CN104312672A - 一种金属防腐防锈油 - Google Patents
一种金属防腐防锈油 Download PDFInfo
- Publication number
- CN104312672A CN104312672A CN201410591522.3A CN201410591522A CN104312672A CN 104312672 A CN104312672 A CN 104312672A CN 201410591522 A CN201410591522 A CN 201410591522A CN 104312672 A CN104312672 A CN 104312672A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- corrosion
- minute
- rare earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金属防腐防锈油,它是由下述重量份的原料组成的:氮川三乙酸1-2、500sn基础油50-60、煤油10-15、乙二胺四乙酸铜二钠盐2-3、脂肪醇聚氧乙烯醚硫酸铵1-2、戊二酸二甲酯2-3、油酸异丁酯1-3、羊毛脂2-4、柠檬酸钾0.8-2、异十三醇聚氧乙烯醚0.1-2、二烷基对二苯酚0.4-1、磷酸氢二铵1-2、稀土缓蚀液压油12-20,本发明的防锈油中加入稀土防锈液压油;其中将聚环氧琥珀酸与磷酸盐混合,可以起到很好的协同作用,具有稳定的缓蚀功能;硅铝溶胶可以促进各物料间的相容性,改善成品的成膜效果;加入的稀土离子可以与在金属基材表面发生吸氧腐蚀过程中产生的OH-产生不溶性络合物,减缓腐蚀的电极反应,起到很好的缓释效果。
Description
技术领域
本发明主要涉及润滑油领域,尤其涉及一种金属防腐防锈油。
背景技术
金属在贮存、运输和使用过程中,由于受环境气氛中水汽、氧气、酸、碱、盐和碳化物等物质的影响,在一定的温度、湿度和时间延续的条件下,会发生物理、化学变化而发生锈蚀。金属的锈蚀,会造成金属的损失和金属零部件功能的衰退和丧失。金属锈蚀是由于金属跟潮湿的空气或电解质溶液接触,发生氧化反应造成的,腐蚀是使紧固件破坏的主要形式之一,对汽车、摩托车以及各种车辆、机械会造成很大的损失。据统计,每年由于金属腐蚀所造成的直接经济损失约占国民经济总产值的2%~4%,为避免锈蚀、减少损失,人们采用了各种各样的方法,用防锈油脂来保护基材是最普遍的方法,而如今的防锈油存在的问题也很多,比如耐腐蚀、耐久性、粘着性、不好,容易出现变硬、脱落、开裂的现象,因此需要不断提高防锈油的综合质量,达到更好的防锈缓蚀效果。
发明内容
本发明目的就是提供一种金属防腐防锈油。
本发明是通过以下技术方案实现的:
一种金属防腐防锈油,它是由下述重量份的原料组成的:
氮川三乙酸1-2、500sn基础油50-60、煤油10-15、乙二胺四乙酸铜二钠盐2-3、脂肪醇聚氧乙烯醚硫酸铵1-2、戊二酸二甲酯2-3、油酸异丁酯1-3、羊毛脂2-4、柠檬酸钾0.8-2、异十三醇聚氧乙烯醚0.1-2、二烷基对二苯酚0.4-1、磷酸氢二铵1-2、稀土缓蚀液压油12-20;
所述的稀土缓蚀液压油是由下述重量份的原料组成的:
聚环氧琥珀酸2-3、正硅酸四乙酯3-5、磷酸二氢钠1-2、十二烷基硫酸钠0.8-1、氧化铝0.7-2、十二烯基丁二酸10-15、液压油100-110、去离子水70-80、氢氧化钠3-5、硝酸铈3-4、Span80 0.5-1;
将磷酸二氢钠与上述去离子水重量的16-20%混合,搅拌均匀后加入聚环氧琥珀酸,充分混合,得酸化缓蚀剂;
取剩余去离子水重量的40-50%与十二烷基硫酸钠混合,搅拌均匀,加入正硅酸四乙酯、氧化铝,搅拌条件下滴加氨水,调节PH为7.8-9,搅拌均匀,得硅铝溶胶;
将十二烯基丁二酸与氢氧化钠混合,搅拌均匀后加入到剩余的去离子水中,充分混合,加入硝酸铈,60-65℃下保温搅拌20-30分钟,得稀土分散液;
将Span80加入到液压油中,搅拌均匀后加入上述稀土分散液、酸化缓蚀剂、硅铝溶胶,80-90℃下保温反应20-30分钟,脱水,即得所述稀土缓蚀液压油。
2、一种如权利要求1所述的金属防腐防锈油的制备方法,其特征在于包括以下步骤:
(1)将羊毛脂与油酸异丁酯混合,50-60℃下保温搅拌6-10分钟,加入到煤油中,加入异十三醇聚氧乙烯醚,搅拌混合20-30分钟;
(2)将氮川三乙酸、柠檬酸钾混合,搅拌均匀后加入戊二酸二甲酯、磷酸氢二铵,70-80℃下保温搅拌10-20分钟;
(3)将上述处理后的各原料混合,加入到反应釜中,充分搅拌均匀,加入500sn基础油,搅拌混合20-30分钟,脱水,控制反应釜温度为80-85℃,搅拌混合2-3小时;
