CN104886835B - One can fill that floss is two-sided wears feather dress fabric and production method thereof - Google Patents
One can fill that floss is two-sided wears feather dress fabric and production method thereof Download PDFInfo
- Publication number
- CN104886835B CN104886835B CN201510247732.5A CN201510247732A CN104886835B CN 104886835 B CN104886835 B CN 104886835B CN 201510247732 A CN201510247732 A CN 201510247732A CN 104886835 B CN104886835 B CN 104886835B
- Authority
- CN
- China
- Prior art keywords
- sided
- floss
- fill
- dress fabric
- feather dress
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses one and can fill that floss is two-sided wears feather dress fabric and production method thereof, its innovative point is in that: described fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is terylene, and the line density of described terylene and chinlon is 15～30D；Described fill the two-sided production method wearing feather dress fabric of floss, including following step: warping, slurry silk axle, lease making, gait, weave.The present invention adopts the chinlon of 15～30D and terylene warp, tram to be respectively interleaved, then through warping, slurry silk axle, lease making, gait, weave these six steps and obtain filling that floss is two-sided wears feather dress fabric, the tradition of floss just can be filled, it is achieved that can directly fill floss after having broken the two layers of cloth sewing of routine.
Description
Technical field
The present invention relates to spinninging technical field, especially one can fill that floss is two-sided wears feather dress fabric
And production method.
Background technology
Down jackets, are the warming clothing of indispensability in winter, are widely accepted now.Existing down jackets are usually in interlayer and fill eider down, then pass through separator bar and whole clothes is divided into fritter, it is prevented that eider down falls to reuniting to bottom.Owing to the gap between cut-off rule is relatively big, existing feather dress fabric there will be the phenomenon running hair mostly, and, most down jackets are all that one side is worn, and this brings a lot of inconvenience to people in dress.
Summary of the invention
It is an object of the invention to design one and can fill two-sided feather dress fabric and the production method thereof of wearing of floss, solve the problem that down jackets run hair.
For achieving the above object, the technical scheme is that one can fill that floss is two-sided wears feather dress fabric and production method thereof, it is characterised in that:
Described fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is terylene, and the line density of described terylene and chinlon is 15～30D；
Described fill the two-sided production method wearing feather dress fabric of floss, including following step: warping, slurry silk axle, lease making, gait, weave.
Further, described production method specifically comprises the following steps that
A) warping step: chinlon is carried out batch warping, described warping step is selected field, Tianjin coltfoal TWN-E warping machine, the speed of described warping machine is 295～305m/min, yarn cake is heavily 6～8kg, the tension force batched is 8～10kg, warp beam hardness is 80～90%, and the tension force of wire vent is 3～5g/ root, roller be pressurised into 0.15～0.25Mpa；
B) slurry silk step: by field, Tianjin coltfoal KSH500-e, the chinlon after warping being starched silk machine stock tank and pads serosity, concentration of slurry is 13～15%, temperature 40～50 DEG C, and the rate of sizing 11～12% mud jacking pressure is 3.5～4.0Mpa, and soaking paste pressure is 3.5～4.0Mpa；Dry the slurry axle making cladding serous coat, drying room temperature 120～140 DEG C then through drying room, slurry axle hardness is 80～90%；In stock tank, percentage elongation controls is 0.1～0.3%, and in cylinder, percentage elongation controls 0.8～1.0%；
C) and axle step: the slurry axle after slurry silk carries out also axle by Toyota's FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, the speed of warp rebeaming machine is 55～65m/min, going out thread tension is 8～10kg, and coiling tension is 100～120kg, and beam of a loom hardness is 80～90%.
D) lease making step: beam of a loom carries out lease making on leasing machine, and the speed controlling of leasing machine is 80～100 pieces/minute.
E) gait step: gait method according to fabric, the chinlon on beam of a loom is sequentially passed through plastic heddle and reed.
