CN104746226A - Weaving process for cotton and flax blended fabric products - Google Patents
Weaving process for cotton and flax blended fabric products Download PDFInfo
- Publication number
- CN104746226A CN104746226A CN201510188357.1A CN201510188357A CN104746226A CN 104746226 A CN104746226 A CN 104746226A CN 201510188357 A CN201510188357 A CN 201510188357A CN 104746226 A CN104746226 A CN 104746226A
- Authority
- CN
- China
- Prior art keywords
- cotton
- loom
- speed
- cloth
- weaving process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a weaving process for cotton and flax blended fabric products. Flax fibers and cotton fibers are spun into blended yarns, and the blended yarns serve as warp yarns and weft yarns which are woven into the cotton and flax blended fabric products. The weaving process includes the steps: winding; warping, sizing and knitting; silicon oil washing and drying; weaving. Warps and wefts are firstly made into twisting cheeses by a winding machine, and the rotating speed of a groove drum in winding is 600+/-5r/min. Flax and the fibers are blended by a special manufacturing process, so that fabrics have effects of bumps, the problems of poor skin-friendly comfort, poor durability and the like of bumps of past granular materials such as rubber matrixes and medical stone filling are changed, and the fabrics have the advantages of super softness, moisture absorbing and sweat releasing properties, light, thin and warmth retention functions and more easiness in care.
Description
Technical field
The invention belongs to textile technology field, be specifically related to a kind of weaving process of cotton ramie blended spinning fabric product.
Background technology
That nowadays understands along with people's living standard improves constantly, and dressing theory is durable, attractive in appearance to comfortable, the health transition of pursuit by original pursuit.Consumer not only requires that the color of fabric, style, feel are unique, and the appearance of the lifting of an urgent demand knit fabric scientific and technological content and greater functionality type knit fabric.
There is the clothing of massage efficacy at present, the salient point of the particle materials such as general employing rubber matrix, medical stone filling, the clothing of this kind of material in pro-skin comfortableness, weave, equal existing defects in durability etc., utilize chemical-fibres filaments Weft Knitted Shell Fabric to weave the salient point with massage efficacy, and the very rare report of fabric of super softness, moisture absorbing and sweat releasing, frivolous warming, durable in use function can be met.Therefore, develop and a there is super softness, moisture absorbing and sweat releasing, frivolous heat-preserving function and the fabric of more easily nursing has wide market prospects.
Summary of the invention
Goal of the invention: the present invention is directed to deficiency, a kind of weaving process of cotton ramie blended spinning fabric product is proposed, the home textile product containing flax fibre and cotton fiber that this technique is made has good bacteriostasis and health-care performance, and there is antiultraviolet, radiation proof function and good sucting wet air permeability, product is more soft than other gunny products comfortable.
Technical scheme: the weaving process of a kind of cotton ramie blended spinning fabric product of the present invention, the blended yarn that employing linen fibre and cotton fiber are spun into, for form through weft weaving, comprises the steps:
(1) winder: first with bobbin winder, warp and parallel are made twisting bobbin, during winder, groove drum rotating speed is 600 ± 5r/min;
(2) warping: under 400-500m/min speed of beaming, is wound on beam of a loom uniformly by the precursor line cake of warping machines by some;
(3) sizing: the warp in some warp beams and parallel are simultaneously drawn by Sizing machines, immerses slurries, and pressure removes remaining liquid, dries;
(4) knitting;
(5) silicone oil is washed;
(6) dry: the softener of use: softener FRD-5 20 ± 5g/L, softener A QG-01EZ 20 ± 5g/L, and adjust ph is 4.5-7.5, dry tenter temperatures 140 ± 5 DEG C, the speed of a motor vehicle is 50 ± 5m/min;
(7) shape;
(8) weave: use the non guide hook loom freely circled in the air, the loom speed of a motor vehicle is at 130 ~ 250r/min; Guide coefficient of friction is 0.4-0.5, and warp tension control is at 50-100kg, and weft tension controls at 50-200CN.
As optimization, described linen fibre: the weight ratio of cotton fiber is 65:35.
