CN102418249A - Dyeing and finishing technology for cuprammonium-linen interwoven fabric and cuprammonium-linen interwoven fabric - Google Patents

Dyeing and finishing technology for cuprammonium-linen interwoven fabric and cuprammonium-linen interwoven fabric Download PDF

Info

Publication number
CN102418249A
CN102418249A CN201110277493XA CN201110277493A CN102418249A CN 102418249 A CN102418249 A CN 102418249A CN 201110277493X A CN201110277493X A CN 201110277493XA CN 201110277493 A CN201110277493 A CN 201110277493A CN 102418249 A CN102418249 A CN 102418249A
Authority
CN
China
Prior art keywords
dyeing
cuprammonium
minutes
mixed
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110277493XA
Other languages
Chinese (zh)
Other versions
CN102418249B (en
Inventor
任伟荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEYI FASHION FACE MATERIAL Co Ltd WUJIANG
Original Assignee
DEYI FASHION FACE MATERIAL Co Ltd WUJIANG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEYI FASHION FACE MATERIAL Co Ltd WUJIANG filed Critical DEYI FASHION FACE MATERIAL Co Ltd WUJIANG
Priority to CN201110277493.XA priority Critical patent/CN102418249B/en
Publication of CN102418249A publication Critical patent/CN102418249A/en
Application granted granted Critical
Publication of CN102418249B publication Critical patent/CN102418249B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a dyeing and finishing technology for a cuprammonium-linen interwoven fabric, which uses a gray cuprammonium-linen interwoven fabric as a raw material. The flow of dyeing and finishing technology is shown as the following: preshrinking-> scouring-> water washing-> enzyme water washing-> dyeing-> water washing-> drying through a setting machine-> adding softener-> setting through the setting machine-> sand washing-> steam setting. By interweaving linen fibers and cuprammonium fibers to obtain the cuprammonium-linen interwoven fabric and by dyeing and finishing the interwoven fabric, the cuprammonium-linen interwoven fabric has the advantages of the two kinds of fibers, the defects that a common linen fabric feels coarse, is apt to be wrinkled and the like are overcome and the fabric is highly comfortable. Beside, compared with a cuprammonium fabric, the cost of the cuprammonium-linen interwoven fabric provided by the invention is lower.

Description

A kind of dyeing finishing technique of cuprammonium mixed-woven linen and cuprammonium flax interwoven fabric
Technical field
The invention belongs to the lining field, particularly a kind of dyeing finishing technique of cuprammonium mixed-woven linen and cuprammonium flax interwoven fabric.
Background technology
In the healthy current society of uphold nature, green living, environmental protection consumption have become people's life new concept, and people make great efforts to build the living environment of a health environment-friendly.Aspect garment material, natural string receives consumer's generally favor once again.As the natural environmental-protective lining of generally acknowledging, flax is owing to it has moisture absorption, well-pressed, nice and cool, intensity advantages of higher enjoys favor, yet; The spinnability and the wrinkle resistance of linen fibre are poor; And flax impurity is more, and the fabric background color is very dark behind the mercerising, and; Common flax product feel is coarse, is prone to fold.
In addition; The also known cuprammonium lining of being processed by CUP is the more welcome lining of another kind, and CUP has meeting breathing, salubrious, antistatic, drapability good four big functions, and its purposes is the same substantially with viscose; But the single fiber of CUP is thinner than viscose; The wearability of its product is splendid, and performance is similar to silk, has the sense of dangling.Add that it has anlistatig preferably function; Even still have good sense of touch in the dress of the area of drying; Can avoid producing sultry discomfort, this is the major reason that makes it to become welcome always underwear lining, and still is in irreplaceable status so far.CUP is pushed lining to from lining at present, becomes the best material of senior suit.It is soft as lining; Gloss is soft; Meet environmental protection dress ornament trend, make senior textile, be specially adapted to and wool, synthetic fiber blending or pure spinning so use always; Do high-grade knitted thing, as make knitting and woven underwear, lady's socks and silk weaving satin silk fabric women's dress shirt, wind coat, trousering, overcoat etc.
Summary of the invention
Technical problem to be solved by this invention provides a kind of dyeing finishing technique of cuprammonium mixed-woven linen; Through this technology gained cuprammonium flax interwoven fabric; Combine cuprammonium lining and flax lining advantage separately, overcome cuprammonium lining and flax lining deficiency separately, lining is comfortable; Gracefulness, and cost is lower.
