CN104774586A - 新型液晶屏粘合剂及其使用方法 - Google Patents

新型液晶屏粘合剂及其使用方法 Download PDF

Info

Publication number
CN104774586A
CN104774586A CN201510172753.5A CN201510172753A CN104774586A CN 104774586 A CN104774586 A CN 104774586A CN 201510172753 A CN201510172753 A CN 201510172753A CN 104774586 A CN104774586 A CN 104774586A
Authority
CN
China
Prior art keywords
component
liquid crystal
sizing material
parts
crystal display
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510172753.5A
Other languages
English (en)
Other versions
CN104774586B (zh
Inventor
郭浩
丁爱顺
朱兴飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Kinlita Chemical Co ltd
Original Assignee
Fudan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fudan University filed Critical Fudan University
Priority to CN201510172753.5A priority Critical patent/CN104774586B/zh
Publication of CN104774586A publication Critical patent/CN104774586A/zh
Application granted granted Critical
Publication of CN104774586B publication Critical patent/CN104774586B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及高分子材料，具体涉及一种新型液晶屏粘合剂及其使用方法。该粘合剂是一种双组份液体硅胶，包括A组份胶料和B组份胶料，其中，A组份胶料由如下重量份配比组份组成：含M、Q链节的含苯丙烯基的硅树脂45~65份、含M、D链节的苯丙烯基硅油35~55份、催化剂0.001~0.01份；B组份胶料如下重量份配比组份组成：含M、Q链节的含苯丙烯基的硅树脂45~65份、含M、D链节的苯丙烯基硅油35~55份、含M、D链节的含氢基的硅油0.1~0.2份、含环氧的增粘剂0.3~1.1份、加成反应抑制剂0.08~0.3份。本发明的新型液晶屏粘合剂具有撕裂强度大、稳定性好、粘附性强弹性体机械强度高、透光率高的特点，对液晶屏、玻璃都有较牢固的粘接。

Description

新型液晶屏粘合剂及其使用方法
技术领域
本发明涉及高分子材料，具体涉及一种新型液晶屏粘合剂及其使用方法。
背景技术
由于大部分现代液晶设备的电子元件、功率电路模块、大型集成电路板等高科技领域进一步实现高性能、高可靠性，因而，对液晶屏粘合剂品质的要求非常高，比如涂抹层薄，透光性好，粘附性强，稳定性好，易于运输储存，对于在生产过程中出现的次品可以以非常简单的方法进行清洗以回收液晶屏，等等。目前，此类产品在国内需求量非常大，但还没有实现国产化，完全依赖进口，价格昂贵。
发明内容
为了满足国内需求量，本发明提供一种新型液晶屏粘合剂及其使用方法。
本发明提出的新型液晶屏粘合剂，包括A组份胶料和B组份胶料，其中，
A组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
催化剂：0.001~0.01份；
B组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
含M、D链节的含氢基的硅油：0.1~0.2份；
含环氧的增粘剂：0.3~1.1份；
加成反应抑制剂：0.08~0.3份；
A组份和B组份的重量比为1：2－2：1。
本发明中，所述含M、Q链节的含苯丙烯基的硅树脂分子式为：(R1R2 2SiO1/2)a(SiO2)b，其中a：2.0~2.5，b:4~6，R1是苯丙烯基，R2 是甲基、乙基、丙基或者丁基中任一种。
　本发明中，所述含M、D链节的苯丙烯基的硅油的分子式为：R1R2 2SiO(R2 2SiO)n (R1R2SiO)mSi R2 2R1，其中n：35~45，m:12~18，R1是苯丙烯基，R2 是甲基、乙基、丙基或者丁基中任一种。
本发明中，所述含环氧的增粘剂：(H2R2 4R3 2SiO)3-9，R3是-CH2CH2CH2SiCH2CH2CH2CH2OCH2(CHCH2O)，R2 是甲基、乙基、丙基或者丁基中任一种。
本发明中，所述含M、D链节的含氢基硅油的分子式为：R2 2HSiO(R2 2SiO)e (HR2SiO)gSi R2 2H，其中e：30~40，g:15~25， R2 是甲基、乙基、丙基或者丁基中任一种。
本发明中，所述催化剂为3-氨基对甲苯甲醚。
本发明中，所述加成反应抑制剂为乙基丁炔醇。
本发明提出一种液晶屏胶粘剂的使用方法，具体为：将A组份胶料和B组份胶料按1:2~2:1的比例充分搅拌均匀，在真空条件下将胶料中的气泡脱除完全，然后与液晶屏与玻璃在50°C~60°C条件下烘烤5~10分钟，即可得到硅树脂型弹性体。
本发明的新型液晶粘合剂具有以下特点：胶料中含的MQ树脂，弹性体机械强度高；胶料中的MQ树脂，弹性体通光率达96%以上（300μm~900μm厚）；胶料中的粘合剂对液晶屏、玻璃都较牢固的粘接。
具体实施方式
以下结合具体实施例，对本发明进行详细说明。
实施例1
A组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
催化剂：0.001~0.01份；
B组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
含M、D链节的含氢基的硅油：0.1~0.2份；
含环氧的增粘剂：0.3~1.1份；
加成反应抑制剂：0.08~0.3份；
胶料使用方法：将A组份胶料和B组份胶料按1:1的比例充分搅拌均匀，在真空条件下将胶料中的气泡脱除完全，然后与液晶屏、玻璃在55°C条件下烘烤8分钟，即可得到与液晶屏、玻璃有良好粘接的硅树脂型弹性体。
实施例2
A组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：50份；
含M、D链节的苯丙烯基硅油：50份；
催化剂：0.008份；
B组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：50份；
含M、D链节的苯丙烯基硅油:50份；
含M、D链节的含氢基的硅油：0.13份；
含环氧的增粘剂：0.5份；
加成反应抑制剂：0.1份；
胶料使用方法：将A组份胶料和B组份胶料按1:2的比例充分搅拌均匀，在真空条件下将胶料中的气泡脱除完全，然后与液晶屏、玻璃在50°C条件下烘烤5分钟，即可得到与液晶屏、玻璃有良好粘接的硅树脂型弹性体。
实施例3
A组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：60份；
含M、D链节的苯丙烯基硅油：40份；
催化剂：0.005份；
B组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：60份；
含M、D链节的苯丙烯基硅油：40份；
含M、D链节的含氢基的硅油：0.2份；
含环氧的增粘剂：1.1份；
加成反应抑制剂：0.3份；
胶料使用方法：将A组份胶料和B组份胶料按2:1的比例充分搅拌均匀，在真空条件下将胶料中的气泡脱除完全，然后与液晶屏、玻璃在60°C条件下烘烤10分钟，即可得到与液晶屏、玻璃有良好粘接的硅树脂型弹性体。
应当理解的是，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。

