CN103468138A - 一种桥面、屋面、涵洞用防水涂料 - Google Patents

一种桥面、屋面、涵洞用防水涂料 Download PDF

Info

Publication number
CN103468138A
CN103468138A CN2013103592340A CN201310359234A CN103468138A CN 103468138 A CN103468138 A CN 103468138A CN 2013103592340 A CN2013103592340 A CN 2013103592340A CN 201310359234 A CN201310359234 A CN 201310359234A CN 103468138 A CN103468138 A CN 103468138A
Authority
CN
China
Prior art keywords
parts
add
coalescence aid
film coalescence
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103592340A
Other languages
English (en)
Inventor
蒋能
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Original Assignee
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd filed Critical Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority to CN2013103592340A priority Critical patent/CN103468138A/zh
Publication of CN103468138A publication Critical patent/CN103468138A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种桥面、屋面、涵洞用防水涂料，它是由下述重量份的原料组成的：沥青52-60、可溶性聚四氟乙烯1-2、十六烷基三甲基氯化铵2-3、季戊四醇3-4、泡花碱2-4、SD528硅丙乳液5-7、聚氧丙烯甘油醚1-2、超细硫酸钡粉15-20、云母粉5-10、磷酸二氢铝1-2、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、成膜助剂2-4、水适量，本发明将的涂料成膜性好，涂膜稳定，光泽度好，柔韧性强，耐侯性、耐酸碱性能优越，能够起到很好的防水效果，而且耐擦洗性强，使用寿命长。

Description

一种桥面、屋面、涵洞用防水涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种桥面、屋面、涵洞用防水涂料。
背景技术
    乳化沥青涂料具有一定的防水性和防腐性，由于沥青本身性能的限制，乳化沥青防水涂料的使用寿命短，康烈性、低温柔性和耐热性等性能较差，适用于防水等级为Ⅲ 、Ⅳ级的工业与民用建筑屋面、厕浴间防水层和地下防潮、防腐涂层的施工，是廉价低档的防水涂料，因此，提高乳化沥青防水涂料的综合性能，以便扩大实用范围是很有必要的。
发明内容
本发明目的就是提供一种桥面、屋面、涵洞用防水涂料。
本发明是通过以下技术方案实现的：
一种桥面、屋面、涵洞用防水涂料，它是由下述重量份的原料组成的：
沥青52-60、可溶性聚四氟乙烯1-2、十六烷基三甲基氯化铵2-3、季戊四醇3-4、泡花碱2-4、SD528硅丙乳液5-7、聚氧丙烯甘油醚1-2、超细硫酸钡粉15-20、云母粉5-10、磷酸二氢铝1-2、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、成膜助剂2-4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液40-50、聚醋酸乙烯乳液5-6、乙烯基三乙氧基硅烷4-5、二丙二醇丁醚1-2、聚乙二醇1000 2-3、氢氧化铝2-4、氧化锡锑0.1-0.2；
将上述聚乙二醇1000与氢氧化铝混合，50-60℃下搅拌反应10-15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，400-500转/分搅拌分散2-4分钟，加入上述预混料与剩余各原料，100-120℃保温静置1-2小时，即得所述成膜助剂。
一种桥面、屋面、涵洞用防水涂料的制备方法，包括以下步骤：
将上述沥青在反应釜中加温至200-230℃，脱水后加入可溶性聚四氟乙烯搅拌1-2 小时,得预混料，将超细硫酸钡粉、云母粉与N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷混合，300-400转/分搅拌分散4-5分钟，出料后加入到上述预混料中，在160-180℃下通过胶体磨研磨均匀，加入除了成膜助剂以外的各原料，充分搅拌混合，冷却至常温，加入成膜助剂，充分搅拌，即得所述桥面、屋面、涵洞用防水涂料。
本发明的优点是：
    本发明将的涂料成膜性好，涂膜稳定，光泽度好，柔韧性强，耐侯性、耐酸碱性能优越，能够起到很好的防水效果，而且耐擦洗性强，使用寿命长。
具体实施方式
实施例1
一种桥面、屋面、涵洞用防水涂料，它是由下述重量份（公斤）的原料组成的：
沥青60、可溶性聚四氟乙烯2、十六烷基三甲基氯化铵3、季戊四醇4、泡花碱4、SD528硅丙乳液7、聚氧丙烯甘油醚1、超细硫酸钡粉20、云母粉10、磷酸二氢铝2、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷2、成膜助剂4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液50、聚醋酸乙烯乳液6、乙烯基三乙氧基硅烷5、二丙二醇丁醚2、聚乙二醇1000 2、氢氧化铝2、氧化锡锑0.2；
将上述聚乙二醇1000与氢氧化铝混合，60℃下搅拌反应15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，500转/分搅拌分散4分钟，加入上述预混料与剩余各原料，120℃保温静置1小时，即得所述成膜助剂。
一种桥面、屋面、涵洞用防水涂料的制备方法，包括以下步骤：
将上述沥青在反应釜中加温至230℃，脱水后加入可溶性聚四氟乙烯搅拌2 小时,得预混料，将超细硫酸钡粉、云母粉与N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷混合，400转/分搅拌分散5分钟，出料后加入到上述预混料中，在180℃下通过胶体磨研磨均匀，加入除了成膜助剂以外的各原料，充分搅拌混合，冷却至常温，加入成膜助剂，充分搅拌，即得所述桥面、屋面、涵洞用防水涂料。
性能测试：
耐酸性：用5%的H2SO4 溶液浸泡25天涂膜表面无变化；
耐碱性：用5%的NaOH 溶液浸泡25 天涂膜表面无变化；
不透水性（0.3MPa、40min）：不透水。

Claims (2)

1.一种桥面、屋面、涵洞用防水涂料，其特征在于它是由下述重量份的原料组成的：
沥青52-60、可溶性聚四氟乙烯1-2、十六烷基三甲基氯化铵2-3、季戊四醇3-4、泡花碱2-4、SD528硅丙乳液5-7、聚氧丙烯甘油醚1-2、超细硫酸钡粉15-20、云母粉5-10、磷酸二氢铝1-2、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、成膜助剂2-4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液40-50、聚醋酸乙烯乳液5-6、乙烯基三乙氧基硅烷4-5、二丙二醇丁醚1-2、聚乙二醇1000 2-3、氢氧化铝2-4、氧化锡锑0.1-0.2；
将上述聚乙二醇1000与氢氧化铝混合，50-60℃下搅拌反应10-15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，400-500转/分搅拌分散2-4分钟，加入上述预混料与剩余各原料，100-120℃保温静置1-2小时，即得所述成膜助剂。
2.一种如权利要求1所述的桥面、屋面、涵洞用防水涂料的制备方法，其特征在于包括以下步骤：
将上述沥青在反应釜中加温至200-230℃，脱水后加入可溶性聚四氟乙烯搅拌1-2 小时,得预混料，将超细硫酸钡粉、云母粉与N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷混合，300-400转/分搅拌分散4-5分钟，出料后加入到上述预混料中，在160-180℃下通过胶体磨研磨均匀，加入除了成膜助剂以外的各原料，充分搅拌混合，冷却至常温，加入成膜助剂，充分搅拌，即得所述桥面、屋面、涵洞用防水涂料。
CN2013103592340A 2013-08-16 2013-08-16 一种桥面、屋面、涵洞用防水涂料 Pending CN103468138A (zh)