As optimization, described yarn dyeing process is: adopt import Italy Ba Zuoni environmental protection O type low tension type dyeing machine, dyeing machine enters water and is in charge of at normal temperatures into cloth, add CD-1000N, it is stirred in the secondary cylinder of dyeing machine and opens automatic feeding system, it will be pumped in dyeing machine automatically, and pH value controls between 3 ~ 6; Then following technological parameter is inputted in computer system: tension force 20-50N, rotating speed 150m/min, nozzle exit pressure 0.2-0.5MP/cm
2, main pump rotating speed 1005r/min, bath raio 1:5, pre-treatment temperature 98 DEG C, heat up 2 DEG C/min, temperature retention time 20min; Then be cooled to normal temperature with the speed of 1.5 DEG C/min, wash 2 times, and add CD-1000N; Then post-processing temperature 50 DEG C is warming up to the speed of 2 DEG C/min, temperature retention time 20-30min.
As optimization, described knitting is: by 40S cotton arrangement loom first; 40S linen-cotton ash is arranged in loom second mouthful; 40S linen-cotton ash is arranged in loom the 3rd mouthful, is follow-uply arranged in order; Start to carry out braiding debugging, have yarn tension to debug; Yarn feeding nozzle position is debugged; The concrete debugging of the knitting needle kinking depth; The tension force debugging etc. of batcher; Loom preliminary debugging completes, at second mouthful of feeding 30D spandex; Now debug, determined that product style is correct, carried out weaving production after the debugging of loom each position is accurate; Grey cloth enters normal production, and revolving speed of knitting machine is 15r/min; Then reviewer carries out grey cloth inspection.
As optimization, add TK-R02 hydrophilic softener in the washed journey of described silicone oil, its consumption is weight ratio 0.5% ~ 1.5%.
As optimization, described setting process is: adopt import Korea S reason and heat setting machine, technological parameter: frame amplitude 155CM, temperature 160-180 DEG C, machine speed 30r/min, nip pressure 2.5t, overfeeding 28, cabinet air quantity: windward 500r/min, leeward 800r/min; Entering cloth roll, to turn down pressure be that 2.5t dips cloth cover; Setting temp. control computer 10 casees temperature 160-180 DEG C; Adjustment overfeeding 28; Enter cloth machine speed 30m/min by sizing, go out cloth and measure cloth fabric width 155CM.
Beneficial effect: the present invention adopts special manufacturing technique that fiber crops and fiber are carried out blending, fabric is made to have the effect of salient point, change the problem such as pro-skin comfortableness, durability of the salient point of the particle such as rubber matrix, medical stone filling material in the past, and this braided fabric have super softness, moisture absorbing and sweat releasing, frivolous heat-preserving function and the advantage of more easily nursing.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Below in conjunction with detailed description of the invention, set forth the present invention further.Should be understood that these embodiments are only not used in for illustration of the present invention to limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention, and these equivalent form of values fall within the application's appended claims limited range equally after the content of having read the present invention's instruction.
Embodiment 1
A weaving process for cotton ramie blended spinning fabric product, adopts blended yarn that linen fibre and cotton fiber are spun into according to weight ratio 65:35 for form through weft weaving, comprises the steps:
(1) winder: first with bobbin winder, warp and parallel are made twisting bobbin, during winder, groove drum rotating speed is 600r/min;
(2) warping: under 400m/min speed of beaming, is wound on beam of a loom uniformly by the precursor line cake of warping machines by some;
(3) sizing: adopt import Italy Ba Zuoni environmental protection O type low tension type dyeing machine, dyeing machine enters water and is in charge of at normal temperatures into cloth, adds CD-1000N, it is stirred in the secondary cylinder of dyeing machine and opens automatic feeding system, it will be pumped in dyeing machine automatically, and pH value controls between 6; Then following technological parameter is inputted in computer system: tension force 20N, rotating speed 150m/min, nozzle exit pressure 0.2MP/cm
2, main pump rotating speed 1005r/min, bath raio 1:5, pre-treatment temperature 98 DEG C, heat up 2 DEG C/min, temperature retention time 20min; Then be cooled to normal temperature with the speed of 1.5 DEG C/min, wash 2 times, and add CD-1000N; Then post-processing temperature 50 DEG C is warming up to the speed of 2 DEG C/min, temperature retention time 20min;
