CN106811854A - Viscose glue twists the production method of silk and Modal/big jacquard home textile of cotton intertexture - Google Patents
Viscose glue twists the production method of silk and Modal/big jacquard home textile of cotton intertexture Download PDFInfo
- Publication number
- CN106811854A CN106811854A CN201611268572.3A CN201611268572A CN106811854A CN 106811854 A CN106811854 A CN 106811854A CN 201611268572 A CN201611268572 A CN 201611268572A CN 106811854 A CN106811854 A CN 106811854A
- Authority
- CN
- China
- Prior art keywords
- silk
- fabric
- viscose glue
- modal
- twists
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The production method of the big jacquard home textile that interweaves the present invention relates to a kind of viscose glue twisting silk and Modal/cotton, the described method comprises the following steps:(1) raw material prepares;(2) section warping;(3) flower pattern, organization design;(4) weave, (5) Final finishing;The viscose glue Silk jacquard home textile soft smooth of technical scheme exploitation, gloss such as silk, preferably embody the silk quality style of fabric, with the items wearability such as excellent hygroscopicity, gas permeability, integrate practicality, comfortableness, attractive in appearance, meet that people are high-grade to family's textile fabric, high-quality pursuit.
Description
Technical field
The present invention relates to a kind of quilt cover, and in particular to a kind of viscose glue twisting silk and Modal/big jacquard weave home textile face of cotton intertexture
The production method of material, belongs to textile product technical field.
Background technology
Viscose rayon softness, moisture absorption, permeability are good, and its gloss, feel, thermal conductivity etc. are close to silk, therefore viscose glue is imitative
Silk broadcloth has inborn superiority.Because viscose rayon is wet strong relatively low, elongation is big, weaving, dyeing and finishing difficulty it is big, existing
In product, usually do weft yarn, few manufacturer production radial direction viscose surface long filament men textile fabrics, due to production technology difficulty and
In process of production to the requirement of technology height, also there are many producers to want to attempt, but experiment effect is unsatisfactory, therefore,
A kind of new scheme of exigence solves the technical problem.
The content of the invention
The present invention is just being directed to the technical problem for existing in the prior art, there is provided a kind of viscose glue twisting silk and Modal/cotton
The production method of the big jacquard home textile that interweaves, the technical scheme proposes to do warp thread using viscose filament yarn, coordinates twisting and Gao Jing
It is close, a big jacquard home textile of Silk is developed to meet the demand in market.
To achieve these goals, technical scheme is as follows, and viscose glue twists silk with Modal/big jacquard weave of cotton intertexture
The production method of family's textile fabric, it is characterised in that the described method comprises the following steps:Fabric specification:Through close 1220/10cm,
413/10cm of filling density, breadth 269.5cm, big figured texture weave.
(1) raw material prepares:Warp thread continuously spins 75D/30f twisting silks from viscose glue, and the twist is 650 twists/m, and weft yarn is not using
Dai Er/cotton matches the 40s yarns of network compact spinning, and this technique productions flow is short and fabric that be fabricated to has gloss as silk and super soft
Soft feel;When the twist be less than certain value when, viscose filament yarn is excessively soft, warping and it is woven during end breakage rate it is high, production
Efficiency is low, and the gloss of elegant is lost through material behind Final finishing, and when the twist is higher than certain value, viscose filament yarn hardens, shaping
Difficulty, meanwhile, the twist is too high, and production efficiency is relatively low, and fabric is rough submissive.
(2) section warping:1) total radical is adjusted first, and warping radical is 58*556+1*492 roots;Bar * bars number wide is
47.38mm*58+41.93mm*1;Displacement is 0.91mm;2) carry out cleaning, to be carried out before production each Xelminator,
The housekeeping of each reed, each deflector roll, the secondly key in tension in Warping Shi Ge roads, tension force will detect progressively, the irregular appearance of tension force
Easily cause Final finishing dyed color inconsistent.3) relevant tension force is adjusted, bobbin cradle tension force is 5.0-6.5CN, and coiling tension is
14kg;4) warped length, due to the characteristic of raw material, warped length is unsuitable oversize, and beam of a loom must be changed into certain hour, to subtract
Few press strip phenomenon between bar and bar.5) points for attention and solution, in on-position, viscose exists section warping operation
The easy residual torque for occurring to be formed because drawing-off is acted on before tension pulley, the silk ring of kink easily causes jump in sizing and simultaneously axle
Reed and phenomenon is hung up, cause monofilament tension force irregular, increase tieing and machine stop times, influence the quality of warping.Asked to solve this
Topic, can suitably increase tension pulley tension force, be advisable with 5.0-6.5CN.In addition, can also place cloth set outside raw material bobbin, gas is controlled
Circle tension force.Kink can be thus solved the problems, such as, production requirement is met.