The present invention also will provide a kind of novel cuprammonium flax interwoven fabric simultaneously, and it has had cuprammonium and flax advantage separately concurrently, and comfortable, gracefulness, and cost is lower,
For solving above technical problem, a kind of technical scheme that the present invention takes is:
A kind of dyeing finishing technique of cuprammonium mixed-woven linen; Grey cloth with said cuprammonium mixed-woven linen is a raw material; The flow process of this dyeing finishing technique is: preshrunk → concise → washing → ferment enzyme washing → dyeing → washing → setting machine oven dry → go up softener → setting machine typing → sand washing → decatize typing, wherein:
Said preshrunk is soaked two in open width two and is rolled in the preshrinking machine and carry out, and the temperature of first tank is controlled to be 68 ℃~72 ℃, and the temperature of second tank is controlled to be 88 ℃~92 ℃;
Said refining is carried out in overflow dyeing machine, and the refining bath raio is controlled to be 1: 20~1: 22, the consisting of of refining solution: liquid caustic soda 34~36g/l; Refining agent 0.8~1.2g/l; Precious 1.3~1.7g/l and all the other be water in the bath, control 78 ℃~82 ℃ of refining temperatures, 100~125 minutes time;
Overflow jet dyeing machine is adopted in said dyeing, and bath raio is controlled to be 1: 20~1: 23, the consisting of of dyeing liquor: REACTIVE DYES 0.1~6%, glauber salt 45~80g/l; Liquid caustic soda 0.6~1.0g/l, soda ash 4~8g/l, precious 1.2~1.8g/l and all the other are water in the bath, dyeing course is following: cloth and water are entered in the overflow jet dyeing machine; Precious in the bath of adding formula ratio, keep 28 ℃~32 ℃ of temperature, changeed 4~6 minutes, be warming up to 38 ℃~42 ℃ then; Add the REACTIVE DYES of formula ratio, change after 13~17 minutes, add the glauber salt of formula ratio again, change after 13~17 minutes; Add the soda ash of formula ratio, change after 13~17 minutes, add the liquid caustic soda of formula ratio; Changeed 32~37 minutes, and finished dyeing, discharge dyeing liquor;
Water-washing process after the said dyeing is: add entry in the overflow jet dyeing machine after dyeing is accomplished, be warming up to 60 ℃~70 ℃, changeed 5~15 minutes; Draining adds the liquid of soaping again, is warming up to 80 ℃~90 ℃; Changeed 10~30 minutes, and discharged the liquid of soaping, add entry at last again; Under 60 ℃~70 ℃, clean, go out cloth;
The oven dry of said setting machine is carried out under 115 ℃~125 ℃ of temperature; The setting temperature of said setting machine typing is 125 ℃~135 ℃;
Described sand washing is carried out in air-flow sand washing machine, and temperature is 70 ℃~80 ℃, and the time is 60~90 minutes;
The temperature of said decatize typing is 140 ℃~150 ℃.
Preferably, above-mentioned REACTIVE DYES are the L type REACTIVE DYES of last its chemical inc of Hai'an promise.According to a concrete aspect, the consisting of of described dyeing liquor: REACTIVE DYES are L-HLF blue 0.1%~0.14%; L-3R yellow 0.25%~0.3%; L-4B is red 0.07%~0.085%, glauber salt 45~55g/l; Liquid caustic soda 0.6~1.0g/l; Soda ash 4~6g/l, precious 1.2~1.8g/l and all the other be water in the bath, the color after the cuprammonium mixed-woven linen dyes is cream-coloured, preferably, dyeing liquor consist of L-HLF indigo plant 0.12%; L-3R yellow 0.26%; L-4B is red 0.079%, glauber salt 50g/l; Liquid caustic soda 0.8g/l; Soda ash 5g/l, precious 1.5g/l and all the other are water in the bath.
According to another concrete aspect, the consisting of of described dyeing liquor: L-3G dark blue 1.5%~2.0%; L-3R yellow 2.2%~2.5%; L-4B is red 0.8%~1.0%, glauber salt 60~80g/l; Liquid caustic soda 0.6~1.0g/l; Soda ash 6~8g/l, precious 1.2~1.8g/l and all the other be water in the bath, the color after the cuprammonium mixed-woven linen dyes is coffee color.Preferably, consisting of of dyeing liquor: L-3G dark blue 1.85%; L-3R yellow 2.47%; L-4B is red 0.96%, glauber salt 70g/l; Liquid caustic soda 0.8g/l; Soda ash 7g/l, precious 1.5g/l and all the other are water in the bath.
