CN105016694A - 一种经久耐用的河砂加气砖 - Google Patents

一种经久耐用的河砂加气砖 Download PDF

Info

Publication number
CN105016694A
CN105016694A CN201510401132.XA CN201510401132A CN105016694A CN 105016694 A CN105016694 A CN 105016694A CN 201510401132 A CN201510401132 A CN 201510401132A CN 105016694 A CN105016694 A CN 105016694A
Authority
CN
China
Prior art keywords
parts
powder
river sand
raw
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510401132.XA
Other languages
English (en)
Inventor
王长富
毛东超
王玉童
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd filed Critical ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority to CN201510401132.XA priority Critical patent/CN105016694A/zh
Publication of CN105016694A publication Critical patent/CN105016694A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种经久耐用的河砂加气砖,其是由下述重量份的原料制得:石子5-8、铝矾土粉10-20、火山岩粉10-20、水泥15-25、河砂5-8、脂肪酸甲醇酰胺0.2-0.4、碳酸氢钠1-2,玻化微珠0.2-0.4、纸浆废液2-4、磷矿渣粉3-5、氢氧化钠1-2,糖蜜0.1-0.3、石膏0.1-0.3、硅粉5-10、安息香酸0.5-1.5、石油磺酸钠1.2-3.1、阿拉伯树胶0.3-1.6。

Description

一种经久耐用的河砂加气砖
技术领域
[0001] 本发明涉及加气砖领域,确切地说是一种经久耐用的河砂加气砖。
背景技术
[0002] 加气砖即“蒸压加气混凝土砌块”,简称加气砖,是通过高温蒸压设备工艺生产的加气混凝土砌块。“加气砖”可以理解为一个简化的或是一个通用的名称。其涵盖的产品范围应该要大一点,即采用包括蒸压在内的其他各种工艺生产的砖品。
[0003] 现在许多先进地区已经全面禁止红砖使用,设计单位在设计楼房的过程中就标明使用加气砖,如使用红砖,质检部门将不予验收,所以目前加气砖生产厂生产的产品供不应求。
发明内容
[0004] 本发明的目的在于提供一种经久耐用的河砂加气砖。
[0005] 上述目的通过以下方案实现:
一种经久耐用的河砂加气砖,其特征在于:其是由下述重量份的原料制得:石子5-8、铝矾土粉10-20、火山岩粉10-20、水泥15-25、河砂5_8、脂肪酸甲醇酰胺0.2-0.4、碳酸氢钠1-2,玻化微珠0.2-0.4、纸浆废液2-4、磷矿渣粉3-5、氢氧化钠1_2,糖蜜0.1-0.3、石膏
0.1-0.3、硅粉5-10、安息香酸0.5-1.5、石油磺酸钠1.2-3.1、阿拉伯树胶0.3-1.6 ;
复配改性混凝土颗粒由下述重量份的原料制得:
硬脂酸0.2-0.5,钛白粉5-7,贝壳粉1-2、丙烯酸乳液1-2、糖蜜2_4、UEA混凝土膨胀剂1-2、玉石粉1-2、碳纳米管2-4、十二醇硫酸钠2.5-3.7、硼酸锌0.8-1.6、石墨粉3.5-4.8、氧化铝 1.5-2.4 ;
复配改性混凝土颗粒的制备方法为:
将所有原料混匀后,于500-700转/分下搅拌10-20分钟后,加适量水分,造粒,颗粒粒径在6-8mm,然后将制好的颗粒于900_920°C下闪烧8_10秒,再取出于200_300°C下烧制5-10分钟后,取出冷却,于浓度为3-6%的盐酸溶液中浸泡10-20分钟,取出,洗净,即得;所述的一种经久耐用的河砂加气砖,其特征在于:
制备方法为:
(D将按重量份取河砂、脂肪酸甲醇酰胺、碳酸氢钠,玻化微珠、纸浆废液、磷矿渣粉混匀,加入适量水,在30-40°C下搅拌5-7分钟后,再加入水泥、铝矾土粉,搅拌均匀,得混合水泥浆料;
(2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,预养,脱模,切割,得砲块还;
(3)将砌块坯放入反应釜中蒸压养护10-15小时,入库即得。
[0006] 本发明的有益效果为:本发明的生产成本低,原料的密实性和抗渗性能好,制得的加气砖不易渗水、开裂,经久耐用寿命长。纸浆废液的加入变废为宝,经济节约,绿色环保。
具体实施方式
[0007] 一种经久耐用的河砂加气砖,其是由下述重量(kg)的原料制得:石子5、铝矾土粉20、火山岩粉10、水泥25、河砂8、脂肪酸甲醇酰胺0.4、碳酸氢钠1,玻化微珠0.4、纸浆废液4、磷矿渣粉5、氢氧化钠1,糖蜜0.3、石膏0.3、硅粉10、安息香酸1.5、石油磺酸钠1.6、阿拉伯树胶0.6 ;
复配改性混凝土颗粒由下述重量(kg)的原料制得:
硬脂酸0.5,钛白粉5,贝壳粉1、丙烯酸乳液2、糖蜜4、UEA混凝土膨胀剂2、玉石粉2、碳纳米管2、十二醇硫酸钠2.5、硼酸锌1.6、石墨粉3.5、氧化铝1.5 ;
复配改性混凝土颗粒的制备方法为:
将所有原料混匀后,于700转/分下搅拌20分钟后,加适量水分,造粒,颗粒粒径在6_8mm,然后将制好的颗粒于920°C下闪烧10秒,再取出于200°C下烧制10分钟后,取出冷却,于浓度为6%的盐酸溶液中浸泡20分钟,取出,洗净,即得;
所述的一种经久耐用的河砂加气砖,
制备方法为:
(1)取河砂、脂肪酸甲醇酰胺、碳酸氢钠,玻化微珠、纸浆废液、磷矿渣粉混匀,加入适量水,在40°C下搅拌5分钟后,再加入水泥、铝矾土粉,搅拌均匀,得混合水泥浆料;
(2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,预养,脱模,切割,得砲块还;
(3)将砌块坯放入反应釜中蒸压养护12小时,入库即得。
[0008] 本砌块的平均容重为590kg/m3,平均值抗压强度为8.1MPa0

