CN103014995A - Alloy germanium fiber and cellulosic fiber blended fabric with touch cool feeling and preparation method thereof - Google Patents
Alloy germanium fiber and cellulosic fiber blended fabric with touch cool feeling and preparation method thereof Download PDFInfo
- Publication number
- CN103014995A CN103014995A CN2012105893723A CN201210589372A CN103014995A CN 103014995 A CN103014995 A CN 103014995A CN 2012105893723 A CN2012105893723 A CN 2012105893723A CN 201210589372 A CN201210589372 A CN 201210589372A CN 103014995 A CN103014995 A CN 103014995A
- Authority
- CN
- China
- Prior art keywords
- cool feeling
- fiber
- sheng
- alloy germanium
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an alloy germanium fiber and cellulosic fiber blended fabric with a touch cool feeling, and a preparation method thereof. The fabric is prepared by blending 25-45% of alloy germanium fiber with 55-75% of cellulosic fiber in percentage by weight. Compared with the prior art, the excellent performance of the cellulosic fiber can be brought into play, the limitation of a material which is polyester fiber does not exit, the usage amount of the material is reduced to the hilt, the functionality is guaranteed at the same time, the effect of the cool feeling is applied, the usage temperature of products is lower than that of like products by 3-4 DEG C, the functions of negative ions, far infrared rays and bacterial resistance and the like are also achieved at the same time, the raw material range of home textiles is expanded, a good market prospect is obtained, and the purpose of the invention is fulfilled.
Description
Technical field
The present invention relates to a kind of blended yarn woven fabric and preparation method thereof, particularly a kind of alloy germanium fiber of contact cool feeling and Sheng-bast fiber blended yarn woven fabric and preparation method thereof.
Background technology
Along with improving constantly of quality of life, people are higher to comfortableness, health and the fashion-orientation requirement of household textiles, are constantly to strengthen enterprise core competence, the new product that exploitation is met the need of market, optimize product structure, improving product specification is the core of enterprise development.
The alloy germanium fiber is a kind of tencel of developing in recent years, the alloy germanium fiber is as carrier take terylene, in spinning process, adopt the good odd-shaped cross section structure of moisture permeability, and add the nice and cool modified master batch of a certain proportion of nanoscale germanium system, making fiber that good cooling effect and certain negative ion health, deodorizing and antistatic effect in use be arranged, is the functional fiber of the energy-conservation and health effect of a kind of low-carbon environment-friendly.But because its material is polyster fibre, traction is very limited.
Sheng-bast fiber is a kind of New Regenerated Cellulosic Fibers, have natural antibacterial, press down the mite performance, it is a kind of New textile material truly, have simultaneously good spinnability, dyeing characteristics beautiful, comfortable and easy to wear, it can remedy the deficiency of natural ramie fiber, greatly improve the class of linen, captured the insurmountable difficult problem of bast fibre spinning over more than 4000 year.
Therefore, need especially a kind of alloy germanium fiber of contact cool feeling and Sheng-bast fiber blended yarn woven fabric and preparation method thereof, to solve the above-mentioned existing problem that exists.
Summary of the invention
The object of the present invention is to provide a kind of alloy germanium fiber of contact cool feeling and Sheng-bast fiber blended yarn woven fabric and preparation method thereof, for the deficiencies in the prior art, improved the unconspicuous problem of conventional cool feeling finishing effect, make fabric cool feeling successful, and washable effective, realized the cool feeling man textile fabric of real meaning.
Technical problem solved by the invention can realize by the following technical solutions:
On the one hand, the invention provides a kind of alloy germanium fiber and Sheng-bast fiber blended yarn woven fabric of contact cool feeling, it is characterized in that, it is formed by alloy germanium fiber and Sheng-bast fiber blending, the percentage by weight of described alloy germanium fiber is 25-45%, and the percentage by weight of described Sheng-bast fiber is 55-75%.
In one embodiment of the invention, the alloy germanium fiber of described contact cool feeling and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
On the other hand, the invention provides a kind of preparation method of alloy germanium fiber and Sheng-bast fiber blended yarn woven fabric of contact cool feeling, it is characterized in that, it comprises the steps: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
In one embodiment of the invention, in described drafting and the rove, and the suitable draft process of strip adoption, slubbing adopts 6 also to close; The drafting multiple of rove is 8 times.
