CN101191269A - Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof - Google Patents

Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof Download PDF

Info

Publication number
CN101191269A
CN101191269A CNA2006101297237A CN200610129723A CN101191269A CN 101191269 A CN101191269 A CN 101191269A CN A2006101297237 A CNA2006101297237 A CN A2006101297237A CN 200610129723 A CN200610129723 A CN 200610129723A CN 101191269 A CN101191269 A CN 101191269A
Authority
CN
China
Prior art keywords
fabric
blended
technique
yawn
tencel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006101297237A
Other languages
Chinese (zh)
Inventor
高雨田
绳丽云
张红
阎贵珠
陈秀敏
许晶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANFANG INVESTMENT HOLDING CO Ltd TIANJIN
Original Assignee
TIANFANG INVESTMENT HOLDING CO Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANFANG INVESTMENT HOLDING CO Ltd TIANJIN filed Critical TIANFANG INVESTMENT HOLDING CO Ltd TIANJIN
Priority to CNA2006101297237A priority Critical patent/CN101191269A/en
Publication of CN101191269A publication Critical patent/CN101191269A/en
Pending legal-status Critical Current

Abstract

The invention relates to a Shengma fiber and tencel blended slub fabric and a manufacturing technique thereof, wherein, the fabric adopts Shengma and tencel blended yarns for weaving, and blended proportion of the blended yarns is that: Shengma to tencel is equal to 30-70 to 70-30. The technique of the invention adopts special technological methods in procedures like spinning, slashing, denting, weaving and so on. The invention has the advantages that: firstly, two environment friendly fibers are reasonably utilized, and the fabric integrates advantages of the two fibers, namely characteristics of natural antibacterium and anti-acariens of the Shengma fiber and characteristics of excellent hygroscopicity, thinness, easy washing and drying, smooth hand feeling and good luster of the tencel; secondly, serviceability of the fabric is good, and the fabric has the characteristics of inability of stimulating human skin, moisture absorption, perspiration, antibacterium, anti-acariens, comfort and favorability for health; thirdly, the manufacturing technique is improved and innovated; effective technique is provided for blended weaving of the two fibers; an ideal environment friendly product is provided for the society; the fabric has good social benefit and economic benefit.

Description

Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof
Technical field
The present invention relates to a kind of fabric and manufacture method thereof of field of textiles, particularly relate to a kind of Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof.
Background technology
In recent years, along with the continuous development of textile technology, textiles has had very big development on kind and processing technology, and environmental protection, safety, health and comfortableness are paid attention in the design of textiles more.Adopt functional tencel spinning, utilize the yarn of different component fiber development complex function, can change yarn texture, performance and function, make the advantage between the different fibers obtain complementation, the new type yarn that obtained performance is good, thus the wearability and the appearance effect of lining improved.
Sheng-bast fiber is numb material regenerated celulose fibre, is raw material with natural fiber crops, adopts technologies such as boiling, bleaching, glue, spinning, post processing, the cellulose in the numb material is extracted, and kept numb material natural antibacterial, but acaricidal property is made fiber.It is a kind of weaving novel material, good spinnability, and it is beautiful, comfortable and easy to wear to dye, and has the characteristic of linen simultaneously again.China is that the world produces numb big country, and numb aboundresources utilizes numb material to produce Sheng-bast fiber, has opened up new approach for natural fiber crops comprehensive utilization, has solved some fiber crops and can not be directly used in spinning and weave and bast fibre spinning leftover bits and pieces waste problem, has remedied the deficiency of natural flax fibre.
It silk (Tencel) is a pure natural reproducibility fiber, is to be that raw material is made with the native cellulose that extract in 100% natural wood pulp of extracting from eucalyptus.Its feature is: have than real silk sensation of softness more, than the outstanding hygroscopicity of cotton, frivolous easily washing easily done, and though do or wet state under its powerful cotton fiber product that surpasses far away, feel is soft and smooth to have a same gloss, is environmental protection raw material newly developed.
At present, about Sheng-bast fiber and tencel blended fabric and also not discovery of manufacture method thereof.