F) weaving step: adopting coltfoal ZW408 double; two water-jet loom in field, Tianjin to carry out weaving and produce, the speed of loom is 550～650rpm, and heald frame opening amount is 40～50mm, and beating traverse is 90～100mm, and loom weight tension force is 3～5kg.
Further, described fill floss two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of described access node, inner it is organized as plain weave, the table warp of the two-sided tissue of described access node, back warp arrangement are than being 1:1, the arrangement of table latitude, back weft is than being 1:1, and described access node is two-sided, and spacing of being organized in broadwise is 300～500.
Further, the described two-sided end count wearing feather dress fabric of floss that fills is 600～700/10cm, and filling density is 540～640/10cm；Door width is 1.45～1.55m.
The invention has the beneficial effects as follows:
(1) present invention adopts the chinlon of 15～30D and terylene warp, tram to be respectively interleaved, then through warping, slurry silk axle, lease making, gait, weave these six steps and obtain filling that floss is two-sided wears feather dress fabric, the tradition of floss just can be filled, it is achieved that can directly fill floss after having broken the two layers of cloth sewing of routine.
(2) weaving step of the present invention have employed the two-sided organizational structure of access node, it is achieved that fabric can directly fill floss, thread count is big simultaneously, thus avoiding the generation boring floss phenomenon.
(3) present invention selects chinlon and terylene, be the silk of original liquid coloring fibre spinning, eliminate staining procedure, and finished product fabric color fastness is good and stablize simultaneously.
(4) present invention is in 6 steps produced, and by setting distinctive technological parameter, reduces cracked ends and lousiness phenomenon so that the production process of the present invention can be smoothed out.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme is elaborated.
Embodiment 1
One can fill that floss is two-sided wears feather dress fabric and production method thereof, it is characterised in that: can fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is the line density of terylene, terylene and chinlon is 15D；
The two-sided production method wearing feather dress fabric of floss can be filled, including following step: warping, slurry silk axle, lease making, gait, weave.
Production method specifically comprises the following steps that
A, warping step: chinlon and terylene are carried out batch warping, select field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 295m/min, yarn cake is heavily 6kg, and the tension force batched is 8kg, and warp beam hardness is 80%, the tension force of wire vent is 3g/ root, roller be pressurised into 0.15Mpa；
B, slurry silk step: by field, Tianjin coltfoal KSH500-e, the chinlon after warping and terylene being starched silk machine stock tank and pads serosity, concentration of slurry is 13%, temperature 40 DEG C, and the rate of sizing 11% mud jacking pressure is 3.5Mpa, and soaking paste pressure is 3.5Mpa；Dry the slurry axle making cladding serous coat, drying room temperature 120 DEG C then through drying room, slurry axle hardness is 90%；In stock tank, percentage elongation controls is 0.1%, and in cylinder, percentage elongation controls 0.8%；
C axle step: the slurry axle after slurry silk is undertaken and axle by Toyota's FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 55m/min, and going out thread tension is 8kg, and coiling tension is 100kg, and beam of a loom hardness is 90%.
D, lease making step: beam of a loom carries out lease making on leasing machine, and the speed controlling of leasing machine is 80 pieces/minute.
E, step of gaiting: gait method according to fabric, the chinlon on beam of a loom is sequentially passed through plastic heddle and reed.
F, weaving step: adopting coltfoal ZW408 double; two water-jet loom in field, Tianjin to carry out weaving and produce, the speed of loom is 550rpm, heald frame opening amount 40mm, and beating traverse is 100mm, and loom weight tension force is 3kg.
Further, can fill floss two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, the inner plain weave that is organized as, the table of the two-sided tissue of access node through, back warp arrangement than being 1:1, the arrangement of table latitude, back weft is than being 1:1, and access node is two-sided, and spacing of being organized in broadwise is 300.
Further, can fill the two-sided end count wearing feather dress fabric of floss is 700/10cm, and filling density is 640/10cm；Door width is 1.45m.
