CN103992086A - 一种耐火耐水加气砖及其制备方法 - Google Patents

一种耐火耐水加气砖及其制备方法 Download PDF

Info

Publication number
CN103992086A
CN103992086A CN201410152304.XA CN201410152304A CN103992086A CN 103992086 A CN103992086 A CN 103992086A CN 201410152304 A CN201410152304 A CN 201410152304A CN 103992086 A CN103992086 A CN 103992086A
Authority
CN
China
Prior art keywords
parts
water
fire
good
steam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410152304.XA
Other languages
English (en)
Other versions
CN103992086B (zh
Inventor
晋元龙
陈德全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ma'an Mountain Bao Long Building Material Co Ltd
Original Assignee
Ma'an Mountain Bao Long Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ma'an Mountain Bao Long Building Material Co Ltd filed Critical Ma'an Mountain Bao Long Building Material Co Ltd
Priority to CN201410152304.XA priority Critical patent/CN103992086B/zh
Publication of CN103992086A publication Critical patent/CN103992086A/zh
Application granted granted Critical
Publication of CN103992086B publication Critical patent/CN103992086B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐火耐水加气砖,由下列重量份的原料制成:粉煤灰60-70、三乙醇胺0.01-0.02、松香树脂0.03-0.06、石膏7-9、纸浆废液2-4、硅树脂聚醚乳液0.8-1、莫来石粉7-10、硼砂1-2、水泥10-12、生石灰15-17、改性锯末8-10、琥珀酸0.1-0.2、加气铝粉8-9、富马酸二甲酯0.4-0.7、碳酸锆铵1-1.3、水适量;本发明加气砖具有优异的耐水性能、耐火性能,而且强度高,耐磨性好,保温性好,隔音性好,干燥收缩率低,抗裂性能好,通过使用纸浆废液,增加了发泡性能,减少了环境污染;通过使用改性锯末,增强了隔热效果,减轻了重量,增加了抗震性能,同时减水效果好,不影响强度。