(4) knitting by 40S cotton arrangement loom first; 40S linen-cotton ash is arranged in loom second mouthful; 40S linen-cotton ash is arranged in loom the 3rd mouthful, is follow-uply arranged in order; Start to carry out braiding debugging, have yarn tension to debug; Yarn feeding nozzle position is debugged; The concrete debugging of the knitting needle kinking depth; The tension force debugging etc. of batcher; Loom preliminary debugging completes, at second mouthful of feeding 30D spandex; Now debug, determined that product style is correct, carried out weaving production after the debugging of loom each position is accurate; Grey cloth enters normal production, and revolving speed of knitting machine is 15r/min; Then reviewer carries out grey cloth inspection;
(5) silicone oil is washed: add TK-R02 hydrophilic softener, and its consumption is weight ratio 0.5%;
(6) dry: the softener of use: softener FRD-5 20 ± 5g/L, softener A QG-01EZ 20 ± 5g/L, and adjust ph is 4.5-7.5, dry tenter temperatures 140 ± 5 DEG C, the speed of a motor vehicle is 50 ± 5m/min;
(7) shape: adopt import Korea S reason and heat setting machine, technological parameter: frame amplitude 155CM, temperature 160 DEG C, machine speed 30r/min, nip pressure 2.5t, overfeeding 28, cabinet air quantity: windward 500r/min, leeward 800r/min; Entering cloth roll, to turn down pressure be that 2.5t dips cloth cover; Setting temp. control computer 10 casees temperature 160 DEG C; Adjustment overfeeding 28; Enter cloth machine speed 30m/min by sizing, go out cloth and measure cloth fabric width 155CM;
(8) weave: use the non guide hook loom freely circled in the air, the loom speed of a motor vehicle is at 130r/min; Guide coefficient of friction is 0.4, and warp tension control is at 50-100kg, and weft tension controls at 50CN.
Embodiment 2
A weaving process for cotton ramie blended spinning fabric product, adopts blended yarn that linen fibre and cotton fiber are spun into according to weight ratio 65:35 for form through weft weaving, comprises the steps:
(1) winder: first with bobbin winder, warp and parallel are made twisting bobbin, during winder, groove drum rotating speed is 605r/min;
(2) warping: under 500m/min speed of beaming, is wound on beam of a loom uniformly by the precursor line cake of warping machines by some;
(3) sizing: adopt import Italy Ba Zuoni environmental protection O type low tension type dyeing machine, dyeing machine enters water and is in charge of at normal temperatures into cloth, adds CD-1000N, it is stirred in the secondary cylinder of dyeing machine and opens automatic feeding system, it will be pumped in dyeing machine automatically, and pH value controls between 6; Then following technological parameter is inputted in computer system: tension force 50N, rotating speed 150m/min, nozzle exit pressure 0.5MP/cm
2, main pump rotating speed 1005r/min, bath raio 1:5, pre-treatment temperature 98 DEG C, heat up 2 DEG C/min, temperature retention time 20min; Then be cooled to normal temperature with the speed of 1.5 DEG C/min, wash 2 times, and add CD-1000N; Then post-processing temperature 50 DEG C is warming up to the speed of 2 DEG C/min, temperature retention time 30min;
(4) knitting by 40S cotton arrangement loom first; 40S linen-cotton ash is arranged in loom second mouthful; 40S linen-cotton ash is arranged in loom the 3rd mouthful, is follow-uply arranged in order; Start to carry out braiding debugging, have yarn tension to debug; Yarn feeding nozzle position is debugged; The concrete debugging of the knitting needle kinking depth; The tension force debugging etc. of batcher; Loom preliminary debugging completes, at second mouthful of feeding 30D spandex; Now debug, determined that product style is correct, carried out weaving production after the debugging of loom each position is accurate; Grey cloth enters normal production, and revolving speed of knitting machine is 15r/min; Then reviewer carries out grey cloth inspection;
(5) silicone oil is washed: add TK-R02 hydrophilic softener, and its consumption is weight ratio 1.5%;
(6) dry: the softener of use: softener FRD-5 20 ± 5g/L, softener A QG-01EZ 20 ± 5g/L, and adjust ph is 4.5-7.5, dry tenter temperatures 140 ± 5 DEG C, the speed of a motor vehicle is 50 ± 5m/min;
(7) shape: adopt import Korea S reason and heat setting machine, technological parameter: frame amplitude 155CM, temperature 180 DEG C, machine speed 30r/min, nip pressure 2.5t, overfeeding 28, cabinet air quantity: windward 500r/min, leeward 800r/min; Entering cloth roll, to turn down pressure be that 2.5t dips cloth cover; Setting temp. control computer 10 casees temperature 180 DEG C; Adjustment overfeeding 28; Enter cloth machine speed 30m/min by sizing, go out cloth and measure cloth fabric width 155CM;
(8) weave: use the non guide hook loom freely circled in the air, the loom speed of a motor vehicle is at 250r/min; Guide coefficient of friction is 0.4-0.5, and warp tension control is at 50-100kg, and weft tension controls at 200CN.