(3) flower pattern, organization design:Flower pattern spends bit width 78cm, length 125cm based on elegant fine and smooth European grain pattern,
In order to embody the silk quality style of fabric, ground tissue is double with latitude, and table organization is five piece three and flies through face satin, and inner tissue is ten piece three and flies
Through face satin;The leaf of flower pattern flies a reinforcement, two reinforcements, three reinforcement filling satins from outer layers towards inner layers using eight piece three, so as to be formed
Stereovision from bright to dark;Floral parts fly a reinforcement, two reinforcements, three reinforcement filling satins using ten piece seven, and pistil part uses
Ten pieces or 12 pieces of twill.During using the tissue progressively strengthened, it is ensured that tissue starting point is identical, tissue is without line floating long long.
Whole fabric highlights classical and modern combination.Fabric tissue is shown in Fig. 1.Vertical line represents warp thread in figure, and horizontal line represents weft yarn, warp thread
Figurative jacquard is intertwined to form with weft yarn.Upper floating-point represents that lower floating-point is represented with " ", in fabric not with " ■ " in figure
Showed by upper and lower floating number tissue change with big figured texture weave.
(4) weave:Weaved using Azithromycin arrow shaft ALPHA-340, when the temperature control in workshop is at 23 DEG C~27 DEG C, relatively
Humidity is 68%~74%, and loom efficiency and fabric quality are all relatively stablized, and need to strictly control workshop moisture temperature, secondly, woven
Technique:Back beam height 0mm, 330 degree of opening time enters 68 degree of sword time, connects sword time 180 degree.The kind is ALPHA-340's
Produced on big jacquard loom, in weaving process, because single fiber is thin, the easy snag broken end of organizine influences weaving efficiency.Therefore,
It is appropriate to reduce warp tension, increase shed opening, it is ensured that opening is clear.To reduce for weft yarn and move back solution tension force, selection is suitable
Storage latitude form.Because fabric looped weft is larger, the auxiliary appliances such as width support, rough surfaced rubber covering are chosen, it is ensured that weaving is smoothed out.
Technical requirements in weaving process:
1) because the product is through close higher, broadwise shrinkage factor is larger, and the width for making coiling system is supportted, rough surfaced rubber covering load increases
Plus, easily there is weft bar and rotten side.Therefore, often to change rough surfaced rubber covering, it is ensured that batch required frictional force.Simultaneously by spiked roller
Make the support of three row's bastard width into, effect is preferable.
2) when lousiness occurs in organizine, timely processing and exchanging, prevents large area organizine from twisting disconnected.To prevent through tram during operation
Line scratch is scared.
3) warp tension is when weaving:2000N, rotating speed:250r/min.
4) control of workshop moisture temperature.If relative humidity is too small, workshop dries, and yarn rubs by reed, heald, menopause tablet
Easily fluffing is wiped, and is easily wound between yarn, the clear Xi in influence opening.When humidity is excessive, viscose filament yarn moisture absorption is excessive to cause strength to drop
Low, according to the actual conditions of production, by the temperature control in workshop at 23 DEG C~27 DEG C, relative humidity is 68%~74%, loom
Efficiency and fabric quality are all relatively stablized.
(5) Final finishing:Fabric uses flat cylinder one-bath dyeing, and using reactive dye, the links of dyeing are it is noted that anti-
Only wrinkle prints, especially shaping process, and process is as follows:Fabric turn over stitch → singe → concise → preboarding → dyeing → washing drying →
Final finishing → finished product;
1) singe:Speed of singing is slow, though being conducive to singing totally, easilys lead to semi-finished product feel and aggravates to subtract firmly partially
Amount, therefore appropriate condition must be controlled;
2) kiering:Cleaning fabric is added in process, accumulative various finishes and dirt;
3) pre-setting:Control one both meets removal fine wrinkle, improves elasticity and stabilization door width requirement, and as reduces fixed as possible
The process conditions of shape temperature, it is to avoid preboarding makes fabric feeling partially hard;
4) dye:Viscose glue, Modal and cotton are dyeed using single bath process reactive dye, though three kinds of raw materials belong to the same sex
Matter, but due to the speed of dye uptake can produce it is deep mixed, so as to realize that Adjacent color knits the fabric of effect;
5) washing drying:Cloth cover is unnecessary and dyestuff that is not reacting for removal, improves the color fastness of fabric;
6) Final finishing:Preshrunk, calendering, stentering forming.
