CN108642648A - A kind of high conformal health-care environmental-protecting fabric and its production method - Google Patents
A kind of high conformal health-care environmental-protecting fabric and its production method Download PDFInfo
- Publication number
- CN108642648A CN108642648A CN201810392168.XA CN201810392168A CN108642648A CN 108642648 A CN108642648 A CN 108642648A CN 201810392168 A CN201810392168 A CN 201810392168A CN 108642648 A CN108642648 A CN 108642648A
- Authority
- CN
- China
- Prior art keywords
- yarn
- mixing
- silk
- fiber
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high conformal health-care environmental-protecting fabrics and preparation method thereof, and the spun silk strand for being adopted as the cop-cop-yarn of fabric quality percentage 56% by warp thread, 44% is made of weft yarn through warping, weaving process；The cop-cop-yarn be adopted as fabric quality percentage 40% mixing covering yarn, 16% silk through in wool spinning technology doubling, double twisting, yarn steaming process be made；The mixing covering yarn for the long-staple cotton fiber that mixes the mercerized wool fiber of covering yarn mass percent 20%, 25% aloe fibre, 25% silk fiber, 30% by forming, and wherein long-staple cotton fiber be the heart yarn of mixing covering yarn.Textile fabric provided by the invention and its production method, it is raw material to select aloe, soft silk, cotton, wool with environment-protecting health-care function etc., and with silk and twist, spun silk interweaves, develop a series of flower pattern novelty, unique style, moisture absorption, ventilative, skin care high conformal health-care environmental-protecting fabric.
Description
Technical field
The present invention relates to spinninging technical fields, and in particular to arrives a kind of high conformal health-care environmental-protecting fabric and its producer
Method.
Technical background
With the continuous improvement of economic continuous development and living standard, people also change the theory of clothes
Become, health care consciousness constantly enhances, and the worsted fabric of traditional classical top grade has no longer met the needs of people, therefore to various weavings
The health of product and dress material, comfortably the requirements such as warming are also continuously improved.Health properties and environmental-protecting performance are the important of textile fabric
Functional parameter, and conformality is an important quality index of textile fabric, it is known that although the fabric of natural fiber has
Comfortably, the advantages of health, environmental protection and certain health, but it is usually present that elasticity is poor, be easy corrugation, conformality is not good enough
Disadvantage；Chemical fibre blended yarn weaved fabric has certain conformality, but it haves the shortcomings that the feature of environmental protection and healthcare function are poor.Develop Gao Pin
Matter and high added value and the new direction that there is the fabric of certain health care functions to become current textile industry.
Invention content
The object of the present invention is to provide a kind of conformality and the good textile fabric of healthcare function, the feature of environmental protection and its productions
Method, the fabric of acquisition it is high-elastic it is conformal, moisture absorption is ventilative, pure color, healthcare function and the feature of environmental protection are all good.
The present invention solve the technical solution that uses of above-mentioned technical problem for：A kind of high conformal health-care environmental-protecting fabric, uses
It is made through warping, weaving process of weft yarn of the spun silk strand of warp thread, 44% of the cop-cop-yarn of fabric quality percentage 56%；Institute
The cop-cop-yarn stated be adopted as fabric quality percentage 40% mixing covering yarn, 16% silk through in wool spinning technology doubling,
Double twisting, yarn steaming process are made；The described mixing covering yarn by for mix covering yarn mass percent 20% mercerized wool fiber,
25% aloe fibre, 25% silk fiber, 30% long-staple cotton fiber composition, wherein long-staple cotton fiber be mix covering yarn
Heart yarn.