Embodiment 2
One can fill that floss is two-sided wears feather dress fabric and production method thereof, it is characterised in that: can fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is the line density of terylene, terylene and chinlon is 30D；The two-sided production method wearing feather dress fabric of floss can be filled, including following step: warping, slurry silk axle, leasing, gait, weave.
Further, production method specifically comprises the following steps that
A) warping step: chinlon and terylene are carried out batch warping, selects field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 305m/min, yarn cake is heavily 8kg, and the tension force batched is 10kg, and warp beam hardness is 80%, the tension force of wire vent is 5g/ root, roller be pressurised into 0.25Mpa；
B) slurry silk step: by field, Tianjin coltfoal KSH500-e, the chinlon after warping and terylene being starched silk machine stock tank and pads serosity, concentration of slurry is 13%, temperature 50 C, the rate of sizing 11%, and mud jacking pressure is 4.0Mpa, and soaking paste pressure is 4.0Mpa；Dry the slurry axle making cladding serous coat, drying room temperature 140 DEG C then through drying room, slurry axle hardness is 80%；In stock tank, percentage elongation controls is 0.3%, and in cylinder, percentage elongation controls 1.0%；
C) and axle step: the slurry axle after slurry silk carries out also axle by Toyota's FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 65m/min, and going out thread tension is 10kg, and coiling tension is 120kg, and beam of a loom hardness is 80%.
D) lease making step: beam of a loom carries out lease making on leasing machine, and the speed controlling of leasing machine is 100 pieces/minute.
E) gait step: gait method according to fabric, the chinlon on beam of a loom is sequentially passed through plastic heddle and reed.
F) weaving step: adopting coltfoal ZW408 double; two water-jet loom in field, Tianjin to carry out weaving and produce, the speed of loom is 550rpm, and heald frame opening amount is 50mm, and beating traverse is 90mm, and loom weight tension force is 5kg.
Further, can fill floss two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, the inner plain weave that is organized as, the table of the two-sided tissue of access node through, back warp arrangement than being 1:1, the arrangement of table latitude, back weft is than being 1:1, and access node is two-sided, and spacing of being organized in broadwise is 300.
Further, can fill the two-sided end count wearing feather dress fabric of floss is 600/10cm, and filling density is 540/10cm；Door width is 1.55m.
Embodiment 3
One can fill that floss is two-sided wears feather dress fabric and production method thereof, it is characterised in that: can fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is the line density of terylene, terylene and chinlon is 20D；The two-sided production method wearing feather dress fabric of floss can be filled, including following step: warping, slurry silk axle, lease making, gait, weave.
Further, production method specifically comprises the following steps that
G) warping step: chinlon carries out batch warping, selects field, Tianjin coltfoal TWN-E warping machine in warping step, the speed of warping machine is 300m/min, yarn cake is heavily 7kg, and the tension force batched is 9kg, and warp beam hardness is 85%, the tension force of wire vent is 4g/ root, roller be pressurised into 0.20Mpa；
H) slurry silk step: by field, Tianjin coltfoal KSH500-e, the chinlon after warping and terylene being starched silk machine stock tank and pads serosity, concentration of slurry is 14%, temperature 45 C, and the rate of sizing 11.5% mud jacking pressure is 3.7Mpa, and soaking paste pressure is 3.8Mpa；Dry the slurry axle making cladding serous coat, drying room temperature 130 DEG C then through drying room, slurry axle hardness is 85%；In stock tank, percentage elongation controls is 0.2%, and in cylinder, percentage elongation controls 0.8%；
I) and axle step: the slurry axle after slurry silk carries out also axle by Toyota's FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 60m/min, and going out thread tension is 10kg, and coiling tension is 110kg, and beam of a loom hardness is 85%.
J) lease making step: beam of a loom carries out lease making on leasing machine, and the speed controlling of leasing machine is 90 pieces/minute.
K) gait step: gait method according to fabric, the chinlon in warp beam is sequentially passed through plastic heddle and reed.