According to a preferred aspect of the present invention, the water-washing process after the said refining is: after refining finishes, discharge refining solution, add entry; Be heated to 65 ℃~75 ℃, washed 15~25 minutes, draining adds water; Be heated to 50 ℃~60 ℃, washed draining 10~15 minutes.The process of described dyeing ferment enzyme washing before is: in the overflow dyeing machine after washing, add ferment enzyme washing lotion, be heated to 45 ℃~55 ℃ and washed 25~35 minutes down; Draining; Add clear water again, be heated to 50 ℃~60 ℃, wash to draining pH be 7~8.The pH of preferred ferment enzyme washing lotion is 4~5, and by acetic acid 1.8~2.2g/l, ferment enzyme 1.3~1.7g/l and surplus are that water is formed.
The another technical scheme that the present invention takes is: a kind of cuprammonium flax interwoven fabric; It obtains after being handled through above-mentioned dyeing finishing technique by the cuprammonium mixed-woven linen, and described cuprammonium flax grey cloth that interweaves is that CUP and parallel are that linen fibre is interwoven by warp.
Because the enforcement of above technical scheme, the present invention compared with prior art has following advantage:
The present invention interweaves linen fibre and CUP and obtains the cuprammonium mixed-woven linen; And to the arrangement of dyeing of this cloth that interweaves; Gained cuprammonium flax lining is except having two kinds of fibers advantage separately concurrently; It is coarse to be able to overcome common flax lining feel, is prone to deficiencies such as fold, and lining has high-comfort.In addition, compare with the cuprammonium lining, cuprammonium flax interwoven fabric cost of the present invention is lower.Consider each item performance of gained cuprammonium flax interwoven fabric of the present invention, it is specially adapted to make the senior leisure overcoat of men and women scholar, casual pants etc.
The specific embodiment
The embodiment of following mask body does further detailed explanation to the present invention, but the invention is not restricted to following examples.
Embodiment 1
Present embodiment provides a kind of dyeing finishing technique of cuprammonium mixed-woven linen, and it comprises the steps:
(1), preshrunk
Preshrunk is soaked two in open width two and is rolled in the preshrinking machine and carry out, and the temperature of first tank is controlled to be 70 ℃, and the temperature of second tank is controlled to be 90 ℃, and purpose is to let grey cloth not have under the tension force in broadwise evenly shrink, in order to avoid form vertical bar crape seal in the overflow dyeing machine the inside.
(2), refining
Refining is carried out in overflow dyeing machine, and the refining bath raio is controlled to be 1: 21, the consisting of of refining solution: liquid caustic soda 35g/l, and refining agent 1g/l, precious 1.5g/l and all the other are water in the bath, 80 ℃ of control refining temperatures are incubated 120 minutes.
(3), washing
After refining finishes, discharge refining solution, add entry, be heated to 70 ℃, washed 20 minutes, draining adds water, is heated to 60 ℃, washes draining 15 minutes.
(4), ferment enzyme washing
In the overflow dyeing machine after washing, add ferment enzyme washing lotion, be heated to 50 ℃, washed 30 minutes; Draining adds clear water again, washes 15 minutes 50 degree washings 10 minutes for 0 ℃; Keep pH value about 7, can dye, wherein; The pH of ferment enzyme washing lotion is 4.5, and by acetic acid 2g/l, ferment enzyme 1.5g/l and surplus are that water is formed.
(5) dyeing
Overflow jet dyeing machine is adopted in dyeing; bath raio is controlled to be 1: 22, the consisting of of dyeing liquor: L-HLF is blue 0.12%, L-3R is yellow 0.26%, L-4B is red 0.079%, glauber salt 50g/l, liquid caustic soda 0.8g/l; soda ash 5g/l; precious 1.5g/l and all the other be water in the bath, the L type REACTIVE DYES that wherein, L-HLF is blue, L-3R is yellow, the red three kinds of dyestuffs of L-4B are its chemical inc production of Hai'an promise.This group dyestuff good level-dyeing property, cuprammonium and flax are painted to such an extent that plucked instrument evenly is difficult for the look flower with bathing, and dye-uptake is higher by 15%~20% than common REACTIVE DYES, is prone to clean, and can reduce 5~6 tons of every cylinders of dyeing waste-water, is beneficial to energy-saving and emission-reduction.
Dyeing course is following: cloth and water entered in the overflow jet dyeing machine, and precious in the bath of adding formula ratio, keep 30 ℃ of temperature, changeed 5 minutes; Be warming up to 40 ℃ then, add the REACTIVE DYES of formula ratio, change after 15 minutes, add the glauber salt of formula ratio again; Change after 15 minutes, add the soda ash of formula ratio, change after 15 minutes, add the liquid caustic soda of formula ratio; Changeed 35 minutes, and finished dyeing, discharge dyeing liquor.Cloth after the dyeing is cream-coloured.
