CN104723783A - Ceramic twisted-plate process - Google Patents
Ceramic twisted-plate process Download PDFInfo
- Publication number
- CN104723783A CN104723783A CN201510124692.5A CN201510124692A CN104723783A CN 104723783 A CN104723783 A CN 104723783A CN 201510124692 A CN201510124692 A CN 201510124692A CN 104723783 A CN104723783 A CN 104723783A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- plate
- mud
- technique
- paste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramic twisted-plate process. The ceramic twisted-plate process comprises the following steps: I. preparing various wet ceramic pastes with the needed colours; II. arranging the wet ceramic pastes with different colours and shapes on a bottom plate according to a design picture composition; III. rolling the bottom plate prepared in the step II, and extending and partially mixing the wet pastes with the different colours and shapes on the bottom plate during the rolling process to form a paste plate with an abundant-level picture; IV. shaping or modelling the paste plate to form a paste blank with a flat shape or a three-dimensional shape; and V. drying the paste blank and then firing to obtain ceramic twisted-plate artware. The process is an initiate ceramic process technique, and through the layer-by-layer arrangement and rolling for the ceramic paste, paste colour lumps are incompletely mixed, colours are irregularly moistened and dyed, and the pictures are abundant in colours and distinct in layers, thus expanding the representation forms of the ceramic artware.
Description
Technical field
The present invention relates to a kind of Novel ceramic artwork manufacture craft.
Background technology
Strand mud (also claiming strand tire) moulding process is had in traditional ceramic process, be that the general ceramic mud of two or more different colours is not exclusively mixed, then make the pottery with decorative effect by throwing or formed in mould method.This pottery strand mud moulding process is not suitable for making the picture enriching level, is also only limitted to the vessel being made with decorative effect by throwing or formed in mould process.
Summary of the invention
The invention provides a kind of new ceramics manufacture craft, base plate adds the general ceramic mud of different colours, shape and size in batches, and carries out the operation of one or many roll-forming, pug color lump is not exclusively mixed, the irregular profit dye of color, mud plate presents the picture having and enrich level.
For achieving the above object, the present invention includes following technical scheme:
A kind of ceramic lag technique, this technique comprises the steps:
I. the ceramic wet mud of various required color is prepared;
II. according to designing picture composition, the ceramic wet mud of different colours, shape is arranged on base plate;
III. carry out roll-in to base plate prepared by Step II, on base plate, the wet mud of different colours, shape extends and part mixing in nipping process, is formed and has the mud plate enriching level picture;
IV. integer or plastotype are carried out to mud plate, form moulded pottery not yet put in a kiln to bake that is dull and stereotyped or three-dimensional shape;
V. fire after moulded pottery not yet put in a kiln to bake drying, obtain ceramic lag handicraft.
Technique as above, preferably, the pug preparing ceramic wet mud in described step I is the conventional pug manufacturing ceramic product.
Technique as above, preferably, the base plate in described Step II is the flat board that ceramic wet mud is made.
Technique as above, preferably, needing according to composition can the operation of repeating said steps II and Step II I, to form the stacking composition of level.
Technique as above, preferably, also comprises surface polishing steps after described Step II I, removes surperficial mud layer, makes mud plate picture clear smooth.
Technique as above, preferably, the formations of described step IV comprises mould molding and pottery and to splice technique.
Technique as above, preferably, the firing temperature of described step V is 300 ~ 1300 DEG C.
On the other hand, the invention provides a kind of ceramic lag handicraft, it adopts technique as above to prepare.
Beneficial effect of the present invention is: this technique is pioneering ceramic process skill and technique, lay roll-in layer by layer by pottery mud, the unique artistic effect of formation nature profit dye, picture color is abundant, level is distinct, expand the form of expression of ceramics, and the originality of each product can have been kept.Meanwhile, this technological operation is simple, without the need to equipment and the instrument of complexity, is convenient to grasp, be easy to promote, has high practicality and commercial value.
Accompanying drawing explanation
Fig. 1 is the pug photo of embodiment 1 step 1.
