CN104841850A - 一种耐高温型砂及其制备方法 - Google Patents
一种耐高温型砂及其制备方法 Download PDFInfo
- Publication number
- CN104841850A CN104841850A CN201510199816.6A CN201510199816A CN104841850A CN 104841850 A CN104841850 A CN 104841850A CN 201510199816 A CN201510199816 A CN 201510199816A CN 104841850 A CN104841850 A CN 104841850A
- Authority
- CN
- China
- Prior art keywords
- clay
- molding sand
- high temperature
- particle
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐高温型砂,由下列重量份的原料制成:黄土10-20、钢渣20-30、β-半水石膏3-4、甲基硅酸钠5-6、茶皂素1-2、CaO4-7、MnO5-8、炉黑5-8、二氧化钛5-8、聚氧化乙烯3-5、粘土200-220、水适量、助剂20-30;本发明型砂通过使用粘土,粒径大小合适,不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收利用;通过使用钢渣,增加了粘土颗粒的耐高温性,不易结块,节约了资源;通过使用甲基硅酸钠、炉黑、聚氧化乙烯,型砂不仅粘结性好,而且流动性好,高温溃散性好。
Description
技术领域
本发明涉及铸造领域,尤其涉及一种耐高温型砂及其制备方法。
背景技术
目前型砂存在的主要问题有:1、粒径大小难控制,如果型砂粒径太大,虽然透气性较好,但是铸件表面比较粗糙,光洁度不好;如果型砂料径太小,导致砂型透气性不好,铸件有气孔产生。2、散热不良,激冷效果差,复杂铸件内部易出现缩松、缩孔现象。3、分散性、流动性不好,易结块、起砂豆。4、易沾污铸件。5、脱模性差。6、对于不同种类的合金缺少针对性的型砂。
传统粘土型砂有很多优点,但是存在不易回收利用,透气性差、流动性不好、分散性不好、溃散性差、散热不好、环境污染严重的缺点。
因此,型砂存在的以上缺点需要克服。
发明内容
本发明的目的在于提供一种耐高温型砂及其制备方法,该型砂不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收利用,不易结块,节约了资源,高温溃散性好。
本发明的技术方案如下:
一种耐高温型砂,其特征在于由下列重量份的原料制成:黄土10-20、钢渣20-30、β-半水石膏3-4、甲基硅酸钠5-6、茶皂素1-2、CaO4-7、MnO5-8、炉黑5-8、二氧化钛5-8、聚氧化乙烯3-5、粘土200-220、水适量、助剂20-30;
所述助剂由下列重量份的原料制成:废瓷18-22、废玻璃2-3、碳酸钠2-3、膨润土3-4、羧甲基纤维素0.5-1、粘土3-4、六偏磷酸钠1-1.4、PP蜡1-1.4、糊精 1-1.4、水适量;制备方法为:将废瓷、废玻璃、碳酸钠、膨润土混合后进行球磨,过200目筛,在1200-1220℃下煅烧5-6小时,粉碎成粒径小于2mm的颗粒;将粘土、羧甲基纤维素、糊精加入4-5重量份水中,搅拌后加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在0.05-2mm,再与其他剩余成分混合,搅拌均匀,即得。
所述耐高温型砂的制备方法,其特征在于包括以下步骤:
(1)将粘土、黄土、钢渣、β-半水石膏、CaO、MnO、二氧化钛混合,粉碎,过50目筛,加入7-9%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在300-400℃下预烧20-25分钟,然后在1100-1200℃下烧结,取出,打磨至表面粗糙度≤0.1mm,得到粘土颗粒;
(2)将甲基硅酸钠、茶皂素、炉黑、聚氧化乙烯混合,研磨10-15分钟,得到混合物料;
(3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2-3%重量份的水混合7-10分钟,即得。
本发明的有益效果
本发明型砂通过使用粘土,粒径大小合适,不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收利用;通过使用钢渣,增加了粘土颗粒的耐高温性,不易结块,节约了资源;通过使用甲基硅酸钠、炉黑、聚氧化乙烯,型砂不仅粘结性好,而且流动性好,高温溃散性好。本发明助剂使用了废瓷、废玻璃,耐热性好,表面包覆有粘土,与粘土颗粒有良好的相容性,同时可增加型砂的流动性、分散性,防止粘土颗粒高温时粘结,利于回收利用。
具体实施方式
一种耐高温型砂,由下列重量份(公斤)的原料制成:黄土15、钢渣25、β-半水石膏3.5、甲基硅酸钠5.5、茶皂素1.5、CaO6、MnO6、炉黑6、二氧化钛6、聚氧化乙烯4、粘土210、水适量、助剂25;
所述助剂由下列重量份(公斤)的原料制成:废瓷20、废玻璃2.5、碳酸钠2.5、膨润土3.5、羧甲基纤维素0.7、粘土3.5、六偏磷酸钠1.2、PP蜡1.2、糊精 1.2、水适量;制备方法为:将废瓷、废玻璃、碳酸钠、膨润土混合后进行球磨,过200目筛,在1210℃下煅烧5.5小时,粉碎成粒径小于2mm的颗粒;将粘土、羧甲基纤维素、糊精加入4.5重量份水中,搅拌后加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在0.05-2mm,再与其他剩余成分混合,搅拌均匀,即得。
所述耐高温型砂的制备方法,包括以下步骤:
(1)将粘土、黄土、钢渣、β-半水石膏、CaO、MnO、二氧化钛混合,粉碎,过50目筛,加入9%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在350℃下预烧23分钟,然后在1150℃下烧结,取出,打磨至表面粗糙度≤0.1mm,得到粘土颗粒;
(2)将甲基硅酸钠、茶皂素、炉黑、聚氧化乙烯混合,研磨13分钟,得到混合物料;
(3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2.5%重量份的水混合9分钟,即得。
本实施例得到的型砂试验数据如下:湿压强度为90KPa,透气性95,热湿拉强度为2.4KPa,常温湿拉强度为22KPa。
Claims (2)
1.一种耐高温型砂,其特征在于由下列重量份的原料制成:黄土10-20、钢渣20-30、β-半水石膏3-4、甲基硅酸钠5-6、茶皂素1-2、CaO4-7、MnO5-8、炉黑5-8、二氧化钛5-8、聚氧化乙烯3-5、粘土200-220、水适量、助剂20-30;
所述助剂由下列重量份的原料制成:废瓷18-22、废玻璃2-3、碳酸钠2-3、膨润土3-4、羧甲基纤维素0.5-1、粘土3-4、六偏磷酸钠1-1.4、PP蜡1-1.4、糊精 1-1.4、水适量;制备方法为:将废瓷、废玻璃、碳酸钠、膨润土混合后进行球磨,过200目筛,在1200-1220℃下煅烧5-6小时,粉碎成粒径小于2mm的颗粒;将粘土、羧甲基纤维素、糊精加入4-5重量份水中,搅拌后加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在0.05-2mm,再与其他剩余成分混合,搅拌均匀,即得。
2.根据权利要求1所述耐高温型砂的制备方法,其特征在于包括以下步骤:
(1)将粘土、黄土、钢渣、β-半水石膏、CaO、MnO、二氧化钛混合,粉碎,过50目筛,加入7-9%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在300-400℃下预烧20-25分钟,然后在1100-1200℃下烧结,取出,打磨至表面粗糙度≤0.1mm,得到粘土颗粒;
(2)将甲基硅酸钠、茶皂素、炉黑、聚氧化乙烯混合,研磨10-15分钟,得到混合物料;
(3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2-3%重量份的水混合7-10分钟,即得。