(6) washing
Add entry in the overflow jet dyeing machine after dyeing is accomplished, be warming up to 60 ℃, changeed 10 minutes, draining adds the liquid of soaping again, is warming up to 85 ℃, changes 15 minutes, discharges the liquid of soaping, and adds entry at last again, under 70 ℃, cleans, and goes out cloth.
(7) back arrangement
Through the cloth of washing, after the centrifugal dehydrator dehydration, manual open-width (not using the scutcher open-width) to prevent the cloth cover rub.Through the setting machine oven dry, 120 ℃ of temperature, 40 meters/minute of the speed of a motor vehicle, softness processing is carried out at flat cylinder in the oven dry back, softener 10g/l, 40 ℃ of * 5 roads, purpose is that the pliability of cloth cover is consistent, again through setting machine typing, 130 ℃ of temperature, 35 meters/minute of the speed of a motor vehicle.Afterwards, cloth is sent into air-flow sand washing machine, under the transmission guide wheel drove, cloth circulated in machine, and is patted by jet-stream wind.Whole process is controlled by computer, 60~90 minutes time, 70 ℃~80 ℃ of temperature, 400~600 meters/minute of circulation cloth speed.The air-flow sand washing is to implement to reach one of important procedure of fabric style characteristic in disclosed this method.Use device name: air-flow sand washing softening finishing machine or feel improvement machine.With the equipment best results that Italy produces, the sand washing temperature should not be too high, prevents the fabric flavescence.The final step arranging process is the decatize typing, and open-width is manual, prevents to damage body, 50 meters/minute of typing cloth speed, temperature 145, overfeeding 8~12%.Make soft, the unique style of cloth cover.
Embodiment 2
According to the dyeing finishing technique of the cuprammonium mixed-woven linen of present embodiment, basically with embodiment 1.No is, the consisting of of the dyeing liquor that adopts in the present embodiment: L-3G dark blue 1.85%; L-3R yellow 2.47%; L-4B is red 0.96%, glauber salt 70g/l; Liquid caustic soda 0.8g/l; Soda ash 7g/l, precious 1.5g/l and all the other are water in the bath.The color of last gained interwoven fabric is coffee-like.
Cuprammonium mixed-woven linen to embodiment 1 and embodiment 2 is checked, and test basis is GB/T16605-2008 " regenerated rayon filament fabric " and GB18401-2003 " national textile product basic security technical specification " category-B, and the result is referring to table 1.The result shows that all items all meets the high-class product requirement of GB/T16605-2008 standard code, meets the category-B requirement of GB18401-2003 standard code.
The performance indications of table 1 cuprammonium mixed-woven linen
Figure BDA0000092318560000051
Figure BDA0000092318560000061
More than the present invention has been done detailed description; Its purpose is to let the personage that is familiar with this art can understand content of the present invention and implements; Can not limit protection scope of the present invention with this; All equivalences of doing according to spirit of the present invention change or modify, and all should be encompassed in protection scope of the present invention.

