CN104861666A - 一种改良抗氧化沥青防水卷材 - Google Patents
一种改良抗氧化沥青防水卷材 Download PDFInfo
- Publication number
- CN104861666A CN104861666A CN201510248894.0A CN201510248894A CN104861666A CN 104861666 A CN104861666 A CN 104861666A CN 201510248894 A CN201510248894 A CN 201510248894A CN 104861666 A CN104861666 A CN 104861666A
- Authority
- CN
- China
- Prior art keywords
- asphalt
- coiled material
- water
- pitch
- lignin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改良抗氧化沥青防水卷材,它是由下述重量份的原料组成的:沥青82-90、硫代二丙酸0.3-0.4、水溶性羊毛脂2-3、溴化聚苯乙烯6-8、甲基硫醇锡0.1-0.2、抗氧剂1010 0.8-2、钙沸石4-6、轻质碳酸钙20-26、马来酸二丁酯2-3、烷基化二苯胺0.1-0.2、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、机械油21-30,本发明将碱木质素进行环氧化处理,木质素分子交联度增加,加入到树脂体系中,可以有效提高成品的绝缘性、机械性能、热稳定性、粘合性和防腐效果,其中将烷基化二苯胺加入到机械油中可以起到很好的高温抗氧化性。
Description
技术领域
本发明主要涉及卷材领域,尤其涉及一种改良抗氧化沥青防水卷材。
背景技术
将沥青类或高分子类防水材料浸渍在胎体上,制作成的防水材料产品,以卷材形式提供,称为防水卷材,是一种可弯曲的片状防水材料。防水卷材主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处,起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品,作为工程基础与建筑物之间无渗漏连接,是整个工程防水的第一道屏障,对整个工程起着至关重要的作用,而沥青是公认的具有较好防水性能的材料,但由于原沥青有低温脆,高温流淌抗、老化性能差的特点,需要通过技术进行改进。目前用于防水的技术改进主要有催化氧化沥青、聚合物改性沥青等,这些方法改性成本较高,工艺复杂,且存在随着时间的延长防水效果差,有的不利于施工等缺陷。
发明内容
本发明目的就是提供一种改良抗氧化沥青防水卷材。
本发明是通过以下技术方案实现的:
一种改良抗氧化沥青防水卷材,它是由下述重量份的原料组成的:
沥青82-90、硫代二丙酸0.3-0.4、水溶性羊毛脂2-3、溴化聚苯乙烯6-8、甲基硫醇锡0.1-0.2、抗氧剂1010 0.8-2、钙沸石4-6、轻质碳酸钙20-26、马来酸二丁酯2-3、烷基化二苯胺0.1-0.2、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、机械油21-30。
2、一种如权利要求1所述的改良抗氧化沥青防水卷材的制备方法,其特征在于包括以下步骤:
(1)将硫代二丙酸、水溶性羊毛脂混合,搅拌均匀后加入碱木质素,50-60℃下保温搅拌4-10分钟,加入上述6%的NaOH溶液,搅拌均匀后加入环氧氯丙烷,80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(2)将钙沸石在浓度为6-10%的氢氧化钠溶液中浸泡1-2小时,取出后水洗、烘干,磨成细粉,与上述沥青重量的10-20%混合,搅拌均匀,得沥青石粉;
