CN104886835A - Two-sided down coat fabric capable of being filled with velvet and production method thereof - Google Patents
Two-sided down coat fabric capable of being filled with velvet and production method thereof Download PDFInfo
- Publication number
- CN104886835A CN104886835A CN201510247732.5A CN201510247732A CN104886835A CN 104886835 A CN104886835 A CN 104886835A CN 201510247732 A CN201510247732 A CN 201510247732A CN 104886835 A CN104886835 A CN 104886835A
- Authority
- CN
- China
- Prior art keywords
- sided
- suede
- warping
- warp
- axle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a two-sided down coat fabric capable of being filled with velvet and a production method thereof. The two-sided down coat fabric capable of being filled with velvet is characterized in that warp yarn is chinlon, weft yarn is polyester, and the linear density of the polyester and the chinlon is 15-30 D. The production method for producing the two-sided down coat fabric capable of being filled with velvet comprises the steps of warping, sizing, re-beaming, warp separation, drafting and weaving. The polyester and the chinlon with the linear density of 15-30 D are adopted as the warp yarn and the weft yarn to be woven and then undergo the steps of warping, sizing, re-beaming, warp separation, drafting and weaving so that the two-sided down coat fabric capable of being filled with velvet is obtained, the tradition that the velvet filling can be performed only after two layers of fabrics are sewn is broken, and the direct velvet filling is achieved.
Description
Technical field
The present invention relates to spinninging technical field, especially one can fill that suede is two-sided wears feather dress fabric
And production method.
Background technology
down jackets, are the warming clothing of indispensability in winter, are widely accepted now.Existing down jackets are generally fill eider down in interlayer, then by separator bar, whole clothes are divided into fritter, prevent eider down from falling to reuniting to bottom.Because the gap between cut-off rule is comparatively large, existing feather dress fabric there will be the phenomenon of running hair mostly, and most down jackets are all that one side is worn, and this brings a lot of inconvenience to people in dress.
Summary of the invention
The object of the invention is to design one and can fill that suede is two-sided wears feather dress fabric and production method thereof, solve the problem that down jackets run hair.
For achieving the above object, technical scheme of the present invention is: one can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that:
The described two-sided raw material wearing feather dress fabric of suede that fills is: warp thread is polyamide fibre, and weft yarn is terylene, and the line density of described terylene and polyamide fibre is 15 ~ 30D;
Describedly fill the two-sided production method of wearing feather dress fabric of suede, comprise following step: warping, slurry silk axle, lease making, gait, weave.
Further, described production method concrete steps are as follows:
A) warping step: batch warping is carried out to polyamide fibre, field, Tianjin coltfoal TWN-E warping machine is selected in described warping step, the speed of described warping machine is 295 ~ 305m/min, yarn cake is heavily 6 ~ 8kg, the tension force batched is 8 ~ 10kg, warp beam hardness is 80 ~ 90%, and the tension force of wire vent is 3 ~ 5g/ root, roller be pressurised into 0.15 ~ 0.25Mpa;
B) silk step is starched: the polyamide fibre after warping is starched silk machine stock tank by field, Tianjin coltfoal KSH500-e and pads slurries, concentration of slurry is 13 ~ 15%, temperature 40 ~ 50 DEG C, and the rate of sizing 11 ~ 12% mud jacking pressure is 3.5 ~ 4.0Mpa, and soaking paste pressure is 3.5 ~ 4.0Mpa; Dry the slurry axle making coated serous coat again through drying room, drying room temperature 120 ~ 140 DEG C, slurry axle hardness is 80 ~ 90%; In stock tank, percentage elongation controls is 0.1 ~ 0.3%, and in cylinder, percentage elongation controls 0.8 ~ 1.0%;
C) and axle step: the slurry axle after slurry silk is undertaken and axle by Toyota FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, the speed of warp rebeaming machine is 55 ~ 65m/min, going out thread tension is 8 ~ 10kg, and coiling tension is 100 ~ 120kg, and beam of a loom hardness is 80 ~ 90%.