L) weaving step: adopting coltfoal ZW408 double; two water-jet loom in field, Tianjin to carry out weaving and produce, the speed of loom is 600rpm, and heald frame opening amount is 45mm, and beating traverse is 95mm, and loom weight tension force is 4kg.
Further, can fill floss two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of access node, the inner plain weave that is organized as, the table of the two-sided tissue of access node through, back warp arrangement than being 1:1, the arrangement of table latitude, back weft is than being 1:1, and access node is two-sided, and spacing of being organized in broadwise is 400.
Further, can fill the two-sided end count wearing feather dress fabric of floss is 650/10cm, and filling density is 590/10cm；Door width is 1.50m.
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. one kind can be filled that floss is two-sided wears feather dress fabric, it is characterised in that:
Described fill floss two-sided wear feather dress fabric raw material be: warp thread is chinlon, and weft yarn is terylene, and the line density of described terylene and chinlon is 15～30D；
Described fill the two-sided production method wearing feather dress fabric of floss, including following step: warping, slurry silk axle, lease making, gait, weave；
Described production method specifically comprises the following steps that
Warping step: chinlon is carried out batch warping, described warping step is selected field, Tianjin coltfoal TWN-E warping machine, the speed of described warping machine is 295～305m/min, 6～8kg, the tension force batched is 8～10kg, warp beam hardness is 80～90%, and the tension force of wire vent is 3～5g/ root, roller be pressurised into 0.15～0.25MPa；
Slurry silk step: by field, Tianjin coltfoal KSH500-e, the chinlon after warping and terylene being starched silk machine stock tank and pads serosity, concentration of slurry is 13～15%, temperature 40～50 DEG C, and the rate of sizing 11～12% mud jacking pressure is 3.5～4.0Mpa, and soaking paste pressure is 3.5～4.0Mpa；Dry the slurry axle making cladding serous coat, drying room temperature 120～140 DEG C then through drying room, slurry axle hardness is 80～90%；In stock tank, percentage elongation controls is 0.1～0.3%, and in cylinder, percentage elongation controls 0.8～1.0%；
And axle step: the slurry axle after slurry silk is undertaken and axle by Toyota's FB150 warp rebeaming machine, and the number of axle is 12 axles, and door width is 177cm, and the speed of warp rebeaming machine is 55～65m/min, and going out thread tension is 8～10kg, and coiling tension is 100～120kg, and beam of a loom hardness is 80～90%.
2. one according to claim 1 can fill that floss is two-sided wears feather dress fabric, it is characterised in that: lease making step: beam of a loom carries out lease making on leasing machine, and the speed controlling of leasing machine is 80～100 pieces/minute.
3. one according to claim 2 can fill that floss is two-sided wears feather dress fabric, it is characterised in that: step of gaiting: gait method according to fabric, the chinlon in warp beam is sequentially passed through plastic heddle and reed.
4. one according to claim 3 can fill that floss is two-sided wears feather dress fabric, it is characterized in that: weaving step: adopt coltfoal ZW408 double; two water-jet loom in field, Tianjin to carry out weaving and produce, the speed of loom is 550～650rpm, heald frame opening amount is 40～50mm, beating traverse is 90～100mm, and loom weight tension force is 3～5kg.
5. the one according to any one in claim 1-4 can fill that floss is two-sided wears feather dress fabric, it is characterized in that: described fill floss two-sided wear feather dress fabric be organized as the two-sided tissue of access node, the table of the two-sided tissue of described access node, inner it is organized as plain weave, the table warp of the two-sided tissue of described access node, back warp arrangement are than being 1:1, the arrangement of table latitude, back weft is than being 1:1, and described access node is two-sided, and spacing of being organized in broadwise is 300～500.
6. one according to claim 5 can fill that floss is two-sided wears feather dress fabric, it is characterised in that: the described two-sided end count wearing feather dress fabric of floss that fills is 600～700/10cm, and filling density is 540～640/10cm；Door width is 1.45～1.55m.