(4)将反应釜温度降低到50-60℃,加入剩余各原料,不断搅拌至常温,过滤出料。
本发明的优点是:
本发明的防锈油中加入稀土防锈液压油;其中将聚环氧琥珀酸与磷酸盐混合,可以起到很好的协同作用,具有稳定的缓蚀功能;硅铝溶胶可以促进各物料间的相容性,改善成品的成膜效果;加入的稀土离子可以与在金属基材表面发生吸氧腐蚀过程中产生的OH-产生不溶性络合物,减缓腐蚀的电极反应,起到很好的缓释效果。
本发明防锈油,实现了低耗能、低排放、无环境污染,稳定性及防护性好等特点,具有附着力强、防腐蚀性能好、物理性能好、使用方便的特点。
具体实施方式
实施例1
一种金属防腐防锈油,其特征在于它是由下述重量份(公斤)的原料组成的:
氮川三乙酸2、500sn基础油60、煤油15、乙二胺四乙酸铜二钠盐3、脂肪醇聚氧乙烯醚硫酸铵1、戊二酸二甲酯3、油酸异丁酯1、羊毛脂2、柠檬酸钾0.8、异十三醇聚氧乙烯醚0.1、二烷基对二苯酚0.4、磷酸氢二铵2、稀土缓蚀液压油20;
所述的稀土缓蚀液压油是由下述重量份的原料组成的:
聚环氧琥珀酸3、正硅酸四乙酯5、磷酸二氢钠2、十二烷基硫酸钠0.8、氧化铝0.7、十二烯基丁二酸15、液压油110、去离子水80、氢氧化钠5、硝酸铈3、Span80 0.5;
将磷酸二氢钠与上述去离子水重量的20%混合,搅拌均匀后加入聚环氧琥珀酸,充分混合,得酸化缓蚀剂;
取剩余去离子水重量的50%与十二烷基硫酸钠混合,搅拌均匀,加入正硅酸四乙酯、氧化铝,搅拌条件下滴加氨水,调节PH为7.8,搅拌均匀,得硅铝溶胶;
将十二烯基丁二酸与氢氧化钠混合,搅拌均匀后加入到剩余的去离子水中,充分混合,加入硝酸铈,65℃下保温搅拌30分钟,得稀土分散液;
将Span80加入到液压油中,搅拌均匀后加入上述稀土分散液、酸化缓蚀剂、硅铝溶胶,90℃下保温反应30分钟,脱水,即得所述稀土缓蚀液压油。
一种金属防腐防锈油的制备方法,其特征在于包括以下步骤:
(1)将羊毛脂与油酸异丁酯混合,60℃下保温搅拌10分钟,加入到煤油中,加入异十三醇聚氧乙烯醚,搅拌混合30分钟;
(2)将氮川三乙酸、柠檬酸钾混合,搅拌均匀后加入戊二酸二甲酯、磷酸氢二铵,70-80℃下保温搅拌20分钟;
(3)将上述处理后的各原料混合,加入到反应釜中,充分搅拌均匀,加入500sn基础油,搅拌混合30分钟,脱水,控制反应釜温度为85℃,搅拌混合2-3小时;
(4)将反应釜温度降低到60℃,加入剩余各原料,不断搅拌至常温,过滤出料。
性能测试:
表观:无沉淀、无分层、无结晶物析出;
腐蚀试验(10#钢、100h、100℃):0级;
盐雾实验(10#钢 A级):7天;
湿热实验(10#钢 A级):20天;
低温附着性:合格。
Claims (2)
1.一种金属防腐防锈油,其特征在于它是由下述重量份的原料组成的:
氮川三乙酸1-2、500sn基础油50-60、煤油10-15、乙二胺四乙酸铜二钠盐2-3、脂肪醇聚氧乙烯醚硫酸铵1-2、戊二酸二甲酯2-3、油酸异丁酯1-3、羊毛脂2-4、柠檬酸钾0.8-2、异十三醇聚氧乙烯醚0.1-2、二烷基对二苯酚0.4-1、磷酸氢二铵1-2、稀土缓蚀液压油12-20;
所述的稀土缓蚀液压油是由下述重量份的原料组成的:
聚环氧琥珀酸2-3、正硅酸四乙酯3-5、磷酸二氢钠1-2、十二烷基硫酸钠0.8-1、氧化铝0.7-2、十二烯基丁二酸10-15、液压油100-110、去离子水70-80、氢氧化钠3-5、硝酸铈3-4、Span80 0.5-1;
将磷酸二氢钠与上述去离子水重量的16-20%混合,搅拌均匀后加入聚环氧琥珀酸,充分混合,得酸化缓蚀剂;
取剩余去离子水重量的40-50%与十二烷基硫酸钠混合,搅拌均匀,加入正硅酸四乙酯、氧化铝,搅拌条件下滴加氨水,调节PH为7.8-9,搅拌均匀,得硅铝溶胶;
将十二烯基丁二酸与氢氧化钠混合,搅拌均匀后加入到剩余的去离子水中,充分混合,加入硝酸铈,60-65℃下保温搅拌20-30分钟,得稀土分散液;
将Span80加入到液压油中,搅拌均匀后加入上述稀土分散液、酸化缓蚀剂、硅铝溶胶,80-90℃下保温反应20-30分钟,脱水,即得所述稀土缓蚀液压油。
2.一种如权利要求1所述的金属防腐防锈油的制备方法,其特征在于包括以下步骤:
(1)将羊毛脂与油酸异丁酯混合,50-60℃下保温搅拌6-10分钟,加入到煤油中,加入异十三醇聚氧乙烯醚,搅拌混合20-30分钟;
(2)将氮川三乙酸、柠檬酸钾混合,搅拌均匀后加入戊二酸二甲酯、磷酸氢二铵,70-80℃下保温搅拌10-20分钟;
(3)将上述处理后的各原料混合,加入到反应釜中,充分搅拌均匀,加入500sn基础油,搅拌混合20-30分钟,脱水,控制反应釜温度为80-85℃,搅拌混合2-3小时;
(4)将反应釜温度降低到50-60℃,加入剩余各原料,不断搅拌至常温,过滤出料。