CN104758261A - 淫羊藿苷plga纳米粒子及制备方法及用途 - Google Patents

淫羊藿苷plga纳米粒子及制备方法及用途 Download PDF

Info

Publication number
CN104758261A
CN104758261A CN201510218289.9A CN201510218289A CN104758261A CN 104758261 A CN104758261 A CN 104758261A CN 201510218289 A CN201510218289 A CN 201510218289A CN 104758261 A CN104758261 A CN 104758261A
Authority
CN
China
Prior art keywords
icariin
solution
plga
nanoparticle
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510218289.9A
Other languages
English (en)
Inventor
孙洪范
缪丹丹
张超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Institute of Biomedical Engineering of CAMS and PUMC
Original Assignee
Institute of Biomedical Engineering of CAMS and PUMC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Institute of Biomedical Engineering of CAMS and PUMC filed Critical Institute of Biomedical Engineering of CAMS and PUMC
Priority to CN201510218289.9A priority Critical patent/CN104758261A/zh
Publication of CN104758261A publication Critical patent/CN104758261A/zh
Pending legal-status Critical Current

Abstract

本发明公开了淫羊藿苷PLGA纳米粒子及制备方法及用途，制备方法为：以二甲基甲酰胺为溶剂配制淫羊藿苷溶液为溶液1；配制PLGA溶液为溶液2；在冰浴和超声下，将溶液1滴加入溶液2中得溶液3；在冰浴和超声下，将溶液3滴加入PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；置于透析袋中透析；将透析袋中的液体离心，冷冻干燥即得淫羊藿苷PLGA纳米粒子。本方法制得的淫羊藿苷PLGA纳米粒子相比未包封的药物，在水中的分散性能显著提高，并缓慢释放淫羊藿苷以延长作用时间，粒子粒径分布均匀，90％以上在100‐300纳米之间。本发明的方法使用的材料简单，方法易操作，重复性好。