Description

一种耐火耐水加气砖及其制备方法
技术领域
[0001] 本发明属于砖领域,尤其涉及一种耐火耐水加气砖及其制备方法。
背景技术
[0002] 加气砖也叫做加气混凝土砌块,应用非常的广泛,主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
[0003]目前加气砖已成为建筑材料行业的主导产品,国家已经逐步禁止使用粘土实心砖,逐渐取而代之的就是加气混凝土砌块,蒸压砖。
[0004] 加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点,可根据当地不同原材料,不同条件来量身定造,原材料来源广泛,可选择河沙、粉煤灰、矿砂等,因地制宜,可以废物利用,有利环保,真正变废为宝。
[0005] 但是随着建筑行业的发展,建筑物越来越高、造型越来越奇特,对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高,另外随着人们生活水平的不断提高,对环境的要求也越来越高,对建筑 物的保温性能、吸音性能、放射性都有更高的要求,甚至要求建筑物具有有益身体健康的性能,因此根据需要,研制更加性能优异的加气砖势在必行。
发明内容
[0006] 本发明的目的在于提供一种耐火耐水加气砖及其制备方法,该加气砖具有优异的耐水性能、耐火性能,而且强度高,耐磨性好,保温性好,隔音性好,干燥收缩率低,抗裂性能好。
[0007] 本发明的技术方案如下:
一种耐火耐水加气砖,其特征在于由下列重量份的原料制成:粉煤灰60-70、三乙醇胺
0.01-0.02、松香树脂0.03-0.06、石膏7-9、纸浆废液2-4、硅树脂聚醚乳液0.8_1、莫来石粉
7-10、硼砂1-2、水泥10-12、生石灰15-17、改性锯末8_10、琥珀酸0.1-0.2、加气铝粉8_9、富马酸二甲酯0.4-0.7、碳酸锆铵1-1.3、水适量;
所述改性锯末由下列重量份的原料制成:磷酸错2-3、锯末12-15、娃酸镁1-2、红磷
0.4-0.7、硼砂0.4-0.6、环烷酸钴0.01-0.02、月桂醇聚氧乙烯醚0.01-0.02、甲基丙烯酸羟乙酯2-3、聚羧酸高效减水剂1-2、丙烯酸1-2、过硫酸铵0.01-0.02、硝酸锆0.5-1.2、石膏晶须3-5、氧化聚乙烯蜡0.8-1、地沟油2-3 ;制作方法为:将锯末粉碎成50-100目颗粒,边搅拌边喷入氧化聚乙烯蜡、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80°C,分散研磨30-40分钟,即得。
[0008] 所述的耐火耐水加气砖的制备方法,其特征在于包括以下步骤:
(O将水泥、生石灰、莫来石粉、石膏、粉煤灰混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;(2)将第(I)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180°C,压力达到ll_13MPa,保持恒定9_12小时;
(4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C以下,出釜,放置28-30天即得。
[0009] 本发明的有益效果
本发明加气砖具有优异的耐水性能、耐火性能,而且强度高,耐磨性好,保温性好,隔音性好,干燥收缩率低,抗裂性能好,通过使用纸浆废液,增加了发泡性能,减少了环境污染;通过使用改性锯末,增强了隔热效果,减轻了重量,增加了抗震性能,同时减水效果好,不影响强度。
具体实施方式
[0010] 一种耐火耐水加气砖,由下列重量份(公斤)的原料制成:粉煤灰65、三乙醇胺 0.02、松香树脂0.04、石膏8、纸浆废液3、硅树脂聚醚乳液0.9、莫来石粉8、硼砂1_2、水泥
11、生石灰16、改性锯末9、琥珀酸0.2、加气铝粉8.6、富马酸二甲酯0.6、碳酸锆铵1.2、水
适量;
所述改性锯末由下列重量份(公斤)的原料制成:磷酸锆2.5、锯末14、硅酸镁1.4、红磷
0.6、硼砂0.5、环烷酸钴0.01、月桂醇聚氧乙烯醚0.01、甲基丙烯酸羟乙酯2.5、聚羧酸高效减水剂1.5、丙烯酸1.5、过硫酸铵0.01、硝酸锆0.8、石膏晶须4、氧化聚乙烯蜡0.9、地沟油
2.5 ;制作方法为:将锯末粉碎成80目颗粒,边搅拌边喷入氧化聚乙烯蜡、地沟油,混合均匀后放置6个小时,再与其他剩余成分混合,加热至78°C,分散研磨37分钟,即得。
[0011] 所述的耐火耐水加气砖的制备方法,包括以下步骤:
(1)将水泥、生石灰、莫来石粉、石膏、粉煤灰混合,送入球磨机中研磨成70目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(I)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.8小时内均匀地通入蒸汽,使蒸养室内的温度升至175°C,压力达到12MPa,保持恒定11小时;
(4)在1.8小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C,出釜,放置29天即得。
[0012] 实验数据:
该加气砖的密度为660kg/m3,耐火温度为760V,导热系数为0.09W / (m.°C ),采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋,粘土砖墙12小时后全部浸透,加气砖墙喷淋72小时后渗水深度为60mm,抗压强度为6.8Mpa,吸声系数0.45。

Claims (2)

1.一种耐火耐水加气砖,其特征在于由下列重量份的原料制成:粉煤灰60-70、三乙醇胺0.01-0.02、松香树脂0.03-0.06、石膏7_9、纸浆废液2_4、硅树脂聚醚乳液0.8_1、莫来石粉7-10、硼砂1-2、水泥10-12、生石灰15-17、改性锯末8_10、琥珀酸0.1-0.2、加气铝粉8-9、富马酸二甲酯0.4-0.7、碳酸锆铵1-1.3、水适量; 所述改性锯末由下列重量份的原料制成:磷酸错2-3、锯末12-15、娃酸镁1-2、红磷0.4-0.7、硼砂0.4-0.6、环烷酸钴0.01-0.02、月桂醇聚氧乙烯醚0.01-0.02、甲基丙烯酸羟乙酯2-3、聚羧酸高效减水剂1-2、丙烯酸1-2、过硫酸铵0.01-0.02、硝酸锆0.5-1.2、石膏晶须3-5、氧化聚乙烯蜡0.8-1、地沟油2-3 ;制作方法为:将锯末粉碎成50-100目颗粒,边搅拌边喷入氧化聚乙烯蜡、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80°C,分散研磨30-40分钟,即得。
2.根据权利要求1所述的耐火耐水加气砖的制备方法,其特征在于包括以下步骤: (O将水泥、生石灰、莫来石粉、石膏、粉煤灰混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料; (2)将第(I)步得到的浆料倒入模具中,得到砖胚体; (3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180°C,压力达到ll-13MPa,保持恒定9-12小时; (4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C以下,出釜,放置28-30天即得。
CN201410152304.XA 2014-04-16 2014-04-16 一种耐火耐水加气砖及其制备方法 Active CN103992086B (zh)