CN104531315A - 一种碳钢材料防锈油 - Google Patents
一种碳钢材料防锈油 Download PDFInfo
- Publication number
- CN104531315A CN104531315A CN201410745681.4A CN201410745681A CN104531315A CN 104531315 A CN104531315 A CN 104531315A CN 201410745681 A CN201410745681 A CN 201410745681A CN 104531315 A CN104531315 A CN 104531315A
- Authority
- CN
- China
- Prior art keywords
- oil
- parts
- film forming
- uniformly mixed
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种碳钢材料防锈油,它是由下述重量份的原料组成的:烯基琥珀酸酐1-2、导热油90-100、柏油3-5、肉豆蔻酸钠皂4-7、苯钾酸钠1-2、戊二酸二甲酯1-2、椰油酸二乙醇酰胺0.4-1、顺丁烯二酸二丁酯1-2、异辛酸锰0.1-0.3、sp-80 1-2、亚磷酸三壬基苯酯2-4、磷酸二铵0.6-1、成膜机械油4-6,本发明加入的成膜机械油:季戊四醇油酸酯具有优异的润滑性、良好的表面成膜性,与十二碳醇酯共混改性,可以明显提高成品的成膜效果,降低成膜温度,加入的稀土镧离子可以与在金属基材表面发生吸氧腐蚀过程中产生的OH-产生不溶性络合物,减缓腐蚀的电极反应,起到很好的缓释效果。
Description
技术领域
本发明主要涉及润滑油领域,尤其涉及一种碳钢材料防锈油。
背景技术
腐蚀是使紧固件破坏的主要形式之一,对汽车、摩托车以及各种车辆、机械会造成很大的损失。据统计,每年由于金属腐蚀所造成的直接经济损失约占国民经济总产值的2-4%,金属在贮存、运输和使用过程中,由于受环境气氛中水汽、氧气、酸、碱、盐和碳化物等物质的影响,在一定的温度、湿度和时间延续的条件下,会发生物理、化学变化而发生锈蚀。金属的锈蚀,会造成金属的损失和金属零部件功能的衰退和丧失。金属锈蚀是由于金属跟潮湿的空气或电解质溶液接触,发生氧化反应造成的,因此需要不断提高防锈油的防锈效果,延长防锈油的保护时间,增强防锈的表面抗性,为降低损失作出努力。
发明内容
本发明目的就是提供一种碳钢材料防锈油。
本发明是通过以下技术方案实现的:
一种碳钢材料防锈油,其特征在于它是由下述重量份的原料组成的:
烯基琥珀酸酐1-2、导热油90-100、柏油3-5、肉豆蔻酸钠皂4-7、苯钾酸钠1-2、戊二酸二甲酯1-2、椰油酸二乙醇酰胺0.4-1、顺丁烯二酸二丁酯1-2、异辛酸锰0.1-0.3、sp-80 1-2、亚磷酸三壬基苯酯2-4、磷酸二铵0.6-1、成膜机械油4-6;
所述的成膜机械油是由下述重量份的原料组成的:
去离子水50-60、十二碳醇酯5-7、季戊四醇油酸酯2-3、交联剂TAIC 0.1-0.2、三乙醇胺油酸皂2-3、硝酸镧3-4、机械油90-100、磷酸二氢锌6-10、28%氨水40-50、硅烷偶联剂KH560 0.1-0.2;
取上述三乙醇胺油酸皂重量的20-30%,加入到季戊四醇油酸酯中,60-70℃下搅拌混合30-40分钟,得乳化油酸酯;
将十二碳醇酯加入到去离子水中,搅拌条件下依次加入乳化油酸酯、交联剂TAIC,在73-80℃下搅拌混合1-2小时,得成膜助剂;
将磷酸二氢锌加入到28%氨水中,搅拌混合6-10分钟;将硝酸镧与硅烷偶联剂KH560混合均匀后加入,搅拌均匀,得稀土氨液;
将剩余的三乙醇胺油酸皂加入到机械油中,搅拌均匀后加入上述成膜助剂、稀土氨液,120-125℃下保温反应20-30分钟,脱水,即得所述成膜机械油。
2、一种如权利要求1所述的碳钢材料防锈油的制备方法,其特征在于包括以下步骤:
(1)将磷酸二铵、苯钾酸钠、戊二酸二甲酯混合,60-70℃下保温搅拌5-10分钟,冷却至常温;
(2)将上述处理后的原料加入到反应釜中,加入导热油、柏油,在100-120℃下搅拌混合20-30分钟,加入亚磷酸三壬基苯酯,降低温度到80-90℃,脱水,搅拌混合2-3小时;
(3)将反应釜温度降低到50-60℃,加入剩余各原料,不断搅拌至常温,过滤出料。
本发明的优点是:
本发明加入的成膜机械油:季戊四醇油酸酯具有优异的润滑性、良好的表面成膜性,与十二碳醇酯共混改性,可以明显提高成品的成膜效果,降低成膜温度,加入的稀土镧离子可以与在金属基材表面发生吸氧腐蚀过程中产生的OH-产生不溶性络合物,减缓腐蚀的电极反应,起到很好的缓释效果。
本发明的防锈油采用导热油为基础油,与各原料复配使用,科学合理,可以有效提高防锈油与基材的结合力,提高抗剥离强度,碳钢材料经本发明处理后,其表面附有一层均质油相防锈层,能在潮湿环境下放置至少一年,保护效果持久。
具体实施方式
实施例1
一种碳钢材料防锈油,其特征在于它是由下述重量份(公斤)的原料组成的:
烯基琥珀酸酐2、导热油90-100、柏油5、肉豆蔻酸钠皂7、苯钾酸钠2、戊二酸二甲酯1、椰油酸二乙醇酰胺0.4、顺丁烯二酸二丁酯2、异辛酸锰0.3、sp-80 1、亚磷酸三壬基苯酯2、磷酸二铵0.6、成膜机械油6;
所述的成膜机械油是由下述重量份的原料组成的:
去离子水60、十二碳醇酯7、季戊四醇油酸酯3、交联剂TAIC 0.2、三乙醇胺油酸皂2、硝酸镧3、机械油90、磷酸二氢锌10、28%氨水50、硅烷偶联剂KH560 0.2;
取上述三乙醇胺油酸皂重量的30%,加入到季戊四醇油酸酯中,60-70℃下搅拌混合40分钟,得乳化油酸酯;
将十二碳醇酯加入到去离子水中,搅拌条件下依次加入乳化油酸酯、交联剂TAIC,在80℃下搅拌混合2小时,得成膜助剂;
将磷酸二氢锌加入到28%氨水中,搅拌混合10分钟;将硝酸镧与硅烷偶联剂KH560混合均匀后加入,搅拌均匀,得稀土氨液;
将剩余的三乙醇胺油酸皂加入到机械油中,搅拌均匀后加入上述成膜助剂、稀土氨液,125℃下保温反应30分钟,脱水,即得所述成膜机械油。
一种碳钢材料防锈油的制备方法,其特征在于包括以下步骤:
(1)将磷酸二铵、苯钾酸钠、戊二酸二甲酯混合,70℃下保温搅拌10分钟,冷却至常温;
(2)将上述处理后的原料加入到反应釜中,加入导热油、柏油,在120℃下搅拌混合30分钟,加入亚磷酸三壬基苯酯,降低温度到90℃,脱水,搅拌混合3小时;
(3)将反应釜温度降低到50℃,加入剩余各原料,不断搅拌至常温,过滤出料。
性能测试:
表观:无沉淀、无分层、无结晶物析出;
腐蚀试验(10#钢、100h、100℃):0级;
盐雾实验(10#钢 A级):7天;
湿热实验(10#钢 A级):20天;
低温附着性:合格。
Claims (2)
1.一种碳钢材料防锈油,其特征在于它是由下述重量份的原料组成的:
烯基琥珀酸酐1-2、导热油90-100、柏油3-5、肉豆蔻酸钠皂4-7、苯钾酸钠1-2、戊二酸二甲酯1-2、椰油酸二乙醇酰胺0.4-1、顺丁烯二酸二丁酯1-2、异辛酸锰0.1-0.3、sp-80 1-2、亚磷酸三壬基苯酯2-4、磷酸二铵0.6-1、成膜机械油4-6;
所述的成膜机械油是由下述重量份的原料组成的:
去离子水50-60、十二碳醇酯5-7、季戊四醇油酸酯2-3、交联剂TAIC 0.1-0.2、三乙醇胺油酸皂2-3、硝酸镧3-4、机械油90-100、磷酸二氢锌6-10、28%氨水40-50、硅烷偶联剂KH560 0.1-0.2;
取上述三乙醇胺油酸皂重量的20-30%,加入到季戊四醇油酸酯中,60-70℃下搅拌混合30-40分钟,得乳化油酸酯;
将十二碳醇酯加入到去离子水中,搅拌条件下依次加入乳化油酸酯、交联剂TAIC,在73-80℃下搅拌混合1-2小时,得成膜助剂;
将磷酸二氢锌加入到28%氨水中,搅拌混合6-10分钟;将硝酸镧与硅烷偶联剂KH560混合均匀后加入,搅拌均匀,得稀土氨液;
将剩余的三乙醇胺油酸皂加入到机械油中,搅拌均匀后加入上述成膜助剂、稀土氨液,120-125℃下保温反应20-30分钟,脱水,即得所述成膜机械油。
2.一种如权利要求1所述的碳钢材料防锈油的制备方法,其特征在于包括以下步骤:
(1)将磷酸二铵、苯钾酸钠、戊二酸二甲酯混合,60-70℃下保温搅拌5-10分钟,冷却至常温;
(2)将上述处理后的原料加入到反应釜中,加入导热油、柏油,在100-120℃下搅拌混合20-30分钟,加入亚磷酸三壬基苯酯,降低温度到80-90℃,脱水,搅拌混合2-3小时;
(3)将反应釜温度降低到50-60℃,加入剩余各原料,不断搅拌至常温,过滤出料。