A kind of production method of high conformal health-care environmental-protecting fabric, includes the following steps：
（1）Mercerized wool fiber is obtained into mercerized wool through crush cutting process and cuts off item；
（2）Aloe fibre, silk fiber are dyed using environment-friendly active dyestuff, mercerized wool cuts off item and selects Lan Nasu
Dyeing；
（3）Heavy twist long-staple cotton is made in Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process
Spun yarn, by silk flock successively through schappe system processing it is concise, system is continuous, at item, slubbing, spun yarn and silk, twisted filament, singeing step system
At spun silk strand；
（4）It will be through step（2）Aloe fibre, silk fiber refueling water and hair, carding process through wool spinning technology after dyeing
The cellulose mixing carded sliver is made, then will mix the carded sliver with dyeing after mercerized wool cut-out item cotton spinning mixing in doubling step and and
Mixing ripe bar is obtained, mixing rove then is made in mixing Roving Frames of the ripe bar through cotton spinning；
（5）Mixing rove and heavy twist long-staple cotton spun yarn are made to mixing cored coil on the spinning process of cotton spinning, then
Mixing cored cylinder yarn is made through the winding procedure in cotton spinning in mixing cored coil；
（6）Cored cylinder yarn will be mixed, cop-cop-yarn is made through the doubling in wool spinning technology, double twisting, yarn steaming process with silk；
（7）Using cop-cop-yarn as warp thread, spun silk strand as weft yarn, high conformal health-care environmental-protecting is made through warping, weaving process
Fabric；The conformal health-care environmental-protecting fabric of height obtained is finally made to the conformal health-care environmental-protecting face of height of the present invention through postfinishing process
Material.
Further, the production method of a kind of high conformal health-care environmental-protecting fabric, includes the following steps：
（1）Mercerized wool fiber is obtained into the mercerized wool that principal length is 36mm through crush cutting process and cuts off item；
（2）Aloe fibre, silk fiber are dyed using reactive dye, dyeing includes the following steps：It sequentially adds first
Auxiliary agent, reactive dye then sequentially add 1/3 alum, 2/3 alum, and 1 degree of speed per minute is then kept to be warming up to 60 degree,
It then keeps the temperature 20 minutes and 1/3 soda ash is added；Continue heat preservation and 2/3 soda ash is added in 20 minutes, then 30 minutes is kept the temperature, most afterwards after
Manage out cylinder；Mercerized wool cuts off item and lanasol dye dyeing, dyeing is selected to include the following steps：Auxiliary agent, dye are sequentially added first
Material, is then warming up to 100 degree, and keeps the temperature 70 minutes, it is last it is post-treated go out cylinder；
（3）Heavy twist long-staple cotton is made in Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process
Spun yarn, wherein twist factor >=500 of heavy twist long-staple cotton spun yarn；By silk flock successively through schappe system processing it is concise, system is continuous, at
Item, slubbing, spun yarn and silk, twisted filament, singeing step are made 120S/ 2 spun silk strands；
（4）Cellulose is made in refueling water and hair, carding process of the aloe fibre, silk fiber after dyeing through wool spinning technology
The carded sliver is mixed, the carded sliver will be then mixed and cut off item in the mixing in doubling step of cotton spinning with the mercerized wool after dyeing and and obtain mixing ripe
Item, then will mixing Roving Frames of the ripe bar through cotton spinning be made mixing rove, wherein mixing in doubling step include slubbing drafting, two simultaneously
Item, three draftings；
（5）Mixing rove and heavy twist long-staple cotton spun yarn are made to mixing cored coil on the spinning process of cotton spinning, wherein
Mix front roller and preceding glue of rear roller feeding, heavy twist long-staple cotton spun yarn of the rove by spinning frame through core-spun yarn device by spinning frame
Roller group at the rear jaw of front roller feed, the mixing yarn and heavy twist long-staple cotton that mixing rove is obtained via draft area drawing-off are thin
Yarn converges at the preceding jaw for the front roller that front roller is formed with preceding rubber roller, and yarn is mixed under twist effect by heavy twist long-staple cotton
Spun yarn is wrapped in center and then obtains required mixing cored coil, then by mixing cored coil through the winder in cotton spinning
Mixing cored cylinder yarn is made in process；
（6）Cored cylinder yarn will be mixed and be made 135 through the doubling in wool spinning technology, double twisting, yarn steaming process with silkS/ 2 mixing stocks
Line；
（7）By 135S/ 2 cop-cop-yarns are as warp thread, 120S/ 2 spun silk strands as weft yarn, through warping, weaving process be made through
The conformal guarantor of height that close and filling density is respectively 403/10cm and 300/10cm, structure is plain weave small jacquard tissue, grammes per square metre is 170g/m
Strong environment-friendlyfabric fabric；Finally the conformal health-care environmental-protecting fabric of height obtained is singed through the bad cloth in postfinishing process successively, braying, baking
The final conformal health-care environmental-protecting fabric of height is made in dry, soft, tank steaming process.