Description

淫羊藿苷PLGA纳米粒子及制备方法及用途
技术领域
本发明属于中药制药技术领域，特别是涉及一种淫羊藿苷PLGA纳米粒子及制备方法。
背景技术
淫羊藿苷是从中药淫羊藿中提取的有效活性成分，是一种黄酮苷类化合物，具有抗肿瘤，促进骨形成，抗骨质疏松，调节机体免疫等药理学活性。淫羊藿苷为水不溶性药物，能微溶于乙醇，乙酸乙酯,不溶于醚、苯、氯仿。聚乳酸-羟基乙酸共聚物(PLGA)是生物相容性可降解高分子聚合物，常用于包载药物，以保护药物活性、缓慢释放药物延长药物作用时间，对于难溶性药物，可以提高其分散性。
PLGA包载药物的纳米粒制备常采用溶剂挥发法，将药物和PLGA溶于沸点较低的二氯甲烷等有机溶剂，通过挥发除去溶剂,但淫羊藿苷既不溶于水，也不溶于醚、苯、氯仿等易挥发性有机溶剂，故现有的溶剂挥发法不适用于制备淫羊藿苷PLGA纳米粒。
发明内容
本发明的目的是克服现有技术的不足，提供一种纳米粒子粒径分布均匀，90％以上在100‐300nm之间的淫羊藿苷PLGA纳米粒子。
本发明的第二个目的是提供一种简便易行的淫羊藿苷PLGA纳米粒子的制备方法。
本发明的第二个目的是提供一种淫羊藿苷PLGA纳米粒子的用途。
本发明的技术方案概述如下：
淫羊藿苷PLGA纳米粒子的制备方法，包括如下步骤：
(1)以二甲基甲酰胺为溶剂配制浓度为0.005-0.02g/ml的淫羊藿苷溶液为溶液1；以二甲基甲酰胺为溶剂配制浓度为0.01-0.08g/ml的PLGA溶液为溶液2；
(2)在冰浴和超声下，按体积比为1-2:3的比例，将溶液1滴加入溶液2中得溶液3；
(3)在冰浴和超声下，按体积比为1:4-10的比例将溶液3滴加入浓度为10g/L-30g/L的PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；
(4)将PLGA淫羊藿苷O/W乳剂置于透析袋中，放入装有水的容器中，在转速20-50rpm透析6-10h；
(5)将透析袋中的液体在4℃离心，收集固化的纳米粒，冷冻干燥即得淫羊藿苷PLGA纳米粒子，所述PLGA为聚乳酸-羟基乙酸共聚物的缩写，所述PVA为聚乙烯醇的缩写。
超声的条件优选为：频率为20HZ,振幅为20％-35％。
离心的转速优选为20,000rpm，离心的时间为30min。
上述方法制备的淫羊藿苷PLGA纳米粒子。
上述淫羊藿苷PLGA纳米粒子在制备促进软骨细胞增殖药物的应用。
本发明的优点：
本方法使用的载药材料PLGA生物相容性好，颗粒小，均匀，溶解性好。本方法制得的淫羊藿苷PLGA纳米粒相比未包封的药物，在水中的分散性能显著提高，并缓慢释放淫羊藿苷以延长作用时间。本发明中的制备方法使用的材料简单，方法易操作，重复性好。制备的纳米粒子粒径分布均匀，粒径在在100‐300nm之间。
附图说明
图1本发明的淫羊藿苷PLGA纳米粒子扫描电镜图。
图2本发明的淫羊藿苷PLGA纳米粒子的粒径图。
图3本发明的淫羊藿苷PLGA纳米粒子的Zeta电位图。
图4本发明的淫羊藿苷PLGA纳米粒子的体外累计释放曲线。
图5本发明的淫羊藿苷PLGA纳米粒子对软骨细胞增殖影响的实验。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
淫羊藿苷购于中国药品生物制品检定所，批号：110737-200415
实施例1
淫羊藿苷PLGA纳米粒子的制备方法，包括如下步骤：
(1)以二甲基甲酰胺为溶剂配制浓度为0.01g/ml的淫羊藿苷溶液为溶液1；以二甲基甲酰胺为溶剂配制浓度为0.05g/ml的PLGA溶液为溶液2；PLGA分子量为7600-11500Da；
(2)在冰浴和超声下，按体积比为1.5:3的比例，将溶液1滴加入溶液2中得溶液3；所述超声频率为20HZ,振幅为30％，超声时间10min,每超声30S间隔5S；
(3)在冰浴和超声下，按体积比为1:6的比例将溶液3滴加入浓度为10g/L的PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；PVA的分子量为30000-70000Da，所述超声频率20HZ,振幅为30％，超声时间15min，每超声30S间隔5S；
(4)将PLGA淫羊藿苷O/W乳剂置于透析袋[MD34(8000-14000D)]中，放入装有水的容器中，在转速30rpm磁力搅拌，透析8h；
(5)将透析袋中的液体在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，用蒸馏水洗涤，在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，冷冻干燥即得淫羊藿苷PLGA纳米粒子。所述PLGA为聚乳酸-羟基乙酸共聚物的缩写，所述PVA为聚乙烯醇的缩写。
实施例2
淫羊藿苷PLGA纳米粒子的制备方法，包括如下步骤：
(1)以二甲基甲酰胺为溶剂配制浓度为0.005g/ml的淫羊藿苷溶液为溶液1；以二甲基甲酰胺为溶剂配制浓度为0.01g/ml的PLGA溶液为溶液2；PLGA分子量为7600-11500Da；
(2)在冰浴和超声下，按体积比为1:3的比例，将溶液1滴加入溶液2中得溶液3；所述超声频率为20HZ,振幅为20％，超声时间15min,每超声30S间隔5S；
(3)在冰浴和超声下，按体积比为1:4的比例将溶液3滴加入浓度为15g/L的PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；PVA的分子量为30000-70000Da，所述超声频率20HZ,振幅为20％，超声时间15min，每超声30S间隔5S；
(4)将PLGA淫羊藿苷O/W乳剂置于透析袋[MD34(8000-14000D)]中，放入装有水的容器中，在转速20rpm磁力搅拌，透析10h；
(5)将透析袋中的液体在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，用蒸馏水洗涤，在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，冷冻干燥即得淫羊藿苷PLGA纳米粒子。
实施例3
淫羊藿苷PLGA纳米粒子的制备方法，包括如下步骤：
(1)以二甲基甲酰胺为溶剂配制浓度为0.02g/ml的淫羊藿苷溶液为溶液1；以二甲基甲酰胺为溶剂配制浓度为0.08g/ml的PLGA溶液为溶液2；PLGA分子量为7600-11500Da；
(2)在冰浴和超声下，按体积比为2:3的比例，将溶液1滴加入溶液2中得溶液3；所述超声频率为20HZ,振幅为35％，超声时间8min,每超声30S间隔5S；
(3)在冰浴和超声下，按体积比为1:10的比例将溶液3滴加入浓度为30g/L的PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；PVA的分子量为30000-70000Da所述超声频率20HZ,振幅为35％，超声时间10min，每超声30S间隔5S；
(4)将PLGA淫羊藿苷O/W乳剂置于透析袋[MD34(8000-14000D)]中，放入装有水的容器中，在转速50rpm磁力搅拌，透析6h；
(5)将透析袋中的液体在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，用蒸馏水洗涤，在4℃，20,000rpm下超速离心30min,收集固化的纳米粒，冷冻干燥即得淫羊藿苷PLGA纳米粒子。
实施例4
淫羊藿苷PLGA纳米粒子体外表征：
(1)粒度分布：取实施例1制备的淫羊藿苷PLGA纳米粒子少许溶于水中，吸取1ml样品溶液，注入到纳米粒度和Zeta电位分析仪的石英测量池和毛细管小池中，测定样品的粒径和Zeta电位，见图1、2和图3。
(2)稳定性测试：将实施例1制备的淫羊藿苷PLGA纳米粒子少许溶于水中，分别于0天，7天，14天，30天取样，测定样品的粒径，多分散体系和Zeta电位,考察纳米粒的长期稳定性，见表1。
表1
(3)缓释测定
用pH＝7.4的磷酸缓冲盐溶液(PBS)作为缓释介质，准确称取实施例1制备的淫羊藿苷PLGA纳米粒子10mg，分散在4mLPBS中，置于双向扩散池的一侧，另一侧加入4mlPBS。在100rpm震荡速度，37℃条件下进行纳米粒的体外释放速度测定，分别在2、4、8、24、48、72、120、168、216、264、336和408h，取单纯加PBS一侧的样4mL，同时补充4mL新鲜PBS。用高效液相色谱检测释放液中游离淫羊藿苷浓度，计算不同时间点药物累积释放百分比，绘制累积释放曲线，见图4。
检测结果所示实施例1制备的淫羊藿苷PLGA纳米粒子粒较均一，得到的纳米粒的平均粒径在180nm左右，且在水中有较好的均一性稳定性，在pH＝7.4的PBS缓冲液中均具有一定的缓释能力。
实验证明，实施例2和实施例3制备的淫羊藿苷PLGA纳米粒子的粒较均一，得到的纳米粒的平均粒径和水中稳定性与实施例1的结果相似，在pH＝7.4的PBS缓冲液中均具有一定的缓释能力。
实施例5
细胞增殖实验
从兔关节软骨里提取软骨细胞，培养至第四代，按1*104接种于96孔板，待贴壁后吸出原培养基，分别加入含有空载纳米粒的培养基，含有淫羊藿苷(0.05％DMSO助溶)的培养基及实施例1制备的淫羊藿苷PLGA纳米粒子的培养基各200ul/孔。(培养基为DMEM培养基,含有10％FBS和1％双抗)
空载纳米粒组，淫羊藿苷组及淫羊藿苷PLGA纳米粒子组每组分别设三种终浓度，其中淫羊藿苷组和淫羊藿苷PLGA纳米粒子组根据含淫羊藿苷药量分别设10-4M，10-5M,10-6M三组，空载纳米粒的三组质量分别对应淫羊藿苷PLGA纳米粒子组的质量。对照组不加药，阴性空白组为培养基。置于37℃，5％CO2的培养箱中培养1，2，3，5，7，9d,MTT法测定细胞生长曲线。
检测结果如图5所示，本发明所示的空载纳米粒对细胞相容性较好，无毒性作用。本发明所示的三组不同浓度淫羊藿苷PLGA纳米粒子(在图中简称载药纳米)在9d，促进软骨细胞增殖率明显高于同浓度的淫羊藿苷组，且无细胞抑制作用。
实验证明，实施例2和实施例3制备的淫羊藿苷PLGA纳米粒子促进软骨细胞增殖率与实施例1相似。