D) lease making step: beam of a loom carries out lease making on leasing machine, the speeds control of leasing machine is at 80 ~ 100 pieces/minute.
E) to gait step: to gait method according to fabric, by the polyamide fibre on beam of a loom successively through plastic heddle and reed.
F) weaving step: adopt coltfoal ZW408 two water-jet loom in field, Tianjin to carry out weaving production, the speed of a motor vehicle of loom is 550 ~ 650rpm, and heald frame opening amount is 40 ~ 50mm, and traverse of beating up is 90 ~ 100mm, and loom weight tension force is 3 ~ 5kg.
Further, described fill suede two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of described access node, be innerly organized as plain weave, table warp, the back warp arrangement ratio of the two-sided tissue of described access node are 1:1, table latitude, back weft arrangement are than for 1:1, and described access node is two-sided, and to be organized in spacing in broadwise be 300 ~ 500.
Further, described fill suede two-sided wear feather dress fabric through close be 600 ~ 700/10cm, filling density is 540 ~ 640/10cm; Door width is 1.45 ~ 1.55m.
The invention has the beneficial effects as follows:
(1) the present invention adopts the polyamide fibre of 15 ~ 30D and terylene to interweave through, tram respectively, again through warping, slurry silk axle, lease making, gait, weave these six steps and obtain filling that suede is two-sided wears feather dress fabric, break conventional two layers of cloth and made the rear tradition just can filling suede, achieved and directly can fill suede.
(2) weaving step of the present invention have employed the two-sided institutional framework of access node, and what achieve fabric directly can fill suede, and thread count is large simultaneously, thus avoids the generation of boring suede phenomenon.
(3) polyamide fibre selected of the present invention and terylene, be the silk of original liquid coloring fibre spinning, eliminate staining procedure, and finished product fabric color fastness is good and stablize simultaneously.
(4) the present invention is in 6 steps of producing, and by setting distinctive technological parameter, reduces cracked ends and lousiness phenomenon, production process of the present invention can be carried out smoothly.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme of the present invention is elaborated.
Embodiment 1
One can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: can fill the two-sided raw material wearing feather dress fabric of suede is: warp thread is polyamide fibre, and weft yarn is terylene, and the line density of terylene and polyamide fibre is 15D;
The two-sided production method of wearing feather dress fabric of suede can be filled, comprise following step: warping, slurry silk axle, lease making, gait, weave.
Production method concrete steps are as follows:
A, warping step: carry out batch warping to polyamide fibre and terylene, select field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 295m/min, yarn cake is heavily 6kg, and the tension force batched is 8kg, and warp beam hardness is 80%, the tension force of wire vent is 3g/ root, roller be pressurised into 0.15Mpa;
B, slurry silk step: the polyamide fibre after warping and terylene are starched silk machine stock tank by field, Tianjin coltfoal KSH500-e and pads slurries, concentration of slurry is 13%, temperature 40 DEG C, and the rate of sizing 11% mud jacking pressure is 3.5Mpa, and soaking paste pressure is 3.5Mpa; Dry the slurry axle making coated serous coat again through drying room, drying room temperature 120 DEG C, slurry axle hardness is 90%; In stock tank, percentage elongation controls is 0.1%, and in cylinder, percentage elongation controls 0.8%;
C axle step: the slurry axle after slurry silk is undertaken and axle by Toyota FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 55m/min, and going out thread tension is 8kg, and coiling tension is 100kg, and beam of a loom hardness is 90%.
D, lease making step: beam of a loom carries out lease making on leasing machine, the speeds control of leasing machine is at 80 pieces/minute.
E, step of gaiting: to gait method according to fabric, by the polyamide fibre on beam of a loom successively through plastic heddle and reed.
F, weaving step: adopt coltfoal ZW408 two water-jet loom in field, Tianjin to carry out weaving production, the speed of a motor vehicle of loom is 550rpm, heald frame opening amount 40mm, and traverse of beating up is 100mm, and loom weight tension force is 3kg.