Further, the mercerized wool fiber is 100SAU mercerized wool items, and the aloe fibre is wool type
1.5D aloe fibres, the silk fiber are the 1.5D silk fibers of wool type, and the silk is 30D silks.
Further, described（4）It walks, the antistatic of grease mass percent 1% is incorporated as in the refueling water process
Agent；In the wool blending step, upper machine moisture regain reaches 14%, bored hair 24 hours；In the carding process, speed is 900r/ when upper machine
min。
Further, described（6）It walks, in the doubling process, the doubling on Italian TUAN types, speed
400m/min, and add a certain amount of oil, ensure that yarn is bright and clean；It is low using Italian GEMINIS double twistings in the double twisting process
Speed is twisted, and 2 sheet metals are added, and prevents from making a pause when guide；In the yarn steaming process, using 88 degree 15 points, 90 degree 20 points 2
A cycle yarn steaming, makes strand fully shape.
Further, described（7）It walks, in the warping process, using the BEN-TRONIC of Benninger of Switzerland
Type warping machine, yarn sizing when warping, the rate of sizing 10% forms coating in yam surface, increases yarn abrasion performance, reduces
Yarn breakage, tension in Warping 14cN, beaming tension 12cN, 400 revs/min of speed；In the weaving process, using Dornier
Rapier loom, shed forms are non-clear opening, back beam height 11, the front and back position 0 of the back rest, warp stop frame height 1.5, anteroposterior position
330 degree, speed 340r/min between setting 5, palm fibre usually；It in the braying process, is washed using import open width, 60 DEG C of brayings, 80 DEG C are boiled
, it is carried out continuously；Steam drying, temperature is used to be less than 100 DEG C in the baking operation；In the softening step, it is added soft
Agent；In the tank steaming process, 110 DEG C of temperature continues 5 minutes.
Compared with prior art, what the present invention had has the beneficial effect that：Textile fabric and its producer provided by the invention
Method, it is raw material to select aloe, soft silk, cotton, wool etc. with environment-protecting health-care function, and with silk and twist, spun silk interweaves, exploitation
A series of flower pattern novelties, unique style, moisture absorption, ventilative, skin care the conformal health-care environmental-protecting fabric of height；The present invention selects a variety of originals
Material is combined, and is given full play to the excellent properties of each raw material, is learnt from other's strong points to offset one's weaknesses, and fabric is made to have superior wearability；Using length
Suede cotton fiber and mercerized wool so that fabric texture is slim and graceful, smooth, moisture absorption is ventilative, simultaneously using the spinning spun yarn of silk long filament and half
It twists and broadwise is all beaten up using bright-coloured spun silk so that fabric color is pure, gloss is beautiful, fine using aloe fibre and soft silk
Dimension makes fabric have skin care, antibacterial, anti-inflammatory, anti-static function, uses the long-staple cotton spun yarn with heavy twist that can realize yarn for heart yarn
Line it is high-elastic conformal.
Specific implementation mode
With reference to specific embodiment, the present invention is described further.
