CN106118524A - 一种防水防霉增强的微孔散热绝缘包扎带 - Google Patents

一种防水防霉增强的微孔散热绝缘包扎带 Download PDF

Info

Publication number
CN106118524A
CN106118524A CN201610473205.0A CN201610473205A CN106118524A CN 106118524 A CN106118524 A CN 106118524A CN 201610473205 A CN201610473205 A CN 201610473205A CN 106118524 A CN106118524 A CN 106118524A
Authority
CN
China
Prior art keywords
minute
waterproof
appropriate
polrvinyl chloride
micropore
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610473205.0A
Other languages
English (en)
Inventor
王喜东
琚雄
琚一雄
周建军
郜海文
张君君
陈玲
张爱华
宋志威
琚辉
琚一辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Deren Electronic Devices Co Ltd
Original Assignee
Hefei Deren Electronic Devices Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Deren Electronic Devices Co Ltd filed Critical Hefei Deren Electronic Devices Co Ltd
Priority to CN201610473205.0A priority Critical patent/CN106118524A/zh
Publication of CN106118524A publication Critical patent/CN106118524A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防水防霉增强的微孔散热绝缘包扎带，由下列重量份的原料制备制成：埃洛石纳米管1.5‑1.6、硅烷偶联剂kh5700.75‑0.77、去离子水适量、无水乙醇适量、十二烷基硫酸钠1.2‑1.4、烷基酚聚氧乙烯醚1.4‑1.5、丙烯酸丁酯55‑60、丙烯酸异辛酯40‑43、等规聚丙烯40‑44、聚氯乙烯53‑55、二亚苄基山梨糖醇3‑4、邻苯二甲酸二辛酯适量、纳米二氧化硅5‑6、单硬脂酸甘油酯3‑4、聚二甲基硅氧烷2‑3、2‑(4－噻唑基)苯并咪唑0.9‑1.1、钙锌稳定剂2‑2.4、硬脂酸3‑4。本发明产品粘接力强，具有优良的物理、机械、防水、防霉等性能，适用于包绕导线和固定线圈。

Description

一种防水防霉增强的微孔散热绝缘包扎带
技术领域
本发明涉及电气技术领域，尤其涉及一种防水防霉增强的微孔散热绝缘包扎带。
背景技术
绝缘包扎带主要用作包缠电线、电缆的接头、接口，除用于普通电气的绝缘外，还广泛应用于工程管道保护、内窥线路保护和汽车线束捆扎保护等领域。现有技术的布基绝缘胶带是由布基和橡胶、松香、填料涂层胶组成，具有较好的机械强度和绝缘效果，但是布基胶带容易老化，防水性、密封性能差，在高温高压下，胶带的屏蔽性能大大下降，导致无法用于更多的领域。现有的聚氮乙烯压敏胶黏带是一种通用型电气胶黏带，其价格低廉，具有优良的电气性能及物理力学性能，电气强度高达60kV/mm，体积电阻率高，具有柔软且易拉伸等特点，还具有优良的耐酸碱、耐老化、耐寒及耐湿等特点，广泛应用于交直流电线的连接缠绕及绝缘保护、 电气设备的制造、 各种线束及电缆的缠包等，其缺点是耐温级别不高，散热性能差。
在《适用于软聚氯乙烯电气胶粘带的乳液压敏胶粘剂及其制造方法》文章中，虽然制成的胶带软化点低、粘结力强、固化快等优点，但是由于聚丙烯酸酯的直链分子结构决定了其耐热性和机械强度等性能不足，此外乳液型丙烯酸酯压敏胶涂布和干燥速度慢、干燥能耗高和表面张力较高等缺点使其应用受到了限制，为拓宽其使用范围，提高其综合性能，有需要对聚氯乙烯基材以及丙烯酸酯压敏胶进行改性。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种防水防霉增强的微孔散热绝缘包扎带。
本发明是通过以下技术方案实现的：
一种防水防霉增强的微孔散热绝缘包扎带，由下列重量份的原料制备制成：埃洛石纳米管1.5-1.6、硅烷偶联剂kh5700.75-0.77、去离子水适量、无水乙醇适量、十二烷基硫酸钠1.2-1.4、烷基酚聚氧乙烯醚1.4-1.5、丙烯酸丁酯55-60、丙烯酸异辛酯40-43、等规聚丙烯40-44、聚氯乙烯53-55、二亚苄基山梨糖醇3-4、邻苯二甲酸二辛酯适量、纳米二氧化硅5-6、单硬脂酸甘油酯3-4、聚二甲基硅氧烷2-3、2-(4－噻唑基)苯并咪唑0.9-1.1、钙锌稳定剂2-2.4、硬脂酸3-4。
所述一种防水防霉增强的微孔散热绝缘包扎带，由以下具体步骤制成：
（1）将埃洛石中加入30-35倍量的无水乙醇中超声分散40-50分钟得到混悬液，然后加入与无水乙醇等量的去离子水以及硅烷偶联剂kh570，加热至70-75℃，搅拌反应24小时后将混合物以4000转/分的速度进行离心，并洗涤至中性，得到的产品在真空干燥箱中以90-100℃烘干，得到改性埃洛石纳米管；
（2）将改性埃洛石纳米管超声分散于80-85倍量的去离子水中，然后加入丙烯酸丁酯、丙烯酸异辛酯、十二烷基硫酸钠，在磁力搅拌机上搅拌均匀，然后升温至80-85℃，加入一半量的烷基酚聚氧乙烯醚，保温30-60分钟后继续加入剩余的烷基酚聚氧乙烯醚，升温至90-95℃，保温60-90分钟后冷却至室温，得到改性丙烯酸乳液；
（3）将纳米二氧化硅与单硬脂酸甘油酯、聚二甲基硅氧烷混合，放入球磨机中，加热至50-60℃球磨60-90分钟后出料送入双螺杆挤出机中，加入聚氯乙烯，控制挤出温度130-140℃，挤出造粒，得到防水增强聚氯乙烯母料；
（4）将聚氯乙烯、步骤（3）得到的防水增强聚氯乙烯母料混合后放入反应釜中，然后加入总量3.5-4倍量的邻苯二甲酸二辛酯以及其余剩余成分，在氮气保护条件下在180℃搅拌60-90分钟后继续保温2-3小时形成铸膜液，将铸膜液通过刮膜机制成平板膜，控制刮膜温度为180℃，最后通过热致相分离技术，经平板膜浸入25℃凝固水浴进行相分离，再经无水乙醇萃取，烘干后得到聚丙烯聚氯乙烯复合微孔膜；
（5）将改性丙烯酸乳液用涂膜器均匀涂布在聚丙烯聚氯乙烯复合微孔膜表面，将其放在75-80℃烘箱烘烤3-4分钟，然后置于40℃恒温老化箱中老化24小时，最后切割成带状，即得。
本发明的优点是：本发明将热致相分离方法应用到压敏型绝缘包扎带基材薄膜的制备中，制成的聚丙烯聚氯乙烯复合微孔薄膜，兼具聚丙烯与聚氯乙烯的优点，防水、耐热性佳，耐化学腐蚀，同时孔隙率适中，分布均匀，微孔与空气相通，可以形成空气绝缘结构，同时散热性能优异；本发明还通过添加改性埃洛石纳米管的方式对聚丙烯酸酯乳液进行改性，改性埃洛石纳米管的增强增韧及其与聚合物基材的强烈相互作用，从而使聚合物分子链移动性变差，使得制成的压敏胶内聚强度和抗蠕变性能明显增强，提高了压敏胶的热稳定性和耐高温性，同时具有良好的剥离强度与初粘力。
本发明在聚合物微孔薄膜的制备中添加纳米二氧化硅、单硬脂酸甘油酯等成分，增强了聚合物的疏水性能；添加2-(4－噻唑基)苯并咪唑，可以防止霉菌的滋生，防止薄膜腐败；本发明产品粘接力强，具有优良的物理、机械、介电性能和防水、防霉等特点，适用于包绕导线和固定线圈。
具体实施方式
一种防水防霉增强的微孔散热绝缘包扎带，由下列重量份（公斤）的原料制备制成：埃洛石纳米管1.5、硅烷偶联剂kh5700.75、去离子水适量、无水乙醇适量、十二烷基硫酸钠1.2、烷基酚聚氧乙烯醚1.4、丙烯酸丁酯55、丙烯酸异辛酯40、等规聚丙烯40、聚氯乙烯53、二亚苄基山梨糖醇3、邻苯二甲酸二辛酯适量、纳米二氧化硅5、单硬脂酸甘油酯3、聚二甲基硅氧烷2、2-(4－噻唑基)苯并咪唑0.9、钙锌稳定剂2、硬脂酸3。
所述一种防水防霉增强的微孔散热绝缘包扎带，由以下具体步骤制成：
（1）将埃洛石中加入30倍量的无水乙醇中超声分散40分钟得到混悬液，然后加入与无水乙醇等量的去离子水以及硅烷偶联剂kh570，加热至70℃，搅拌反应24小时后将混合物以4000转/分的速度进行离心，并洗涤至中性，得到的产品在真空干燥箱中以90℃烘干，得到改性埃洛石纳米管；
（2）将改性埃洛石纳米管超声分散于80倍量的去离子水中，然后加入丙烯酸丁酯、丙烯酸异辛酯、十二烷基硫酸钠，在磁力搅拌机上搅拌均匀，然后升温至80℃，加入一半量的烷基酚聚氧乙烯醚，保温30分钟后继续加入剩余的烷基酚聚氧乙烯醚，升温至90℃，保温60分钟后冷却至室温，得到改性丙烯酸乳液；
（3）将纳米二氧化硅与单硬脂酸甘油酯、聚二甲基硅氧烷混合，放入球磨机中，加热至50℃球磨60分钟后出料送入双螺杆挤出机中，加入聚氯乙烯，控制挤出温度130℃，挤出造粒，得到防水增强聚氯乙烯母料；
（4）将聚氯乙烯、步骤（3）得到的防水增强聚氯乙烯母料混合后放入反应釜中，然后加入总量3.5倍量的邻苯二甲酸二辛酯以及其余剩余成分，在氮气保护条件下在180℃搅拌60分钟后继续保温2小时形成铸膜液，将铸膜液通过刮膜机制成平板膜，控制刮膜温度为180℃，最后通过热致相分离技术，经平板膜浸入25℃凝固水浴进行相分离，再经无水乙醇萃取，烘干后得到聚丙烯聚氯乙烯复合微孔膜；
（5）将改性丙烯酸乳液用涂膜器均匀涂布在聚丙烯聚氯乙烯复合微孔膜表面，将其放在75℃烘箱烘烤3分钟，然后置于40℃恒温老化箱中老化24小时，最后切割成带状，即得。
本发明制成的绝缘包扎带，通过测试，产品的拉伸强度大于15牛顿/厘米，符合国家标准；取适量样品粘贴在试样板上时，以300毫米/分的速度滚压来回三次，存放30分钟，180°剥离强度达到国家标准。

