CN104496560B - The preparation method of the acupuncture needle shape gloss crystalline ceramics art work - Google Patents
The preparation method of the acupuncture needle shape gloss crystalline ceramics art work Download PDFInfo
- Publication number
- CN104496560B CN104496560B CN201410731864.0A CN201410731864A CN104496560B CN 104496560 B CN104496560 B CN 104496560B CN 201410731864 A CN201410731864 A CN 201410731864A CN 104496560 B CN104496560 B CN 104496560B
- Authority
- CN
- China
- Prior art keywords
- preparation
- acupuncture needle
- needle shape
- art work
- crystalline ceramics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The preparation method who the present invention relates to a kind of acupuncture needle shape gloss crystalline ceramics art work, comprises colour former preparation process, glaze preparation process and ceramics preparation process. Prepared ceramics glaze is flavous metallic luster, in glaze layer, has golden flower to separate out, and there is flavous spicule at golden flower edge, and exquisite abnormal, decoration degree is high.
Description
Technical field
The present invention relates to the preparation method of ceramics, more specifically, relate to a kind of preparation method of the acupuncture needle shape gloss crystalline ceramics art work.
Background technology
Ceramics, as the very important part in traditional Chinese culture field, is of long standing and well established, of extensive knowledge and profound scholarship. Along with economic development, handicraft miscellaneous constantly emerges. In the face of this present situation, want to allow time-honored ceramics technique shine new life, be just necessary reform, the fashion element of modern society is fused in ceramics, make its public aesthetic view that more meets society and grade, more can cater to present youthful taste.
Summary of the invention
The preparation method who the object of this invention is to provide a kind of acupuncture needle shape gloss crystalline ceramics art work, the ceramics exquisiteness that it makes is attractive in appearance, has decorative value.
The object of the invention is achieved by the following technical programs:
The preparation method that a kind of acupuncture needle shape gloss crystalline ceramics art work is provided, comprises the following steps:
Step 1: the preparation of colour former;
Be manganese oxide 58.5% by mass fraction, cupric oxide 13.5%, nickel oxide 6.5%, titanium oxide 11%, zinc oxide 10.5% takes, and mixes levigately, obtains colour former;
Step 2: the preparation of glaze;
Be colour former 12% by mass fraction, quartz 30.5%, Datong District's soil 14%, glass dust 20%, plumbous boron frit 7%, vanadic anhydride 9%, spinelle 7.5% takes, and to expect: ball: the ratio of water=1:2:0.7 enters ball milling 25h, then adds 0.5% sodium phosphate trimer, cross 250 mesh sieves and tail over 0.1%, obtain glaze;
Step 3: the preparation of the acupuncture needle shape gloss crystalline ceramics art work;
Glazing on the base substrate of ceramics, enters kiln and calcines 10h the temperature range of 1250～1300 DEG C, then, at 1050～1120 DEG C of insulation 2h, obtains the acupuncture needle shape gloss crystalline ceramics art work.
Preferably, the enameling method in step 3 is for drenching glaze or soaking glaze.
Preferably, the glazing thickness in step 3 is 0.8～1mm.
Add colour former to the larger effect of glaze surface tension, be easy to the generation of crystal and grow up, after crystal development is complete, be protruding flower shape, there is the object of similar acupuncture needle shape at flower shape edge, and third dimension is extremely strong.
Compared with prior art, the present invention has following beneficial effect:
The preparation method who the invention provides a kind of acupuncture needle shape gloss crystalline ceramics art work, the ceramics exquisiteness that it makes is attractive in appearance, has decorative value.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
The present embodiment discloses a kind of preparation method of the acupuncture needle shape gloss crystalline ceramics art work, comprises the following steps:
Step 1: the preparation of colour former;
Be manganese oxide 58.5% by mass fraction, cupric oxide 13.5%, nickel oxide 6.5%, titanium oxide 11%, zinc oxide 10.5% takes, and mixes levigately, obtains colour former;
Step 2: the preparation of glaze;
Be colour former 12% by mass fraction, quartz 30.5%, Datong District's soil 14%, glass dust 20%, plumbous boron frit 7%, vanadic anhydride 9%, spinelle 7.5% takes, and to expect: ball: the ratio of water=1:2:0.7 enters ball milling 25h, then adds 0.5% sodium phosphate trimer, cross 250 mesh sieves and tail over 0.1%, obtain glaze;
Step 3: the preparation of the acupuncture needle shape gloss crystalline ceramics art work;
On the base substrate of ceramics, drench glaze, glazing thickness is 0.9mm, enters kiln and calcines 10h the temperature range of 1280 DEG C, then, at 1050 DEG C of insulation 2h, obtains the acupuncture needle shape gloss crystalline ceramics art work.