Relative to prior art, advantages of the present invention is as follows:1) the whole Technical Design of the present invention is ingenious, big jacquard weave man
Textile fabric is formed by warp and weft interweaving, and warp thread is mutually crossing at right angle configuration across weft yarns, and warp thread is continuously spun using viscose glue
75D/30f twists silk, and the twist is 650 twists/m, and weft yarn uses the 40s yarns of Modal/cotton blend;2) technical scheme is developed
Viscose glue Silk jacquard home textile soft smooth, gloss such as silk preferably embodies the silk quality style of fabric, with excellent suction
The items wearability such as moist, gas permeability, integrates practicality, comfortableness, attractive in appearance, meets people to family's textile fabric top grade
Secondary, high-quality pursuit;3) whole production process and uncomplicated, easy operation, are easy to large-scale popularization and application.
Brief description of the drawings
Fig. 1 is flower pattern organization design schematic diagram of the present invention.
Specific embodiment
In order to deepen the understanding of the present invention and understanding, with reference to specific embodiment, the invention will be further described
And introduction.
Embodiment 1:Referring to Fig. 1, the producer of a kind of viscose glue twisting silk and Modal/big jacquard home textile of cotton intertexture
Method, the described method comprises the following steps:Fabric specification:Through close 1220/10cm, filling density 413/10cm, breadth 269.5cm,
Big figured texture weave.
(1) raw material prepares, and warp thread continuously spins 75D/30f twisting silks from viscose glue, and the twist is 650 twists/m, and weft yarn is not using
Dai Er/cotton matches the 40s yarns of network compact spinning, and this technique productions flow is short and fabric that be fabricated to has gloss as silk and super soft
Soft feel;When the twist be less than certain value when, viscose filament yarn is excessively soft, warping and it is woven during end breakage rate it is high, production
Efficiency is low, and the gloss of elegant is lost through material behind Final finishing.When the twist is higher than certain value, viscose filament yarn hardens, shaping
Difficulty, meanwhile, the twist is too high, and production efficiency is relatively low, and fabric is rough submissive.
(2) section warping:Warping radical is 58*556+1*492 roots;Bar * bars number wide is 47.38mm*58+41.93mm*1;
Displacement is 0.91mm.Each Xelminator, each reed, the housekeeping of each deflector roll are carried out before production, secondly warping
The key in Li Shige roads, tension force will detect progressively, and tension force is irregular, and to easily cause Final finishing dyed color inconsistent.Bobbin cradle tension force
It is 5.0-6.5CN, coiling tension is 14kg;It is specifically intended that due to the characteristic of raw material, warped length is unsuitable oversize, and necessarily
Beam of a loom must be changed into time, to reduce the press strip phenomenon between bar and bar.Section warping operation in on-position, viscose
The easy residual torque for occurring to be formed because drawing-off is acted on before tension pulley, the silk ring of kink easily causes in sizing and simultaneously axle
Jump reed and hang up phenomenon, cause monofilament tension force irregular, increase tieing and machine stop times, influence the quality of warping.To solve this
Problem, can suitably increase tension pulley tension force, be advisable with 5.0-6.5CN.In addition, can also place cloth set outside raw material bobbin, control
Balloon tension.Kink can be thus solved the problems, such as, production requirement is met.Required during section warping process operations as follows:1) it is raw
Each Xelminator, each reed, the housekeeping of each deflector roll are carried out before product;2) bobbin will check whether bad cylinder on, take
Silk, climbs that silk is serious need to be pulled off superficial layer, is handled with care during feeding, in order to avoid scratch raw material;3) tension in Warping control Shi Ge roads
Key, monofilament tension force must keep the uniformity, tension force progressively to detect.Winding part requirement even tension could be produced.
Under the premise of normal driving is ensured, tension force can be small then small.Tension force is irregular, easily causes Final finishing dyed color inconsistent;4) wear
Put on from the right during reed, worn from bottom to top, untill having worn;5) bar of warping is long can not be long, controls within 800 meters,
And beaming operation must be completed within a certain period of time, the humiture in strict control workshop, whole good beam of a loom must be sealed and packed,
Prevent hygroscopic deformation.