Claims (5)

1.淫羊藿苷PLGA纳米粒子的制备方法，其特征是包括如下步骤：
(1)以二甲基甲酰胺为溶剂配制浓度为0.005-0.02g/ml的淫羊藿苷溶液为溶液1；以二甲基甲酰胺为溶剂配制浓度为0.01-0.08g/ml的PLGA溶液为溶液2；
(2)在冰浴和超声下，按体积比为1-2:3的比例，将溶液1滴加入溶液2中得溶液3；
(3)在冰浴和超声下，按体积比为1:4-10的比例将溶液3滴加入浓度为10g/L-30g/L的PVA水溶液中,形成PLGA淫羊藿苷O/W乳剂；
(4)将PLGA淫羊藿苷O/W乳剂置于透析袋中，放入装有水的容器中，在转速20-50rpm透析6-10h；
(5)将透析袋中的液体在4℃离心，收集固化的纳米粒，冷冻干燥即得淫羊藿苷PLGA纳米粒子，所述PLGA为聚乳酸-羟基乙酸共聚物的缩写，所述PVA为聚乙烯醇的缩写。
2.根据权利要求1所述的淫羊藿苷PLGA纳米粒子的制备方法，其特征是所述超声的条件为：频率为20HZ,振幅为20％-35％。
3.根据权利要求1所述的淫羊藿苷PLGA纳米粒子的制备方法，其特征是所述离心的转速为20,000rpm，离心的时间为30min。
4.权利要求1的方法制备的淫羊藿苷PLGA纳米粒子。
5.权利要求2的淫羊藿苷PLGA纳米粒子在制备促进软骨细胞增殖药物的应用。
CN201510218289.9A 2015-04-30 2015-04-30 淫羊藿苷plga纳米粒子及制备方法及用途 Pending CN104758261A (zh)