CN104805694A - 一种抗静电腈纶纤维的制作方法 - Google Patents

一种抗静电腈纶纤维的制作方法 Download PDF

Info

Publication number
CN104805694A
CN104805694A CN201510188245.6A CN201510188245A CN104805694A CN 104805694 A CN104805694 A CN 104805694A CN 201510188245 A CN201510188245 A CN 201510188245A CN 104805694 A CN104805694 A CN 104805694A
Authority
CN
China
Prior art keywords
parts
acrylic fiber
finishing agent
antistatic
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510188245.6A
Other languages
English (en)
Inventor
陶文祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XIANGYING SPECIAL FIBER Co Ltd
Original Assignee
CHANGSHU XIANGYING SPECIAL FIBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XIANGYING SPECIAL FIBER Co Ltd filed Critical CHANGSHU XIANGYING SPECIAL FIBER Co Ltd
Priority to CN201510188245.6A priority Critical patent/CN104805694A/zh
Publication of CN104805694A publication Critical patent/CN104805694A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗静电腈纶纤维的制作方法，具体步骤包括：1）配置整理剂，取脂肪醇聚氧乙烯醚硫酸钠8～10份、脂肪醇聚氧乙烯丙基磺酸钠11～13份、丁醇20～22份、硬脂酸钾4～7份、水100～118份加热至75℃后搅拌均匀，制成整理剂；2）将腈纶纤维浸泡在步骤（1）中的整理剂内，压力2.3~2.4kg/cm2，带液率55~59％；3）对步骤（2）中的腈纶纤维烘干后将腈纶纤维在110~114℃之间恒温2~3小时。通过上述方式，本发明一种抗静电腈纶纤维的制作方法，该方法制作的腈纶纤维通过抗静电处理，可以防止使用时的静电，保证人们的正常使用。

Description

一种抗静电腈纶纤维的制作方法
技术领域
本发明涉及纤维领域，尤其涉及一种抗静电腈纶纤维的制作方法。
背景技术
不同质料的服装产生的静电会使衣服相互纠缠，穿着不便。衣料与皮肤电荷不同时，会相互吸附出现“裙抱腿”现象，使人步行困难。化纤衣服因静电严重，特易吸附空气中带异号电荷的尘埃微粒，易使衣服沾污；化纤衣服还特别易吸附头皮屑。贴身穿着化纤内衣，皮肤会产生刺痒感，穿着舒适性下降。穿着化纤衣服，由于摩擦起电，产生的静电压很高，在触摸金属物件等可导电物或与人握手时便会放电，产生电击感而令人不适。
发明内容
本发明主要解决的技术问题是提供一种抗静电腈纶纤维的制作方法。
为解决上述技术问题，本发明采用的一个技术方案是：一种抗静电腈纶纤维的制作方法，具体步骤包括：
1）配置整理剂，取脂肪醇聚氧乙烯醚硫酸钠8～10份、脂肪醇聚氧乙烯丙基磺酸钠11～13份、丁醇20～22份、硬脂酸钾4～7份、水100～118份加热至75℃后搅拌均匀，制成整理剂；
2）将腈纶纤维浸泡在步骤（1）中的整理剂内，压力2.3~2.4kg/cm2，带液率55~59％；
3）对步骤（2）中的腈纶纤维烘干后将腈纶纤维在110~114℃之间恒温2~3小时。
在本发明一个较佳实施例中，优选的所述整理剂的配置成分包括脂肪醇聚氧乙烯醚硫酸钠9份、脂肪醇聚氧乙烯丙基磺酸钠12份、丁醇21份、硬脂酸钾5份、水110份。
在本发明一个较佳实施例中，优选的所述步骤（2）中压力2.3kg/cm2，带液率57％。
在本发明一个较佳实施例中，优选的所述步骤（3）将腈纶纤维在110℃恒温2.5小时。
本发明的有益效果是：本发明一种抗静电腈纶纤维的制作方法，该方法制作的腈纶纤维通过抗静电处理，可以防止使用时的静电，保证人们的正常使用。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：一种抗静电腈纶纤维的制作方法，具体步骤包括：
1）配置整理剂，取脂肪醇聚氧乙烯醚硫酸钠8～10份、脂肪醇聚氧乙烯丙基磺酸钠11～13份、丁醇20～22份、硬脂酸钾4～7份、水100～118份加热至75℃后搅拌均匀，制成整理剂；
本实施例中优选的所述整理剂的配置成分包括脂肪醇聚氧乙烯醚硫酸钠9份、脂肪醇聚氧乙烯丙基磺酸钠12份、丁醇21份、硬脂酸钾5份、水110份。
2）将腈纶纤维浸泡在步骤（1）中的整理剂内，压力2.3~2.4kg/cm2，带液率55~59％；
本实施例中优选的所述步骤（2）中压力2.3kg/cm2，带液率57％。
3）对步骤（2）中的腈纶纤维烘干后将腈纶纤维在110~114℃之间恒温2~3小时。
本实施例中，优选的所述步骤（3）将腈纶纤维在110℃恒温2.5小时。
与现有技术相比，本发明一种抗静电腈纶纤维的制作方法，该方法制作的腈纶纤维通过抗静电处理，可以防止使用时的静电，保证人们的正常使用。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种抗静电腈纶纤维的制作方法，其特征在于，具体步骤包括：
1）配置整理剂，取脂肪醇聚氧乙烯醚硫酸钠8～10份、脂肪醇聚氧乙烯丙基磺酸钠11～13份、丁醇20～22份、硬脂酸钾4～7份、水100～118份加热至75℃后搅拌均匀，制成整理剂；
2）将腈纶纤维浸泡在步骤（1）中的整理剂内，压力2.3~2.4kg/cm2，带液率55~59％；
3）对步骤（2）中的腈纶纤维烘干后将腈纶纤维在110~114℃之间恒温2~3小时。
2.根据权利要求1所述的一种抗静电腈纶纤维的制作方法，其特征在于：优选的所述整理剂的配置成分包括脂肪醇聚氧乙烯醚硫酸钠9份、脂肪醇聚氧乙烯丙基磺酸钠12份、丁醇21份、硬脂酸钾5份、水110份。
3.根据权利要求1所述的一种抗静电腈纶纤维的制作方法，其特征在于：优选的所述步骤（2）中压力2.3kg/cm2，带液率57％。
4.根据权利要求1所述的一种抗静电腈纶纤维的制作方法，其特征在于：优选的所述步骤（3）将腈纶纤维在110℃恒温2.5小时。
CN201510188245.6A 2015-04-21 2015-04-21 一种抗静电腈纶纤维的制作方法 Pending CN104805694A (zh)