(3) flower pattern, organization design:Flower pattern spends bit width 78cm, length 125cm based on elegant fine and smooth European grain pattern,
In order to embody the silk quality style of fabric, ground tissue is double with latitude, and table organization is five piece three and flies through face satin, and inner tissue is ten piece three and flies
Through face satin;The leaf of flower pattern flies a reinforcement, two reinforcements, three reinforcement filling satins from outer layers towards inner layers using eight piece three, so as to be formed
Stereovision from bright to dark;Floral parts fly a reinforcement, two reinforcements, three reinforcement filling satins using ten piece seven, and pistil part uses
Ten pieces or 12 pieces of twill.During using the tissue progressively strengthened, it is ensured that tissue starting point is identical, tissue is without line floating long long.
Whole fabric highlights classical and modern combination.Fabric tissue is shown in Fig. 1.Vertical line represents warp thread in figure, and horizontal line represents weft yarn, warp thread
Figurative jacquard is intertwined to form with weft yarn.Upper floating-point represents that lower floating-point is represented with " ", in fabric not with " ■ " in figure
Showed by upper and lower floating number tissue change with big figured texture weave.
(4) weave:Weaved using Azithromycin arrow shaft ALPHA-340, when the temperature control in workshop is at 23 DEG C~27 DEG C, relatively
Humidity is 68%~74%, and loom efficiency and fabric quality are all relatively stablized, and need to strictly control workshop moisture temperature, secondly, woven
Technique:Back beam height 0mm, 330 degree of opening time enters 68 degree of sword time, connects sword time 180 degree.The kind is ALPHA-340's
Produced on big jacquard loom, in weaving process, because single fiber is thin, the easy snag broken end of organizine influences weaving efficiency.Therefore,
It is appropriate to reduce warp tension, increase shed opening, it is ensured that opening is clear.To reduce for weft yarn and move back solution tension force, selection is suitable
Storage latitude form.Because fabric looped weft is larger, the auxiliary appliances such as width support, rough surfaced rubber covering are chosen, it is ensured that weaving is smoothed out.
Technical requirements in weaving process:1) because the product is through close higher, broadwise shrinkage factor is larger, makes coiling system
Width support, rough surfaced rubber covering load increase, and weft bar and rotten side easily occur.Therefore, often to change rough surfaced rubber covering, it is ensured that needed for batching
Frictional force.Make spiked roller the support of into three row's bastard width simultaneously, effect is preferable;2) when lousiness occurs in organizine, timely processing and exchanging,
Prevent large area organizine from twisting disconnected.To prevent that the scratch of longitude and latitude silk thread is scared during operation;3) warp tension is when weaving:2000N, turns
Speed:250r/min;4) control of workshop moisture temperature.If relative humidity is too small, workshop dries, and yarn is by reed, heald, menopause
Piece friction easily fluffing, and easily wound between yarn, the clear Xi in influence opening.When humidity is excessive, viscose filament yarn moisture absorption is excessive to cause strong
Power reduction, according to the actual conditions of production, by the temperature control in workshop at 23 DEG C~27 DEG C, relative humidity is 68%~74%,
Loom efficiency and fabric quality are all relatively stablized;(5) Final finishing:Fabric uses flat cylinder one-bath dyeing, using reactive dye, dyeing
Links it is noted that preventing wrinkle from printing, especially shaping process, process is as follows:Fabric is turned over and stitches → singe → concise → preboarding
→ dyeing → washing drying → Final finishing → finished product;1) singe:Speed of singing is slow, though being conducive to singing totally, is easy to lead
Cause semi-finished product feel partially hard and aggravate decrement, therefore appropriate condition must be controlled;2) kiering:Cleaning fabric adds in process
Plus, accumulative various finishes and dirt;3) pre-setting:Control one both meets removal fine wrinkle, improves elasticity and stabilization door
Width requirement, and the process conditions of setting temperature are reduced as far as possible, it is to avoid preboarding makes fabric feeling partially hard;) 4) dye:Using one
Bath method reactive dye are dyeed to viscose glue, Modal and cotton, though three kinds of raw materials belong to connatural, and it is fast due to dye uptake
Slowly can produce it is deep mixed, so as to realize that Adjacent color knits the fabric of effect;5) washing drying:Removal cloth cover it is unnecessary and do not occur
The dyestuff of reaction, improves the color fastness of fabric;6) Final finishing:Preshrunk, calendering, stentering forming.