Claims (2)

1.一种经久耐用的河砂加气砖,其特征在于:其是由下述重量份的原料制得:石子5-8、铝矾土粉10-20、火山岩粉10-20、水泥15-25、河砂5-8、脂肪酸甲醇酰胺0.2-0.4、碳酸氢钠1-2,玻化微珠0.2-0.4、纸浆废液2-4、磷矿渣粉3-5、氢氧化钠1_2,糖蜜0.1-0.3、石膏0.1-0.3、硅粉5-10、安息香酸0.5-1.5、石油磺酸钠1.2-3.1、阿拉伯树胶0.3-1.6 ; 复配改性混凝土颗粒由下述重量份的原料制得: 硬脂酸0.2-0.5,钛白粉5-7,贝壳粉1-2、丙烯酸乳液1-2、糖蜜2_4、UEA混凝土膨胀剂1-2、玉石粉1-2、碳纳米管2-4、十二醇硫酸钠2.5-3.7、硼酸锌0.8-1.6、石墨粉3.5-4.8、氧化铝 1.5-2.4 ; 复配改性混凝土颗粒的制备方法为: 将所有原料混匀后,于500-700转/分下搅拌10-20分钟后,加适量水分,造粒,颗粒粒径在6-8mm,然后将制好的颗粒于900_920°C下闪烧8_10秒,再取出于200_300°C下烧制5-10分钟后,取出冷却,于浓度为3-6%的盐酸溶液中浸泡10-20分钟,取出,洗净,即得。
2.根据权利要求1所述的一种经久耐用的河砂加气砖,其特征在于: 制备方法为: (D将按重量份取河砂、脂肪酸甲醇酰胺、碳酸氢钠,玻化微珠、纸浆废液、磷矿渣粉混匀,加入适量水,在30-40°C下搅拌5-7分钟后,再加入水泥、铝矾土粉,搅拌均匀,得混合水泥浆料; (2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,预养,脱模,切割,得砲块还; (3)将砌块坯放入反应釜中蒸压养护10-15小时,入库即得。
CN201510401132.XA 2015-07-10 2015-07-10 一种经久耐用的河砂加气砖 Pending CN105016694A (zh)