Embodiment 3
A weaving process for cotton ramie blended spinning fabric product, adopts blended yarn that linen fibre and cotton fiber are spun into according to weight ratio 65:35 for form through weft weaving, comprises the steps:
(1) winder: first with bobbin winder, warp and parallel are made twisting bobbin, during winder, groove drum rotating speed is 605r/min;
(2) warping: under 450m/min speed of beaming, is wound on beam of a loom uniformly by the precursor line cake of warping machines by some;
(3) sizing: adopt import Italy Ba Zuoni environmental protection O type low tension type dyeing machine, dyeing machine enters water and is in charge of at normal temperatures into cloth, adds CD-1000N, it is stirred in the secondary cylinder of dyeing machine and opens automatic feeding system, it will be pumped in dyeing machine automatically, and pH value controls between 4; Then following technological parameter is inputted in computer system: tension force 30N, rotating speed 150m/min, nozzle exit pressure 0.3MP/cm
2, main pump rotating speed 1005r/min, bath raio 1:5, pre-treatment temperature 98 DEG C, heat up 2 DEG C/min, temperature retention time 20min; Then be cooled to normal temperature with the speed of 1.5 DEG C/min, wash 2 times, and add CD-1000N; Then post-processing temperature 50 DEG C is warming up to the speed of 2 DEG C/min, temperature retention time 25min;
(4) knitting by 40S cotton arrangement loom first; 40S linen-cotton ash is arranged in loom second mouthful; 40S linen-cotton ash is arranged in loom the 3rd mouthful, is follow-uply arranged in order; Start to carry out braiding debugging, have yarn tension to debug; Yarn feeding nozzle position is debugged; The concrete debugging of the knitting needle kinking depth; The tension force debugging etc. of batcher; Loom preliminary debugging completes, at second mouthful of feeding 30D spandex; Now debug, determined that product style is correct, carried out weaving production after the debugging of loom each position is accurate; Grey cloth enters normal production, and revolving speed of knitting machine is 15r/min; Then reviewer carries out grey cloth inspection;
(5) silicone oil is washed: add TK-R02 hydrophilic softener, and its consumption is weight ratio 1%;
(6) dry: the softener of use: softener FRD-5 20 ± 5g/L, softener A QG-01EZ 20 ± 5g/L, and adjust ph is 4.5-7.5, dry tenter temperatures 140 ± 5 DEG C, the speed of a motor vehicle is 50 ± 5m/min;
(7) shape: adopt import Korea S reason and heat setting machine, technological parameter: frame amplitude 155CM, temperature 170 DEG C, machine speed 30r/min, nip pressure 2.5t, overfeeding 28, cabinet air quantity: windward 500r/min, leeward 800r/min; Entering cloth roll, to turn down pressure be that 2.5t dips cloth cover; Setting temp. control computer 10 casees temperature 170 DEG C; Adjustment overfeeding 28; Enter cloth machine speed 30m/min by sizing, go out cloth and measure cloth fabric width 155CM;
(8) weave: use the non guide hook loom freely circled in the air, the loom speed of a motor vehicle is at 130 ~ 250r/min; Guide coefficient of friction is 0.4-0.5, and warp tension control is at 50-100kg, and weft tension controls at 100CN.
The present invention adopts special manufacturing technique that fiber crops and fiber are carried out blending, fabric is made to have the effect of salient point, change the problem such as pro-skin comfortableness, durability of the salient point of the particle such as rubber matrix, medical stone filling material in the past, and this braided fabric have super softness, moisture absorbing and sweat releasing, frivolous heat-preserving function and the advantage of more easily nursing.
