CN105648787A - High temperature and pressure dyeing process for cotton and linen fabrics - Google Patents
High temperature and pressure dyeing process for cotton and linen fabrics Download PDFInfo
- Publication number
- CN105648787A CN105648787A CN201610177159.XA CN201610177159A CN105648787A CN 105648787 A CN105648787 A CN 105648787A CN 201610177159 A CN201610177159 A CN 201610177159A CN 105648787 A CN105648787 A CN 105648787A
- Authority
- CN
- China
- Prior art keywords
- blue
- linen
- cotton fabric
- cotton
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high temperature and pressure dyeing process for cotton and linen fabrics. The process comprises the following specific steps: weaving, preparing for dyeing, dyeing, fixing, cooling and taking out a material, and discharging. By adopting the specific process, the cotton and linen fabrics have very good fastness to wet treatment and fastness to sunlight, and the problems that the colored light is changed and the fading is easy in the prior art are solved.
Description
Technical field
The present invention relates to garment material field, particularly the high-temperature pressure dyeing technique of a kind of linen-cotton fabric.
Background technology
The plant growing seed fraction having Cotton Gossypii and pyrene fiber crops respectively out that cotton and fiber crops are all temperate zones is adopted, through drying, and machine threshing, decomposite seed and linen-cotton part, through machine pressing, through being woven into line, cloth, eventually passing dye and making, finished product.
Linen-cotton cotton clothes have returned to the sight line of people again, have started a kind of pseudo-classic Never Ending Fashion. Because linen-cotton belongs to coarse cloth, all there are sewn by hand, manufacturing process Green natural environmental-protective, environment protection health, from plantation to hand woven fabric goods, does not use pesticide and chemistry stain, textile, without chemical noxious materials such as methanol, azos, is the optimal textile next to the skin of human body. Soft with quality, cool in summer and warm in winter, permeability is special good again, can sweat on active adsorption human body skin and slight perspiration, make body temperature recover rapidly normal, be really achieved ventilative, the effect of absorbing sweat. Its physical characteristic has antistatic, and anti-demodicid mite is antipruritic, and pH value is in acidity, and skin is non-stimulated, meets environmental protection and health requirements. Not easily rubbing with the hands, not crimping, owing to linen-cotton wiring is thick, its surface can form numerous massage point, human body is had image less than massage effect.
In prior art, printing and dyeing to Cotton and Linen are dyeing and weavings, easily fade, the problems such as dyeing, if by washing after linen-cotton be placed under sunlight shine wash time, easily make linen-cotton fabric fade, when this can find one that linen-cotton fabric is printed and dyed with regard to urgent hope, possess moisture resistant fastness and the method for sun-resistant degree.
Summary of the invention
Goal of the invention: the invention aims to solve the deficiencies in the prior art, it is provided that the high-temperature pressure dyeing technique of a kind of linen-cotton fabric, the linen-cotton fabric after this PROCESS FOR TREATMENT has good moisture resistant fastness and sun-resistant degree.
Technical scheme: in order to realize object above, specifically comprising the following steps that of the high-temperature pressure dyeing technique of a kind of linen-cotton fabric of the present invention
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 10min��20min with the clear water of 50 DEG C��60 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine being warming up to 35 DEG C��45 DEG C, dissolves dyestuff and diffusant, wiring solution-forming injects dye vat, dye 10min��15min, add sodium chloride 7g/L��15g/L, after dye 10min��15min, again add sodium chloride 8g/L��15g/L, continuous dye 30min��45min;
(d) fixation
Dyestuff in dye vat is continued 40min��50min and is slowly warmed up to 80 DEG C��90 DEG C, be slowly added to sodium carbonate liquor 4g/L��6g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 80 DEG C��85 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes is washed, soaped, discharging can be dried after upper softening agent.
As present invention further optimization, the dyestuff in step b takes from any one or multiple mixing in orange X-GN, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, emerald green blue GW-HA.
As present invention further optimization, softening agent in step f is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent, textile is in the course of processing, after repeatedly processing, feel can become coarse, general synthetic fabrics is worse, especially Superfine Fibre Fabric. In order to make fabric have softness, smooth, comfortable feel, it is necessary to it is arranged, widely used is arrange with softening agent.
Beneficial effect: the high-temperature pressure dyeing technique of a kind of linen-cotton fabric provided by the invention, by adopting specific process, makes linen-cotton fabric have good moisture resistant fastness and sun-resistant degree, solves the phenomenon of changes of shade and fugitive color in prior art.
Detailed description of the invention
Below in conjunction with embodiment, it is further elucidated with the present invention.
The present invention provides the high-temperature pressure dyeing technique of a kind of linen-cotton fabric, and specifically comprising the following steps that of this technique weave cotton cloth-standby dye-dyeing-fixation-cooling feeding-discharging.