A kind of high conformal health-care environmental-protecting fabric is passed through by the 1.5D aloe fibres through hyperchromatic wool type, 1.5D silk fibers
The cellulose mixing carded sliver is made in refueling water and hair, the carding process of wool spinning technology, then will be after the mixing carded sliver and dyeing
100SAU mercerized wools cut off item cotton spinning mixing in doubling step and and obtain mixing ripe bar, then will mixing ripe bar through the thick of cotton spinning
Mixing rove is made in yarn process, and Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process are made
Mixing cored is made in mixing rove and heavy twist long-staple cotton spun yarn by heavy twist long-staple cotton spun yarn on the spinning process of cotton spinning
Yarn, wherein heavy twist long-staple cotton spun yarn be mix covering yarn heart yarn, mixing covering yarn include 20% mercerized wool fiber, 25%
Aloe fibre, 25% silk fiber, 30% long-staple cotton fiber, then will through made of the winding procedure in cotton spinning mix
It closes cored cylinder yarn and is made 135 through the doubling in wool spinning technology, double twisting, yarn steaming process with 30D silksS/ 2 cop-cop-yarns, then with
135S/ 2 cop-cop-yarns are warp thread, 120S/ 2 spun silk strands are weft yarn, and it is respectively 403/10cm and 300/ to be made through close and filling density
The conformal health-care environmental-protecting fabric of height that 10cm, structure are plain weave small jacquard tissue, grammes per square metre is 170g/m, wherein high conformal health-care environmental-protecting
Fabric includes 40% mixing covering yarn, 16% silk, 44% spun silk yarn, finally by high conformal health-care environmental-protecting fabric after
It arranges and the required conformal health-care environmental-protecting fabric of height is made.
In order to realize the production of the conformal health-care environmental-protecting fabric of above-mentioned height, the present invention uses following production method, including with
Lower step：
（1）100SAU mercerized wools item is obtained into the 100SAU mercerized wools that principal length is 36mm through crush cutting process and cuts off item；
（2）The 1.5D silk fibers of the 1.5D aloe fibres of wool type, wool type are dyed using environment-friendly active dyestuff, are considered
Contain a certain amount of protein to aloe, soft silk, emerald pearl fiber, therefore strictly controls the use of alkali in dyeing course
Amount, avoids protein content from losing, and keeps the distinctive feel style of fabric, and dyeing includes the following steps, sequentially add first auxiliary agent,
Dyestuff then sequentially adds 1/3 alum, 2/3 alum, then keeps 1 degree of speed per minute to be warming up to 60 degree, then keeps the temperature 20
1/3 soda ash is added in minute.Continue heat preservation and 2/3 soda ash be added in 20 minutes, then keep the temperature 30 minutes, it is last it is post-treated go out cylinder；Silk
Light wool cuts off item and selects import lanasol dye, keeps the nucleophilic group of amino acid in wool irreversible covalent because forming one
Key reaches the wet fastness requirement of high standard to being soundly bonded on wool fiber, and dyeing includes the following steps, first according to
Secondary addition auxiliary agent, dyestuff, are then warming up to 100 degree, and keep the temperature 70 minutes, it is last it is post-treated go out cylinder；
（3）Heavy twist long-staple cotton is made in Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process
Spun yarn, the wherein twist factor of heavy twist long-staple cotton spun yarn are more than or equal to 500；By silk flock successively through schappe system processing it is concise, system
Silk floss is made 120 at item, slubbing, spun yarn and silk, twisted filament, singeing stepS/ 2 spun silk strands；
（4）By the 1.5D aloe fibres of the wool type after dyeing, wool type refueling water of the 1.5D silk fibers through wool spinning technology and
The cellulose mixing carded sliver is made in hair, carding process, will then mix the carded sliver and exists with the 100SAU mercerized wools cut-out item after dyeing
The mixing in doubling step of cotton spinning and and obtain mixing ripe bar, mixing rove then is made in mixing Roving Frames of the ripe bar through cotton spinning,
Middle mixing in doubling step includes slubbing drafting, two draftings, three draftings；
（5）Mixing rove and heavy twist long-staple cotton spun yarn are made to mixing cored coil on the spinning process of cotton spinning, wherein
Mix front roller and preceding glue of rear roller feeding, heavy twist long-staple cotton spun yarn of the rove by spinning frame through core-spun yarn device by spinning frame
Roller group at the rear jaw of front roller feed, the mixing yarn and heavy twist long-staple cotton that mixing rove is obtained via draft area drawing-off are thin
Yarn converges at the preceding jaw for the front roller that front roller is formed with preceding rubber roller, and yarn is mixed under twist effect by heavy twist long-staple cotton
Spun yarn is wrapped in center and then obtains required mixing cored coil, then by mixing cored coil through the winder in cotton spinning
Mixing cored cylinder yarn is made in process；
（6）Cored cylinder yarn will be mixed and be made 135 through the doubling in wool spinning technology, double twisting, yarn steaming process with 30D silksS/ 2 mixing
Strand；
（7）By 135S/ 2 cop-cop-yarns are as warp thread, 120S/ 2 spun silk strands as weft yarn, through warping, weaving process be made through
The conformal guarantor of height that close and filling density is respectively 403/10cm and 300/10cm, structure is plain weave small jacquard tissue, grammes per square metre is 170g/m
Strong environment-friendlyfabric fabric；Finally the conformal health-care environmental-protecting fabric of height obtained is singed through the bad cloth in postfinishing process successively, braying, baking
The final conformal health-care environmental-protecting fabric of height is made in dry, soft, tank steaming process.