(3)将烷基化二苯胺加入到机械油中,升高温度为110-120℃,加入马来酸二丁酯、熔化后的溴化聚苯乙烯,搅拌条件下加入沥青石粉、环氧化木质素,保温搅拌40-50分钟,出料冷却,得木质素树脂粘结剂;
(4)将剩余的沥青加热熔化,脱水,加入甲基硫醇锡,调节温度为190-230℃,加入木质素树脂粘结剂,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
本发明的优点是:
本发明将碱木质素进行环氧化处理,木质素分子交联度增加,加入到树脂体系中,可以有效提高成品的绝缘性、机械性能、热稳定性、粘合性和防腐效果,其中将烷基化二苯胺加入到机械油中可以起到很好的高温抗氧化性。
具体实施方式
实施例1:
一种改良抗氧化沥青防水卷材,它是由下述重量份的原料组成的:
沥青90、硫代二丙酸0.4、水溶性羊毛脂3、溴化聚苯乙烯8、甲基硫醇锡0.1、抗氧剂1010 0.8、钙沸石6、轻质碳酸钙26、马来酸二丁酯3、烷基化二苯胺0.2、6%的NaOH溶液40、碱木质素10、环氧氯丙烷2、机械油30。
一种改良抗氧化沥青防水卷材的制备方法,包括以下步骤:
(1)将硫代二丙酸、水溶性羊毛脂混合,搅拌均匀后加入碱木质素,60℃下保温搅拌10分钟,加入上述6%的NaOH溶液,搅拌均匀后加入环氧氯丙烷,85℃下保温反应4小时,冷却后用38%盐酸溶液调节PH为6,减压抽滤,干燥,得环氧化木质素;
(2)将钙沸石在浓度为6-10%的氢氧化钠溶液中浸泡2小时,取出后水洗、烘干,磨成细粉,与上述沥青重量的20%混合,搅拌均匀,得沥青石粉;
(3)将烷基化二苯胺加入到机械油中,升高温度为120℃,加入马来酸二丁酯、熔化后的溴化聚苯乙烯,搅拌条件下加入沥青石粉、环氧化木质素,保温搅拌50分钟,出料冷却,得木质素树脂粘结剂;
(4)将剩余的沥青加热熔化,脱水,加入甲基硫醇锡,调节温度为230℃,加入木质素树脂粘结剂,保温搅拌20分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。
性能测试:
拉伸强度:1.47MPa;
延伸率:276%;
低温柔性:-30℃、2h对折无裂纹;
耐热度:120℃、5h不起泡不发粘。
Claims (2)
1.一种改良抗氧化沥青防水卷材,其特征在于它是由下述重量份的原料组成的:
沥青82-90、硫代二丙酸0.3-0.4、水溶性羊毛脂2-3、溴化聚苯乙烯6-8、甲基硫醇锡0.1-0.2、抗氧剂1010 0.8-2、钙沸石4-6、轻质碳酸钙20-26、马来酸二丁酯2-3、烷基化二苯胺0.1-0.2、6%的NaOH溶液30-40、碱木质素6-10、环氧氯丙烷2-3、机械油21-30。
2.一种如权利要求1所述的改良抗氧化沥青防水卷材的制备方法,其特征在于包括以下步骤:
(1)将硫代二丙酸、水溶性羊毛脂混合,搅拌均匀后加入碱木质素,50-60℃下保温搅拌4-10分钟,加入上述6%的NaOH溶液,搅拌均匀后加入环氧氯丙烷,80-85℃下保温反应4-5小时,冷却后用38%盐酸溶液调节PH为3-6,减压抽滤,干燥,得环氧化木质素;
(2)将钙沸石在浓度为6-10%的氢氧化钠溶液中浸泡1-2小时,取出后水洗、烘干,磨成细粉,与上述沥青重量的10-20%混合,搅拌均匀,得沥青石粉;
(3)将烷基化二苯胺加入到机械油中,升高温度为110-120℃,加入马来酸二丁酯、熔化后的溴化聚苯乙烯,搅拌条件下加入沥青石粉、环氧化木质素,保温搅拌40-50分钟,出料冷却,得木质素树脂粘结剂;
(4)将剩余的沥青加热熔化,脱水,加入甲基硫醇锡,调节温度为190-230℃,加入木质素树脂粘结剂,保温搅拌20-30分钟,加入剩余各原料,通过胶体磨研磨充分,即得改性沥青混料;
(5)将上述改性沥青混料送至成型涂油槽,胎基从成型槽中穿过进行涂装,然后根据需要控制合适的厚度,覆膜,冷却成型,所述的胎基为聚酯胎。