Summary of the invention
In order to overcome the weak point of existing product and production technology, the invention provides a kind of Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof.This fabric combines the advantage of two kinds of fibers, is a kind of desirable environment-friendly products, has bigger market potential.
Technical scheme of the present invention is to realize like this.
A kind of Sheng-bast fiber and tencel blended bamboo node fabric, this fabric adopts Sheng-bast fiber and tencel blended bamboo node weaving yarns, and the blending rate of described blended slub yarn is:
Sheng-bast fiber: day silk=30~70: 70~30 are weight percentage.
The joint of described blended slub yarn is long to be 5cm, and joint slightly is 2.1 times, per 24 joints, one circulation.
The pitch of described blended slub yarn is distributed as 184,226,150,181,105,220,159,241,212,200,211,116,207,199,129,255,142,147,160,127,128,194,135,148, is unit with cm.
The manufacturing technique of this fabric mainly is following steps:
(1), cotton cleaning process
Crotalaria sp, the clot separately in cotton cleaning process of day silk, 1054 rev/mins of griping cotton machine hired roughnecks, FA106 adopts kirschner beater, 445 rev/mins of speed, 10 rev/mins of A076 lap roller speed, lap dry weight 390 gram/rice, 30.6 meters of lap length;
(2), carding step
Licker-in speed is 800 rev/mins, 330 rev/mins of cylinder speeds, 15 rev/mins of doffer speeds, cylinder and cover plate space 0.23mm, 0.23mm, 0.254mm, 0.254mm, 0.3mm;
(3), mixing in doubling step
Amalgamation adopts bigger back zone to stretch oneself and yawn multiple, and mixing two, mixing three is to improve the flat back zone of bar solid carbon dioxide to stretch oneself and yawn multiple grasp less than normal, specific as follows:
Amalgamation Mix two Mix three
Number of doubling 8 (5 crotalaria sp/3 sky silks) ??6 ??6
Multiple is stretched oneself and yawn in the back zone ??1.856 ??1.459 ??1.303
Always stretch oneself and yawn multiple ??8.14 ??6.5 ??6.2
/ 5 meters of dry weight grams ??18 ??16.6 ??16
Roller gauge mm ??7*18 ??7*18 ??7*18
Horn mouth diameter mm ??3.4 ??3.4 ??3.2
(4), rove operation
The back zone is stretched oneself and yawn multiple and is selected 1.22 times, roving twist factor 80 ,/10 meters of dry weight 4.0 grams, roller gauge 10*22*32.5mm;
(5), spinning process
The yarn roller 20*35mm that spaces, nip gauge 3.0mm, 1.29 times of multiples, twist factor 353 are stretched oneself and yawn in the back zone;
(6), winding procedure
1000 meters/minute of groove drum speed, the clear parameter 2.4*5 of electricity, air splicer joint;
(7), sizing operation
Slurry formula is as follows:
Converted starch HB-93:25kg
Smooth agent: 2kg
Farina CP-L:25kg
Sheet alkali: 100g
PVA:??????????????25kg
Mould inhibitor NL-4:75ml
Propylene class P-T:4kg
Water: 500L;
Sizing technique is as follows:
Slurry oven temperature, degree: 98 ℃~100 ℃
Slurry case viscosity: 14~15 seconds
Slurry pot temperature: 90 ℃~95 ℃
Slurry pot viscosity: 11~12 seconds
The rate of sizing: 13 ± 1%
Regain: 9%~10%
I speed squeezing pressure: 7KN
II speed squeezing pressure: 16KN
The sizing speed of a motor vehicle: 25~30 meters/minute;
(8), pass operation
Use No. 115.5 reed, combine for 8, the ground warp limit is gone into through every reed 2, and the menopause tablet method of wearing is 1,2,3,4,5,6.The limit yarn is through 1,2 and combines, and ground warp is through 3,4,5,6,7,8 to sum up, and the method for wearing is gaited by the crape tissue;
(9), weaving process
Knitting technology is as follows: 300 ° of opening times, go into 90 ° of latitude times, and 32 ° of opening angles are gone into 75 ° of latitude times, and 240 ° of weft yarn times of advent, the opening traverse is 107,90,73,50,40,86,73,60; Heald frame height is 134*4+135*4; Warp tension 1.8KN; Main jet is chewed pressure 2.8Kg, auxilliary nozzle pressure 3~4Kg.