Claims (2)

1.一种防水防霉增强的微孔散热绝缘包扎带，其特征在于，由下列重量份的原料制备制成：埃洛石纳米管1.5-1.6、硅烷偶联剂kh5700.75-0.77、去离子水适量、无水乙醇适量、十二烷基硫酸钠1.2-1.4、烷基酚聚氧乙烯醚1.4-1.5、丙烯酸丁酯55-60、丙烯酸异辛酯40-43、等规聚丙烯40-44、聚氯乙烯53-55、二亚苄基山梨糖醇3-4、邻苯二甲酸二辛酯适量、纳米二氧化硅5-6、单硬脂酸甘油酯3-4、聚二甲基硅氧烷2-3、2-(4－噻唑基)苯并咪唑0.9-1.1、钙锌稳定剂2-2.4、硬脂酸3-4。
2.根据权利要求1所述一种防水防霉增强的微孔散热绝缘包扎带，其特征在于，由以下具体步骤制成：
（1）将埃洛石中加入30-35倍量的无水乙醇中超声分散40-50分钟得到混悬液，然后加入与无水乙醇等量的去离子水以及硅烷偶联剂kh570，加热至70-75℃，搅拌反应24小时后将混合物以4000转/分的速度进行离心，并洗涤至中性，得到的产品在真空干燥箱中以90-100℃烘干，得到改性埃洛石纳米管；
（2）将改性埃洛石纳米管超声分散于80-85倍量的去离子水中，然后加入丙烯酸丁酯、丙烯酸异辛酯、十二烷基硫酸钠，在磁力搅拌机上搅拌均匀，然后升温至80-85℃，加入一半量的烷基酚聚氧乙烯醚，保温30-60分钟后继续加入剩余的烷基酚聚氧乙烯醚，升温至90-95℃，保温60-90分钟后冷却至室温，得到改性丙烯酸乳液；
（3）将纳米二氧化硅与单硬脂酸甘油酯、聚二甲基硅氧烷混合，放入球磨机中，加热至50-60℃球磨60-90分钟后出料送入双螺杆挤出机中，加入聚氯乙烯，控制挤出温度130-140℃，挤出造粒，得到防水增强聚氯乙烯母料；
（4）将聚氯乙烯、步骤（3）得到的防水增强聚氯乙烯母料混合后放入反应釜中，然后加入总量3.5-4倍量的邻苯二甲酸二辛酯以及其余剩余成分，在氮气保护条件下在180℃搅拌60-90分钟后继续保温2-3小时形成铸膜液，将铸膜液通过刮膜机制成平板膜，控制刮膜温度为180℃，最后通过热致相分离技术，经平板膜浸入25℃凝固水浴进行相分离，再经无水乙醇萃取，烘干后得到聚丙烯聚氯乙烯复合微孔膜；
（5）将改性丙烯酸乳液用涂膜器均匀涂布在聚丙烯聚氯乙烯复合微孔膜表面，将其放在75-80℃烘箱烘烤3-4分钟，然后置于40℃恒温老化箱中老化24小时，最后切割成带状，即得。
CN201610473205.0A 2016-06-24 2016-06-24 一种防水防霉增强的微孔散热绝缘包扎带 Pending CN106118524A (zh)