是通过以下技术方案实现的:
一种阻燃沥青防水卷材,它是由下述重量份的原料组成的:
沥青80-90、白油膏0.8-2、硅酸镁1-2、壬基酚聚氧乙烯醚0.2-1、聚偏氟乙烯4-6、甲基异噻唑啉酮0.5-1、水合硼酸锌4-6、滑石粉27-30、烯基丁二酸酯2-3、皮胶1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、c5石油树脂4-6。
一种阻燃沥青防水卷材的制备方法,包括以下步骤:
(1)将上述甲基异噻唑啉酮加入到6%的NaOH溶液中,搅拌均匀,加入皮胶、碱木质素,搅拌均匀后加入环氧氯丙烷,80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(2)将聚偏氟乙烯加热熔化,加入上述羟基硅油、壬基酚聚氧乙烯醚,送入乳化机中,60-100转/分搅拌分散10-14分钟,加入软化后的c5石油树脂、环氧化木质素,在100-120℃的油浴锅中保温30-40分钟,出料冷却,得木质素树脂粘结剂;
(3)将沥青加热熔化,脱水,加入白油膏、烯基丁二酸酯,调节温度为190-230℃,加入木质素树脂粘结剂,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(4)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
本发明的优点是:
本发明将碱木质素、皮胶、甲基异噻唑啉酮混合进行环氧化处理,木质素分子交联度增加,加入到树脂体系中,可以有效提高成品的绝缘性、机械性能、热稳定性、粘合性和防腐效果,其中加入的滑石粉、水合硼酸锌具有很好的阻燃性能。
具体实施方式
实施例1:
一种阻燃沥青防水卷材,它是由下述重量份的原料组成的:
沥青90、白油膏0.8、硅酸镁1、壬基酚聚氧乙烯醚0.2、聚偏氟乙烯6、甲基异噻唑啉酮0.5、水合硼酸锌4、滑石粉30、烯基丁二酸酯3、皮胶1、羟基硅油30、6%的NaOH溶液40、碱木质素10、环氧氯丙烷2、c5石油树脂4。
一种阻燃沥青防水卷材的制备方法,包括以下步骤:
(1)将上述甲基异噻唑啉酮加入到6%的NaOH溶液中,搅拌均匀,加入皮胶、碱木质素,搅拌均匀后加入环氧氯丙烷,85℃下保温反应4小时,冷却后用38%盐酸溶液调节PH为3,减压抽滤,干燥,得环氧化木质素;
(2)将聚偏氟乙烯加热熔化,加入上述羟基硅油、壬基酚聚氧乙烯醚,送入乳化机中,100转/分搅拌分散14分钟,加入软化后的c5石油树脂、环氧化木质素,在120℃的油浴锅中保温40分钟,出料冷却,得木质素树脂粘结剂;
(3)将沥青加热熔化,脱水,加入白油膏、烯基丁二酸酯,调节温度为230℃,加入木质素树脂粘结剂,保温搅拌30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(4)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
性能测试:
拉伸强度:1.50MPa;
延伸率:278%;
低温柔性:-30℃、2h对折无裂纹;
耐热度:120℃、5h不起泡不发粘。
Claims (2)
1.一种阻燃沥青防水卷材,其特征在于它是由下述重量份的原料组成的:
沥青80-90、白油膏0.8-2、硅酸镁1-2、壬基酚聚氧乙烯醚0.2-1、聚偏氟乙烯4-6、甲基异噻唑啉酮0.5-1、水合硼酸锌4-6、滑石粉27-30、烯基丁二酸酯2-3、皮胶1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、c5石油树脂4-6。
2.一种如权利要求1所述的阻燃沥青防水卷材的制备方法,其特征在于包括以下步骤:
(1)将上述甲基异噻唑啉酮加入到6%的NaOH溶液中,搅拌均匀,加入皮胶、碱木质素,搅拌均匀后加入环氧氯丙烷,80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(2)将聚偏氟乙烯加热熔化,加入上述羟基硅油、壬基酚聚氧乙烯醚,送入乳化机中,60-100转/分搅拌分散10-14分钟,加入软化后的c5石油树脂、环氧化木质素,在100-120℃的油浴锅中保温30-40分钟,出料冷却,得木质素树脂粘结剂;
(3)将沥青加热熔化,脱水,加入白油膏、烯基丁二酸酯,调节温度为190-230℃,加入木质素树脂粘结剂,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(4)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。