Further perfect technical solution is as follows for present invention process：
Preferably,（4）In step, the large percentage that the cotton of this fabric and regenerated celulose fibre account for is considered in refueling water process,
And cellulose fibre is wet strong low, therefore add water less, the grease total amount added should control within the 10% of fiber total amount, in grease
The ratio of water should be less than 1/3, avoid fibre damage in carding process serious, at the same for when preventing carding since electrostatic is rubbed
Greatly, 1% antistatic agent of fiber total amount is added；Raw material is sufficiently mixed uniformly in wool blending step, machine moisture regain is made to reach 14%,
Bored hair 24 hours, makes the grease of addition fully be absorbed by fiber；In carding process, when combing, therefore by cylinder, the speed tune of licker-in
Soon, abundant carded fiber reduces card nailing neps, and speed is 900r/min when upper machine.
The（6）In step, in doubling process, it is contemplated that the shrinkage of two kinds of yarns is different, and 30D silks are thin and slide, and elasticity is small, because
This selection doubling on Italian TUAN types, speed 400m/min, and added appropriate oil, ensure that yarn is bright and clean；Double twisting process
In, it using Italian GEMINIS double twistings, is twisted using low speed, adds 2 sheet metals, prevented from making a pause when guide, make yarn
Without handle；In yarn steaming process, using 88 degree 15 points, 90 degree 20 points 2 cycle yarn steamings, so that strand is fully shaped, be conducive to knit
It makes.
The（7）In step, in warping process, the BEN-TRONIC type warping machines of Switzerland Benninger are selected, yarn when warping
Line starching, the rate of sizing 10% form coating, increase yarn abrasion performance in yam surface, reduce yarn breakage, and warping is opened
Power 14cN, beaming tension 12cN, 400 revs/min of speed；In weaving process, considering that broadwise spun silk is smooth, yarn count is thin, and the twist is low,
Therefore to the more demanding of loom, using Dornier rapier looms, open type wefting insertion and can the shed open of independent setting when closing
Between greatly reduce friction between warp thread and weft yarn, reduce it is disconnected avoids weft tension excessively high through staplings, not will produce looped weft,
Left and right selvedge is smooth, wefting insertion length uniformity, ensures quality；Shed forms is non-clear opening, back beam height 11, the back rest
Front and back position 0, warp stop frame height 1.5, front and back position 5, palm fibre usually between 330 degree, speed 340r/min；In braying process, make
It is washed with import open width, 60 DEG C of brayings, 80 DEG C of crabbings are carried out continuously, have both reached braying effect, do not generate folding line, also do not damage fibre
Dimension；Steam drying, temperature is used to be less than 100 DEG C, keep fabric feeling soft in baking operation；In softening step, softening agent is added,
Assign the more soft plentiful feel of fabric；In tank steaming process, 110 DEG C of temperature continues 5 minutes, keeps the fabric after arrangement both soft
It is not only sliding but also plentiful, integrate the style of lousiness cotton.
It should further illustrate, the present invention is not limited to the embodiment above, anyone is under the inspiration of the present invention
It can all obtain other various forms of products, however, make any variation in its structure or method, every have and the application
Technical solution as same or similar, is within the scope of the present invention.
