CN102978923A - 一种防水涤棉混纺织物的生产方法 - Google Patents
一种防水涤棉混纺织物的生产方法 Download PDFInfo
- Publication number
- CN102978923A CN102978923A CN201210498441XA CN201210498441A CN102978923A CN 102978923 A CN102978923 A CN 102978923A CN 201210498441X A CN201210498441X A CN 201210498441XA CN 201210498441 A CN201210498441 A CN 201210498441A CN 102978923 A CN102978923 A CN 102978923A
- Authority
- CN
- China
- Prior art keywords
- cotton
- blended fabric
- production method
- polyester blended
- polyester cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防水涤棉混纺织物的生产方法,包括步骤为:将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和非离子表面活性剂依次加入反应釜中,搅拌逐渐升温至70-80℃,往反应釜中滴加偶氮二异丁腈,继续反应,冷却得到混合乳液;混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,再进行烘干并烘焙,得到防水的涤棉混纺织物。通过上述方式,本发明提供的一种防水涤棉混纺织物的生产方法,制得的涤棉混纺织物不具有良好的防水功能,整理后能保持涤棉混纺织物原有的色泽,手感柔软,穿着清爽舒适,整个生产过程产生废气废物少,有效降低对环境的污染,整理剂质量好,使用后能增加涤棉混纺织物的品质。
Description
技术领域
本发明涉及纺织面料领域,特别是涉及一种防水涤棉混纺织物的生产方法。
背景技术
织物整理剂是指再纺织品离开织机后到成品前对织物进行加工整理赋予纺织品某种特殊功能的试剂。按照功能上划分通常有阻燃整理剂、抗静电整理剂、。卫生整理剂、防污和易去污整理剂、拒水拒油整理剂等类别。在织物上施加一种具有特殊化学分子结构的整理剂,改变纤维表面的组成,并牢牢地附着于纤维或与纤维化学结合,使织物不再被水和常用的食用油所润湿,这样的整理剂为拒水拒油整理剂。
传统的拒水拒油整理剂整理织物后使织物手感发硬,处理耐久性不够,使用一段时间后拒水拒油效果不明显,人穿着透气性差,舒适感不强,不能够很好的增加织物的附加值,反而使织物的品质降低。
发明内容
本发明主要解决的技术问题是提供一种防水涤棉混纺织物的生产方法,能有效提高涤纶织物的防水性能。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种防水涤棉混纺织物的生产方法,包括步骤为:
(1)将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和非离子表面活性剂依次加入反应釜中,搅拌逐渐升温至70-80℃,往反应釜中滴加偶氮二异丁腈,继续反应,冷却得到混合乳液;
(2)混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,再进行烘干并烘焙,得到防水的涤棉混纺织物。
在本发明一个较佳实施例中,步骤(1)中所述非离子表面活性剂为失水山梨醇脂肪酸酯。
在本发明一个较佳实施例中,步骤(1)中所述继续反应的时间为3-4小时。
在本发明一个较佳实施例中,步骤(2)中所述一浸一轧的轧余率为60-80%。
本发明的有益效果是:本发明的防水涤棉混纺织物的生产方法,制得的涤棉混纺织物不具有良好的防水功能,整理后能保持涤棉混纺织物原有的色泽,手感柔软,穿着清爽舒适,整个生产过程产生废气废物少,有效降低对环境的污染,整理剂质量好,使用后能增加涤棉混纺织物的品质。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
实施例一:
(1)将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和失水山梨醇脂肪酸酯依次加入反应釜中,搅拌逐渐升温至80℃,往反应釜中滴加偶氮二异丁腈,继续反应3小时,冷却得到混合乳液;
(2)混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,轧余率为70%,再进行烘干并烘焙,得到防水的涤棉混纺织物。
实施例二:
(1)将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和失水山梨醇脂肪酸酯依次加入反应釜中,搅拌逐渐升温至70℃,往反应釜中滴加偶氮二异丁腈,继续反应4小时,冷却得到混合乳液;
(2)混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,轧余率为60%,再进行烘干并烘焙,得到防水的涤棉混纺织物。
实施例三:
(1)将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和失水山梨醇脂肪酸酯依次加入反应釜中,搅拌逐渐升温至75℃,往反应釜中滴加偶氮二异丁腈,继续反应4小时,冷却得到混合乳液;
(2)混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,轧余率为80%,再进行烘干并烘焙,得到防水的涤棉混纺织物。
本发明揭示的防水涤棉混纺织物的生产方法,制得的涤棉混纺织物不具有良好的防水功能,整理后能保持涤棉混纺织物原有的色泽,手感柔软,穿着清爽舒适,整个生产过程产生废气废物少,有效降低对环境的污染,整理剂质量好,使用后能增加涤棉混纺织物的品质。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种防水涤棉混纺织物的生产方法,其特征在于,包括步骤为:
(1)将水、甲基丙烯酸六氟丁酯、丙烯酸正丁酯、甲基丙烯酸甲酯和非离子表面活性剂依次加入反应釜中,搅拌逐渐升温至70-80℃,往反应釜中滴加偶氮二异丁腈,继续反应,冷却得到混合乳液;
(2)混合乳液、水和交联剂进行混合得到整理液,对涤棉混纺织物进行一浸一轧整理,再进行烘干并烘焙,得到防水的涤棉混纺织物。
2.根据权利要求1所述的防水涤棉混纺织物的生产方法,其特征在于,步骤(1)中所述非离子表面活性剂为失水山梨醇脂肪酸酯。
3.根据权利要求1所述的防水涤棉混纺织物的生产方法,其特征在于,步骤(1)中所述继续反应的时间为3-4小时。
4.根据权利要求1所述的防水涤棉混纺织物的生产方法,其特征在于,步骤(2)中所述一浸一轧的轧余率为60-80%。