Usefulness of the present invention is: 1. rationally utilized two kinds of environmental protection fibers, its fabric combines the advantage of two kinds of fibers, promptly the natural antibacterial of Sheng-bast fiber, press down acaricidal property and hygroscopicity that day silk is outstanding, frivolous easily wash easily do, feel is soft and smooth, the characteristic of good luster; 2. the fabric taking is good, can not stimulate human skin, and moisture absorbing and sweat releasing antibioticly presses down mite, and is comfortable, helps health; 3. improve to some extent on manufacturing technique and innovate, weaving for two kinds of fiber blends provides effective technology, for society provides a kind of desirable environment-friendly products, has better social benefit and economic benefit.
The specific embodiment
The invention will be further described below in conjunction with embodiment.
Sheng-bast fiber of this programme and tencel blended bamboo node fabric adopt Sheng-bast fiber and tencel blended bamboo node weaving yarns, and the blending rate of described blended slub yarn is:
Sheng-bast fiber: day silk=30~70: 70~30 are weight percentage.
Specific embodiment is as follows:
One, raw material selects for use and fabric
1, the selection of raw material and proportioning
Crotalaria sp selects to be suitable for the specification of cotton spinning apparatus spinning, and its fineness is 1.67dtex, and length is 38mm.Because it is lower that Sheng-bast fiber is done fracture strength, only is 2.19CN/dtex, therefore, select to do the higher silk fiber blended brute force that improves yarn of fracture strength, the technical indicator of selected day silk is: fineness 1.33dtex, length 38mm does fracture strength 3.93CN/dtex.This tencel fiber fineness is thin powerful high, can improve the spinnability and the brute force of high grade yarn, helps the spinning of this kind and weaves.In order to keep the crotalaria sp characteristic, present embodiment adopts crotalaria sp 60%, and the blending rate of day silk 40% from Fabric Style, is selected the bigger tencel fiber of rigidity for use, increases the wide and elasticity of fabric.
2, fabric
1. yarn
Hygroscopic, perspiratory and antibacterial according to crotalaria sp presses down acaricidal property, relatively is fit to frivolous garment material in summer, and in order to make the crotalaria sp lining reach the appearance style of imitating natural hemp product, so adopt 40 s~50 sBlended slub yarn improves the hemp product style, and its slub yarn is designed to: basic yarn 50 s(11.8tex), save long 5cm, save thick 2.1 times, per 24 joints, one circulation, pitch is distributed as 184,226,150,181,105,220,159,241,212,200,211,116,207,199,129,255,142,147,160,127,128,194,135,148 (are unit with cm), and bamboo section number number is 12.14tex.
Every square metre of longitude and latitude ring of design textile adds and is combined into about 7000.
2. fabric
The fabric tissue specification adopts novel crape tissue, the crape tissue is used for the light and thin type fabric more, utilize warp, the criss-cross arrangement of latitude floating-point of different length in the tissue, make tissue surface form irregular rough fine particle shape outward appearance and wrinkling, make lining have thick refreshing bast fiber fabrics feel, take all factors into consideration factors such as the style of fabric and tightness degree, the fabric of present embodiment adopts following specification:
Yarn: blending rate be 60/40 50 sSheng-bast fiber and tencel blended bamboo node,
Fabric specification: 50 s* 50 s* 120*80*63 " blended bamboo node fabric.
Two, technological process
1, spinning technological process
After adopting crotalaria sp, tencel fiber clot respectively, slivering, at the process route of drafting mixing.Its technological process is: FA002 bale plucker-A035 mixing and blowing machine-FA106 opener-A092 tandem feeder-A076 lapper-FA201 carding machine-FA302 drawing frame (mixing of three roads)-FA457 Speed frames-FA506 fine spining machine-field, village 21C automatic winder.