Claims (7)
1. a kind of high conformal health-care environmental-protecting fabric, it is characterised in that：The cop-cop-yarn for being adopted as fabric quality percentage 56% is warp
Yarn, 44% spun silk strand be made through warping, weaving process of weft yarn；The cop-cop-yarn is adopted as fabric quality percentage
40% mixing covering yarn, 16% silk are made through the doubling in wool spinning technology, double twisting, yarn steaming process；The mixing cored
Yarn is by mix the mercerized wool fiber of covering yarn mass percent 20%, 25% aloe fibre, 25% silk fiber, 30%
Long-staple cotton fiber forms, and wherein long-staple cotton fiber be the heart yarn of mixing covering yarn, outsourcing mercerized wool fiber, aloe fibre and soft
Silk fiber mixed yarn.
2. a kind of production method of high conformal health-care environmental-protecting fabric, which is characterized in that include the following steps：
（1）Mercerized wool fiber is obtained into mercerized wool through crush cutting process and cuts off item；
（2）Aloe fibre, silk fiber are dyed using environment-friendly active dyestuff, mercerized wool cuts off item and selects Lan Nasu
Dyeing；
（3）Heavy twist long-staple cotton is made in Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process
Spun yarn, by silk flock successively through schappe system processing it is concise, system is continuous, at item, slubbing, spun yarn and silk, twisted filament, singeing step system
At spun silk strand；
（4）It will be through step（2）Aloe fibre, silk fiber refueling water and hair, carding process through wool spinning technology after dyeing
The cellulose mixing carded sliver is made, then will mix the carded sliver with dyeing after mercerized wool cut-out item cotton spinning mixing in doubling step and and
Mixing ripe bar is obtained, mixing rove then is made in mixing Roving Frames of the ripe bar through cotton spinning；
（5）Mixing rove and heavy twist long-staple cotton spun yarn are made to mixing cored coil on the spinning process of cotton spinning, then
Mixing cored cylinder yarn is made through the winding procedure in cotton spinning in mixing cored coil；
（6）Cored cylinder yarn will be mixed, cop-cop-yarn is made through the doubling in wool spinning technology, double twisting, yarn steaming process with silk；
（7）Using cop-cop-yarn as warp thread, spun silk strand as weft yarn, high conformal health-care environmental-protecting is made through warping, weaving process
Fabric；The conformal health-care environmental-protecting fabric of height obtained is finally made to the conformal health-care environmental-protecting face of height of the present invention through postfinishing process
Material.
3. a kind of production method of high conformal health-care environmental-protecting fabric according to claim 2, which is characterized in that including following
Step：
（1）Mercerized wool fiber is obtained into the mercerized wool that principal length is 36mm through crush cutting process and cuts off item；
（2）Aloe fibre, silk fiber are dyed using reactive dye, dyeing includes the following steps：It sequentially adds first
Auxiliary agent, reactive dye then sequentially add 1/3 alum, 2/3 alum, and 1 degree of speed per minute is then kept to be warming up to 60 degree,
It then keeps the temperature 20 minutes and 1/3 soda ash is added；Continue heat preservation and 2/3 soda ash is added in 20 minutes, then 30 minutes is kept the temperature, most afterwards after
Manage out cylinder；Mercerized wool cuts off item and lanasol dye dyeing, dyeing is selected to include the following steps：Auxiliary agent, dye are sequentially added first
Material, is then warming up to 100 degree, and keeps the temperature 70 minutes, it is last it is post-treated go out cylinder；
（3）Heavy twist long-staple cotton is made in Blowing carding of the long-staple cotton fiber through cotton spinning, combing, drafting, rove, spinning process
Spun yarn, wherein twist factor >=500 of heavy twist long-staple cotton spun yarn；By silk flock successively through schappe system processing it is concise, system is continuous, at
Item, slubbing, spun yarn and silk, twisted filament, singeing step are made 120S/ 2 spun silk strands；
（4）Cellulose is made in refueling water and hair, carding process of the aloe fibre, silk fiber after dyeing through wool spinning technology
The carded sliver is mixed, the carded sliver will be then mixed and cut off item in the mixing in doubling step of cotton spinning with the mercerized wool after dyeing and and obtain mixing ripe
