CN103306006B - A kind of chemical fibre cotton functionality memory calms down the preparation method of fabric - Google Patents

A kind of chemical fibre cotton functionality memory calms down the preparation method of fabric Download PDF

Info

Publication number
CN103306006B
CN103306006B CN201310176965.1A CN201310176965A CN103306006B CN 103306006 B CN103306006 B CN 103306006B CN 201310176965 A CN201310176965 A CN 201310176965A CN 103306006 B CN103306006 B CN 103306006B
Authority
CN
China
Prior art keywords
fabric
temperature
speed
dyeing
weave
Prior art date
Application number
CN201310176965.1A
Other languages
Chinese (zh)
Other versions
CN103306006A (en
Inventor
孙德荣
孙德明
王振功
邱成
Original Assignee
徐州斯尔克纤维科技股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 徐州斯尔克纤维科技股份有限公司 filed Critical 徐州斯尔克纤维科技股份有限公司
Priority to CN201310176965.1A priority Critical patent/CN103306006B/en
Publication of CN103306006A publication Critical patent/CN103306006A/en
Application granted granted Critical
Publication of CN103306006B publication Critical patent/CN103306006B/en

Abstract

The invention provides a kind of chemical fibre cotton functionality memory and calm down the preparation method of fabric, comprise operation: warp-wise adopts the super imitative cotton yarn of 50D----130D, broadwise adopts the ptt fiber of 50D-100D to be raw material, and the ptt fiber content < 50% of fabric, adopt multi-arm water jet looms to weave, the tension force of warp, broadwise silk thread controls between 0.12-1G/D, adopts common disperse dyeing, dyeing maximum temperature sets 105 DEG C---120 DEG C, finally carry out shaping process.Gained fabric of the present invention has the comprehensive effect of strong cotton texture, shape-retaining ability and calming down property.

Description

A kind of chemical fibre cotton functionality memory calms down the preparation method of fabric

Technical field

The present invention relates to a kind of preparation method of fabric, refer more particularly to a kind of chemical fibre cotton functionality memory and calm down fabric.

Background technology

Not only domestic market, the category of memory fabric is a lot, also having of chemical fibre cotton, but has cotton function but also have and calm down the fabric of comprehensive function of function and almost do not have.

Summary of the invention

The preparation method of the chemical fiber plus material that the object of the present invention is to provide a kind of strong cotton texture, shape-retaining ability and calming down property extremely strong, the fabric produced by this making aspect has the extremely strong resultant effect of strong cotton texture, shape-retaining ability and calming down property.

Concrete scheme of the present invention is as follows:

Chemical fibre cotton functionality memory calms down the preparation method of fabric, comprises following operation:

(1) raw material is selected

The warp-wise of described fabric adopts the super imitative cotton yarn of 50D-130D, and broadwise adopts the ptt fiber of 50D-100D, and the ptt fiber content < 50% of fabric.

(2) weaving process

Adopt multi-arm water jet looms to weave, the tension force of warp, broadwise silk thread controls between 0.12-1G/D.

(3) dyeing process

Adopt common disperse dyeing, dyeing maximum temperature sets 105 DEG C-120 DEG C.

(4) shaping process

The preparation method of foregoing a kind of chemical fibre cotton functionality memory fabric,

Described weaving process also comprises:

Sizing concentration is 11%, sizing temperature 46 DEG C, and baking temperature is 125 DEG C-145 DEG C, the loom speed of a motor vehicle 470 revs/min, and warp tension controls between 0.25-0.6G/D;

Described dyeing process also comprises:

Fabric is carried out lax refining process: solution temperature 95 DEG C in concise groove, speed of a motor vehicle 50-60M/ minute, fabric time of staying 20-25 second in concise groove;

During dyeing, dye material solution carries out heating from normal temperature and makes programming rate be 1.5 DEG C/min, is raised to maximum temperature 120 DEG C, is incubated 30 minutes, and then carries out being cooled to normal temperature with the speed of 2 DEG C/min.

Described shaping process also comprises:

Stentering forming: fabric setting temperature 165 DEG C, cropping adopts mode of shaking.

Compared with prior art, the present invention has the following advantages:

1, gained fabric of the present invention has the comprehensive effect of strong cotton texture, shape-retaining ability and calming down property.

2, gained fabric panel broadwise standard elastic of the present invention extends 12-25%, standard elastic response rate more than 80%.Wash shrinkage rate within 1.5%, have fluffy cotton sense, pendency and resilience good, calming down property of folding line is good.

Detailed description of the invention:

Be described further below in conjunction with embodiment:

Embodiment 1

The imitative cotton yarn of 80D/49F selected by warp thread, and the PTT long filament (tram adds 8T/CM, 1S1Z) of 75D/24F selected by weft yarn, tissue adopt simple plain weave, upper machine through close 60/CM, upper machine filling density 38/CM.