2, weaving process flow process
Warping-sizing-denting-weave-check-grade-Xiu knits-finished product.
Three, emphasis procedure technology
1, cotton cleaning process
Crotalaria sp, the clot separately in cotton cleaning process of day silk, bale breaking balance moisture regain in advance, workshop moisture temperature grasp bigger than normal.
The length regularity of two kinds of fibers is good, contain assorted few, cotton cleaning process shortening flow process is taked the technological principle of " duty is grabbed less and grabbed, how pine is few beats, gently combs and lack to fall ", suitably reduces each speed, 1054 rev/mins of griping cotton machine hired roughnecks, FA106 adopts kirschner beater, 445 rev/mins of speed, 10 rev/mins of A076 lap roller speed, lap dry weight 390 gram/rice, 30.6 meters of lap length.
2, carding step
According to fiber properties, the grasp bigger than normal of carding step humiture takes many combs to lack the technological principle of falling, feed plate-licker-in distance suitably strengthens, reduce licker-in and reduce fibre damage, suitably control little leakage at the bottom of inlet/outlet space, reduce noil, increase licker-in and cylinder differential surface speed, dwindle spacing of doffer and cylinder, favourable and fibre migration suitably strengthens cylinder and cover plate spaces, control the combing of fiber well, reduce cotton knot.Licker-in speed is 800 rev/mins, 330 rev/mins of cylinder speeds, 15 rev/mins of doffer speeds, cylinder and cover plate space 0.23mm, 0.23mm, 0.254mm, 0.254mm, 0.3mm ,/5 meters of weight of card sliver Sheng-bast fiber 17.6 grams ,/5 meters of tencel fiber 19.5 grams.The Sheng-bast fiber spinning is smooth, web sinking suspension during sky silk comb and parallel cotton fibers prior to spinning, and process improves workshop moisture temperature, the adjustment equipment state is resolved substantially.Crotalaria sp carded sliver weight CV%6.22, bar is done CV%7.06, cotton knot 1.It silk carded sliver weight CV%4.07, bar is done CV%5.92, cotton knot 0.
3, mixing in doubling step
Drafting is with the mixture homogeneity of two kinds of fibers of abundant raising, improves the extended parallelization and the sliver inherent quality of fiber and attaches most importance to, and adopts three roads and closes.Strengthen workshop moisture temperature, the front leather roller of amalgamation is through antistatic treatment, and the horn mouth diameter can not be too little.
For stretching fiber better, amalgamation adopts bigger back zone to stretch oneself and yawn multiple, mixes two, mixes three for stretching oneself and yawn multiple grasp less than normal in the flat back zone of raising bar solid carbon dioxide.
Specific as follows:
Amalgamation Mix two Mix three
Number of doubling 8 (5 crotalaria sp/3 sky silks) ??6 ??6
Multiple is stretched oneself and yawn in the back zone ??1.856 ??1.459 ??1.303
Always stretch oneself and yawn multiple ??8.14 ??6.5 ??6.2
/ 5 meters of dry weight grams ??18 ??16.6 ??16
Roller gauge mm ??7*18 ??7*18 ??7*18
Horn mouth diameter mm ??3.4 ??3.4 ??3.2
Mix three weight CV%0.53, bar is done CV%3.88, reaches better level.
4, rove operation
Because fibre uniformity is good, multiple is stretched oneself and yawn in the back zone can be slightly larger, guaranteeing under the situation that spun yarn is normally stretched oneself and yawn that roving twist factor grasp bigger than normal produces accident and stretches oneself and yawn when preventing the spun yarn unwinding.The back zone is stretched oneself and yawn multiple and is selected 1.22 times, roving twist factor 80 ,/10 meters of dry weight 4.0 grams, roller gauge 10*22*32.5mm.