In one embodiment of the invention, arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling.
Further, described cool feeling finishing agent selects a kind of among the fibroin cool feeling finishing agent TK COOL SP-6 of TAKAMATSU OIL or the amino acid cool feeling arrangement TK COOL 53K to carry out composite forming with TASTEX COOL-EX TANATEXCHEMICALS, and composite ratio is 1:1-2.
Further, the pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 100-120 ℃, and the time is 40-60s.
In one embodiment of the invention, the fabric of putting in order after the described cool feeling is washed 10 times and is hanged down 3 ℃ afterwards than not putting low 3-4 ℃ of fabric temperature in order.
The alloy germanium fiber of contact cool feeling of the present invention and Sheng-bast fiber blended yarn woven fabric and preparation method thereof, compared with prior art, the premium properties of Sheng-bast fiber was brought into play, making again it not be subjected to material is the restriction of polyster fibre, its use amount is dropped to minimum, the functional guarantee of while, on this basis in conjunction with putting in order after the cool feeling, make the product serviceability temperature lower 3-4 ℃ than like product, also have simultaneously anion, far infrared and the function such as antibiotic concurrently, expand house and spun the raw material scope, good market prospects have been arranged, realized purpose of the present invention.
Characteristics of the present invention can be consulted the detailed description of the following better embodiment of this case and be obtained to be well understood to.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, further set forth the present invention below in conjunction with concrete.
The alloy germanium fiber of contact cool feeling of the present invention and Sheng-bast fiber blended yarn woven fabric, it is formed by alloy germanium fiber and Sheng-bast fiber blending, and the percentage by weight of described alloy germanium fiber is 25-45%, and the percentage by weight of described Sheng-bast fiber is 55-75%.
In the present invention, the alloy germanium fiber of described contact cool feeling and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
The alloy germanium fiber of contact cool feeling of the present invention and the preparation method of Sheng-bast fiber blended yarn woven fabric, it comprises the steps: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
In the present invention, in described drafting and the rove, and the suitable draft process of strip adoption, slubbing adopts 6 also to close; The drafting multiple of rove is 8 times.
And strip adoption is along draft process, is conducive to stretching of crotch behind the fiber, improves bar evenness; Guarantee that production environment relative humidity about 65%, reduces the speed of a motor vehicle, twine the roller phenomenon to prevent; Slubbing adopts 6 also to close, and reduces the total draft multiple, prevents the excessive drawing-off of fiber and affects bar and do.The grasp less than normal of regular roving feeding and drafting multiple.Test shows, drafting multiple generally should be controlled at about 8 times, worsens for preventing out that hardhead or bar are done, and back zone drafting multiple should grasp bigger than normal.
For making the cloth cover lines clear, embody the due style of fabric, should rationally adjust through the position line when weaving.Middle because of through close higher for weaving, heald frame is more, easily causes opening unclear, and the wefting insertion difficulty easily produces through problems such as fault such as contracting, looped wefts, and emphasis is analyzed, studies, adjusted techniques such as brown frame, the back rest, warp stop frame height and Opening Travels; And to main jet, auxiliary jet pressure, Filling Insertion Time has been done corresponding adjustment; Rationally the control warp tension guarantees that opening is clear, and wefting insertion is smooth, has improved loom efficiency, has stablized grey quality.
In the present invention, arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling.
Described cool feeling finishing agent selects a kind of among the fibroin cool feeling finishing agent TK COOL SP-6 of TAKAMATSU OIL or the amino acid cool feeling arrangement TK COOL 53K to carry out composite forming with TASTEX COOL-EX TANATEXCHEMICALS, and composite ratio is 1:1-2.
The pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 100-120 ℃, and the time is 40-60s.
In the present invention, the fabric of putting in order after the described cool feeling is washed 10 times and is hanged down 3 ℃ afterwards than not putting low 3-4 ℃ of fabric temperature in order.
Embodiment 1
Step: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
Wherein, the percentage by weight of alloy germanium fiber is 25%, and the percentage by weight of Sheng-bast fiber is 75%.
Arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling, described cool feeling finishing agent selects the fibroin cool feeling finishing agent TK COOL SP-6 of TAKAMATSU OIL and the TASTEX COOL-EX of TANATEXCHEMICALS to carry out composite forming, and composite ratio is 1:1.The pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 100 ℃, and the time is 40s.
The alloy germanium fiber for preparing and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
Embodiment 2
Step: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
Wherein, the percentage by weight of alloy germanium fiber is 45%, and the percentage by weight of Sheng-bast fiber is 55%.
Arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling, and described cool feeling finishing agent selects the TASTEX COOL-EX of amino acid cool feeling arrangement TK COOL 53K and TANATEXCHEMICALS to carry out composite forming, and composite ratio is 1:1.5.The pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 120 ℃, and the time is 60s.
The alloy germanium fiber for preparing and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
Embodiment 3
Step: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
Wherein, the percentage by weight of alloy germanium fiber is 35%, and the percentage by weight of Sheng-bast fiber is 65%.
Arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling, described cool feeling finishing agent selects the fibroin cool feeling finishing agent TK COOL SP-6 of TAKAMATSU OIL and the TASTEX COOL-EX of TANATEXCHEMICALS to carry out composite forming, and composite ratio is 1:2.The pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 110 ℃, and the time is 50s.
The alloy germanium fiber for preparing and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
Above demonstration and described basic principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications; these changes and improvements all fall in the claimed scope of the invention, and the claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (8)
1. the alloy germanium fiber of a contact cool feeling and Sheng-bast fiber blended yarn woven fabric is characterized in that, it is formed by alloy germanium fiber and Sheng-bast fiber blending, and the percentage by weight of described alloy germanium fiber is 25-45%, and the percentage by weight of described Sheng-bast fiber is 55-75%.
2. the alloy germanium fiber of contact cool feeling as claimed in claim 1 and Sheng-bast fiber blended yarn woven fabric is characterized in that, the alloy germanium fiber of described contact cool feeling and the size changing rate of Sheng-bast fiber blended yarn woven fabric are warp-wise≤5.0%, broadwise≤5.0%; Fabric anion burst size is 〉=2800/cm
3, wash 10 times after anion burst size 〉=2500/cm
3To the bacteriostasis rate of Escherichia coli, staphylococcus aureus, candida albicans all more than 95%.
3. the preparation method of the alloy germanium fiber of a contact cool feeling and Sheng-bast fiber blended yarn woven fabric is characterized in that, it comprises the steps: arrangement → finished product after warping → sizing → drafting and rove → weave → cool feeling.
4. the preparation method of the alloy germanium fiber of contact cool feeling as claimed in claim 3 and Sheng-bast fiber blended yarn woven fabric is characterized in that, in described drafting and the rove, and the suitable draft process of strip adoption, slubbing adopts 6 also to close; The drafting multiple of rove is 8 times.
5. the preparation method of the alloy germanium fiber of contact cool feeling as claimed in claim 3 and Sheng-bast fiber blended yarn woven fabric is characterized in that, arrangement is also oven dry after adopting the cool feeling finishing agent to pad after the described cool feeling.
6. the preparation method of the alloy germanium fiber of contact cool feeling as claimed in claim 5 and Sheng-bast fiber blended yarn woven fabric, it is characterized in that, described cool feeling finishing agent selects a kind of among the fibroin cool feeling finishing agent TK COOL SP-6 of TAKAMATSU OIL or the amino acid cool feeling arrangement TK COOL 53K to carry out composite forming with TASTEX COOL-EX TANATEXCHEMICALS, and composite ratio is 1:1-2.
7. the preparation method of the alloy germanium fiber of contact cool feeling as claimed in claim 5 and Sheng-bast fiber blended yarn woven fabric is characterized in that, the pick-up that described cool feeling finishing agent pads is 70%, and the temperature of described oven dry is 100-120 ℃, and the time is 40-60s.
8. the preparation method of the alloy germanium fiber of contact cool feeling as claimed in claim 3 and Sheng-bast fiber blended yarn woven fabric is characterized in that, the fabric of putting in order after the described cool feeling is washed 10 times afterwards than not putting low 3 ℃ of fabric temperature in order than not putting low 3-4 ℃ of fabric temperature in order.