CN104891914A - 一种利用造纸黑液制备加气砖方法 - Google Patents

一种利用造纸黑液制备加气砖方法 Download PDF

Info

Publication number
CN104891914A
CN104891914A CN201510262159.5A CN201510262159A CN104891914A CN 104891914 A CN104891914 A CN 104891914A CN 201510262159 A CN201510262159 A CN 201510262159A CN 104891914 A CN104891914 A CN 104891914A
Authority
CN
China
Prior art keywords
parts
aluminum oxide
black liquid
carbonizing chamber
coal gangue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510262159.5A
Other languages
English (en)
Inventor
朱春
朱世军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bangbu Ying Jun Novel Wall Material Co Ltd
Original Assignee
Bangbu Ying Jun Novel Wall Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bangbu Ying Jun Novel Wall Material Co Ltd filed Critical Bangbu Ying Jun Novel Wall Material Co Ltd
Priority to CN201510262159.5A priority Critical patent/CN104891914A/zh
Publication of CN104891914A publication Critical patent/CN104891914A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种利用造纸黑液制备加气砖方法，按照如下步骤进行：（1）、取下列质量份的干基原料：生石灰20-30份、煤矸石15-18份、水泥12-14份、活性废渣20-30份、氧化铝5-7份、改性黄土4-6份、消泡剂2-5份；本发明的废建筑垃圾用量大、节能环保，缓解废建筑垃圾堆存处理带来的环境污染问题，同时为空心砖提供了新的原料。

Description

一种利用造纸黑液制备加气砖方法
技术领域
本发明涉及新型建材领域，具体属于一种利用造纸黑液制备加气砖方法。
背景技术
造纸黑液中含有大量的悬浮性固体、有机污染物和有毒物质，直接排放到水体中会造成严重的污染。其主要危害有：含有大量纤维、色素和无机盐的造纸废水会使水体变黑，并有特殊的恶臭味；含高浓度有机污染物的造纸黑液的生化耗氧量(BOD)可高达5000~40000g/L，会大量消耗水中的溶解氧，影响水质；黑液中大量存在的碱性物质会使水体的pH值急剧升高，破坏水体环境的平衡。
造纸黑液的处理与工业生产相结合，是一种新的研究方向。
发明内容
本发明的目的在于提供一种利用造纸黑液制备加气砖方法，造纸黑液用量大、节能环保，缓解造纸黑液处理带来的环境污染问题，同时为加气砖提供了新的原料来源。
本发明的技术方案如下：
一种利用造纸黑液制备加气砖方法，其特征在于按照如下步骤进行：
    （1）、取下列质量份的干基原料：
     生石灰                        20-30份
     煤矸石                        15-18份
     水泥                           12-14份
     活性废渣                       20-30份
     氧化铝                         5-7份
     改性黄土                       4-6份
     消泡剂                         2-5份；
（2）、先将生石灰和活性废渣破碎，磨细后再与改性黄土、氧化铝、煤矸石和适量造纸黑液进行轮碾成型，轮碾成型同时添加消泡剂，生坯砌块在0.8-0.9Mpa蒸汽室内养护20-22h，然后送进碳化室；
（3）、将烟道气通过风机和管道输送到碳化室，碳化室C02气体的浓度为7土12%，碳化室的温度控制在40~60℃，使空气相对湿度保持在90-95%，碳化时间为 28~32h；
（4）、碳化后的砌块切割成相应的尺寸，即得加气空心砖成品。
取下列质量份的干基原料：
     生石灰                        25份
     煤矸石                        16份
     水泥                           13份
     活性废渣                       25份
     氧化铝                         6份
     改性黄土                       5份
     消泡剂                         4份。
本发明与现有技术相比具有如下优点：
与其他建筑材料相比，本发明所用城市无机垃圾无需经过脱水、干燥处理即可直接使用，废建筑垃圾用量大，均超过50%。
与加气砌块相比，本发明的主要原料为城市无机垃圾，有利于解决城市无机垃圾堆存处理而带来的环境污染问题。
总之，本发明结合我国城市无机垃圾量大、利用率低的实际情况，充分利用了各种物料的组成结构和化学特性，形成了以硅铝酸钙、水化硅酸钙等为主体的矿物结构，其产品性能符合建筑用承重和非承重墙体材料质量要求。砌块主要原材料为废建筑垃圾，使用量大，有利于解决城市无机垃圾堆存处理而带来的环境污染问题，为城市无机垃圾的资源化利用开辟了一条新的利用途径。
具体实施方式
一种利用造纸黑液制备加气砖方法，按照如下步骤进行：
    （1）、取下列质量份的干基原料：
     生石灰                        25份
     煤矸石                        16份
     水泥                           13份
     活性废渣                       25份
     氧化铝                         6份
     改性黄土                       5份
     消泡剂                         4份；
（2）、先将生石灰和活性废渣破碎，磨细后再与改性黄土、氧化铝、煤矸石和适量造纸黑液进行轮碾成型，轮碾成型同时添加消泡剂，生坯砌块在0.8-0.9Mpa蒸汽室内养护20-22h，然后送进碳化室；
（3）、将烟道气通过风机和管道输送到碳化室，碳化室C02气体的浓度为7土12%，碳化室的温度控制在40~60℃，使空气相对湿度保持在90-95%，碳化时间为28~32h；
（4）、碳化后的砌块切割成相应的尺寸，即得加气空心砖成品。

Claims (2)

1.一种利用造纸黑液制备加气砖方法，其特征在于按照如下步骤进行：
    （1）、取下列质量份的干基原料：
     生石灰                        20-30份
     煤矸石                        15-18份
     水泥                           12-14份
     活性废渣                       20-30份
     氧化铝                         5-7份
     改性黄土                       4-6份
     消泡剂                         2-5份；
（2）、先将生石灰和活性废渣破碎，磨细后再与改性黄土、氧化铝、煤矸石和适量造纸黑液进行轮碾成型，轮碾成型同时添加消泡剂，生坯砌块在0.8-0.9Mpa蒸汽室内养护20-22h，然后送进碳化室；
（3）、将烟道气通过风机和管道输送到碳化室，碳化室C02气体的浓度为7土12%，碳化室的温度控制在40~60℃，使空气相对湿度保持在90-95%，碳化时间为 28~32h；
（4）、碳化后的砌块切割成相应的尺寸，即得加气空心砖成品。
2.根据权利要求1所述利用造纸黑液制备加气砖方法，其特征在于：
取下列质量份的干基原料：
     生石灰                        25份
     煤矸石                        16份
     水泥                           13份
     活性废渣                       25份
     氧化铝                         6份
     改性黄土                       5份
     消泡剂                         4份。
CN201510262159.5A 2015-05-22 2015-05-22 一种利用造纸黑液制备加气砖方法 Pending CN104891914A (zh)