Further, can fill suede two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, be innerly organized as plain weave, table warp, the back warp arrangement ratio of the two-sided tissue of access node are 1:1, table latitude, back weft arrangement are than for 1:1, and access node is two-sided, and to be organized in spacing in broadwise be 300.
Further, can fill suede two-sided wear feather dress fabric through close be 700/10cm, filling density is 640/10cm; Door width is 1.45m.
Embodiment 2
One can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: can fill the two-sided raw material wearing feather dress fabric of suede is: warp thread is polyamide fibre, and weft yarn is terylene, and the line density of terylene and polyamide fibre is 30D; The two-sided production method of wearing feather dress fabric of suede can be filled, comprise following step: warping, slurry silk axle, leasing, gait, weave.
Further, production method concrete steps are as follows:
A) warping step: carry out batch warping to polyamide fibre and terylene, selects field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 305m/min, yarn cake is heavily 8kg, and the tension force batched is 10kg, and warp beam hardness is 80%, the tension force of wire vent is 5g/ root, roller be pressurised into 0.25Mpa;
B) silk step is starched: the polyamide fibre after warping and terylene are starched silk machine stock tank by field, Tianjin coltfoal KSH500-e and pads slurries, concentration of slurry is 13%, temperature 50 C, the rate of sizing 11%, and mud jacking pressure is 4.0Mpa, and soaking paste pressure is 4.0Mpa; Dry the slurry axle making coated serous coat again through drying room, drying room temperature 140 DEG C, slurry axle hardness is 80%; In stock tank, percentage elongation controls is 0.3%, and in cylinder, percentage elongation controls 1.0%;
C) and axle step: the slurry axle after slurry silk is undertaken and axle by Toyota FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 65m/min, and going out thread tension is 10kg, and coiling tension is 120kg, and beam of a loom hardness is 80%.
D) lease making step: beam of a loom carries out lease making on leasing machine, the speeds control of leasing machine is at 100 pieces/minute.
E) to gait step: to gait method according to fabric, by the polyamide fibre on beam of a loom successively through plastic heddle and reed.
F) weaving step: adopt coltfoal ZW408 two water-jet loom in field, Tianjin to carry out weaving production, the speed of a motor vehicle of loom is 550rpm, and heald frame opening amount is 50mm, and traverse of beating up is 90mm, and loom weight tension force is 5kg.
Further, can fill suede two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, be innerly organized as plain weave, table warp, the back warp arrangement ratio of the two-sided tissue of access node are 1:1, table latitude, back weft arrangement are than for 1:1, and access node is two-sided, and to be organized in spacing in broadwise be 300.
Further, can fill suede two-sided wear feather dress fabric through close be 600/10cm, filling density is 540/10cm; Door width is 1.55m.
Embodiment 3
One can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: can fill the two-sided raw material wearing feather dress fabric of suede is: warp thread is polyamide fibre, and weft yarn is terylene, and the line density of terylene and polyamide fibre is 20D; The two-sided production method of wearing feather dress fabric of suede can be filled, comprise following step: warping, slurry silk axle, lease making, gait, weave.
Further, production method concrete steps are as follows:
G) warping step: carry out batch warping to polyamide fibre, selects field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 300m/min, yarn cake is heavily 7kg, and the tension force batched is 9kg, and warp beam hardness is 85%, the tension force of wire vent is 4g/ root, roller be pressurised into 0.20Mpa;
H) silk step is starched: the polyamide fibre after warping and terylene are starched silk machine stock tank by field, Tianjin coltfoal KSH500-e and pads slurries, concentration of slurry is 14%, temperature 45 C, and the rate of sizing 11.5% mud jacking pressure is 3.7Mpa, and soaking paste pressure is 3.8Mpa; Dry the slurry axle making coated serous coat again through drying room, drying room temperature 130 DEG C, slurry axle hardness is 85%; In stock tank, percentage elongation controls is 0.2%, and in cylinder, percentage elongation controls 0.8%;
I) and axle step: the slurry axle after slurry silk is undertaken and axle by Toyota FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 60m/min, and going out thread tension is 10kg, and coiling tension is 110kg, and beam of a loom hardness is 85%.