Embodiment 2
The present embodiment discloses a kind of preparation method of the acupuncture needle shape gloss crystalline ceramics art work, comprises the following steps:
Step 1: the preparation of colour former;
Be manganese oxide 58.5% by mass fraction, cupric oxide 13.5%, nickel oxide 6.5%, titanium oxide 11%, zinc oxide 10.5% takes, and mixes levigately, obtains colour former;
Step 2: the preparation of glaze;
Be colour former 12% by mass fraction, quartz 30.5%, Datong District's soil 14%, glass dust 20%, plumbous boron frit 7%, vanadic anhydride 9%, spinelle 7.5% takes, and to expect: ball: the ratio of water=1:2:0.7 enters ball milling 25h, then adds 0.5% sodium phosphate trimer, cross 250 mesh sieves and tail over 0.1%, obtain glaze;
Step 3: the preparation of the acupuncture needle shape gloss crystalline ceramics art work;
On the base substrate of ceramics, drench glaze, glazing thickness is 1mm, enters kiln and calcines 10h the temperature range of 1300 DEG C, then, at 1100 DEG C of insulation 2h, obtains the acupuncture needle shape gloss crystalline ceramics art work.
Embodiment 3
The present embodiment discloses a kind of preparation method of the acupuncture needle shape gloss crystalline ceramics art work, comprises the following steps:
Step 1: the preparation of colour former;
Be manganese oxide 58.5% by mass fraction, cupric oxide 13.5%, nickel oxide 6.5%, titanium oxide 11%, zinc oxide 10.5% takes, and mixes levigately, obtains colour former;
Step 2: the preparation of glaze;
Be colour former 12% by mass fraction, quartz 30.5%, Datong District's soil 14%, glass dust 20%, plumbous boron frit 7%, vanadic anhydride 9%, spinelle 7.5% takes, and to expect: ball: the ratio of water=1:2:0.7 enters ball milling 25h, then adds 0.5% sodium phosphate trimer, cross 250 mesh sieves and tail over 0.1%, obtain glaze;
Step 3: the preparation of the acupuncture needle shape gloss crystalline ceramics art work;
On the base substrate of ceramics, drench glaze, glazing thickness is 0.9mm, enters kiln and calcines 10h the temperature range of 1260 DEG C, then, at 1060 DEG C of insulation 2h, obtains the acupuncture needle shape gloss crystalline ceramics art work.
The prepared acupuncture needle shape of above-mentioned 1～3 embodiment gloss crystalline ceramics art work, its glaze is flavous metallic luster, in glaze layer, has golden flower to separate out, and golden flower surface is partially bright, and there is flavous spicule at golden flower edge, and exquisite abnormal, decoration degree is high.
Claims (3)
1. a preparation method for the acupuncture needle shape gloss crystalline ceramics art work, is characterized in that, comprises the following steps:
Step 1: the preparation of colour former;
Be manganese oxide 58.5% by mass fraction, cupric oxide 13.5%, nickel oxide 6.5%, titanium oxide 11%, zinc oxide 10.5% takes, and mixes levigately, obtains colour former;
Step 2: the preparation of glaze;
Be colour former 12% by mass fraction, quartz 30.5%, Datong District's soil 14%, glass dust 20%, plumbous boron frit 7%, vanadic anhydride 9%, spinelle 7.5% takes, and to expect: ball: the ratio of water=1:2:0.7 is put into grinding in ball grinder 25h, then adds 0.5% sodium phosphate trimer, cross 250 mesh sieves and tail over 0.1%, obtain glaze;
Step 3: the preparation of the acupuncture needle shape gloss crystalline ceramics art work;
Glazing on the base substrate of ceramics, enters kiln and calcines 10h the temperature range of 1250～1300 DEG C, then, at 1050～1120 DEG C of insulation 2h, obtains the acupuncture needle shape gloss crystalline ceramics art work.
2. the preparation method of the acupuncture needle shape gloss crystalline ceramics art work according to claim 1, is characterized in that, the enameling method in step 3 is for drenching glaze or soaking glaze.
3. the preparation method of the acupuncture needle shape gloss crystalline ceramics art work according to claim 1, is characterized in that, the glazing thickness in step 3 is 0.8～1mm.