Claims (10)

1. the dyeing finishing technique of a cuprammonium mixed-woven linen; It is characterized in that: the grey cloth with said cuprammonium mixed-woven linen is a raw material; The flow process of said dyeing finishing technique is: preshrunk → concise → washing → ferment enzyme washing → dyeing → washing → setting machine oven dry → go up softener → setting machine typing → sand washing → decatize typing, wherein:
Said preshrunk is soaked two in open width two and is rolled in the preshrinking machine and carry out, and the temperature of first tank is controlled to be 68 ℃~72 ℃, and the temperature of second tank is controlled to be 88 ℃~92 ℃;
Said refining is carried out in overflow dyeing machine, and the refining bath raio is controlled to be 1:20~1:22, the consisting of of refining solution: liquid caustic soda 34~36g/l; Refining agent 0.8~1.2g/l; Precious 1.3~1.7g/l and all the other be water in the bath, control 78 ℃~82 ℃ of refining temperatures, 100~125 minutes time;
Overflow jet dyeing machine is adopted in said dyeing, and bath raio is controlled to be 1:20~1:23, the consisting of of dyeing liquor: REACTIVE DYES 0.1~6%, glauber salt 45~80g/l; Liquid caustic soda 0.6~1.0 g/l, soda ash 4~8g/l, precious 1.2~1.8 g/l and all the other are water in the bath, dyeing course is following: cloth and water are entered in the overflow jet dyeing machine; Precious in the bath of adding formula ratio, keep 28 ℃~32 ℃ of temperature, changeed 4~6 minutes, be warming up to 38 ℃~42 ℃ then; Add the REACTIVE DYES of formula ratio, change after 13~17 minutes, add the glauber salt of formula ratio again, change after 13~17 minutes; Add the soda ash of formula ratio, change after 13~17 minutes, add the liquid caustic soda of formula ratio; Changeed 32~37 minutes, and finished dyeing, discharge dyeing liquor;
Water-washing process after the said dyeing is: add entry in the overflow jet dyeing machine after dyeing is accomplished, be warming up to 60 ℃~70 ℃, changeed 5~15 minutes; Draining adds the liquid of soaping again, is warming up to 80 ℃~90 ℃; Changeed 10~30 minutes, and discharged the liquid of soaping, add entry at last again; Under 60 ℃~70 ℃, clean, go out cloth;
The oven dry of said setting machine is carried out under 115 ℃~125 ℃ of temperature; The setting temperature of said setting machine typing is 125 ℃~135 ℃;
Described sand washing is carried out in air-flow sand washing machine, and temperature is 70 ℃~80 ℃, and the time is 60~90 minutes;
The temperature of said decatize typing is 140 ℃~150 ℃.
2. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 1 is characterized in that: described REACTIVE DYES are the L type REACTIVE DYES that promise its chemical inc in last Hai'an is produced.
3. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 2 is characterized in that: the consisting of of described dyeing liquor: L-HLF blue 0.1%~0.14%; L-3R yellow 0.25%~0.3%; L-4B is red 0.07%~0.085%, glauber salt 45~55g/l; Liquid caustic soda 0.6~1.0 g/l; Soda ash 4~6g/l, precious 1.2~1.8 g/l and all the other are water in the bath, the color after the cuprammonium mixed-woven linen dyes is cream-coloured.
4. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 3 is characterized in that: the consisting of of described dyeing liquor: L-HLF blue 0.12%; L-3R yellow 0.26%; L-4B is red 0.079%, glauber salt 50g/l; Liquid caustic soda 0.8 g/l; Soda ash 5g/l, precious 1.5g/l and all the other are water in the bath.
5. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 2 is characterized in that: the consisting of of described dyeing liquor: L-3G dark blue 1.5%~2.0%; L-3R yellow 2.2%~2.5%; L-4B is red 0.8%~1.0%, glauber salt 60~80g/l; Liquid caustic soda 0.6~1.0 g/l; Soda ash 6~8g/l, precious 1.2~1.8 g/l and all the other be water in the bath, the color after the cuprammonium mixed-woven linen dyes is coffee color.
6. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 5 is characterized in that: the consisting of of described dyeing liquor: L-3G dark blue 1.85%; L-3R yellow 2.47%; L-4B is red 0.96%, glauber salt 70g/l; Liquid caustic soda 0.8 g/l; Soda ash 7g/l, precious 1.5 g/l and all the other are water in the bath.
7. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 1 is characterized in that: the water-washing process after the said refining is: after refining finishes, discharge refining solution; Add entry, be heated to 65 ℃~75 ℃, washed 15~25 minutes; Draining adds water, is heated to 50 ℃~60 ℃; Washed draining 10~15 minutes.
8. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 7; It is characterized in that: the process of described dyeing ferment enzyme washing before is: in the overflow dyeing machine after washing, add ferment enzyme washing lotion, be heated to 45 ℃~55 ℃ and washed 25~35 minutes down; Draining; Add clear water again, be heated to 50 ℃~60 ℃, wash to draining pH be 7~8.
9. the dyeing finishing technique of cuprammonium mixed-woven linen according to claim 8 is characterized in that: the pH of described ferment enzyme washing lotion is 4~5, and it is by acetic acid 1.8~2.2g/l, and ferment enzyme 1.3~1.7g/l and surplus are that water is formed.
10. cuprammonium flax interwoven fabric; It is characterized in that: said interwoven fabric obtains after being handled through the described dyeing finishing technique of each claim in the claim 1 to 9 by the cuprammonium mixed-woven linen, and described cuprammonium flax grey cloth that interweaves is that CUP and parallel are that linen fibre is interwoven by warp.
CN201110277493.XA 2011-09-19 2011-09-19 Dyeing and finishing technology for cuprammonium-linen interwoven fabric and cuprammonium-linen interwoven fabric Active CN102418249B (en)