Embodiment 1
Specifically comprising the following steps that of the high-temperature pressure dyeing technique of a kind of linen-cotton fabric
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 10min with the clear water of 50 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine is warming up to 35 DEG C, dissolve dyestuff and diffusant, wiring solution-forming injects dye vat, dye 10min, add sodium chloride 7g/L, sodium chloride 8g/L is again added after dye 10min, continuous dye 30min, orange X-GN taken from by dyestuff, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA,
(d) fixation
Dyestuff in dye vat is continued 40min and is slowly warmed up to 80 DEG C, be slowly added to sodium carbonate liquor 4g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 80 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes being washed, soaped, can dry discharging after upper softening agent, described softening agent is ester based quaternary ammonium salt softening agent.
Embodiment 2
Specifically comprising the following steps that of the high-temperature pressure dyeing technique of a kind of linen-cotton fabric
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 12min with the clear water of 52 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine is warming up to 38 DEG C, dissolve dyestuff and diffusant, wiring solution-forming injects dye vat, dye 12min, add sodium chloride 8g/L, sodium chloride 10g/L is again added after dye 12min, continuous dye 35min, orange X-GN taken from by dyestuff, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA,
(d) fixation
Dyestuff in dye vat is continued 42min and is slowly warmed up to 85 DEG C, be slowly added to sodium carbonate liquor 5g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 82 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes being washed, soaped, can dry discharging after upper softening agent, described softening agent is fatty acid ester type softening agent.
Embodiment 3
Specifically comprising the following steps that of the high-temperature pressure dyeing technique of a kind of linen-cotton fabric
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 18min with the clear water of 58 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine is warming up to 40 DEG C, dissolve dyestuff and diffusant, wiring solution-forming injects dye vat, dye 13min, add sodium chloride 10g/L, sodium chloride 12g/L is again added after dye 13min, continuous dye 40min, orange X-GN taken from by dyestuff, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA,
(d) fixation
Dyestuff in dye vat is continued 48min and is slowly warmed up to 85 DEG C, be slowly added to sodium carbonate liquor 5g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 83 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes being washed, soaped, can dry discharging after upper softening agent, described softening agent is right wax pattern softening agent.
Embodiment 4
Specifically comprising the following steps that of the high-temperature pressure dyeing technique of a kind of linen-cotton fabric
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 20min with the clear water of 60 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine is warming up to 45 DEG C, dissolve dyestuff and diffusant, wiring solution-forming injects dye vat, dye 15min, add sodium chloride 15g/L, sodium chloride 8g/L��15g/L is again added after dye 15min, continuous dye 45min, orange X-GN taken from by dyestuff, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA,
(d) fixation
Dyestuff in dye vat is continued 50min and is slowly warmed up to 90 DEG C, be slowly added to sodium carbonate liquor 6g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 85 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes being washed, soaped, can dry discharging after upper softening agent, described softening agent is polyethylene softening agent.
Above-mentioned detailed description of the invention only for technology design and the feature of the present invention are described, its objective is to allow and is familiar with these those skilled in the art and will appreciate that present disclosure and implement according to this, can not limit the scope of the invention with this. All equivalents made according to spirit of the invention or modification, all should be encompassed within protection scope of the present invention.
Claims (3)
1. the high-temperature pressure dyeing technique of a linen-cotton fabric, it is characterised in that: specifically comprising the following steps that of this technique
A () is weaved cotton cloth
Linen-cotton fabric is formed by the textile technology braiding of RING SPINNING by tossa, Caulis et Folium Lini fibre, bamboo carbon fiber and cotton fiber;
(b) standby dye
Linen-cotton fabric being loaded high temperature-pressure dyeing machine, processes 10min ~ 20min with the clear water of 50 DEG C ~ 60 DEG C, decontamination of overflowing is assorted;
C () is dyeed
Clear water in high temperature-pressure dyeing machine being warming up to 35 DEG C ~ 45 DEG C, dissolves dyestuff and diffusant, wiring solution-forming injects dye vat, dye 10min ~ 15min, add sodium chloride 7g/L ~ 15g/L, after dye 10min ~ 15min, again add sodium chloride 8g/L ~ 15g/L, continuous dye 30min ~ 45min;
(d) fixation
Dyestuff in dye vat is continued 40min ~ 50min and is slowly warmed up to 80 DEG C ~ 90 DEG C, be slowly added to sodium carbonate liquor 4g/L ~ 6g/L and carry out fixation;
(e) cooling feeding
Close heating, inject cold water and be cooled to 80 DEG C ~ 85 DEG C, open air bleeding valve, emptying steam, residual liquid of draining, take out linen-cotton fabric;
(f) discharging
The complete linen-cotton fabric that dyes is washed, soaped, discharging can be dried after upper softening agent.
2. the high-temperature pressure dyeing technique of a kind of linen-cotton fabric according to claim 1, it is characterized in that: orange X-GN taken from by the described dyestuff in step b, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA.
3. the dyeing of a kind of linen-cotton fabric according to claim 1, it is characterised in that: the softening agent in step f is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent.