CN103468139A - 一种阻燃防水涂料 - Google Patents

一种阻燃防水涂料 Download PDF

Info

Publication number
CN103468139A
CN103468139A CN201310359589XA CN201310359589A CN103468139A CN 103468139 A CN103468139 A CN 103468139A CN 201310359589X A CN201310359589X A CN 201310359589XA CN 201310359589 A CN201310359589 A CN 201310359589A CN 103468139 A CN103468139 A CN 103468139A
Authority
CN
China
Prior art keywords
add
stirring
strong
coalescence aid
film coalescence
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310359589XA
Other languages
English (en)
Inventor
蒋能
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Original Assignee
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd filed Critical Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority to CN201310359589XA priority Critical patent/CN103468139A/zh
Publication of CN103468139A publication Critical patent/CN103468139A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃防水涂料，它是由下述重量份的原料组成的：石油沥青65-70、液体丁腈橡胶LR82010-14、凹凸棒土10-20、水滑石粉8-10、十二烷基苯磺酸钠1-2、磷酸二氢铵2-3、聚丙烯酰胺2-3、三氧化二锑1-2、3-(异丁烯酰氧)丙基三甲氧基硅烷1-2、6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉0.1-0.2、成膜助剂2-4、水适量，本发明的涂料耐候性强，涂膜稳定、粘结性强，高温不流淌、低温不龟裂，耐老化、耐腐蚀、阻燃、防水性强。

Description

一种阻燃防水涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种阻燃防水涂料。
背景技术
    乳化沥青涂料具有一定的防水性和防腐性，由于沥青本身性能的限制，乳化沥青防水涂料的使用寿命短，康烈性、低温柔性和耐热性等性能较差，适用于防水等级为Ⅲ 、Ⅳ级的工业与民用建筑屋面、厕浴间防水层和地下防潮、防腐涂层的施工，是廉价低档的防水涂料，因此，提高乳化沥青防水涂料的综合性能，以便扩大实用范围是很有必要的。
发明内容
本发明目的就是提供一种阻燃防水涂料。
本发明是通过以下技术方案实现的：
一种阻燃防水涂料，它是由下述重量份的原料组成的：
石油沥青65-70、液体丁腈橡胶LR820 10-14、凹凸棒土10-20、水滑石粉8-10、十二烷基苯磺酸钠1-2、磷酸二氢铵2-3、聚丙烯酰胺2-3、三氧化二锑1-2、3-(异丁烯酰氧)丙基三甲氧基硅烷1-2、6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉0.1-0.2、成膜助剂2-4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液40-50、聚醋酸乙烯乳液5-6、乙烯基三乙氧基硅烷4-5、二丙二醇丁醚1-2、聚乙二醇1000 2-3、氢氧化铝2-4、氧化锡锑0.1-0.2；
将上述聚乙二醇1000与氢氧化铝混合，50-60℃下搅拌反应10-15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，400-500转/分搅拌分散2-4分钟，加入上述预混料与剩余各原料，100-120℃保温静置1-2小时，即得所述成膜助剂。
一种阻燃防水涂料的制备方法，包括以下步骤：
向石油沥青中加入液体丁腈橡胶LR820，加热升高温度至140-160℃，用胶体磨研磨，达到完全均匀分散为止，降低至常温，得预混料；将上述凹凸棒土、磷酸二氢铵、水滑石粉混合，加入3-(异丁烯酰氧)丙基三甲氧基硅烷，500-600转/分搅拌分散4-5分钟，与上述预混料混合，在60-70℃下搅拌分散20-30分钟，加入除了成膜助剂以为的各原料，充分搅拌后加入成膜助剂，即得所述阻燃防水涂料。
本发明的优点是：
    本发明的涂料耐侯性强，涂膜稳定、粘结性强，高温不流淌、低温不龟裂，耐老化、耐腐蚀、阻燃、防水性强。
具体实施方式
实施例1
一种阻燃防水涂料，它是由下述重量份（公斤）的原料组成的：
石油沥青70、液体丁腈橡胶LR820 14、凹凸棒土10、水滑石粉10、十二烷基苯磺酸钠2、磷酸二氢铵3、聚丙烯酰胺3、三氧化二锑1、3-(异丁烯酰氧)丙基三甲氧基硅烷1、6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉0.2、成膜助剂4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液50、聚醋酸乙烯乳液5、乙烯基三乙氧基硅烷5、二丙二醇丁醚1、聚乙二醇1000 3、氢氧化铝2、氧化锡锑0.2；
将上述聚乙二醇1000与氢氧化铝混合，60℃下搅拌反应15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，500转/分搅拌分散2分钟，加入上述预混料与剩余各原料，120℃保温静置1小时，即得所述成膜助剂。
一种阻燃防水涂料的制备方法，包括以下步骤：
向石油沥青中加入液体丁腈橡胶LR820，加热升高温度至160℃，用胶体磨研磨，达到完全均匀分散为止，降低至常温，得预混料；将上述凹凸棒土、磷酸二氢铵、水滑石粉混合，加入3-(异丁烯酰氧)丙基三甲氧基硅烷，600转/分搅拌分散5分钟，与上述预混料混合，在70℃下搅拌分散30分钟，加入除了成膜助剂以为的各原料，充分搅拌后加入成膜助剂，即得所述阻燃防水涂料。
性能测试：
延伸性：877%；
粘结强度：2.64MPa；
不透水性（0.3MPa、40min）：不透水。

Claims (2)

1.一种阻燃防水涂料，其特征在于它是由下述重量份的原料组成的：
石油沥青65-70、液体丁腈橡胶LR820 10-14、凹凸棒土10-20、水滑石粉8-10、十二烷基苯磺酸钠1-2、磷酸二氢铵2-3、聚丙烯酰胺2-3、三氧化二锑1-2、3-(异丁烯酰氧)丙基三甲氧基硅烷1-2、6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉0.1-0.2、成膜助剂2-4、水适量；
所述的成膜助剂是由下述重量份的原料组成的：
EVA乳液40-50、聚醋酸乙烯乳液5-6、乙烯基三乙氧基硅烷4-5、二丙二醇丁醚1-2、聚乙二醇1000 2-3、氢氧化铝2-4、氧化锡锑0.1-0.2；
将上述聚乙二醇1000与氢氧化铝混合，50-60℃下搅拌反应10-15分钟，冷却至常温后加入氧化锡锑，得预混料，将EVA乳液与聚醋酸乙烯乳液混合，搅拌均匀后加入乙烯基三乙氧基硅烷，400-500转/分搅拌分散2-4分钟，加入上述预混料与剩余各原料，100-120℃保温静置1-2小时，即得所述成膜助剂。
2.一种如权利要求1所述的阻燃防水涂料的制备方法，其特征在于包括以下步骤：
向石油沥青中加入液体丁腈橡胶LR820，加热升高温度至140-160℃，用胶体磨研磨，达到完全均匀分散为止，降低至常温，得预混料；将上述凹凸棒土、磷酸二氢铵、水滑石粉混合，加入3-(异丁烯酰氧)丙基三甲氧基硅烷，500-600转/分搅拌分散4-5分钟，与上述预混料混合，在60-70℃下搅拌分散20-30分钟，加入除了成膜助剂以为的各原料，充分搅拌后加入成膜助剂，即得所述阻燃防水涂料。
CN201310359589XA 2013-08-16 2013-08-16 一种阻燃防水涂料 Pending CN103468139A (zh)