CN104559045B - 一种干式变压器用预浸复合材料的制备方法 - Google Patents
一种干式变压器用预浸复合材料的制备方法 Download PDFInfo
- Publication number
- CN104559045B CN104559045B CN201410830892.8A CN201410830892A CN104559045B CN 104559045 B CN104559045 B CN 104559045B CN 201410830892 A CN201410830892 A CN 201410830892A CN 104559045 B CN104559045 B CN 104559045B
- Authority
- CN
- China
- Prior art keywords
- preparation
- heat stable
- polyester
- stable resin
- nonwoven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开的一种预浸渍复合材料的制备方法，由聚酯薄膜聚酯纤维非织布柔软复合材料浸渍耐热树脂预浸液后经烘干制成；所述耐热树脂预浸液由环氧线性酚醛树脂、磷化环氧树脂、多官能基芳香族聚酯、共聚物、催化剂和溶剂制备而成。制备方法是：将聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。本发明与传统的预浸渍复合材料相比，固化温度低，固化时间短，且固化物具有优异电气性能、粘结性能、耐热性能及阻燃性，能够满足F级绝缘的要求。
Description
技术领域
本发明涉及干式变压器线圈包扎及匝间绝缘用的一种新型预浸复合材料的制备方法。
背景技术
现有的干式变压器线圈及匝间绝缘所使用绝缘材料成型后，在电性能、粘结性能、耐热性等方面存在一定缺陷，其固化温度较高、固化时间较长。
发明内容
本发明的目的在于针对现有干式变压器线圈及匝间绝缘材料所存在的上述问题，专门研发和提供一种新型干式变压器线圈及匝间绝缘用预浸复合材料的制备方法，采用这一方法制备的绝缘预浸复合材料，具有优良的电性能、粘结性能、耐热性能及阻燃性。
本发明所要解决的技术问题可以通过以下技术方案来实现：
一种预浸渍复合材料的制备方法，由聚酯薄膜聚酯纤维非织布柔软复合材料浸渍耐热树脂预浸液后经烘干制成；
所述耐热树脂预浸液由以下重量百分比的原料制备而成：
制备方法是：将聚酯薄膜聚酯纤维非织布柔软复合材料，放入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。
在本发明的一个优选实施例中，所述溶剂选自甲基乙烯酮、环己酮、丙二醇甲醚醋酸酯中的一种或两种以上的混合。
在本发明的一个优选实施例中，所述催化剂选自咪唑化合物、有机磷化合物、有机磷酸酯化合物、磷酸盐、三烷基胺、4-(二甲基胺基)吡啶、四级铵盐、脲化合物等其中一种。
本发明与传统的预浸渍复合材料相比，固化温度低，固化时间短，且固化物具有优异电气性能、粘结性能、耐热性能及阻燃性，能够满足F级绝缘的要求。
具体实施方式
实施例1
一种预浸渍复合材料的制备方法，取市售聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。所述耐热树脂预浸液由以下质量百分比的原料制备而成：
制备方法是：取市售聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。
实施例2
一种预浸渍复合材料的制备方法，将聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。所述耐热树脂由以下质量百分比的原料制备而成：
制备方法是：将聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。
Claims (3)
1.一种预浸渍复合材料的制备方法，由聚酯薄膜聚酯纤维非织布柔软复合材料浸渍耐热树脂经烘焙制成；
所述耐热树脂预浸液由以下重量百分比的原料制备而成：
制备方法是：将聚酯薄膜聚酯纤维非织布柔软复合材料，浸入上述耐热树脂，经130～150℃条件下烘焙，后收卷即可。
2.如权利要求1所述的预浸渍复合材料的制备方法，其特征在于，所述溶剂选自甲基乙烯酮、环己酮、丙二醇甲醚醋酸酯中的一种或两种以上的混合。
3.如权利要求1所述的预浸渍复合材料的制备方法，其特征在于，所述催化剂选自咪唑化合物、有机磷化合物、磷酸盐、三烷基胺、4-(二甲基胺基)吡啶、四级铵盐、脲化合物其中一种。