Claims (6)
1. a weaving process for cotton ramie blended spinning fabric product, is characterized in that: the blended yarn that employing linen fibre and cotton fiber are spun into, for form through weft weaving, comprises the steps:
(1) winder: first with bobbin winder, warp and parallel are made twisting bobbin, during winder, groove drum rotating speed is 600 ± 5r/min;
(2) warping: under 400-500m/min speed of beaming, is wound on beam of a loom uniformly by the precursor line cake of warping machines by some;
(3) sizing: the warp in some warp beams and parallel are simultaneously drawn by Sizing machines, immerses slurries, and pressure removes remaining liquid, dries;
(4) knitting;
(5) silicone oil is washed;
(6) dry: the softener of use: softener FRD-5 20 ± 5g/L, softener A QG-01EZ 20 ± 5g/L, and adjust ph is 4.5-7.5, dry tenter temperatures 140 ± 5 DEG C, the speed of a motor vehicle is 50 ± 5m/min;
(7) shape;
(8) weave: use the non guide hook loom freely circled in the air, the loom speed of a motor vehicle is at 130 ~ 250r/min; Guide coefficient of friction is 0.4-0.5, and warp tension control is at 50-100kg, and weft tension controls at 50-200CN.
2. the weaving process of a kind of cotton ramie blended spinning fabric product according to claim 1, is characterized in that: described linen fibre: the weight ratio of cotton fiber is 65:35.
3. the weaving process of a kind of cotton ramie blended spinning fabric product according to claim 1, it is characterized in that: described yarn dyeing process is: adopt import Italy Ba Zuoni environmental protection O type low tension type dyeing machine, dyeing machine enters water and is in charge of at normal temperatures into cloth, add CD-1000N, it is stirred in the secondary cylinder of dyeing machine and opens automatic feeding system, it will be pumped in dyeing machine automatically, and pH value controls between 3 ~ 6; Then following technological parameter is inputted in computer system: tension force 20-50N, rotating speed 150m/min, nozzle exit pressure 0.2-0.5MP/cm
2, main pump rotating speed 1005r/min, bath raio 1:5, pre-treatment temperature 98 DEG C, heat up 2 DEG C/min, temperature retention time 20min; Then be cooled to normal temperature with the speed of 1.5 DEG C/min, wash 2 times, and add CD-1000N; Then post-processing temperature 50 DEG C is warming up to the speed of 2 DEG C/min, temperature retention time 20-30min.
4. the weaving process of a kind of cotton ramie blended spinning fabric product according to claim 1, is characterized in that: described knitting is: by 40S cotton arrangement loom first; 40S linen-cotton ash is arranged in loom second mouthful; 40S linen-cotton ash is arranged in loom the 3rd mouthful, is follow-uply arranged in order; Start to carry out braiding debugging, have yarn tension to debug; Yarn feeding nozzle position is debugged; The concrete debugging of the knitting needle kinking depth; The tension force debugging etc. of batcher; Loom preliminary debugging completes, at second mouthful of feeding 30D spandex; Now debug, determined that product style is correct, carried out weaving production after the debugging of loom each position is accurate; Grey cloth enters normal production, and revolving speed of knitting machine is 15r/min; Then reviewer carries out grey cloth inspection.
5. the weaving process of a kind of cotton ramie blended spinning fabric product according to claim 1, it is characterized in that: add TK-R02 hydrophilic softener in the washed journey of described silicone oil, its consumption is weight ratio 0.5% ~ 1.5%.
6. the weaving process of a kind of cotton ramie blended spinning fabric product according to claim 1, it is characterized in that: described setting process is: adopt import Korea S reason and heat setting machine, technological parameter: frame amplitude 155CM, temperature 160-180 DEG C, machine speed 30r/min, nip pressure 2.5t, overfeeding 28, cabinet air quantity: windward 500r/min, leeward 800r/min; Entering cloth roll, to turn down pressure be that 2.5t dips cloth cover; Setting temp. control computer 10 casees temperature 160-180 DEG C; Adjustment overfeeding 28; Enter cloth machine speed 30m/min by sizing, go out cloth and measure cloth fabric width 155CM.