CN105038274A - 一种桐油改性沥青防水卷材 - Google Patents
一种桐油改性沥青防水卷材 Download PDFInfo
- Publication number
- CN105038274A CN105038274A CN201510459034.1A CN201510459034A CN105038274A CN 105038274 A CN105038274 A CN 105038274A CN 201510459034 A CN201510459034 A CN 201510459034A CN 105038274 A CN105038274 A CN 105038274A
- Authority
- CN
- China
- Prior art keywords
- parts
- tung oil
- add
- lignin
- pitch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种桐油改性沥青防水卷材,它是由下述重量份的原料组成的:沥青82-90、二苯基硅二醇0.7-1、桐油0.4-1、苄基三乙基氯化铵1-2、沉淀白炭黑30-34、甲基丙烯酸异辛酯2-3、二烷基二硫代磷酸锌0.4-1、硬酯酸单甘油酯1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、乙二酸1-2,本发明将碱木质素进行环氧化处理,木质素分子交联度增加,与酯化沥青混合可以进一步提高成品的绝缘性、机械性能、热稳定性和粘合性,本发明采用桐油改性酯化沥青,可以提高表面抗水性。
Description
技术领域
本发明主要涉及卷材领域,尤其涉及一种桐油改性沥青防水卷材。
背景技术
将沥青类或高分子类防水材料浸渍在胎体上,制作成的防水材料产品,以卷材形式提供,称为防水卷材,是一种可弯曲的片状防水材料。防水卷材主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处,起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品,作为工程基础与建筑物之间无渗漏连接,是整个工程防水的第一道屏障,对整个工程起着至关重要的作用,而沥青是公认的具有较好防水性能的材料,但由于原沥青有低温脆,高温流淌抗、老化性能差的特点,需要通过技术进行改进。目前用于防水的技术改进主要有催化氧化沥青、聚合物改性沥青等,这些方法改性成本较高,工艺复杂,且存在随着时间的延长防水效果差,有的不利于施工等缺陷。
发明内容
本发明目的就是提供一种桐油改性沥青防水卷材。
本发明是通过以下技术方案实现的:
一种桐油改性沥青防水卷材,它是由下述重量份的原料组成的:
沥青82-90、二苯基硅二醇0.7-1、桐油0.4-1、苄基三乙基氯化铵1-2、沉淀白炭黑30-34、甲基丙烯酸异辛酯2-3、二烷基二硫代磷酸锌0.4-1、硬酯酸单甘油酯1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、乙二酸1-2。
2、一种如权利要求1所述的桐油改性沥青防水卷材的制备方法,其特征在于包括以下步骤:
(1)将二苯基硅二醇、乙二酸混合送入搅拌器中,120-130℃下保温搅拌20-30分钟,加入上述沥青重量的6-10%、桐油,升高温度为190-200℃,保温搅拌30-40分钟,冷却,与甲基丙烯酸异辛酯混合,搅拌均匀,得酯化沥青;
(2)将苄基三乙基氯化铵加入到6%的NaOH溶液中,加入碱木质素,搅拌均匀后加入环氧氯丙烷,在80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(3)将上述酯化沥青、环氧化木质素混合加入到羟基硅油中,加入二烷基二硫代磷酸锌,送入反应釜中,加热到120-125℃,保温搅拌30-40分钟,冷却出料,得木质素粘结剂;
(4)将剩余的沥青加热熔化,加入木质素粘结剂,搅拌均匀混合脱水,调节温度为190-230℃,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
本发明的优点是:
本发明将碱木质素进行环氧化处理,木质素分子交联度增加,与酯化沥青混合可以进一步提高成品的绝缘性、机械性能、热稳定性和粘合性,本发明采用桐油改性酯化沥青,可以提高表面抗水性。
具体实施方式
实施例1:
一种桐油改性沥青防水卷材,它是由下述重量份的原料组成的:
沥青90、二苯基硅二醇0.7、桐油0.4-1、苄基三乙基氯化铵1、沉淀白炭黑34、甲基丙烯酸异辛酯3、二烷基二硫代磷酸锌0.4、硬酯酸单甘油酯1、羟基硅油30、6%的NaOH溶液40、碱木质素10、环氧氯丙烷3、乙二酸2。
一种桐油改性沥青防水卷材的制备方法,包括以下步骤:
(1)将二苯基硅二醇、乙二酸混合送入搅拌器中,130℃下保温搅拌30分钟,加入上述沥青重量的10%、桐油,升高温度为200℃,保温搅拌40分钟,冷却,与甲基丙烯酸异辛酯混合,搅拌均匀,得酯化沥青;
(2)将苄基三乙基氯化铵加入到6%的NaOH溶液中,加入碱木质素,搅拌均匀后加入环氧氯丙烷,在85℃下保温反应5小时,冷却后用38%盐酸溶液调节PH为6,减压抽滤,干燥,得环氧化木质素;
(3)将上述酯化沥青、环氧化木质素混合加入到羟基硅油中,加入二烷基二硫代磷酸锌,送入反应釜中,加热到125℃,保温搅拌40分钟,冷却出料,得木质素粘结剂;
(4)将剩余的沥青加热熔化,加入木质素粘结剂,搅拌均匀混合脱水,调节温度为230℃,保温搅拌30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
性能测试:
拉伸强度:1.72MPa;
延伸率:264%;
低温柔性:-30℃、2h对折无裂纹;
耐热度:120℃、5h不起泡不发粘。
Claims (2)
1.一种桐油改性沥青防水卷材,其特征在于它是由下述重量份的原料组成的:
沥青82-90、二苯基硅二醇0.7-1、桐油0.4-1、苄基三乙基氯化铵1-2、沉淀白炭黑30-34、甲基丙烯酸异辛酯2-3、二烷基二硫代磷酸锌0.4-1、硬酯酸单甘油酯1-2、羟基硅油20-30、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、乙二酸1-2。
2.一种如权利要求1所述的桐油改性沥青防水卷材的制备方法,其特征在于包括以下步骤:
(1)将二苯基硅二醇、乙二酸混合送入搅拌器中,120-130℃下保温搅拌20-30分钟,加入上述沥青重量的6-10%、桐油,升高温度为190-200℃,保温搅拌30-40分钟,冷却,与甲基丙烯酸异辛酯混合,搅拌均匀,得酯化沥青;
(2)将苄基三乙基氯化铵加入到6%的NaOH溶液中,加入碱木质素,搅拌均匀后加入环氧氯丙烷,在80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(3)将上述酯化沥青、环氧化木质素混合加入到羟基硅油中,加入二烷基二硫代磷酸锌,送入反应釜中,加热到120-125℃,保温搅拌30-40分钟,冷却出料,得木质素粘结剂;
(4)将剩余的沥青加热熔化,加入木质素粘结剂,搅拌均匀混合脱水,调节温度为190-230℃,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。