Fig. 2 is the patterning operation photo of embodiment 1 step 2.
Fig. 3 is the roll operation photo of embodiment 1 step 3.
Fig. 4 is the roll operation photo of embodiment 1 step 3.
Fig. 5 is the polishing operation photo of embodiment 1 step 4.
Fig. 6 is the Porcelain Art painting photo of " spring " by name that application present invention process makes.
Fig. 7 is the porcelain skill vessel photo that application present invention process makes.
Detailed description of the invention
Below in conjunction with drawings and Examples, the invention will be further described.
Embodiment 1
Adopt ceramic lag technique of the present invention to make ceramics, comprise the steps:
1. get the raw materials ready
The present invention can use the conventional pug manufacturing ceramic product, according to the composition of firing condition adjustment pug.Need according to composition wet mud pug being made various required color, its humid control is ensureing to have ductility and plasticity, see Fig. 1 in step subsequently.
2. composition
The wet mud of selected color is made base plate, according to designing picture composition, the ceramic wet mud of different colours, shape is arranged on base plate, see Fig. 2.
3. roll-in
Carry out roll-in to base plate prepared by step 2, on base plate, the wet mud of different colours, shape extends and part mixing in nipping process, is formed and has the mud plate enriching level picture, see Fig. 3 and Fig. 4.
The operation that can repeat step 2 and step 3 is needed, to form the stacking composition of level according to composition.
4. polishing
Polishing is carried out to the mud plate of roll-forming, removes surperficial mud layer, make mud plate picture clear smooth, see Fig. 5.
5. plastotype
Integer or plastotype are carried out to mud plate, forms moulded pottery not yet put in a kiln to bake that is dull and stereotyped or three-dimensional shape.
6. fire
After the abundant drying of moulded pottery not yet put in a kiln to bake, conventional ceramic burning equipment and technique is adopted to fire finished product.
7. product
Fig. 6 and Fig. 7 is the works that author of the present invention uses above-mentioned technique and creates, and Fig. 6 is dull and stereotyped works, and Fig. 7 is the pottery adopting mould-forming process to make.Firing temperature is respectively 1280 DEG C and 460 DEG C.
Be more than the description of this invention, under not departing from the present invention and designing the prerequisite of spirit, the various distortion that the common engineers and technicians in this area make technical scheme of the present invention and replacement, all should fall in protection domain that claim of the present invention determines.
Claims (8)
1. a ceramic lag technique, is characterized in that, this technique comprises the steps:
I. the ceramic wet mud of various required color is prepared;
II. according to designing picture composition, the ceramic wet mud of different colours, shape is arranged on base plate;
III. carry out roll-in to base plate prepared by Step II, on base plate, the wet mud of different colours, shape extends and part mixing in nipping process, is formed and has the mud plate enriching level picture;
IV. integer or plastotype are carried out to mud plate, form moulded pottery not yet put in a kiln to bake that is dull and stereotyped or three-dimensional shape;
V. fire after moulded pottery not yet put in a kiln to bake drying, obtain ceramic lag handicraft.
2. technique according to claim 1, is characterized in that, the pug preparing ceramic wet mud in described step I is the conventional pug manufacturing ceramic product.
3. technique according to claim 1, is characterized in that, the base plate in described Step II is the flat board that ceramic wet mud is made.
4. technique according to claim 1, is characterized in that, needing according to composition can the operation of repeating said steps II and Step II I, to form the stacking composition of level.
5. technique according to claim 1, is characterized in that, also comprises surface polishing steps after described Step II I, removes surperficial mud layer, makes mud plate picture clear smooth.
6. technique according to claim 1, is characterized in that, the formations of described step IV comprises mould molding and pottery and to splice technique.
7. the technique according to any one of claim 1-6, is characterized in that, the firing temperature of described step V is 300 ~ 1300 DEG C.
8. a ceramic lag handicraft, is characterized in that, it adopts the technique according to any one of claim 1-7 to prepare.