Claims (8)

1.新型液晶屏粘合剂，包括A组份胶料和B组份胶料，其特征是，
A组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
催化剂：0.001~0.01份；
B组份胶料由如下重量份配比组份组成：
含M、Q链节的含苯丙烯基的硅树脂：45~65份；
含M、D链节的苯丙烯基硅油：35~55份；
含M、D链节的含氢基的硅油：0.1~0.2份；
含环氧的增粘剂：0.3~1.1份；
加成反应抑制剂：0.08~0.3份；
A组份和B组份的重量比为1：2－2：1。
2.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述含M、Q链节的含苯丙烯基的硅树脂分子式为：(R1R2 2SiO1/2)a(SiO2)b，其中a：2.0~2.5，b:4~6，R1是苯丙烯基，R2 是甲基、乙基、丙基或者丁基中任一种。
3.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述含M、D链节的苯丙烯基的硅油的分子式为：R1R2 2SiO(R2 2SiO)n (R1R2SiO)mSi R2 2R1，其中n：35~45，m:12~18，R1是苯丙烯基，R2 是甲基、乙基、丙基或者丁基中任一种。
4.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述含环氧的增粘剂：(H2R2 4R3 2SiO)3-9，R3是-CH2CH2CH2SiCH2CH2CH2CH2OCH2(CHCH2O)，R2 是甲基、乙基、丙基或者丁基中任一种。
5.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述含M、D链节的含氢基硅油的分子式为：R2 2HSiO(R2 2SiO)e (HR2SiO)gSi R2 2H，其中e：30~40，g:15~25， R2 是甲基、乙基、丙基或者丁基中任一种。
6.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述催化剂为3-氨基对甲苯甲醚。
7.根据权利要求1所述的液晶屏胶粘剂，其特征是，所述加成反应抑制剂为乙基丁炔醇。
8.一种如权利要求1至8所述的液晶屏胶粘剂的使用方法，其特征是，将A组份胶料和B组份胶料按1:2~2:1的比例充分搅拌均匀，在真空条件下将胶料中的气泡脱除完全，然后与液晶屏与玻璃在50°C~60°C条件下烘烤5~10分钟，即可得到硅树脂型弹性体。
CN201510172753.5A 2015-04-14 2015-04-14 新型液晶屏粘合剂及其使用方法 Active CN104774586B (zh)