J) lease making step: beam of a loom carries out lease making on leasing machine, the speeds control of leasing machine is at 90 pieces/minute.
K) to gait step: to gait method according to fabric, by the polyamide fibre in warp beam successively through plastic heddle and reed.
L) weaving step: adopt coltfoal ZW408 two water-jet loom in field, Tianjin to carry out weaving production, the speed of a motor vehicle of loom is 600rpm, and heald frame opening amount is 45mm, and traverse of beating up is 95mm, and loom weight tension force is 4kg.
Further, can fill suede two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, be innerly organized as plain weave, table warp, the back warp arrangement ratio of the two-sided tissue of access node are 1:1, table latitude, back weft arrangement are than for 1:1, and access node is two-sided, and to be organized in spacing in broadwise be 400.
Further, can fill suede two-sided wear feather dress fabric through close be 650/10cm, filling density is 590/10cm; Door width is 1.50m.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (7)
1. can fill that suede is two-sided wears feather dress fabric and a production method thereof, it is characterized in that:
The described two-sided raw material wearing feather dress fabric of suede that fills is: warp thread is polyamide fibre, and weft yarn is terylene, and the line density of described terylene and polyamide fibre is 15 ~ 30D;
Describedly fill the two-sided production method of wearing feather dress fabric of suede, comprise following step: warping, slurry silk axle, lease making, gait, weave.
2. one according to claim 1 can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: described production method concrete steps are as follows:
Warping step: batch warping is carried out to polyamide fibre, field, Tianjin coltfoal TWN-E warping machine is selected in described warping step, the speed of described warping machine is 295 ~ 305m/min, 6 ~ 8kg, the tension force batched is 8 ~ 10kg, warp beam hardness is 80 ~ 90%, and the tension force of wire vent is 3 ~ 5g/ root, roller be pressurised into 0.15 ~ 0.25Mpa;
Slurry silk step: the polyamide fibre after warping and terylene are starched silk machine stock tank by field, Tianjin coltfoal KSH500-e and pads slurries, concentration of slurry is 13 ~ 15%, temperature 40 ~ 50 DEG C, and the rate of sizing 11 ~ 12% mud jacking pressure is 3.5 ~ 4.0Mpa, and soaking paste pressure is 3.5 ~ 4.0Mpa; Dry the slurry axle making coated serous coat again through drying room, drying room temperature 120 ~ 140 DEG C, slurry axle hardness is 80 ~ 90%; In stock tank, percentage elongation controls is 0.1 ~ 0.3%, and in cylinder, percentage elongation controls 0.8 ~ 1.0%;
And axle step: the slurry axle after slurry silk is undertaken and axle by Toyota FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 55 ~ 65m/min, and going out thread tension is 8 ~ 10kg, and coiling tension is 100 ~ 120kg, and beam of a loom hardness is 80 ~ 90%.
3. lease making step: beam of a loom carries out lease making on leasing machine, the speeds control of leasing machine is at 80 ~ 100 pieces/minute.
4. to gait step: to gait method according to fabric, by the polyamide fibre in warp beam successively through plastic heddle and reed.
5. weaving step: adopt coltfoal ZW408 two water-jet loom in field, Tianjin to carry out weaving production, the speed of a motor vehicle of loom is 550 ~ 650rpm, and heald frame opening amount is 40 ~ 50mm, and traverse of beating up is 90 ~ 100mm, and loom weight tension force is 3 ~ 5kg.
6. one according to claim 1 can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: described fill suede two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of described access node, be innerly organized as plain weave, table warp, the back warp arrangement ratio of the two-sided tissue of described access node are 1:1, table latitude, back weft arrangement are than for 1:1, and described access node is two-sided, and to be organized in spacing in broadwise be 300 ~ 500.
7. one according to claim 1 can fill that suede is two-sided wears feather dress fabric and production method thereof, it is characterized in that: described fill suede two-sided wear feather dress fabric through close be 600 ~ 700/10cm, filling density is 540 ~ 640/10cm; Door width is 1.45 ~ 1.55m.