CN104624992A - 青铜线材生产工艺 - Google Patents
青铜线材生产工艺 Download PDFInfo
- Publication number
- CN104624992A CN104624992A CN201310551842.1A CN201310551842A CN104624992A CN 104624992 A CN104624992 A CN 104624992A CN 201310551842 A CN201310551842 A CN 201310551842A CN 104624992 A CN104624992 A CN 104624992A
- Authority
- CN
- China
- Prior art keywords
- annealing
- technique
- low
- wire rod
- casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种青铜线材生产工艺，工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→低氧退火→检验包装。其中，连铸温度l160℃～1250℃，连铸速度0.8～1.6米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度40～85℃，退火加入氮气作保护气，退火温度390～410℃，保温时间90～120分钟。产品弹性高，耐腐蚀、耐摩擦性好，其切削，焊接性能、铸造性能优良，机械性能好，工艺相对简单，流程易于控制，生产成本低，生产效率高。
Description
技术领域
本发明属于铜合金线材生产工艺，具体涉及一种青铜线材生产工艺。
背景技术
铜合金线材的主要应用领域为拉链制造业、气门芯、条帽线制造业、焊料制造业、眼镜框制造业、接插件制造业、饰件、按纽、钟表制造业及汽车制造业等。青铜线材主要应用于制造弹性元件、高耐磨的接插件和端子、仪表游丝、张丝、养护焊接耐磨和耐蚀件、金属制网等领域。近年来，由于信息产业的迅猛发展，锡青铜线的需求量迅速增加，其发展方向是提高线材强度，如将锡的含量提高到9％，即可代替铍青铜、白青铜。
发明内容
本发明的目的在于，提供一种青铜线材生产工艺，操作方便。
本发明提供的青铜线材生产工艺，工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→低氧退火→检验包装。其中，连铸温度l160℃～1250℃，连铸速度0.8～1.6米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度40～85℃，退火加入氮气作保护气，退火温度390～410℃，保温时间90～120分钟。
本发明提供的青铜线材生产工艺，其有益效果在于，产品弹性高，耐腐蚀、耐摩擦性好，其切削，焊接性能、铸造性能优良，机械性能好，工艺相对简单，流程易于控制，生产成本低，生产效率高。
具体实施方式
下面结合一个实施例，对本发明提供的青铜线材生产工艺进行详细的说明。
实施例
工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→低氧退火→检验包装。其中，连铸温度l160℃～1250℃，连铸速度0.8～1.6米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度40～85℃，退火加入氮气作保护气，退火温度390～410℃，保温时间90～120分钟。
Claims (1)
1.一种青铜线材生产工艺，其特征在于，工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→低氧退火→检验包装；其中，连铸温度l160℃～1250℃，连铸速度0.8～1.6米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度40～85℃，退火加入氮气作保护气，退火温度390～410℃，保温时间90～120分钟。