5, spinning process
Under the principle that spinning process spaces greatly in the back zone, stretches oneself and yawn for a short time, heavily pressurizes, because fibre uniformity is good, multiple is stretched oneself and yawn in the back zone can be slightly larger.Will rationally control nip gauge, excessively go out details easily, too small stretching oneself and yawn do not left " hardhead ", selects the low slightly proparea roller of hardness for use, and the control floating fiber improves the yarn evenness level, reduces filoplume, reduces details, improves the yarn qualities level.The yarn roller 20*35mm that spaces, nip gauge 3.0mm, 1.29 times of multiples, twist factor 353 are stretched oneself and yawn in the back zone.
6, winding procedure
Winding procedure will suitably reduce groove drum speed, perform the technique initialization work of electronic yarn clearer, mix up splicer, guarantee joint quality, note the bright and clean no burr of yarn path, reduce filoplume, reduce the deterioration of yarn qualities, 1000 meters/minute of groove drum speed, the clear parameter 2.4*5 of electricity, the air splicer joint is protected piecing strength and is reached more than 85% of raw yarn strength.
The end product quality level: single strong CV%10.2, disconnected strong by 13.1 (looking), and weight CV%3.1, heavy by partially-2.7, blackboard cotton knot 3, knot heterozygosis meter 3.
7, sizing operation
A crotalaria sp and a day silk all are regenerated celulose fibres, and according to the similar principle that mixes, slurry formula is auxiliary slurry based on starch slurry with PVA for increasing the serous coat brute force.
Slurry formula is as follows:
Converted starch HB-93:25kg
Smooth agent: 2kg
Farina CP-L:25kg
Sheet alkali: 100g
PVA:?????????25kg
Mould inhibitor NL-4:75ml
Propylene class P-T:4kg
Water: 500L.
Sizing uses Zhengzhou frame factory Sizing machines, adopts the not stratified sizing route of double flute double-clip-double-nip.Sizing adopts small tension receiving coil, low elongation, middle pressure, and soaking into lining of sizing taken into account.The wet district of sizing tension force is as far as possible little, reduces the sizing elongation.
Sizing technique is as follows:
Slurry oven temperature, degree: 98 ℃~100 ℃
Slurry case viscosity: 14~15 seconds
Slurry pot temperature: 90 ℃~95 ℃
Slurry pot viscosity: 11~12 seconds
The rate of sizing: 13 ± 1%
Regain: 9%~10%
I speed squeezing pressure: 7KN
II speed squeezing pressure: 16KN
The sizing speed of a motor vehicle: 25~30 meters/minute.
8, pass operation
Use No. 115.5 reed, combine for 8, adopt automatic drawing-in machine to pass, this crape of input is organized drafting plan on automatic drawing-in machine, and drawing-in machine is finished automatically and passed.The ground warp limit is gone into through every reed 2, and the menopause tablet method of wearing is 1,2,3,4,5,6.The limit yarn is through 1,2 and combines, and ground warp is through 3,4,5,6,7,8 to sum up, and the method for wearing is gaited by the crape tissue.
9, weaving process
Fabric adopts advanced Picanol multi-arm air-jet loom weaving, and knitting technology is as follows: 300 ° of opening times, go into 90 ° of latitude times, and 32 ° of opening angles are gone into 75 ° of latitude times, 240 ° of weft yarn times of advent.The opening traverse is 107,90,73,50,40,86,73,60.Heald frame height is 134*4+135*4.Warp tension 1.8KN.Main jet is chewed pressure 2.8Kg, auxilliary nozzle pressure 3-4Kg.600 rev/mins of loom rotating speeds.
This fabric particle is clear, and gloss is soft, and cloth cover has the significantly concavo-convex outward appearance of creasing, and the thin ring of longitude and latitude is evenly distributed, and fabric feeling is well-pressed, has the hemp product style.

Claims (4)

1. Sheng-bast fiber and tencel blended bamboo node fabric, it is characterized in that: this fabric adopts Sheng-bast fiber and tencel blended bamboo node weaving yarns, and the blending rate of described blended slub yarn is:
Sheng-bast fiber: day silk=30~70: 70~30 are weight percentage.
2. fabric according to claim 1 is characterized in that: the joint of described blended slub yarn is long to be 5cm, and joint slightly is 2.1 times, per 24 joints, one circulation.