Item, then will mixing Roving Frames of the ripe bar through cotton spinning be made mixing rove, wherein mixing in doubling step include slubbing drafting, two simultaneously
Item, three draftings；
（5）Mixing rove and heavy twist long-staple cotton spun yarn are made to mixing cored coil on the spinning process of cotton spinning, wherein
Mix front roller and preceding glue of rear roller feeding, heavy twist long-staple cotton spun yarn of the rove by spinning frame through core-spun yarn device by spinning frame
Roller group at the rear jaw of front roller feed, the mixing yarn and heavy twist long-staple cotton that mixing rove is obtained via draft area drawing-off are thin
Yarn converges at the preceding jaw for the front roller that front roller is formed with preceding rubber roller, and yarn is mixed under twist effect by heavy twist long-staple cotton
Spun yarn is wrapped in center and then obtains required mixing cored coil, then by mixing cored coil through the winder in cotton spinning
Mixing cored cylinder yarn is made in process；
（6）Cored cylinder yarn will be mixed and be made 135 through the doubling in wool spinning technology, double twisting, yarn steaming process with silkS/ 2 mixing stocks
Line；
（7）By 135S/ 2 cop-cop-yarns are as warp thread, 120S/ 2 spun silk strands as weft yarn, through warping, weaving process be made through
The conformal guarantor of height that close and filling density is respectively 403/10cm and 300/10cm, structure is plain weave small jacquard tissue, grammes per square metre is 170g/m
Strong environment-friendlyfabric fabric；Finally the conformal health-care environmental-protecting fabric of height obtained is singed through the bad cloth in postfinishing process successively, braying, baking
The final conformal health-care environmental-protecting fabric of height is made in dry, soft, tank steaming process.
4. a kind of production method of high conformal health-care environmental-protecting fabric according to claim 2 or 3, it is characterised in that：It is described
Mercerized wool fiber be 100SAU mercerized wool items, the aloe fibre be wool type 1.5D aloe fibres, described is soft
Silk fiber is the 1.5D silk fibers of wool type, and the silk is 30D silks.
5. a kind of production method of high conformal health-care environmental-protecting fabric according to claim 2 or 3, it is characterised in that：It is described
（4）Step, the grease overall control being added in the refueling water process aloe fibre, silk fiber total amount 10% within,
The ratio of water is less than 1/3 in grease, while 1% antistatic agent of fiber total amount is added；In the wool blending step, upper machine moisture regain
Reach 14%, bored hair 24 hours；In the carding process, speed is 900r/min when upper machine.
6. a kind of production method of high conformal health-care environmental-protecting fabric according to claim 2 or 3, it is characterised in that：It is described
（6）It walks, in the doubling process, the doubling on Italian TUAN types, speed 400m/min, and add a certain amount of oil,
Ensure that yarn is bright and clean；In the double twisting process, using Italian GEMINIS double twistings, low speed is twisted, and adds 2 sheet metals,
It prevents from making a pause when guide；In the yarn steaming process, using 88 degree 15 points, 90 degree 20 points 2 cycle yarn steamings, keep strand fully fixed
Type.
7. a kind of production method of high conformal health-care environmental-protecting fabric according to claim 2 or 3, it is characterised in that：It is described
（7）Step, in the warping process, using the BEN-TRONIC type warping machines of Benninger of Switzerland, when warping on yarn
Slurry, the rate of sizing 10% form coating, increase yarn abrasion performance, reduction yarn breakage, tension in Warping in yam surface
14cN, beaming tension 12cN, 400 revs/min of speed；In the weaving process, using Dornier rapier looms, shed forms is
Non- clear opening, back beam height 11, the front and back position 0 of the back rest, warp stop frame height 1.5, front and back position 5, palm fibre usually between 330 degree,
Speed 340r/min；It in the braying process, is washed using import open width, 60 DEG C of brayings, 80 DEG C of crabbings are carried out continuously；The baking
Steam drying, temperature is used to be less than 100 DEG C in dry process；In the softening step, softening agent is added；In the tank steaming process,
110 DEG C of temperature continues 5 minutes.