It should be noted that above-described embodiment, not for limiting protection scope of the present invention, in above-mentioned technical proposal
On the basis of done equivalents or replacement each fall within the scope that the claims in the present invention are protected.
Claims (4)
1. viscose glue twists the production method of silk and Modal/big jacquard home textile of cotton intertexture, it is characterised in that methods described bag
Include following steps:
(1) raw material prepares:Warp thread continuously spins 75D/30f twisting silks from viscose glue, and the twist is 650 twists/m, and weft yarn is using not generation
That/cotton matches the 40s yarns of network compact spinning;
(2) section warping:Each Xelminator, each reed, the housekeeping of each deflector roll are carried out before production, secondly warping
Tension force, tension force will progressively detect that bobbin cradle tension force is that 5.0-6.5CN is advisable, and coiling tension is 14kg;
(3) flower pattern, organization design:Flower bit width 78cm, length 125cm, in order to embody the silk quality style of fabric, ground tissue latitude
Double, table organization is five piece three and flies through face satin, and inner tissue is ten piece three and flies through face satin;The leaf of flower pattern is used from outer layers towards inner layers
Eight piece three flies a reinforcement, two reinforcements, three reinforcement filling satins, so as to form the stereovision from bright to dark;Floral parts use ten pieces
Seven fly a reinforcement, two reinforcements, three reinforcement filling satins, and pistil part uses ten pieces or 12 pieces of twill;
(4) weave:At 23 DEG C~27 DEG C, relative humidity is 68%~74% to the temperature control in workshop, loom efficiency and cloth cover matter
Amount is all relatively stablized, and need to strictly control workshop moisture temperature, secondly, woven technique:Back beam height 0mm, 330 degree of opening time, enters
68 degree of sword time, connect sword time 180 degree;
(5) Final finishing:Fabric uses flat cylinder one-bath dyeing, using reactive dye.
2. viscose glue according to claim 1 twists the production method of silk and Modal/big jacquard home textile of cotton intertexture, its
It is characterised by, the step (2) section warping concrete operations are as follows:
(1) each Xelminator, each reed, the housekeeping of each deflector roll to be carried out before producing;
(2) bobbin will check whether bad cylinder on, take silk, climb that silk is serious need to be pulled off superficial layer, be handled with care during upper bobbin, with
Exempt to abrade raw material;
(3) key in tension in Warping control Shi Ge roads, monofilament tension force must keep the uniformity, tension force progressively to detect, wind
Means suitable even tension could be produced, and under the premise of normal driving is ensured, tension force can be small then small, and tension force is irregular, easily causes
Final finishing dyed color is inconsistent;Tensity size is 1.5-2.0KG;
(4) put on from the right during denting, worn from bottom to top, untill having worn;
(5) bar of warping is long can not be long, controls within 800 meters, and beaming operation must be completed within a certain period of time, when
Between within 28 hours, the humiture in strict control workshop, whole good beam of a loom must be sealed and packed, prevents hygroscopic deformation.
3. viscose glue according to claim 1 twists the production method of silk and Modal/big jacquard home textile of cotton intertexture, its
It is characterised by, in step (4) weaving process, warp tension is during weaving:2000N, rotating speed:250r/min.
4. viscose glue according to claim 1 twists the production method of silk and Modal/big jacquard home textile of cotton intertexture, its
It is characterised by, step (5) postfinishing process is as follows:Fabric is turned over and stitches → singe → concise → preboarding → dyeing → washing baking
Dry → Final finishing → finished product;Wherein 1) singe, two sides is singed, speed of singing is fast, speed 70-80m/min, flame control temperature
In 700-800 degrees Celsius of 2) kiering:Cleaning fabric is added in process, accumulative various finishes and dirt;3) it is pre-
Sizing:180 degrees Celsius of setting temperature, speed 25-30m/min, shrinkage control had so both met removal fine wrinkle, had improved bullet 4%
Property and stablize the requirement of door width, avoid preboarding to make fabric feeling partially hard again;4) dye:Using single bath process reactive dye to viscous
Glue, Modal and cotton carry out dyeing 5) washing drying:Cloth cover is unnecessary and dyestuff that is not reacting for removal, improves the color of fabric
Fastness;6) Final finishing:Preshrunk, calendering, stentering forming.