3. fabric according to claim 2, it is characterized in that: the pitch of described blended slub yarn is distributed as 184,226,150,181,105,220,159,241,212,200,211,116,207,199,129,255,142,147,160,127,128,194,135,148, is unit with cm.
4. the manufacturing technique of Sheng-bast fiber and tencel blended bamboo node fabric is characterized in that this manufacturing technique mainly is following steps:
(1), cotton cleaning process
Crotalaria sp, the clot separately in cotton cleaning process of day silk, 1054 rev/mins of griping cotton machine hired roughnecks, FA106 adopts kirschner beater, 445 rev/mins of speed, 10 rev/mins of A076 lap roller speed, lap dry weight 390 gram/rice, 30.6 meters of lap length;
(2), carding step
Licker-in speed is 800 rev/mins, 330 rev/mins of cylinder speeds, 15 rev/mins of doffer speeds, cylinder and cover plate space 0.23mm, 0.23mm, 0.254mm, 0.254mm, 0.3mm;
(3), mixing in doubling step
Amalgamation adopts bigger back zone to stretch oneself and yawn multiple, and mixing two, mixing three is to improve the flat back zone of bar solid carbon dioxide to stretch oneself and yawn multiple grasp less than normal, specific as follows:
Amalgamation Mix two Mix three Number of doubling 8 (5 crotalaria sp/3 sky silks) ??6 ??6 Multiple is stretched oneself and yawn in the back zone ??1.856 ??1.459 ??1.303 Always stretch oneself and yawn multiple ??8.14 ??6.5 ??6.2 / 5 meters of dry weight grams ??18 ??16.6 ??16 Roller gauge mm ??7*18 ??7*18 ??7*18 Horn mouth diameter mm ??3.4 ??3.4 ??3.2
(4), rove operation
The back zone is stretched oneself and yawn multiple and is selected 1.22 times, roving twist factor 80 ,/10 meters of dry weight 4.0 grams, roller gauge 10*22*32.5mm;
(5), spinning process
The yarn roller 20*35mm that spaces, nip gauge 3.0mm, 1.29 times of multiples, twist factor 353 are stretched oneself and yawn in the back zone;
(6), winding procedure
1000 meters/minute of groove drum speed, the clear parameter 2.4*5 of electricity, air splicer joint;
(7), sizing operation
Slurry formula is as follows:
Converted starch HB-93:25kg
Smooth agent: 2kg
Farina CP-L:25kg
Sheet alkali: 100g
PVA:??????????????25kg
Mould inhibitor NL-4:75ml
Propylene class P-T:4kg
Water: 500L;
Sizing technique is as follows:
Slurry oven temperature, degree: 98 ℃~100 ℃
Slurry case viscosity: 14~15 seconds
Slurry pot temperature: 90 ℃~95 ℃
Slurry pot viscosity: 11~12 seconds
The rate of sizing: 13 ± 1%
Regain: 9%~10%
I speed squeezing pressure: 7KN
II speed squeezing pressure: 16KN
The sizing speed of a motor vehicle: 25~30 meters/minute;
(8), pass operation
Use No. 115.5 reed, combine for 8, the ground warp limit is gone into through every reed 2, and the menopause tablet method of wearing is 1,2,3,4,5,6.The limit yarn is through 1,2 and combines, and ground warp is through 3,4,5,6,7,8 to sum up, and the method for wearing is gaited by the crape tissue;
(9), weaving process
Knitting technology is as follows: 300 ° of opening times, go into 90 ° of latitude times, and 32 ° of opening angles are gone into 75 ° of latitude times, and 240 ° of weft yarn times of advent, the opening traverse is 107,90,73,50,40,86,73,60; Heald frame height is 134*4+135*4; Warp tension 1.8KN; Main jet is chewed pressure 2.8Kg, auxilliary nozzle pressure 3~4Kg.
CNA2006101297237A 2006-11-29 2006-11-29 Sheng-bast fiber and tencel blended bamboo node fabric and manufacturing technique thereof Pending CN101191269A (en)