To weave cotton cloth preparation

Sizing concentration is 11%, sizing temperature 46 degree; Baking temperature is 125-145 degree; Warp tension control is between 0.12-0.45G/D, and slurry vehicle speed is at 125-200 m/min.

To weave cotton cloth enforcement

Adopt water jet looms, the loom speed of a motor vehicle 470 turns; Warp tension controls between 0.25-0.6G/D.

Dye pre-treatment

Fabric is carried out lax concise: solution temperature 95 DEG C in concise groove, speed of a motor vehicle 50-60M/ minute, fabric time of staying 20-25 second in concise groove.

Pre-setting: temperature 185 degree, speed of a motor vehicle 55M/ minute, cropping adopts mode of shaking.

Dying operation

During dyeing, dye material solution carries out heating from normal temperature and makes programming rate be 1.5 DEG C/min, is raised to maximum temperature 120 DEG C, is incubated 30 minutes, and then carries out being cooled to normal temperature with the speed of 2 DEG C/min.

Final finishing engineering

Stentering forming: temperature 165 degree, speed: 60M/ speed, cropping adopts mode of shaking.

The finished product evaluation of physical property result of gained fabric is as follows: the broadwise elastic extension 20% of fabric, elastic recovery rate 90%; Washing shrinkage factor 1%, powerful 10.3 newton of warp-wise, powerful 8.6 newton of broadwise, dyeing COLOR FASTNESS level Four.

Embodiment 2

The imitative cotton yarn of 80D/49F selected by warp thread, and the PTT long filament (tram adds 8T/CM, 1S1Z) of 75D/24F selected by weft yarn. tissue adopt simple plain weave, upper machine through close 60/CM, upper machine filling density 38/CM.

To weave cotton cloth preparation

Sizing concentration is 11%, sizing temperature 46 degree; Baking temperature is 125-145 degree; Warp tension control is between 0.12-0.45G/D, and slurry vehicle speed is at 125-200 m/min;

To weave cotton cloth enforcement

Adopt water jet looms, the loom speed of a motor vehicle 470 turns; Warp tension controls between 0.25-0.6G/D.

Dye pre-treatment

Fabric is carried out lax concise: solution temperature 95 DEG C in concise groove, speed of a motor vehicle 50-60M/ minute, fabric time of staying 20-25 second in concise groove.

Pre-setting: temperature 185 degree, speed of a motor vehicle 55M/ minute, cropping adopts mode of shaking.

Dying operation

During dyeing, dye material solution carries out heating from normal temperature and makes programming rate be 1.5 DEG C/min, is raised to maximum temperature 120 DEG C, is incubated 30 minutes, and then carries out being cooled to normal temperature with the speed of 2 DEG C/min.

Final finishing engineering

Stentering forming: temperature 165 degree, speed: 60M/ speed, cropping adopts mode of shaking.

The finished product evaluation of physical property result of gained fabric is as follows: the broadwise elastic extension 21% of fabric, elastic recovery rate 85%; Washing shrinkage factor 1%, powerful 10.5 newton of warp-wise, powerful 8.4 newton of broadwise, dyeing COLOR FASTNESS level Four.

Claims (1)

1. chemical fibre cotton functionality memory calms down a preparation method for fabric, it is characterized in that comprising following operation:
(1) raw material is selected
The imitative cotton yarn of 80D/49F selected by organizine, and tram selects the PTT long filament of 75D/24F, and tram adds 8T/CM, 1S1Z, tissue adopt simple plain weave, upper machine through close 60/CM, upper machine filling density 38/CM;
(2) weaving process
To weave cotton cloth preparation
Sizing concentration is 11%, sizing temperature 46 DEG C; Baking temperature is 125-145 DEG C; Warp tension controls between 0.12-0.45G/D, and slurry vehicle speed is at 125-200 m/min;
To weave cotton cloth enforcement
Multi-arm water jet looms is adopted to weave, the loom speed of a motor vehicle 470 revs/min; Warp tension controls between 0.25-0.6G/D, and the tension force of broadwise silk thread controls between 0.12-1G/D;
(3) dyeing process
Dye pre-treatment
Fabric is carried out lax concise: solution temperature 95 DEG C in concise groove, speed of a motor vehicle 50-60M/ minute, fabric time of staying 20-25 second in concise groove;
Pre-setting: temperature 185 degree, speed of a motor vehicle 55M/ minute, cropping adopts mode of shaking;
Dying operation
Adopt common disperse dyeing, during dyeing, dye material solution carries out heating from normal temperature and makes programming rate be 1.5 DEG C/min, is raised to maximum temperature 120 DEG C, is incubated 30 minutes, and then carries out being cooled to normal temperature with the speed of 2 DEG C/min;
(4) shaping process
Stentering forming: fabric setting temperature 165 DEG C, cropping adopts mode of shaking.
CN201310176965.1A 2013-05-14 2013-05-14 A kind of chemical fibre cotton functionality memory calms down the preparation method of fabric CN103306006B (en)